CN109370238A - A kind of cerate and preparation method thereof for batik - Google Patents
A kind of cerate and preparation method thereof for batik Download PDFInfo
- Publication number
- CN109370238A CN109370238A CN201811418550.XA CN201811418550A CN109370238A CN 109370238 A CN109370238 A CN 109370238A CN 201811418550 A CN201811418550 A CN 201811418550A CN 109370238 A CN109370238 A CN 109370238A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- wax
- batik
- cerate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The cerate and preparation method thereof that the invention discloses a kind of for batik, the wax are made of paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin, lanolin magnesium soap, neopelex and triethylamine.The present invention is low in cost, osmotic effect is good, adhesive capacity is strong, waxing is uniform, is not likely to produce cracking and pigment figure occurs.
Description
Technical field
The present invention relates to a kind of blended wax, especially a kind of cerate and preparation method thereof for batik.
Background technique
Batik is the ancient ethnic group's folk tradition textile printing and dyeing handicraft in China, Gu claim wax, with twist figured silk fabrics (tie dyeing),
Press from both sides figured silk fabrics (hollow out stamp) and the referred to as big stamp skill of Ancient Times in China three.Batik is good at by the nationalitys such as Guizhou, Yunnan Miao ethnic group, the Bouyei.
Batik is to be dipped in dewaxing with wax spatula and drawn to disseminate with indigo after Hua Yubu, both contaminates wax, cloth cover takes on blue bottom white flower or white background is blue
Colored multiple patterns, meanwhile, in dip dyeing, as the wax exposure cracking of resist agent, make cloth cover that special " ice line " be presented, it is outstanding to have
Glamour.Since batik pattern is abundant, tone is plain, unique style, for making dress and personal adornment and various life utilities, it appears
Simple generous, pure and fresh pleasing, rich in national characters, the market demand increases year by year.
But the wax material in wax operation is being drawn in existing wax printing technology, generally use single paraffin or single
Beeswax heat carries out picture wax operation after melting.The hardness of paraffin is larger, is used for picture wax and operates easy exposure cracking in dyeing course
Pigment figure is generated, but its adhesiveness is lower, being easy to fall off in dyeing course causes to generate stain.The adhesiveness of beeswax is not easy well
It falls off, but its hardness is lower, and exposure cracking is difficult in dyeing course and generates pigment figure, while its asking there is also higher cost
Topic.For above-mentioned problem, the prior art is by the way that paraffin and beeswax to be simply mixed, while keeping its adhesiveness preferable
Enough exposure crackings, but it still has the problems such as permeability is poor, waxing is uneven.And due to the superficiality of different clothes
Can be different, it needs to be surface-treated for different clothes.
Summary of the invention
The cerate and preparation method thereof that the object of the present invention is to provide a kind of for batik.The present invention is low in cost, seeps
Saturating effect is good, adhesive capacity is strong, waxing is uniform, is not likely to produce cracking and pigment figure occurs.
Technical solution of the present invention: a kind of cerate for batik, the wax are to be made of raw material from the following weight: paraffin
50 ~ 60 parts, 20 ~ 40 parts of beeswax, 10 ~ 20 parts of rapeseed oil wax, 2 ~ 3 parts of C 5 petroleum resin, 30 ~ 50 parts of lanolin magnesium soap, 12
2 ~ 3 parts of sodium alkyl benzene sulfonate, 10 ~ 20 parts of triethylamine.
2. a kind of cerate for batik according to claim 1, it is characterised in that: the wax is by following weight
The raw material of part is made: 55 parts of paraffin, 30 parts of beeswax, and 15 parts of rapeseed oil wax, 2.5 parts of C 5 petroleum resin, 40 parts of lanolin magnesium soap,
2.5 parts of neopelex, 15 parts of triethylamine.
3. a kind of preparation method of cerate for batik according to claim 1 or 2, it is characterised in that: the party
Method includes the following steps；
A: paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin and lanolin magnesium soap are distinguished into heating and melting, and are uniformly mixed, is obtained
A product；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: neopelex and triethylamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
The invention has the advantages that by using paraffin and beeswax as base-material,
The hardness of paraffin is higher, beeswax adhesion property is preferable, not only has a preferable adhesion property, but also not also easy tortoise
It splits.
By adding rapeseed oil wax, C 5 petroleum resin, lanolin magnesium soap, neopelex and triethylamine, into
One step improves the performance of wax, improves the quality of wax, keeps wax uniform, improve the permeance property of wax, retentivity is preferable after waxing, no
Easily it is cracked.In conclusion the present invention is low in cost, osmotic effect is good, adhesive capacity is strong, waxing is uniform, it is not likely to produce tortoise
It splits and pigment figure occurs.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.A kind of cerate for batik, the wax are to be prepared from the following raw materials: paraffin 55kg, beeswax 30kg, dish
Seed oil wax 15kg, C 5 petroleum resin 2.5kg, lanolin magnesium soap 40kg, neopelex 2.5kg, triethylamine 15kg.
The preparation method of the above-mentioned cerate for batik, it is characterised in that: this approach includes the following steps；
A: paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin and lanolin magnesium soap are distinguished into heating and melting, and are uniformly mixed, is obtained
A product；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: neopelex and triethylamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Embodiment 2.A kind of cerate for batik, the wax with raw material by being made: paraffin 50kg, beeswax 20kg, vegetable seed
Oily wax 10kg, C 5 petroleum resin 2kg, lanolin magnesium soap 30kg, neopelex 2kg, triethylamine 10kg.
The preparation method of the above-mentioned cerate for batik, this approach includes the following steps；
A: paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin and lanolin magnesium soap are distinguished into heating and melting, and are uniformly mixed, is obtained
A product；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: neopelex and triethylamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Embodiment 3.A kind of cerate for batik, the wax are to be prepared from the following raw materials: paraffin 60kg, beeswax 40kg, dish
Seed oil wax 20kg, C 5 petroleum resin 3kg, lanolin magnesium soap 50kg, neopelex 3kg, triethylamine 20kg.
The preparation method of the above-mentioned cerate for batik, this approach includes the following steps；
A: paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin and lanolin magnesium soap are distinguished into heating and melting, and are uniformly mixed, is obtained
A product；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: neopelex and triethylamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.
Claims (3)
1. a kind of cerate for batik, it is characterised in that: the wax is to be made of raw material from the following weight: 50 ~ 60 parts of paraffin,
20 ~ 40 parts of beeswax, 10 ~ 20 parts of rapeseed oil wax, 2 ~ 3 parts of C 5 petroleum resin, 30 ~ 50 parts of lanolin magnesium soap, detergent alkylate sulphur
2 ~ 3 parts of sour sodium, 10 ~ 20 parts of triethylamine.
2. a kind of cerate for batik according to claim 1, it is characterised in that: the wax is by following parts by weight
Raw material is made: 55 parts of paraffin, 30 parts of beeswax, and 15 parts of rapeseed oil wax, 2.5 parts of C 5 petroleum resin, 40 parts of lanolin magnesium soap, 12
2.5 parts of sodium alkyl benzene sulfonate, 15 parts of triethylamine.
3. a kind of preparation method of cerate for batik according to claim 1 or 2, it is characterised in that: this method packet
Include following steps；
A: paraffin, beeswax, rapeseed oil wax, C 5 petroleum resin and lanolin magnesium soap are distinguished into heating and melting, and are uniformly mixed, is obtained
A product；
B: A product are cooled to room temperature, and obtain B product；
C: B product are heated to melting completely, are stirred 15min, are obtained C product；
D: neopelex and triethylamine are added into C product, stirs evenly, obtains D product；
E: by D product be cooled to room temperature to get.