CN105062285B - A kind of one-component glaze paint wall finiss and preparation method thereof - Google Patents
A kind of one-component glaze paint wall finiss and preparation method thereof Download PDFInfo
- Publication number
- CN105062285B CN105062285B CN201510514772.1A CN201510514772A CN105062285B CN 105062285 B CN105062285 B CN 105062285B CN 201510514772 A CN201510514772 A CN 201510514772A CN 105062285 B CN105062285 B CN 105062285B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- glaze paint
- wall finiss
- paint wall
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of one-component glaze paint wall finiss and preparation method thereof, it is desirable to provide a kind of good decorative property, economic, environmental protection, but also with good resistance to soiling, the glaze finishing coat of fungus-resistant and preparation method thereof；Its technical solution is such：The one-component glaze paint wall finiss is made of following components：Pulp stage is by 10 25 mass parts of deionized water, 20 50 mass parts of filler, No. 1 0.25 3 mass parts of auxiliary agent composition；Letdown phase is by 15 25 mass parts of water-based acrylic resin, 10 25 mass parts of waterborne polyurethane resin, the mass parts composition of No. 2 auxiliary agents≤2；Building coating technical field.
Description
Technical field
The present invention relates to building coating field, there is provided a kind of preparation method of one-component glaze paint wall finiss.
Technical background
As the improvement of people's living standards, people increasingly focus on the quality of life, the requirement to living environment is also got over
Come higher, wall finiss also receives much concern as the important component of a household.The rhythm of life is getting faster, and is mixed in reinforcing bar
Inside the city for coagulating soil, what we faced all day is the pressure of live and work, we are to spend indoors at about 80% time,
The cleaning of indoor environment affects our mood, and metope largely our visual sensory of left and right.We see
It has been used to ice-cold ceramic tile metope, has also detested that dusty emulsion paint wall.People expect a kind of resistance to soiling for possessing ceramic tile, at the same time
Metope ice-cold not as ceramic tile again,
The glaze finishing coat occurred on the market is mostly the wall finiss of two-component, and two-component cures certain paint film for providing densification and reaches
To good resistant effect, but often price is higher, and construction is cumbersome, cannot be widely applied.The glaze of the present invention
Finishing coat is developed using these factors as starting point, will be liked deeply by masses.
The content of the invention
It is an object of the invention to provide a kind of good decorative property, economic, environmental protection, but also with good resistance to soiling, mould proof suppression
Glaze finishing coat of bacterium and preparation method thereof.
For this reason, technical method provided by the invention is such：
A kind of one-component glaze paint wall finiss, the finishing coat are made of following components：
Pulp stage
Deionized water 10-25 mass parts
Filler 20-50 mass parts
No. 1 auxiliary agent 0.25-3 mass parts
Letdown phase
Water-based acrylic resin 15-25 mass parts
Waterborne polyurethane resin 10-25 mass parts
The mass parts of No. 2 auxiliary agents≤2.
Further, above-mentioned one-component glaze paint wall finiss, described No. 1 auxiliary agent by 0.1-1.5 mass parts dispersants,
0.1-1 mass parts wetting agents, 0.05-0.5 mass parts defoamer composition.
Further, above-mentioned one-component glaze paint wall finiss, the filler is by 4-15 mass parts calcium carbonate, 15-30 matter
Measure part titanium dioxide, 1-5 mass parts calcined kaolin composition.
Further, above-mentioned one-component glaze paint wall finiss, described No. 2 auxiliary agents are by 1-3 mass parts coalescents, 1-3
Mass parts PG, 0.5-1.5 mass parts thickener, 0.1-0.3 mass parts defoamer composition.
Further, above-mentioned one-component glaze paint wall finiss, the water-based acrylic resin are Ahmedabad richness company
" RS-2806 " pure-acrylic emulsion.
Further, above-mentioned one-component glaze paint wall finiss, the preferred Guangzhou production association high score of the waterborne polyurethane resin
" L-2967 " of sub- Co., Ltd.
The latter solution of the present invention is such：The method for preparing above-mentioned component glaze paint wall finiss, includes successively
Following step：
(1) raw material of pulp stage described in claim 1 is slowly added in Scattered Kettle by pulp stage successively while stirring,
60~120min is stirred in 1000~1200rpm, so that slurry fineness is less than 30um；
(2) raw material described in letdown phase described in claim 1 is slowly added to step (1) pulp stage Scattered Kettle successively
In, 30~60min is stirred with 600~800rpm, filtering, that is, obtain one-component glaze paint wall finiss finished product.
Compared with prior art, technical method provided by the invention has the following advantages that：
1st, the water-based acrylic resin in technical solution provided by the invention has excellent weatherability and hardness, water-based poly-
Urethane resin has the advantages that pliability is good, adhesive force is good, by preferably two kinds of good resins of compatibility it is reasonably combined, comprehensive two
The advantages of kind resin, then the rationally ratio of adjustment resin and color stuffing, make the coating of preparation form fine and close thing after brushing curing
Manage paint film.
2nd, one-component glaze paint wall finiss provided by the invention is environmentally friendly, high resistant, and decorative effect is excellent, scrubbing resistance, fungus-resistant,
It can meet finishing requirements, it can be widely applied to the fields such as house ornamentation, underground parking, quick hotel, office space, so as to give
People provide the living environment of safety clean.
3rd, one-component glaze paint wall finiss provided by the invention, which possesses good alkali resistance, can accomplish that bottom surface is unified, twice one-tenth
Type, greatly improves construction efficiency.
Embodiment
With reference to embodiment, the claim of the present invention is described in further details, but is not formed to this
Any restrictions of invention, the modification of anyone limited number of time made in the claims in the present invention protection domain, still in the present invention
Claims within.
Embodiment 1
Pulp stage
It is scattered by raw material input Scattered Kettle, being stirred with 1200rpm, it is less than 30um to slurry fineness, normally
Scattered 60min, material are added when disperseing.
Letdown phase
Above-mentioned letdown phase component is put into foregoing pulp stage component, and reduces mixing speed to 600rpm, stirring
Scattered 60min, filtering, packaging can obtain 100kg glaze paint wall finisses.
The water of first pass addition about 10% or so before brushing, effectively scattered more than 2min, is brushed to processed good putty
On wall, it is to be dried 4~6 it is small when, then brush second time, the water of second time addition about 5% or so, it is to be dried after up to decorative effect
It is good, scrubbing resistance, the mercerising one-component glaze paint wall finiss of fungus-resistant.
Embodiment 2
Pulp stage
It is scattered by raw material input Scattered Kettle, being stirred with 1200rpm, it is less than 30um to slurry fineness, normally
Scattered 60min, material are added when disperseing.
Letdown phase
Above-mentioned letdown phase component is put into foregoing pulp stage component, and reduces mixing speed to 600rpm, stirring
Scattered 60min, filtering, packaging can obtain 100kg glaze paint wall finisses.
The water of first pass addition about 10% or so before brushing, effectively scattered more than 2min, is brushed to processed good putty
On wall, it is to be dried 4~6 it is small when, then brush second time, the water of second time addition about 5% or so, it is to be dried after up to decorative effect
It is good, scrubbing resistance, the shell light one-component glaze paint wall finiss of fungus-resistant.
Embodiment 3
Pulp stage
It is scattered by raw material input Scattered Kettle, being stirred with 1200rpm, it is less than 30um to slurry fineness, normally
Scattered 60min, material are added when disperseing.
Letdown phase
Above-mentioned letdown phase component is put into foregoing pulp stage component, and reduces mixing speed to 600rpm, stirring
Scattered 60min, filtering, packaging can obtain 100kg glaze paint wall finisses.
The water of first pass addition about 10% or so before brushing, effectively scattered more than 2min, is brushed to processed good putty
On wall, it is to be dried 4~6 it is small when, then brush second time, the water of second time addition about 5% or so, it is to be dried after up to decorative effect
It is good, scrubbing resistance, the matt one-component glaze paint wall finiss of fungus-resistant.
Effect example 1
The mercerising type one-component glazing type material of the embodiment of the present invention 1 is subjected to decoration construction to new wall, brushes wall finiss
Scrub resistance and resistance to soiling are fine after curing, only need to gently wipe and spot is completely eliminated.
Effect example 2
Fungus-resistant detection is carried out to the one-component glaze paint wall finiss, it was confirmed that the wall finiss has good fungus-resistant to imitate
Fruit.Testing result is as follows：
Table 1：Mould proof experimental result
Above-described embodiment is the preferable embodiment of the present invention, but embodiments of the present invention and from above-described embodiment
Limitation, other any Spirit Essences without departing from the present invention with made under principle change, modification, replacement, combine, simplification,
Equivalent substitute mode is should be, is included within protection scope of the present invention.
Claims (2)
1. a kind of one-component glaze paint wall finiss, it is characterised in that be made of following components：
Pulp stage
Deionized water 10-25 mass parts；
Filler 20-50 mass parts；
No. 1 auxiliary agent 0.25-3 mass parts；
Letdown phase
Water-based acrylic resin 15-25 mass parts；
Waterborne polyurethane resin 10-25 mass parts；
No. 2 auxiliary agent 0.5-3 mass parts；
No. 1 auxiliary agent is by 0.1-1.5 mass parts dispersants, 0.1-1 mass parts wetting agents, 0.05-0.5 mass parts defoamers
Composition；
The filler is made of 4-15 parts of mass parts calcium carbonate, 15-30 mass parts titanium dioxide, 1-5 mass parts calcined kaolins；
No. 2 auxiliary agents are by 1-3 mass parts coalescents, 1-3 mass parts PG, 0.5-1.5 mass parts thickeners, 0.1-0.3
Mass parts defoamer forms；
The waterborne polyurethane resin is the L-2967 of Guangzhou Chan Xie macromolecules Co., Ltd；
The water-based acrylic resin is " RS-2806 " pure-acrylic emulsion of Ahmedabad richness company.
2. prepare the method for the one-component glaze paint wall finiss described in claim 1, it is characterised in that comprise the following steps successively：
(1) raw material of pulp stage described in claim 1 is slowly added in Scattered Kettle by pulp stage successively while stirring, in
1000~1200rpm stirs 60~120min, so that slurry fineness is less than 30 μm；
(2) raw material described in letdown phase described in claim 1 is slowly added in step (1) pulp stage Scattered Kettle successively,
30~60min is stirred with 600~800rpm, filtering, that is, obtain one-component glaze paint wall finiss finished product.