CN109181544A - A kind of manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion - Google Patents
A kind of manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion Download PDFInfo
- Publication number
- CN109181544A CN109181544A CN201810922307.5A CN201810922307A CN109181544A CN 109181544 A CN109181544 A CN 109181544A CN 201810922307 A CN201810922307 A CN 201810922307A CN 109181544 A CN109181544 A CN 109181544A
- Authority
- CN
- China
- Prior art keywords
- proportion
- parts
- ordor removing
- agent
- negative ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacturing methods of the net aldehyde skin texture wall film slurry of water negative ion, successively deionized water under stirring, the antifreeze wetting agent of ordor removing, the antifreeze dispersing agent of ordor removing, first part of composite anti-foaming agent, conch meal, rutile titanium white powder, negative ion powder, higher boiling ordor removing film forming agent, ordor removing removes aldehyde lotion, full ordor removing pure-acrylic emulsion without ammonia PH regulator, inorganic thickening agent, second part of composite anti-foaming agent, ordor removing environment-friendly composite anticorrosive mildewproof algaecide are added into dispersion cylinder, can effectively reduce the penetrating odor and VOC content of skin texture wall film slurry.
Description
Technical field
The present invention relates to a kind of manufacturing methods of the net aldehyde skin texture wall film slurry of water negative ion.
Background technique
Skin texture wall film starches solidifiable and forms skin texture wall film, is decorative material for wall surface emerging at present, due to its plasticity
By force, metope can be made to show unique stereoscopic effect, makes the more aobvious fashion of metope, beautiful, so that it be made to receive the majority of consumers
Welcome.But the ordor removing effect and VOC content of skin texture wall film can not fully meet customer demand.
Therefore, it is necessary to be further improved.
Summary of the invention
It is an object of the invention to overcome above-mentioned the shortcomings of the prior art, and provide a kind of net aldehyde flesh of water negative ion
The manufacturing method for managing wall film slurry can effectively reduce the penetrating odor and VOC content of skin texture wall film slurry.
The object of the present invention is achieved like this:
A kind of manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion, made of following steps；
Step 1: ingredient according to the weight ratio:
Except 15-25 parts of aldehyde lotion,
Full 15-20 parts of ordor removing pure-acrylic emulsion,
15-20 parts of conch meal,
20-25 parts of rutile titanium white powder,
1-1.5 parts of negative ion powder,
Antifreeze dispersing agent 0.25-0.35 parts of ordor removing,
Antifreeze wetting agent 0.18-0.22 parts of ordor removing,
0.3-0.5 parts of composite anti-foaming agent,
0.7-1 parts of inorganic thickening agent,
Ordor removing without 0.08-0.12 parts of ammonia PH regulator,
2.3-2.8 parts of higher boiling ordor removing film forming agent,
0.3-0.5 parts of anticorrosive mildewproof algaecide of ordor removing environment-friendly composite,
13-18 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing is antifreeze
Dispersing agent, first part of composite anti-foaming agent, conch meal, rutile titanium white powder, negative ion powder, higher boiling ordor removing film forming agent, ordor removing without
Ammonia PH regulator removes aldehyde lotion, full ordor removing pure-acrylic emulsion, inorganic thickening agent, second part of composite anti-foaming agent, ordor removing environment-friendly composite
Anticorrosive mildewproof algaecide；
Step 3: uniform with high-speed stirred on dispersion machine, the net aldehyde skin texture wall film slurry of water negative ion to obtain 100 parts.
The proportion of ionized water in the step 2 is 17.19 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.19 part, ordor removing
The proportion of antifreeze dispersing agent is 0.27 part, and the proportion of first part of composite anti-foaming agent is 0.16 part, and the proportion of conch meal conch meal is
18 parts, the proportion of rutile titanium white powder is 24.6 parts, and the proportion of negative ion powder is 1.09 parts, the proportion of higher boiling ordor removing film forming agent
It is 2.5 parts, proportion of the ordor removing without ammonia PH regulator is 0.08 part, except the proportion of aldehyde lotion is 16 parts, full ordor removing pure-acrylic emulsion
Proportion is 18.5 parts, and the proportion of inorganic thickening agent is 0.78 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, ordor removing environmental protection
The proportion of composite anti-corrosion mildew and algae agent is 0.44 part.
The proportion of ionized water in the step 2 is 16 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, and ordor removing is antifreeze
The proportion of dispersing agent is 0.29 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 18.7
Part, the proportion of rutile titanium white powder is 23.34 parts, and the proportion of negative ion powder is 1.5 parts, and the proportion of higher boiling ordor removing film forming agent is
2.4 parts, proportion of the ordor removing without ammonia PH regulator is 0.09 part, except the proportion of aldehyde lotion is 15.87 parts, full ordor removing pure-acrylic emulsion
Proportion is 20 parts, and the proportion of inorganic thickening agent is 0.81 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, and ordor removing environmental protection is multiple
The proportion of mould assembly anticorrosive mildewproof algaecide is 0.4 part.
The proportion of ionized water in the step 2 is 15 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, and ordor removing is antifreeze
The proportion of dispersing agent is 0.3 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 16.25
Part, the proportion of rutile titanium white powder is 25 parts, and the proportion of negative ion powder is 1 part, and the proportion of higher boiling ordor removing film forming agent is 2.5
Part, proportion of the ordor removing without ammonia PH regulator is 0.1 part, and except the proportion of aldehyde lotion is 20 parts, the proportion of full ordor removing pure-acrylic emulsion is
18 parts, the proportion of inorganic thickening agent is 0.80 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, and ordor removing environment-friendly composite is anti-
The proportion of rotten mildew and algae agent is 0.45 part.
The proportion of ionized water in the step 2 is 14.28 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.21 part, ordor removing
The proportion of antifreeze dispersing agent is 0.33 part, and the proportion of first part of composite anti-foaming agent is 0.17 part, and the proportion of conch meal conch meal is
19 parts, the proportion of rutile titanium white powder is 23.58 parts, and the proportion of negative ion powder is 1 part, and the proportion of higher boiling ordor removing film forming agent is
2.3 parts, proportion of the ordor removing without ammonia PH regulator is 0.11 part, and except the proportion of aldehyde lotion is 22 parts, full ordor removing pure-acrylic emulsion is matched
Than being 15.5 parts, the proportion of inorganic thickening agent is 0.87 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, and ordor removing environmental protection is multiple
The proportion of mould assembly anticorrosive mildewproof algaecide is 0.35 part.
The proportion of ionized water in the step 2 is 16.11 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.22 part, ordor removing
The proportion of antifreeze dispersing agent is 0.35 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 18
Part, the proportion of rutile titanium white powder is 18.5 parts, and the proportion of negative ion powder is 1.4 parts, and the proportion of higher boiling ordor removing film forming agent is
2.80 parts, proportion of the ordor removing without ammonia PH regulator is 0.12 part, except the proportion of aldehyde lotion is 24.5 parts, full ordor removing pure-acrylic emulsion
Proportion is 16 parts, and the proportion of inorganic thickening agent is 1 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, ordor removing environment-friendly composite
The proportion of anticorrosive mildewproof algaecide is 0.5 part.
The proportion of ionized water in the step 2 is 17.9 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.18 part, ordor removing
The proportion of antifreeze dispersing agent is 0.25 part, and the proportion of first part of composite anti-foaming agent is 0.1 part, and the proportion of conch meal conch meal is
15.97 parts, the proportion of rutile titanium white powder is 22.2 parts, and the proportion of negative ion powder is 1 part, the proportion of higher boiling ordor removing film forming agent
It is 2.8 parts, proportion of the ordor removing without ammonia PH regulator is 0.1 part, and except the proportion of aldehyde lotion is 20 parts, full ordor removing pure-acrylic emulsion is matched
Than being 18 parts, the proportion of inorganic thickening agent is 1 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, and ordor removing environment-friendly composite is anti-
The proportion of rotten mildew and algae agent is 0.3 part.
The beneficial effects of the present invention are:
The net aldehyde skin texture wall film slurry of the water negative ion manufactured by this manufacturing method can effectively reduce the irritation of skin texture wall film
Smell reaches ordor removing effect, while further decreases VOC content, reaches to become zero releasing effect, and skin texture wall film also has mould proof
Antibacterial effect.
Specific embodiment
The present invention will be further described below with reference to examples.
First embodiment
The manufacturing method of the net aldehyde skin texture wall film slurry of this water negative ion, made of following steps；
Step 1: ingredient according to the weight ratio:
Except 15-25 parts of aldehyde lotion,
Full 15-20 parts of ordor removing pure-acrylic emulsion,
15-20 parts of conch meal,
20-25 parts of rutile titanium white powder,
1-1.5 parts of negative ion powder,
Antifreeze dispersing agent 0.25-0.35 parts of ordor removing,
Antifreeze wetting agent 0.18-0.22 parts of ordor removing,
0.3-0.5 parts of composite anti-foaming agent,
0.7-1 parts of inorganic thickening agent,
Ordor removing without 0.08-0.12 parts of ammonia PH regulator,
2.3-2.8 parts of higher boiling ordor removing film forming agent,
0.3-0.5 parts of anticorrosive mildewproof algaecide of ordor removing environment-friendly composite,
13-18 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing is antifreeze
Dispersing agent, first part of composite anti-foaming agent, conch meal, rutile titanium white powder, negative ion powder, higher boiling ordor removing film forming agent, ordor removing without
Ammonia PH regulator removes aldehyde lotion, full ordor removing pure-acrylic emulsion, inorganic thickening agent, second part of composite anti-foaming agent, ordor removing environment-friendly composite
Anticorrosive mildewproof algaecide；
Step 3: uniform with high-speed stirred on dispersion machine, the net aldehyde skin texture wall film slurry of water negative ion to obtain 100 parts；
The manufacturing method of the net aldehyde skin texture wall film slurry of this water negative ion is used except aldehyde lotion is combined with full ordor removing pure-acrylic emulsion,
In except aldehyde lotion guarantee the skin texture wall film to be formed except aldehyde performance；
Lotion total amount of adding can improve the water resistance of product compared with existing product height after adding full ordor removing pure-acrylic emulsion；
Ordor removing does not distribute organic amine taste without ammonia PH regulator, and has dispersion moistening, increases the scrub resistance of product；
The antifreeze wetting agent of ordor removing guarantees dispersion moistening, it is possible to reduce solvent such as ethylene glycol when use, the addition of propandiols；
Higher boiling ordor removing film forming agent reduces product by VOC content；
Ordor removing environment-friendly composite anticorrosive mildewproof algaecide, fundamentally reduces the content of formaldehyde, while guaranteeing the mould proof anti-of paint film
Algae property；
Wherein conch meal, the powders such as rutile titanium white powder and negative ion powder are free of heavy metal, and wherein conch meal not only has not
Emitting formaldehyde, benzene, ammonia, TVOC(volatile organic compounds) etc. pernicious gases, and there is absorption, decompose these harmful gas
The function of body, simultaneously because conch meal main component is calcium carbonate, so its powder rigidity is high, good weatherability has simultaneously
Good filling power can more embody the texture degree of paint film；
Rutile titanium white powder imparts paint film high covering power and weatherability；
The addition of negative ion powder can make paint film long-term negative ion release, achieve the purpose that fresh air, allow the more healthy length of people
Longevity.
Further, the proportion of the ionized water in step 2 is 17.19 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.19
Part, the proportion of the antifreeze dispersing agent of ordor removing is 0.27 part, and the proportion of first part of composite anti-foaming agent is 0.16 part, conch meal conch meal
Proportion is 18 parts, and the proportion of rutile titanium white powder is 24.6 parts, and the proportion of negative ion powder is 1.09 parts, higher boiling ordor removing film forming agent
Proportion be 2.5 parts, ordor removing without ammonia PH regulator proportion be 0.08 part, except aldehyde lotion proportion be 16 parts, full ordor removing pure C
The proportion of lotion is 18.5 parts, and the proportion of inorganic thickening agent is 0.78 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, only
The proportion of taste ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.44 part, the net aldehyde flesh of water negative ion manufactured by the present embodiment
Wall film slurry is managed, purifying formaldehyde efficiency is 80%, and toluene purification efficiency is 55%, continued effectiveness 72%.
Second embodiment
The present embodiment and first embodiment the difference is that: the manufacturing method of this water negative ion net aldehyde skin texture wall film slurry
The proportion of ionized water in step 2 is 16 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, the proportion of the antifreeze dispersing agent of ordor removing
It is 0.29 part, the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 18.7 parts, rutile titanium white
The proportion of powder is 23.34 parts, and the proportion of negative ion powder is 1.5 parts, and the proportion of higher boiling ordor removing film forming agent is 2.4 parts, ordor removing without
The proportion of ammonia PH regulator is 0.09 part, and except the proportion of aldehyde lotion is 15.87 parts, the proportion of full ordor removing pure-acrylic emulsion is 20 parts,
The proportion of inorganic thickening agent is 0.81 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, ordor removing ordor removing environment-friendly composite anti-corrosion
The proportion of mildew and algae agent is 0.4 part, the net aldehyde skin texture wall film slurry of water negative ion manufactured by the present embodiment, purifying formaldehyde efficiency
It is 78%, toluene purification efficiency is 50%, continued effectiveness 70%.
Remaining does not describe the same first embodiment in part, is not repeated herein.
3rd embodiment
The present embodiment and first embodiment the difference is that: the manufacturing method of this water negative ion net aldehyde skin texture wall film slurry
The proportion of ionized water in step 2 is 15 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, the proportion of the antifreeze dispersing agent of ordor removing
It is 0.3 part, the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 16.25 parts, rutile titanium white
The proportion of powder is 25 parts, and the proportion of negative ion powder is 1 part, and the proportion of higher boiling ordor removing film forming agent is 2.5 parts, and ordor removing is without ammonia PH tune
The proportion for saving agent is 0.1 part, and except the proportion of aldehyde lotion is 20 parts, the proportion of full ordor removing pure-acrylic emulsion is 18 parts, inorganic thickening agent
Proportion be 0.80 part, the proportion of second part of composite anti-foaming agent is 0.2 part, ordor removing ordor removing environment-friendly composite anticorrosive mildewproof algaecide
Proportion be 0.45 part, the net aldehyde skin texture wall film slurry of water negative ion manufactured by the present embodiment, purifying formaldehyde efficiency is 85%, first
Benzene purification efficiency is 57%, continued effectiveness 75%.
Remaining does not describe the same first embodiment in part, is not repeated herein.
Fourth embodiment
The present embodiment and first embodiment the difference is that: the manufacturing method of this water negative ion net aldehyde skin texture wall film slurry
The proportion of ionized water in step 2 is 14.28 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.21 part, the antifreeze dispersing agent of ordor removing
Proportion is 0.33 part, and the proportion of first part of composite anti-foaming agent is 0.17 part, and the proportion of conch meal conch meal is 19 parts, rutile titanium
The proportion of white powder is 23.58 parts, and the proportion of negative ion powder is 1 part, and the proportion of higher boiling ordor removing film forming agent is 2.3 parts, ordor removing without
The proportion of ammonia PH regulator is 0.11 part, and except the proportion of aldehyde lotion is 22 parts, the proportion of full ordor removing pure-acrylic emulsion is 15.5 parts, nothing
The proportion of machine thickener is 0.87 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, and ordor removing ordor removing environment-friendly composite anti-corrosion is anti-
The proportion of mould algaecide is 0.35 part, the net aldehyde skin texture wall film slurry of water negative ion manufactured by the present embodiment, purifying formaldehyde efficiency
It is 87%, toluene purification efficiency is 60%, continued effectiveness 80%.
Remaining does not describe the same first embodiment in part, is not repeated herein.
5th embodiment
The present embodiment and first embodiment the difference is that: the manufacturing method of this water negative ion net aldehyde skin texture wall film slurry
The proportion of ionized water in step 2 is 16.11 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.22 part, the antifreeze dispersing agent of ordor removing
Proportion is 0.35 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of conch meal conch meal is 18 parts, rutile titanium
The proportion of white powder is 18.5 parts, and the proportion of negative ion powder is 1.4 parts, and the proportion of higher boiling ordor removing film forming agent is 2.80 parts, ordor removing
The proportion of no ammonia PH regulator is 0.12 part, and except the proportion of aldehyde lotion is 24.5 parts, the proportion of full ordor removing pure-acrylic emulsion is 16 parts,
The proportion of inorganic thickening agent is 1 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, and ordor removing ordor removing environment-friendly composite anti-corrosion is anti-
The proportion of mould algaecide is 0.5 part, the net aldehyde skin texture wall film slurry of water negative ion manufactured by the present embodiment, and purifying formaldehyde efficiency is
90%, toluene purification efficiency is 63%, continued effectiveness 85%.
Remaining does not describe the same first embodiment in part, is not repeated herein.
Sixth embodiment.
The present embodiment and first embodiment the difference is that: the manufacturer of this water negative ion net aldehyde skin texture wall film slurry
The proportion of ionized water in the step of method two is 17.9 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.18 part, the antifreeze dispersion of ordor removing
The proportion of agent is 0.25 part, and the proportion of first part of composite anti-foaming agent is 0.1 part, and the proportion of conch meal conch meal is 15.97 parts, gold
The proportion of red stone titanium dioxide is 22.2 parts, and the proportion of negative ion powder is 1 part, and the proportion of higher boiling ordor removing film forming agent is 2.8 parts, only
Proportion of the taste without ammonia PH regulator is 0.1 part, and except the proportion of aldehyde lotion is 20 parts, the proportion of full ordor removing pure-acrylic emulsion is 18 parts,
The proportion of inorganic thickening agent is 1 part, and the proportion of second part of composite anti-foaming agent is 0.2 part, and ordor removing ordor removing environment-friendly composite anti-corrosion is anti-
The proportion of mould algaecide is 0.3 part, the net aldehyde skin texture wall film slurry of water negative ion manufactured by the present embodiment, and purifying formaldehyde efficiency is
85%, toluene purification efficiency is 58%, continued effectiveness 78%.
Remaining does not describe the same first embodiment in part, is not repeated herein.
The net aldehyde skin texture wall film slurry of present invention water negative ion produced is constructed from can opening to upper wall, then is completed all to moving in
It is air fresh type；Simultaneously as lotion amount contained in formula is high compared with the prior art, so scrub resistance is extraordinary；
, can be with decomposing, purifying formaldehyde in air except the addition of aldehyde lotion, then cooperate the use of conch meal, so that wall reabsorbs nuisance
It is able to decompose and purify at once after matter, the addition of negative ion powder more can discharge anion after the completion of above-mentioned function, so that air
It is more pure and fresh, allow people more to have good health and a long life, the addition of ordor removing environment-friendly composite anticorrosive mildewproof algaecide solves wall from source
The anti-algae property of antibacterial and mouldproof, will not the long algae of mildew dry paint is under rugged environment；Simultaneously as the golden red of recipe
Stone titanium dioxide covering power, good weatherability, and this finished product can adjust a color, so as to keep metope not dull.Have in summary
Performance fundamentally solves the problems, such as formaldehyde, while can be the bright and colourful of wall decoration, and it is long not fear mildew
It is pure and fresh to be also able to maintain room air on this basis for algae.
Above-described embodiment is preferred embodiment of the invention, and the present invention can also have other embodiments.The technology of this field
Personnel can also make equivalent deformation or replacement on the premise of without prejudice to spirit of the invention, these equivalent variation or replacement are wrapped
It is contained in range set by the claim of this application.
Claims (7)
1. a kind of manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion, which is characterized in that made of following steps；
Step 1: ingredient according to the weight ratio:
Except 15-25 parts of aldehyde lotion,
Full 15-20 parts of ordor removing pure-acrylic emulsion,
15-20 parts of conch meal,
20-25 parts of rutile titanium white powder,
1-1.5 parts of negative ion powder,
Antifreeze dispersing agent 0.25-0.35 parts of ordor removing,
Antifreeze wetting agent 0.18-0.22 parts of ordor removing,
0.3-0.5 parts of composite anti-foaming agent,
0.7-1 parts of inorganic thickening agent,
Ordor removing without 0.08-0.12 parts of ammonia PH regulator,
2.3-2.8 parts of higher boiling ordor removing film forming agent,
0.3-0.5 parts of anticorrosive mildewproof algaecide of ordor removing environment-friendly composite,
13-18 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing is antifreeze
Dispersing agent, first part of composite anti-foaming agent, conch meal, rutile titanium white powder, negative ion powder, higher boiling ordor removing film forming agent, ordor removing without
Ammonia PH regulator removes aldehyde lotion, full ordor removing pure-acrylic emulsion, inorganic thickening agent, second part of composite anti-foaming agent, ordor removing environment-friendly composite
Anticorrosive mildewproof algaecide；
Step 3: uniform with high-speed stirred on dispersion machine, the net aldehyde skin texture wall film slurry of water negative ion to obtain 100 parts.
2. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 17.19 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.19 part, the antifreeze dispersion of ordor removing
The proportion of agent is 0.27 part, and the proportion of first part of composite anti-foaming agent is 0.16 part, and the proportion of the conch meal conch meal is
18 parts, the proportion of the rutile titanium white powder is 24.6 parts, and the proportion of the negative ion powder is 1.09 parts, the higher boiling ordor removing
The proportion of film forming agent is 2.5 parts, and proportion of the ordor removing without ammonia PH regulator is 0.08 part, and the proportion except aldehyde lotion is 16
Part, the proportion of the full ordor removing pure-acrylic emulsion is 18.5 parts, and the proportion of the inorganic thickening agent is 0.78 part, and described second part is multiple
The proportion for closing defoaming agent is 0.2 part, and the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.44 part.
3. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 16 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, the antifreeze dispersing agent of ordor removing
Proportion is 0.29 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of the conch meal conch meal is 18.7
Part, the proportion of the rutile titanium white powder is 23.34 parts, and the proportion of the negative ion powder is 1.5 parts, the higher boiling ordor removing at
The proportion of film is 2.4 parts, and proportion of the ordor removing without ammonia PH regulator is 0.09 part, and the proportion except aldehyde lotion is
15.87 parts, the proportion of the full ordor removing pure-acrylic emulsion is 20 parts, and the proportion of the inorganic thickening agent is 0.81 part, described second
The proportion of part composite anti-foaming agent is 0.2 part, and the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.4 part.
4. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 15 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.2 part, the antifreeze dispersing agent of ordor removing
Proportion is 0.3 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of the conch meal conch meal is 16.25
Part, the proportion of the rutile titanium white powder is 25 parts, and the proportion of the negative ion powder is 1 part, the higher boiling ordor removing film forming agent
Proportion be 2.5 parts, proportion of the ordor removing without ammonia PH regulator is 0.1 part, and the proportion except aldehyde lotion is 20 parts, described
The proportion of full ordor removing pure-acrylic emulsion is 18 parts, and the proportion of the inorganic thickening agent is 0.80 part, second part of composite anti-foaming agent
Proportion be 0.2 part, the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.45 part.
5. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 14.28 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.21 part, the antifreeze dispersion of ordor removing
The proportion of agent is 0.33 part, and the proportion of first part of composite anti-foaming agent is 0.17 part, and the proportion of the conch meal conch meal is
19 parts, the proportion of the rutile titanium white powder is 23.58 parts, and the proportion of the negative ion powder is 1 part, the higher boiling ordor removing at
The proportion of film is 2.3 parts, and proportion of the ordor removing without ammonia PH regulator is 0.11 part, and the proportion except aldehyde lotion is 22
Part, the proportion of the full ordor removing pure-acrylic emulsion is 15.5 parts, and the proportion of the inorganic thickening agent is 0.87 part, and described second part is multiple
The proportion for closing defoaming agent is 0.3 part, and the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.35 part.
6. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 16.11 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.22 part, the antifreeze dispersion of ordor removing
The proportion of agent is 0.35 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of the conch meal conch meal is 18
Part, the proportion of the rutile titanium white powder is 18.5 parts, and the proportion of the negative ion powder is 1.4 parts, the higher boiling ordor removing at
The proportion of film is 2.80 parts, and proportion of the ordor removing without ammonia PH regulator is 0.12 part, and the proportion except aldehyde lotion is
24.5 parts, the proportion of the full ordor removing pure-acrylic emulsion is 16 parts, and the proportion of the inorganic thickening agent is 1 part, and described second part multiple
The proportion for closing defoaming agent is 0.3 part, and the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.5 part.
7. the manufacturing method of the net aldehyde skin texture wall film slurry of water negative ion according to claim 1, it is characterised in that: the step
The proportion of ionized water in two is 17.9 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.18 part, the antifreeze dispersion of ordor removing
The proportion of agent is 0.25 part, and the proportion of first part of composite anti-foaming agent is 0.1 part, and the proportion of the conch meal conch meal is
15.97 parts, the proportion of the rutile titanium white powder is 22.2 parts, and the proportion of the negative ion powder is 1 part, the higher boiling ordor removing
The proportion of film forming agent is 2.8 parts, and proportion of the ordor removing without ammonia PH regulator is 0.1 part, and the proportion except aldehyde lotion is 20
Part, the proportion of the full ordor removing pure-acrylic emulsion is 18 parts, and the proportion of the inorganic thickening agent is 1 part, and described second part compound to disappear
The proportion of infusion is 0.2 part, and the proportion of the ordor removing environment-friendly composite anticorrosive mildewproof algaecide is 0.3 part.