CN109294521A - 一种玻璃防尘液及其制备方法 - Google Patents
一种玻璃防尘液及其制备方法 Download PDFInfo
- Publication number
- CN109294521A CN109294521A CN201811160170.0A CN201811160170A CN109294521A CN 109294521 A CN109294521 A CN 109294521A CN 201811160170 A CN201811160170 A CN 201811160170A CN 109294521 A CN109294521 A CN 109294521A
- Authority
- CN
- China
- Prior art keywords
- dust
- parts
- glass
- proof liquid
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种玻璃防尘液及其制备方法，防尘液包括以下组分：二氧化硅、丙三醇、氧化钙、季戊四醇、乙醇、氧化铈、表面活性剂、碳酸氢铵、聚乙二醇、月桂醇硫酸钠、去离子水。制备过程为将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至40‑45℃，搅拌20‑30分钟，然后降至室温，加入碳酸氢铵，继续搅拌10‑20分钟，得到玻璃防尘液。本发明提供的玻璃防尘液具有良好的防尘效果。
Description
技术领域
本发明属于化工用品领域，具体涉及一种玻璃防尘液及其制备方法。
背景技术
玻璃作为日常生活中经常使用的用品，已经与人们密不可分，对于玻璃的性能提升一直时候技术人员不断研究的热点，而玻璃的其他性能要求也逐渐提高，如玻璃表面脏污，积灰等导致玻璃耐脏性变差，往往用一段时间后就需要专门的擦拭。玻璃表面的尘污积累主要四由于玻璃表面能够与水进行一定程度的吸合，而尘粒落到玻璃表面积累主要是由于尘粒带有的水分粘粘在了玻璃上，久而久之形成了尘污，因此开发一种能够发挥防尘作用的产品用于玻璃制品中，具有重大的意义。
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种玻璃防尘液及其制备方法，提升防尘效果。
本发明的技术方案如下：
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅2-4份、丙三醇2-3份、氧化钙0.5-1份、季戊四醇5-10份、乙醇5-10份、氧化铈0.5-1份、表面活性剂0.5-1份、碳酸氢铵0.5-1份、聚乙二醇1-3份、月桂醇硫酸钠0.5-1份、去离子水30-40份。
所述的玻璃防尘液，所述二氧化硅为纳米二氧化硅。
所述的玻璃防尘液，乙醇为无水乙醇。
所述的玻璃防尘液，表面活性剂为吐温80。
所述的玻璃防尘液，所述聚乙二醇为聚乙二醇600。
所述的玻璃防尘液，所述氧化铈的粒径为50μm以下。
所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至40-45℃，搅拌20-30分钟，然后降至室温，加入碳酸氢铵，继续搅拌10-20分钟，得到玻璃防尘液。
本发明提供的玻璃防尘液，在使用时将其直接喷洒在玻璃上，然后用柔软的毛巾擦拭干净即可，其能够在玻璃表面形成一层致密的保护膜，该保护膜的接触角在112°以上，能够很好的驱离水性物质，进而能够达到很好的防尘效果。
具体实施方式：
实施例1
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅2份、丙三醇2份、氧化钙0.5份、季戊四醇5份、乙醇5份、氧化铈0.5份、表面活性剂0.5份、碳酸氢铵0.5份、聚乙二醇1份、月桂醇硫酸钠0.5份、去离子水30份。
以上所述二氧化硅为纳米二氧化硅，乙醇为无水乙醇，表面活性剂为吐温80，所述聚乙二醇为聚乙二醇600，所述氧化铈的粒径为50μm以下。
以上所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至40℃，搅拌20分钟，然后降至室温，加入碳酸氢铵，继续搅拌10分钟，得到玻璃防尘液。
实施例2
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅3份、丙三醇2份、氧化钙0.6份、季戊四醇6份、乙醇6份、氧化铈0.7份、表面活性剂0.6份、碳酸氢铵0.6份、聚乙二醇2份、月桂醇硫酸钠0.7份、去离子水32份。
以上所述二氧化硅为纳米二氧化硅，乙醇为无水乙醇，表面活性剂为吐温80，所述聚乙二醇为聚乙二醇600，所述氧化铈的粒径为50μm以下。
以上所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至42℃，搅拌22分钟，然后降至室温，加入碳酸氢铵，继续搅拌13分钟，得到玻璃防尘液。
实施例3
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅3份、丙三醇3份、氧化钙0.7份、季戊四醇6份、乙醇8份、氧化铈0.7份、表面活性剂0.8份、碳酸氢铵0.7份、聚乙二醇2份、月桂醇硫酸钠0.9份、去离子水35份。
以上所述二氧化硅为纳米二氧化硅，乙醇为无水乙醇，表面活性剂为吐温80，所述聚乙二醇为聚乙二醇600，所述氧化铈的粒径为50μm以下。
以上所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至43℃，搅拌25分钟，然后降至室温，加入碳酸氢铵，继续搅拌16分钟，得到玻璃防尘液。
实施例4
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅3份、丙三醇3份、氧化钙0.9份、季戊四醇8份、乙醇8份、氧化铈0.7份、表面活性剂0.8份、碳酸氢铵0.8份、聚乙二醇2份、月桂醇硫酸钠1份、去离子水39份。
以上所述二氧化硅为纳米二氧化硅，乙醇为无水乙醇，表面活性剂为吐温80，所述聚乙二醇为聚乙二醇600，所述氧化铈的粒径为50μm以下。
以上所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至43℃，搅拌25分钟，然后降至室温，加入碳酸氢铵，继续搅拌18分钟，得到玻璃防尘液。
实施例5
一种玻璃防尘液，包括以下重量份计的组分：二氧化硅4份、丙三醇3份、氧化钙1份、季戊四醇10份、乙醇10份、氧化铈1份、表面活性剂1份、碳酸氢铵1份、聚乙二醇3份、月桂醇硫酸钠1份、去离子水40份。
以上所述二氧化硅为纳米二氧化硅，乙醇为无水乙醇，表面活性剂为吐温80，所述聚乙二醇为聚乙二醇600，所述氧化铈的粒径为50μm以下。
以上所述的玻璃防尘液的制备方法，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至45℃，搅拌30分钟，然后降至室温，加入碳酸氢铵，继续搅拌20℃，得到玻璃防尘液。
以上实施例提供的玻璃防尘液，在使用时将其直接喷洒在玻璃上，然后用柔软的毛巾擦拭干净即可，其能够在玻璃表面形成一层致密的保护膜，该保护膜的接触角在112°以上，能够很好的驱离水性物质，进而能够达到很好的防尘效果。
Claims (7)
1.一种玻璃防尘液，其特征在于，包括以下重量份计的组分：二氧化硅2-4份、丙三醇2-3份、氧化钙0.5-1份、季戊四醇5-10份、乙醇5-10份、氧化铈0.5-1份、表面活性剂0.5-1份、碳酸氢铵0.5-1份、聚乙二醇1-3份、月桂醇硫酸钠0.5-1份、去离子水30-40份。
2.根据权利要求1所述的玻璃防尘液，其特征在于，所述二氧化硅为纳米二氧化硅。
3.根据权利要求1所述的玻璃防尘液，其特征在于，乙醇为无水乙醇。
4.根据权利要求1所述的玻璃防尘液，其特征在于，表面活性剂为吐温80。
5.根据权利要求1所述的玻璃防尘液，其特征在于，所述聚乙二醇为聚乙二醇600。
6.根据权利要求1所述的玻璃防尘液，其特征在于，所述氧化铈的粒径为50μm以下。
7.权利要求1所述的玻璃防尘液的制备方法，其特征在于，将二氧化硅、丙三醇、季戊四醇、乙醇、氧化铈加入去离子水中，搅拌混合，然后加入表面活性剂、聚乙二醇、月桂醇硫酸钠、氧化钙，加热至40-45℃，搅拌20-30分钟，然后降至室温，加入碳酸氢铵，继续搅拌10-20分钟，得到玻璃防尘液。