CN109239814A - 一种抗紫外线护目镜片及其制备方法 - Google Patents
一种抗紫外线护目镜片及其制备方法 Download PDFInfo
- Publication number
- CN109239814A CN109239814A CN201811129404.5A CN201811129404A CN109239814A CN 109239814 A CN109239814 A CN 109239814A CN 201811129404 A CN201811129404 A CN 201811129404A CN 109239814 A CN109239814 A CN 109239814A
- Authority
- CN
- China
- Prior art keywords
- parts
- uvioresistant
- screening glass
- modified epoxy
- eyeglass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗紫外线护目镜片及其制备方法。该镜片包括以下按重量份数计的组分：乙二醇碳酸酯60‑85份、丙烯基二甘醇碳酸酯30‑48份、改性环氧树脂12‑24份、纳米碳1‑7份、碳纤维14‑38份、植物提取物10‑28份、二氧化硅13‑23份、维生素E 1‑3份、紫外吸收剂2‑4份、脱模剂0.1‑0.3份、海藻精3‑8份、丙烯醇2‑4份；所述改性环氧树脂由环氧树脂、多巴胺溶液和螺环类化合物混合而成。与现有技术相比，本发明抗紫外线护目镜片及其制备方法，所得镜片的抗紫外线能力强，耐磨性好，由于氮杂螺环类化合物和海藻精的协同作用，提高了镜片的滤蓝光量，提高了保护效果，且来源环保，对人体无伤害。
Description
技术领域
本发明涉及镜片制备领域，具体涉及一种抗紫外线护目镜片及其制备方法。
背景技术
防护眼镜为一种滤光镜，可以改变透光强度和光谱，避免辐射光对眼睛造成伤害，最有效和最常用的方法是佩戴防护眼镜。目前市场上的护目镜片不仅结构复杂，而且功能单一，层状结构的镜片长期使用，容易损坏，因此，需要从镜片的材质上着手，提供一种更耐用，防辐射效果更好的镜片，满足人们的生活需求。
申请号200610111337.5，名称为一种丙烯基二甘醇碳酸酯护目镜片及其制造方法，其生产原料包括以下重量份组分：丙烯基二甘醇碳酸酯380-960，甲基丙烯酸甲酯90-400，丙烯腈5-15，甲基丙烯乙二醇酯4-16，二丁酯10-32，偶氮化合物4-15，棕榈酸异丙酯3-10，2-羟基-4-正辛氧基二苯甲酮1.2-5.5，聚酯丙烯酸树脂2.4-10，抗氧剂18-50，增白剂6-22，硬脂酸2.2-9.5。本发明具有良好的吸收紫外线的功能，有效地保护操作人员的眼睛，镜片不粘接焊渣，延长了镜片的使用寿命，镜片硬度大，镜片耐高温、耐严寒。但是该镜片的耐磨性差，尤其是作为焊接罩用护目镜，时间长便会影响视线。
申请号201711412046.4，名称为树脂眼镜片，包括以下质量份比的原料：聚碳酸酯50～70份，烯丙基二甘醇酸脂10～20份，季戊四醇四巯基乙酸酯10～20份，纤维硝酸酯15～20份，丙烯醇2～4份，紫外线吸收剂1～3份，偶联剂3～5份，催化剂0.5～1.5份，脱模剂0.5～1.5份。本发明与现有技术相比可以使得树脂镜片具有优良折射率和透光率的同时，能够大大提高树脂镜片的防雾性能，有利于提高眼镜的舒适性。虽然树脂眼镜片透光性好，但耐磨性能有限，使用后需要精心保护，否则需要经常更换，增加了成本。
发明内容
针对现有技术不足，本发明的目的在于提供一种抗紫外线护目镜片及其制备方法，该护目镜片吸收紫外线的能力强，硬度高，不易破碎，耐磨损，不易产生划痕。
一种抗紫外线护目镜片，包括以下按重量份数计的组分：乙二醇碳酸酯60-85份、丙烯基二甘醇碳酸酯30-48份、改性环氧树脂12-24份、纳米碳1-7份、碳纤维14-38份、植物提取物10-28份、二氧化硅13-23份、维生素E 1-3份、 紫外吸收剂2-4份、脱模剂0.1-0.3份、海藻精3-8份、丙烯醇2-4份；所述改性环氧树脂由环氧树脂、多巴胺溶液和螺环类化合物混合而成。
作为改进的是，上述抗紫外线护目镜片，包括以下按重量份数计的组分：乙二醇碳酸酯78份、丙烯基二甘醇碳酸酯42份、改性环氧树脂18份、纳米碳4份、碳纤维30份、植物提取物22份、二氧化硅18份、维生素E 2份、 紫外吸收剂3份、脱模剂0.2份、海藻精6份、丙烯醇3份。
作为改进的是，所述植物提取物为银杏叶提取物。
作为改进的是，所述改性环氧树脂的制备方法，将环氧树脂放入球磨机中磨碎，并浸入多巴胺溶液中，再加入螺环类化合物，搅拌均匀后，喷雾干燥，即可。
作为改进的是，所述环氧树脂、多巴胺溶液和螺环类化合物的摩尔比为6:3:5。
作为改进的是，所述螺环类化合物为氮杂螺环类化合物。
上述抗紫外线护目镜片的制备方法，包括以下步骤：
步骤1，称取各组分混合物；
步骤2，将乙二醇碳酸酯、丙烯基二甘醇碳酸酯和改性环氧树脂投入反应釜中，加热至融化后，加入纳米碳、碳纤维和二氧化硅，继续加热至，全部融化，得混合物A；
步骤3，向混合物A中加入植物提取物、维生素E、海藻精和丙烯醇，搅拌后，投入挤出机中挤出母粒；
步骤4，将母粒投入模具中，再次熔融后，加入紫外吸收剂和脱模剂，搅拌均匀，即得护目镜片。
有益效果：
与现有技术相比，本发明抗紫外线护目镜片及其制备方法，所得镜片的抗紫外线能力强，耐磨性好，由于氮杂螺环类化合物和海藻精的协同作用，提高了镜片的滤蓝光量，提高了保护效果，且来源环保，对人体无伤害。另外，制备方法简单，化学添加剂少，制备过程中对环境友好度高。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种抗紫外线护目镜片，包括以下按重量份数计的组分：乙二醇碳酸酯60份、丙烯基二甘醇碳酸酯30份、改性环氧树脂12份、纳米碳1份、碳纤维14份、银杏叶提取物10份、二氧化硅13份、维生素E 1份、 紫外吸收剂2份、脱模剂0.1份、海藻精3份、丙烯醇2份；所述改性环氧树脂的制备方法，将环氧树脂放入球磨机中磨碎，并浸入多巴胺溶液中，再加入螺环类化合物，搅拌均匀后，喷雾干燥，即可，其中，环氧树脂、多巴胺溶液和氮杂螺环类化合物的摩尔比为6:3:5。
上述抗紫外线护目镜片的制备方法，包括以下步骤：
步骤1，称取各组分混合物；
步骤2，将乙二醇碳酸酯、丙烯基二甘醇碳酸酯和改性环氧树脂投入反应釜中，加热至融化后，加入纳米碳、碳纤维和二氧化硅，继续加热至全部融化，得混合物A；
步骤3，向混合物A中加入植物提取物、维生素E、海藻精和丙烯醇，搅拌后，投入挤出机中挤出母粒；
步骤4，将母粒投入模具中，再次熔融后，加入紫外吸收剂和脱模剂，搅拌均匀，即得护目镜片。
按照常规的检测方法对镜片进行测试，本发明镜片有效过滤42%以上的有害蓝光，透光率保持在82%以上，对于视觉的清晰度和真实性有着很好的贡献。20000转下打磨后，镜片的磨损量为5%。制备过程中，将酯类混合后，再加入其他组分，保证各组分混合均一性，最后添加紫外吸收剂和脱模剂，有效提高了镜片的抗紫外能力。
实施例2
一种抗紫外线护目镜片，包括以下按重量份数计的组分：
乙二醇碳酸酯78份、丙烯基二甘醇碳酸酯42份、改性环氧树脂18份、纳米碳4份、碳纤维30份、银杏叶提取物22份、二氧化硅18份、维生素E 2份、 紫外吸收剂3份、脱模剂0.2份、海藻精6份、丙烯醇3份。所述改性环氧树脂的制备方法，将环氧树脂放入球磨机中磨碎，并浸入多巴胺溶液中，再加入螺环类化合物，搅拌均匀后，喷雾干燥，即可，其中，环氧树脂、多巴胺溶液和氮杂螺环类化合物的摩尔比为6:3:5。
上述抗紫外线护目镜片的制备方法，包括以下步骤：
步骤1，称取各组分混合物；
步骤2，将乙二醇碳酸酯、丙烯基二甘醇碳酸酯和改性环氧树脂投入反应釜中，加热至融化后，加入纳米碳、碳纤维和二氧化硅，继续加热至全部融化，得混合物A；
步骤3，向混合物A中加入植物提取物、维生素E、海藻精和丙烯醇，搅拌后，投入挤出机中挤出母粒；
步骤4，将母粒投入模具中，再次熔融后，加入紫外吸收剂和脱模剂，搅拌均匀，即得护目镜片。
按照常规的检测方法对镜片进行测试，本发明镜片有效过滤51%以上的有害蓝光，透光率保持在87%以上，对于视觉的清晰度和真实性有着很好的贡献。20000转下打磨后，镜片的磨损量为2%。制备过程中，将酯类混合后，再加入其他组分，保证各组分混合均一性，最后添加紫外吸收剂和脱模剂，有效提高了镜片的抗紫外能力。
实施例3
一种抗紫外线护目镜片，包括以下按重量份数计的组分：乙二醇碳酸酯60-85份、丙烯基二甘醇碳酸酯30-48份、改性环氧树脂12-24份、纳米碳1-7份、碳纤维14-38份、银杏叶提取物10-28份、二氧化硅13-23份、维生素E 1-3份、 紫外吸收剂2-4份、脱模剂0.1-0.3份、海藻精3-8份、丙烯醇2-4份；所述改性环氧树脂的制备方法，将环氧树脂放入球磨机中磨碎，并浸入多巴胺溶液中，再加入螺环类化合物，搅拌均匀后，喷雾干燥，即可，其中，环氧树脂、多巴胺溶液和氮杂螺环类化合物的摩尔比为6:3:5。
上述抗紫外线护目镜片的制备方法，包括以下步骤：
步骤1，称取各组分混合物；
步骤2，将乙二醇碳酸酯、丙烯基二甘醇碳酸酯和改性环氧树脂投入反应釜中，加热至融化后，加入纳米碳、碳纤维和二氧化硅，继续加热至全部融化，得混合物A；
步骤3，向混合物A中加入植物提取物、维生素E、海藻精和丙烯醇，搅拌后，投入挤出机中挤出母粒；
步骤4，将母粒投入模具中，再次熔融后，加入紫外吸收剂和脱模剂，搅拌均匀，即得护目镜片。
按照常规的检测方法对镜片进行测试，本发明镜片有效过滤38%以上的有害蓝光，透光率保持在80%以上，对于视觉的清晰度和真实性有着很好的贡献。20000转下打磨后，镜片的磨损量为7%。制备过程中，将酯类混合后，再加入其他组分，保证各组分混合均一性，最后添加紫外吸收剂和脱模剂，有效提高了镜片的抗紫外能力。
对比例1
除不含海藻精外，其余同实施例2。
由于对比例1中不含有海藻精，缺少了活性成分海藻酸，滤光的能力降低。按照常规的检测方法对镜片进行测试，本发明镜片有效过滤28%的有害蓝光，透光率保持在65%。
对比例2
除改性环氧树脂更改为环氧树脂外，其余同实施例2。
改性处理的环氧树脂，负载了氮杂螺环类化合物，提高了镜片的滤过性能。按照常规的检测方法对镜片进行测试，本发明镜片有效过滤25%的有害蓝光，透光率保持在62%。
通过比较实施例2与对比例1-2可知，本发明的护目镜由于氮杂螺环类化合物和海藻精的协同作用，提高了镜片的滤蓝光量，提高了保护效果，且来源环保，对人体无伤害。
以上所述，仅为本发明较佳的具体实施方式，本发明的保护范围不限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可显而易见地得到的技术方案的简单变化或等效替换均落入本发明的保护范围内。
Claims (7)
1.一种抗紫外线护目镜片，其特征在于，包括以下按重量份数计的组分：乙二醇碳酸酯60-85份、丙烯基二甘醇碳酸酯30-48份、改性环氧树脂12-24份、纳米碳1-7份、碳纤维14-38份、植物提取物10-28份、二氧化硅13-23份、维生素E 1-3份、 紫外吸收剂2-4份、脱模剂0.1-0.3份、海藻精3-8份、丙烯醇2-4份；所述改性环氧树脂由环氧树脂、多巴胺溶液和螺环类化合物混合而成。
2.根据权利要求1所述的一种抗紫外线护目镜片，其特征在于，包括以下按重量份数计的组分：乙二醇碳酸酯78份、丙烯基二甘醇碳酸酯42份、改性环氧树脂18份、纳米碳4份、碳纤维30份、植物提取物22份、二氧化硅18份、维生素E 2份、 紫外吸收剂3份、脱模剂0.2份、海藻精6份、丙烯醇3份。
3.根据权利要求1所述的一种抗紫外线护目镜片，其特征在于，所述植物提取物为银杏叶提取物。
4.根据权利要求1所述的一种抗紫外线护目镜片，其特征在于，所述改性环氧树脂的制备方法，将环氧树脂放入球磨机中磨碎，并浸入多巴胺溶液中，再加入螺环类化合物，搅拌均匀后，喷雾干燥，即可。
5.根据权利要求1所述的一种抗紫外线护目镜片，其特征在于，所述环氧树脂、多巴胺溶液和螺环类化合物的摩尔比为6:3:5。
6.根据权利要求1所述的一种抗紫外线护目镜片，其特征在于，所述螺环类化合物为氮杂螺环类化合物。
7.基于权利要求1所述的一种抗紫外线护目镜片的制备方法，其特征在于，包括以下步骤：步骤1，称取各组分混合物；步骤2，将乙二醇碳酸酯、丙烯基二甘醇碳酸酯和改性环氧树脂投入反应釜中，加热至融化后，加入纳米碳、碳纤维和二氧化硅，继续加热至，全部融化，得混合物A；步骤3，向混合物A中加入植物提取物、维生素E、海藻精和丙烯醇，搅拌后，投入挤出机中挤出母粒；步骤4，将母粒投入模具中，再次熔融后，加入紫外吸收剂和脱模剂，搅拌均匀，即得护目镜片。