CN109295582A - It is a kind of super soft to lead wet yarn - Google Patents
It is a kind of super soft to lead wet yarn Download PDFInfo
- Publication number
- CN109295582A CN109295582A CN201811514004.6A CN201811514004A CN109295582A CN 109295582 A CN109295582 A CN 109295582A CN 201811514004 A CN201811514004 A CN 201811514004A CN 109295582 A CN109295582 A CN 109295582A
- Authority
- CN
- China
- Prior art keywords
- yarn
- layer
- wetness
- dry
- comfortable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Super soft wet yarn, including yarn body are led the invention discloses a kind of;The yarn body includes heart yarn, wetness-guiding layer, dry and comfortable layer and skin-friendly layer;The heart yarn, wetness-guiding layer, dry and comfortable layer and skin-friendly layer are radially set gradually from inside to outside along the yarn body;The heart yarn is formed by 20-50 root nanofibers without twisting Split Down;The wetness-guiding layer is wrapped over outside the heart yarn by terylene super fine denier silk spiral and is formed;The dry and comfortable layer is wrapped over outside the wetness-guiding layer by polypropylene fibre superfine denier fiber spiral and is formed;The skin-friendly layer is wrapped over outside the dry and comfortable layer by tencel fiber spiral and is formed;The yarn body is 7-11dpf.Soft yarns of the present invention are very thin, have good spinnability, and quick moisture absorption may be implemented in comfortable feel, keep yam surface dry and comfortable, skin-friendly is good.
Description
Technical field
It is the present invention relates to yarn field, in particular to a kind of super soft to lead wet yarn.
Background technique
Currently, yarn in the market is varied.According to the different function of fabric, the structure of the yarn of fabric is made also not
Together.In the market, some yarns have anti-ultraviolet function, and some yarns have skin-protecting function, and yarn also has antibacterial function
Energy.But often the yarn of Single Fiber weaving has a single function, comprehensive performance is undesirable.Covering yarn is also known as composite yarn or cladding
Yarn, it is a kind of new type yarn as made of two or more fiber combinations.The existing general line footpath of covering yarn is thicker,
Although can be compound by multiple fiber, the deficiency of Single Fiber be made up, flexibility is poor, while wet transmitting performance is undesirable.
Summary of the invention
In order to solve the above technical problems, the present invention provides it is a kind of it is super it is soft lead wet yarn, using nanofibers without twisting
As heart yarn, flexibility is good for Split Down, by wetness-guiding layer and dry and comfortable layer, skin-friendly layer is made to keep dry and comfortable, at the same have it is good lead it is wet
Performance, solves that existing soft yarns are poor, while the problem that wet transmitting performance is undesirable.
In order to achieve the above objectives, technical scheme is as follows: a kind of super soft to lead wet yarn, including yarn body;Institute
Stating yarn body includes heart yarn, wetness-guiding layer, dry and comfortable layer and skin-friendly layer;The heart yarn, wetness-guiding layer, dry and comfortable layer and skin-friendly layer are described in
Yarn body is radially set gradually from inside to outside;The heart yarn is formed by 20-50 root nanofibers without twisting Split Down;It is described to lead
Wet layer is wrapped over outside the heart yarn by terylene super fine denier silk spiral and is formed;The dry and comfortable layer is wrapped over by polypropylene fibre superfine denier fiber spiral
It is formed outside the wetness-guiding layer;The skin-friendly layer is wrapped over outside the dry and comfortable layer by tencel fiber spiral and is formed;The yarn body
For 7-11dpf.
As a preferred solution of the present invention, the heart yarn is by carbon nano-fiber silk or nano spandex silk without twisting Split Down
It forms.
As a preferred solution of the present invention, the wetness-guiding layer with a thickness of 150-350nm.
As a preferred solution of the present invention, the wetness-guiding layer carries out spiral looping by 7-12 root terylene super fine denier silk.
As a preferred solution of the present invention, the dry and comfortable layer carries out spiral looping by 4-6 root polypropylene fibre superfine denier fiber.
As a preferred solution of the present invention, the tencel fiber is anion nanometer tencel fiber.
Through the above technical solutions, the beneficial effect of technical solution of the present invention is: soft yarns of the present invention are very thin, have good
Good spinnability, comfortable feel make yarn soft-touch using the nanofibers Split Down of no twisting as heart yarn, while can
To select nanofibers as needed, using carbon nano-fiber silk as heart yarn, structural strength is good, not easy to break, Ke Yizuo
For the use of electric heating yarn;Using nano spandex silk as heart yarn, elasticity is good;The present invention is using polypropylene fibre superfine denier fiber as dry
Refreshing layer, polypropylene fibre has good penetrability, but polypropylene fibre itself is non-hygroscopic, and the wet transmitting performance of terylene super fine denier silk is very excellent
It is different, cooperate with polypropylene fibre superfine denier fiber, under the action of wicking, quick moisture absorption may be implemented, keeps yam surface dry
It is refreshing;And tencel fiber, as skin-friendly layer, feel is smooth, and surface hairiness is few, and skin-friendly is good.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with
It obtains other drawings based on these drawings.
Fig. 1 is the structural diagram of the present invention.
Number and corresponding component title represented by letter in figure:
1. the dry and comfortable layer of 2. wetness-guiding layer of heart yarn 3.
4. skin-friendly layer.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment
In conjunction with Fig. 1, super soft wet yarn, including yarn body are led the invention discloses a kind of;Yarn body include heart yarn 1,
Wetness-guiding layer 2, dry and comfortable layer 3 and skin-friendly layer 4.Heart yarn 1, wetness-guiding layer 2, dry and comfortable layer 3 and skin-friendly layer 4 are radial from inside to outside along yarn body
It sets gradually.Heart yarn 1 is formed by 20-50 root nanofibers without twisting Split Down.Wetness-guiding layer 2 is by terylene super fine denier silk spiral looping
It is formed outside heart yarn 1.Dry and comfortable layer 3 is wrapped over outside wetness-guiding layer 2 by polypropylene fibre superfine denier fiber spiral and is formed;Skin-friendly layer 4 is by tencel fiber
Spiral is wrapped over outside dry and comfortable layer 3 and is formed.Yarn body is 7-11dpf.
Heart yarn 1 can select different nanofibers according to the performance of required yarn body, it is preferred that heart yarn 1 is by receiving
Rice carbon fiber wire or nano spandex silk are formed without twisting Split Down.Excellent using carbon nano-fiber silk anti-microbial property, tension failure is strong
Degree is high, and antistatic property is good, while can use as conductive heater functional yarn.And using nano spandex silk, elasticity is good, thoroughly
Gas is good, can be used in that various sportswear fabrics are made.
In order to keep yarn body softness very thin, while making that there is good wicking effect between wetness-guiding layer 2 and dry and comfortable layer 3
Answer, wetness-guiding layer 2 with a thickness of 150-350nm.Wetness-guiding layer 2 carries out spiral looping by 7-12 root terylene super fine denier silk.Dry and comfortable layer 3 by
4-6 root polypropylene fibre superfine denier fiber carries out spiral looping.
In order to which with good antimicrobial health care function, tencel fiber is anion nanometer tencel fiber.
By above-mentioned specific embodiment, the beneficial effects of the present invention are: soft yarns of the present invention are very thin, have it is good can
The property spun, comfortable feel make yarn soft-touch using the nanofibers Split Down of no twisting as heart yarn 1, while can basis
It needs to select nanofibers, using carbon nano-fiber silk as heart yarn 1, structural strength is good, and it is not easy to break, it can be used as electricity and add
Hot yarn uses;Using nano spandex silk as heart yarn 1, elasticity is good;The present invention is using polypropylene fibre superfine denier fiber as dry and comfortable layer
3, polypropylene fibre has good penetrability, but polypropylene fibre itself is non-hygroscopic, and the wet transmitting performance of terylene super fine denier silk is very excellent, with
Quick moisture absorption may be implemented under the action of wicking in the cooperation of polypropylene fibre superfine denier fiber, keeps yam surface dry and comfortable;And
For tencel fiber as skin-friendly layer 4, feel is smooth, and surface hairiness is few, and skin-friendly is good.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (6)
1. super soft wet yarn is led a kind of, which is characterized in that including yarn body;The yarn body includes heart yarn, wetness-guiding layer, does
Refreshing layer and skin-friendly layer;The heart yarn, wetness-guiding layer, dry and comfortable layer and skin-friendly layer are radially successively set from inside to outside along the yarn body
It sets;The heart yarn is formed by 20-50 root nanofibers without twisting Split Down;The wetness-guiding layer is by terylene super fine denier silk spiral looping
It is formed outside the heart yarn;The dry and comfortable layer is wrapped over outside the wetness-guiding layer by polypropylene fibre superfine denier fiber spiral and is formed;The pro-skin
Layer is wrapped over outside the dry and comfortable layer by tencel fiber spiral and is formed;The yarn body is 7-11dpf.
2. super soft wet yarn is led according to claim 1, which is characterized in that the heart yarn is by carbon nano-fiber silk or nanometer
Spandex thread is formed without twisting Split Down.
Super soft lead wet yarn 3. according to claim 1, which is characterized in that the wetness-guiding layer with a thickness of 150-350nm.
4. super soft wet yarn is led according to claim 3, which is characterized in that the wetness-guiding layer is by 7-12 root terylene super fine denier
Silk carries out spiral looping.
5. super soft wet yarn is led according to claim 4, which is characterized in that the dry and comfortable layer is by 4-6 root polypropylene fibre super fine denier
Silk carries out spiral looping.
6. super soft wet yarn is led according to claim 5, which is characterized in that the tencel fiber is anion nanometer tencel
Fiber.