CN109266023A - A kind of batik mixing cerate and preparation method thereof - Google Patents
A kind of batik mixing cerate and preparation method thereof Download PDFInfo
- Publication number
- CN109266023A CN109266023A CN201811412087.8A CN201811412087A CN109266023A CN 109266023 A CN109266023 A CN 109266023A CN 201811412087 A CN201811412087 A CN 201811412087A CN 109266023 A CN109266023 A CN 109266023A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- batik
- mixing
- cerate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of batik mixing cerates and preparation method thereof, which is made of paraffin, beeswax, sheep oil, modified organic silicon, stearic acid, 10~16 parts of neopelex and triethanolamine.The present invention is low in cost, osmotic effect is good, adhesive capacity is strong, waxing is uniform, is not likely to produce cracking and pigment figure occurs.
Description
Technical field
The present invention relates to a kind of blended wax, especially a kind of batik mixing cerate and preparation method thereof.
Background technique
Batik is the ancient ethnic group's folk tradition textile printing and dyeing handicraft in China, Gu claim wax, with twist figured silk fabrics (tie dyeing),
Press from both sides figured silk fabrics (hollow out stamp) and the referred to as big stamp skill of Ancient Times in China three.Batik is good at by the nationalitys such as Guizhou, Yunnan Miao ethnic group, the Bouyei.
Batik is to be dipped in dewaxing with wax spatula and drawn to disseminate with indigo after Hua Yubu, both contaminates wax, cloth cover takes on blue bottom white flower or white background is blue
Colored multiple patterns, meanwhile, in dip dyeing, as the wax exposure cracking of resist agent, make cloth cover that special " ice line " be presented, it is outstanding to have
Glamour.Since batik pattern is abundant, tone is plain, unique style, for making dress and personal adornment and various life utilities, it appears
Simple generous, pure and fresh pleasing, rich in national characters, the market demand increases year by year.
But the wax material in wax operation is being drawn in existing wax printing technology, generally use single paraffin or single
Beeswax heat carries out picture wax operation after melting.The hardness of paraffin is larger, is used for picture wax and operates easy exposure cracking in dyeing course
Pigment figure is generated, but its adhesiveness is lower, being easy to fall off in dyeing course causes to generate stain.The adhesiveness of beeswax is not easy well
It falls off, but its hardness is lower, and exposure cracking is difficult in dyeing course and generates pigment figure, while its asking there is also higher cost
Topic.For above-mentioned problem, the prior art is by the way that paraffin and beeswax to be simply mixed, while keeping its adhesiveness preferable
Enough exposure crackings, but it still has the problems such as permeability is poor, waxing is uneven.And due to the superficiality of different clothes
Can be different, it needs to be surface-treated for different clothes.
Summary of the invention
The object of the present invention is to provide a kind of batik mixing cerates and preparation method thereof.The present invention is low in cost, seeps
Saturating effect is good, adhesive capacity is strong, waxing is uniform, is not likely to produce cracking and pigment figure occurs.
Technical solution of the present invention: a kind of batik mixing cerate, which is to be made of raw material from the following weight: paraffin
50 ~ 60 parts, 20 ~ 40 parts of beeswax, 10 ~ 20 parts of sheep oil, 2 ~ 3 parts of modified organic silicon, 30 ~ 50 parts of stearic acid, dodecyl benzene sulfonic acid
10~16 parts 2 ~ 3 parts of sodium, 10 ~ 20 parts of triethanolamine.
2. a kind of batik according to claim 1 mixing cerate, it is characterised in that: the wax is by following weight
The raw material of part is made: 55 parts of paraffin, 30 parts of beeswax, and 15 parts of sheep oil, 2.5 parts of modified organic silicon, 40 parts of stearic acid, detergent alkylate
10~16 parts 2.5 parts of sodium sulfonate, 15 parts of triethanolamine.
3. a kind of preparation method of batik mixing cerate according to claim 1 or 2, it is characterised in that: the party
Method includes the following steps；
A: paraffin, beeswax, sheep oil, modified organic silicon and stearic acid are distinguished into heating and melting, and are uniformly mixed, A product are obtained；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: 10~16 parts of neopelex and triethanolamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
The invention has the advantages that by using paraffin and beeswax as base-material,
The hardness of paraffin is higher, beeswax adhesion property is preferable, not only has a preferable adhesion property, but also not also easy tortoise
It splits.
By adding sheep oil, modified organic silicon, stearic acid, 10~16 parts of neopelex and triethanolamine, into
One step improves the performance of wax, improves the quality of wax, keeps wax uniform, improve the permeance property of wax, retentivity is preferable after waxing, no
Easily it is cracked.In conclusion the present invention is low in cost, osmotic effect is good, adhesive capacity is strong, waxing is uniform, it is not likely to produce tortoise
It splits and pigment figure occurs.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.A kind of batik mixing cerate, which is to be prepared from the following raw materials: paraffin 55kg, beeswax 30kg, sheep
Oily 15kg, modified organic silicon 2.5kg, stearic acid 40kg, neopelex 10~16 parts of 2.5kg, triethanolamine 15kg.
The preparation method of above-mentioned batik mixing cerate, it is characterised in that: this approach includes the following steps；
A: paraffin, beeswax, sheep oil, modified organic silicon and stearic acid are distinguished into heating and melting, and are uniformly mixed, A product are obtained；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: 10~16 parts of neopelex and triethanolamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Embodiment 2.A kind of batik mixing cerate, the wax with raw material by being made: paraffin 50kg, beeswax 20kg, sheep oil
10kg, modified organic silicon 2kg, stearic acid 30kg, neopelex 10~16 parts of 2kg, triethanolamine 10kg.
The above-mentioned batik preparation method of mixing cerate, this approach includes the following steps；
A: paraffin, beeswax, sheep oil, modified organic silicon and stearic acid are distinguished into heating and melting, and are uniformly mixed, A product are obtained；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: 10~16 parts of neopelex and triethanolamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Embodiment 3.A kind of batik mixing cerate, which is to be prepared from the following raw materials: paraffin 60kg, beeswax 40kg, sheep
Oily 20kg, modified organic silicon 3kg, stearic acid 50kg, neopelex 10~16 parts of 3kg, triethanolamine 20kg.
The above-mentioned batik preparation method of mixing cerate, this approach includes the following steps；
A: paraffin, beeswax, sheep oil, modified organic silicon and stearic acid are distinguished into heating and melting, and are uniformly mixed, A product are obtained；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: 10~16 parts of neopelex and triethanolamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Claims (3)
1. a kind of batik mixing cerate, it is characterised in that: the wax is to be made of raw material from the following weight: 50 ~ 60 parts of paraffin,
20 ~ 40 parts of beeswax, 10 ~ 20 parts of sheep oil, 2 ~ 3 parts of modified organic silicon, 30 ~ 50 parts of stearic acid, neopelex 10~16
2 ~ 3 parts, 10 ~ 20 parts of triethanolamine of part.
2. a kind of batik according to claim 1 mixing cerate, it is characterised in that: the wax is by following parts by weight
Raw material is made: 55 parts of paraffin, 30 parts of beeswax, and 15 parts of sheep oil, 2.5 parts of modified organic silicon, 40 parts of stearic acid, dodecyl benzene sulfonic acid
10~16 parts 2.5 parts of sodium, 15 parts of triethanolamine.
3. a kind of preparation method of batik mixing cerate according to claim 1 or 2, it is characterised in that: this method packet
Include following steps；
A: paraffin, beeswax, sheep oil, modified organic silicon and stearic acid are distinguished into heating and melting, and are uniformly mixed, A product are obtained；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: 10~16 parts of neopelex and triethanolamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.