CN109233469A - A kind of air purifying preparation and preparation method thereof - Google Patents
A kind of air purifying preparation and preparation method thereof Download PDFInfo
- Publication number
- CN109233469A CN109233469A CN201810811632.4A CN201810811632A CN109233469A CN 109233469 A CN109233469 A CN 109233469A CN 201810811632 A CN201810811632 A CN 201810811632A CN 109233469 A CN109233469 A CN 109233469A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- air purifying
- purifying preparation
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of air purifying preparation and preparation method thereof, the air purifying preparation includes that following parts by weight prepare raw material: 10~20 parts of water-soluble resin, 0.2~1 part of coalescing agent, 1~3 part of visible light catalyst, 0.1~0.8 part of silane coupling agent, 1~3 part of nanometer anion powder, 0.2~0.6 part of substrate wetting agents, 0.5~2 part of Nano silver solution, 0.2~0.8 part of defoaming agent, 0.3~1 part of dispersing agent and 70~80 parts of water.By adding visible light catalyst, nanometer anion powder and Nano silver solution in water-soluble resin, the formaldehyde in air can be effectively removed, sterilization rate can reach 99% or more, and can also into air releasing negative oxygen ion, indoor air quality can be greatly promoted.The preparation process of air purifying preparation is simple, and obtained air purifying preparation can be sprayed directly, is easy to construct.
Description
Technical field
The present invention relates to technical field of air purification more particularly to a kind of air purifying preparation and preparation method thereof.
Background technique
With the improvement of living standards, requirement of the people to house ornamentation is also higher and higher, although all when selecting finishing material
Selection environmental protection, standard compliant product as far as possible, but the pollutant of the releases such as various furniture, wallpaper and finishing paint is mutually folded
Add, still results in indoor air quality and do not reach requirement.
In indoor air environment, formaldehyde is most important polluter, has very strong teratogenesis and carcinogenicity, to the mankind
Health hazard is larger, and contactee is gently then made to generate dizziness, eyes stung, unsmooth breath or the generation diseases such as asthma, heavy then can draw
Send out immunologic dysfunction, allotriosmia, abnormal pulmonary function and dysfunction of liver etc..
There are a large amount of purifying formaldehyde coating, such as addition Formaldehyde decomposition material, bamboo charcoal coating, diatom mash currently on the market
Material and light catalyzed coating etc., although PARA FORMALDEHYDE PRILLS(91,95) has certain decomposition, discomposing effect is limited, and all there is apply
The problem of work is more troublesome, and professional is needed to construct.Therefore, develop that a kind of purifying formaldehyde effect is good, simple easily construction
Indoor air purification agent to improve air quality and guarantee the mankind health have significant practical significance.
Summary of the invention
The technical problems to be solved by the present invention are: provide a kind of air purifying preparation and preparation method thereof, PARA FORMALDEHYDE PRILLS(91,95) it is net
It is good to change effect, is easy to construct.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention are as follows:
A kind of air purifying preparation prepares raw material including following parts by weight: 10~20 parts of water-soluble resin, coalescing agent
0.2~1 part, 1~3 part of visible light catalyst, 0.1~0.8 part of silane coupling agent, 1~3 part of nanometer anion powder, substrate wetting
0.2~0.6 part of agent, 0.5~2 part of Nano silver solution, 0.2~0.8 part of defoaming agent, 0.3~1 part of dispersing agent and 70~80 parts of water.
Another technical solution that the present invention uses are as follows:
A kind of preparation method of air purifying preparation, by the parts by weight of the air purifying preparation, soluble resin of fetching water respectively,
Coalescing agent, silane coupling agent, nanometer anion powder, substrate wetting agents, Nano silver solution, defoaming agent, is divided visible light catalyst
Powder and water；By 0.1~0.5 part of silane coupling agent, 10~20 parts of water, 0.1~0.2 part of defoaming agent, 0.1~0.4 part
Dispersing agent and visible light catalyst mixed, obtain catalysis slurry；By remaining silane coupling agent, 10~15 parts of water,
0.1~0.2 part of defoaming agent, 0.1~0.4 part of dispersing agent and nanometer anion powder are mixed, and anion slurry is obtained；It will
Substrate wetting agents, water-soluble resin, coalescing agent, 10~20 parts of water, remaining dispersing agent and remaining defoaming agent are mixed
It closes, obtains resin slurry；Catalysis slurry, anion slurry and resin slurry are mixed, be then added Nano silver solution and
Remaining water obtains the air purifying preparation.
The beneficial effects of the present invention are: by adding visible light catalyst, nanometer anion powder in water-soluble resin
And Nano silver solution, the formaldehyde in air can be effectively removed, sterilization rate can reach 99% or more, and can also be into air
Releasing negative oxygen ion can greatly promote indoor air quality.The preparation process of air purifying preparation is simple, obtained air purifying preparation
It can directly be sprayed, be easy to construct.
Specific embodiment
To explain the technical content, the achieved purpose and the effect of the present invention in detail, it is explained below in conjunction with embodiment.
The most critical design of the present invention is: by adding visible light catalyst, nano-negative ion in water-soluble resin
Powder and Nano silver solution can effectively remove the formaldehyde in air, greatly promote indoor air quality.
A kind of air purifying preparation prepares raw material including following parts by weight: 10~20 parts of water-soluble resin, coalescing agent
0.2~1 part, 1~3 part of visible light catalyst, 0.1~0.8 part of silane coupling agent, 1~3 part of nanometer anion powder, substrate wetting
0.2~0.6 part of agent, 0.5~2 part of Nano silver solution, 0.2~0.8 part of defoaming agent, 0.3~1 part of dispersing agent and 70~80 parts of water.
As can be seen from the above description, the beneficial effects of the present invention are: by adding visible light catalytic in water-soluble resin
Agent, nanometer anion powder and Nano silver solution, can effectively remove the formaldehyde in air, and sterilization rate can reach 99% or more, and
And can also into air releasing negative oxygen ion, indoor air quality can be greatly promoted.
Further, the water-soluble resin is water-soluble styrene-acrylic resin, soluble polyurethane and water-soluble fluorine carbon resin
At least one of.
Further, the coalescing agent is Lauryl Alcohol ester, butyl glycol ether, propylene glycol phenylate and hexylene glycol butyl ether vinegar
At least one of acid esters.
Further, the visible light catalyst is nano-titanium dioxide.
Further, the silane coupling agent is methacryloxypropyl silane, silicon ester, amino silane and epoxy group silicon
At least one of alkane.
Seen from the above description, the type of water-soluble resin, coalescing agent and silane coupling agent can according to need progress
Selection.
Further, the partial size of the nanometer anion powder is less than 50nm, and anion burst size is greater than 5000ions/cm3。
Further, the content of nano silver is greater than 3000ppm in the Nano silver solution.
Another technical solution of the present invention are as follows:
A kind of preparation method of air purifying preparation, by the parts by weight of the air purifying preparation, soluble resin of fetching water respectively,
Coalescing agent, silane coupling agent, nanometer anion powder, substrate wetting agents, Nano silver solution, defoaming agent, is divided visible light catalyst
Powder and water；By 0.1~0.5 part of silane coupling agent, 10~20 parts of water, 0.1~0.2 part of defoaming agent, 0.1~0.4 part
Dispersing agent and visible light catalyst mixed, obtain catalysis slurry；By remaining silane coupling agent, 10~15 parts of water,
0.1~0.2 part of defoaming agent, 0.1~0.4 part of dispersing agent and nanometer anion powder are mixed, and anion slurry is obtained；It will
Substrate wetting agents, water-soluble resin, coalescing agent, 10~20 parts of water, remaining dispersing agent and remaining defoaming agent are mixed
It closes, obtains resin slurry；Catalysis slurry, anion slurry and resin slurry are mixed, be then added Nano silver solution and
Remaining water obtains the air purifying preparation.
Seen from the above description, the preparation process of air purifying preparation is simple, and obtained air purifying preparation can be carried out directly
Spraying, is easy to construct, and advantageously reduces cost, colorless and transparent after film forming, does not influence the appearance and color of coated article, can directly spray
It is applied on metope, ceiling, furniture and curtain.
It further, further include adjusting the pH value of air purifying preparation to 7~8.
Further, further include successively to the air purifying preparation be filtered with it is filling.
Seen from the above description, it is readily transported and constructs after filling, 2~3min, that is, sprayable is shaken before constructing.
Embodiment one
The embodiment of the present invention one are as follows: a kind of preparation method of air purifying preparation comprises the following processes:
Weigh respectively 10 parts of water-soluble resin, 0.2 part of coalescing agent, 1 part of visible light catalyst, 0.7 part of silane coupling agent,
3 parts of nanometer anion powder, 0.4 part of substrate wetting agents, 1 part of Nano silver solution, 0.7 part of defoaming agent, 0.9 part of dispersing agent and water 70
Part, the solvent of Nano silver solution is water.The water-soluble resin is water-soluble styrene-acrylic resin, soluble polyurethane and water-soluble fluorine
At least one of carbon resin, the coalescing agent are Lauryl Alcohol ester, butyl glycol ether, propylene glycol phenylate and hexylene glycol butyl ether
At least one of acetate, the visible light catalyst are nano-titanium dioxide, and the silane coupling agent is methacryl
The partial size of at least one of oxysilane, silicon ester, amino silane and epoxy radicals silicone hydride, the nanometer anion powder is less than
50nm, anion burst size are greater than 5000ions/cm3, the content of nano silver is greater than 3000ppm in the Nano silver solution.
0.2 part of silane coupling agent is added in 10 parts of water, adds 0.1 part of defoaming agent and 0.2 part of dispersing agent,
It stirs evenly, is then slowly added into 1 part of visible light catalyst, stirred under ultrasonication, catalysis slurry is prepared, it is standby
With；
0.5 part of silane coupling agent is added in 15 parts of water, adds 0.2 part of defoaming agent and 0.4 part of dispersing agent,
It stirs evenly, is then slowly added into 3 parts of nanometer anion powder, stirred under ultrasonication, anion slurry is prepared, it is standby
With；
35 parts of water, 0.3 part of dispersing agent, 0.4 part of substrate wetting agents, 0.4 part of defoaming agent are sequentially added into stirring
In cylinder, 10 parts of water-soluble resin is then added, stirs at low speed, is then slowly added into 0.2 part of coalescing agent, fills each component
Divide and be uniformly mixed, obtains resin slurry, it is spare；
Holding stirs at low speed, and catalysis slurry and anion slurry is slowly added in resin slurry, after mixing evenly again
Be slowly added into 1.0 parts of Nano silver solution, be added remaining water, adjust pH value to 7~8, be then successively filtered with it is canned,
Obtain air purifying preparation.
Embodiment two
The embodiment of the present invention two are as follows: a kind of preparation method of air purifying preparation comprises the following processes:
20 parts of water-soluble resin is weighed respectively, 1 part of coalescing agent, 3 parts of visible light catalyst, 0.8 part of silane coupling agent, is received
1 part of negative ion powder of rice, 0.6 part of substrate wetting agents, 2 parts of Nano silver solution, 0.8 part of defoaming agent, 1 part of dispersing agent and 80 parts of water, receive
The silver-colored solution of rice is the aqueous solution of nano silver.The water-soluble resin is water-soluble styrene-acrylic resin, soluble polyurethane and water solubility
At least one of fluorocarbon resin, the coalescing agent are Lauryl Alcohol ester, butyl glycol ether, propylene glycol phenylate and hexylene glycol fourth
At least one of ether acetate, the visible light catalyst are nano-titanium dioxide, and the silane coupling agent is metering system
The partial size of at least one of acyloxy silane, silicon ester, amino silane and epoxy radicals silicone hydride, the nanometer anion powder is less than
50nm, anion burst size are greater than 5000ions/cm3, the content of nano silver is greater than 3000ppm in the Nano silver solution.
0.3 part of silane coupling agent is added in 20 parts of water, adds 0.2 part of defoaming agent and 0.3 part of dispersing agent,
It stirs evenly, is then slowly added into 3 parts of visible light catalyst, stirred under ultrasonication, catalysis slurry is prepared, it is standby
With；
0.5 part of silane coupling agent is added in 15 parts of water, adds 0.2 part of defoaming agent and 0.4 part of dispersing agent,
It stirs evenly, is then slowly added into 1 part of nanometer anion powder, stirred under ultrasonication, anion slurry is prepared, it is standby
With；
35 parts of water, 0.3 part of dispersing agent, 0.6 part of substrate wetting agents, 0.4 part of defoaming agent are sequentially added into stirring
In cylinder, 20 parts of water-soluble resin is then added, stirs at low speed, is then slowly added into 1 part of coalescing agent, keep each component abundant
It is uniformly mixed, obtains resin slurry, it is spare；
Holding stirs at low speed, and catalysis slurry and anion slurry is slowly added in resin slurry, after mixing evenly again
Be slowly added into 2 parts of Nano silver solution, be added remaining water, adjust pH value to 7~8, be then successively filtered with it is canned, obtain
To air purifying preparation.
Embodiment three
The embodiment of the present invention three are as follows: a kind of preparation method of air purifying preparation comprises the following processes:
Weigh respectively 15 parts of water-soluble resin, 0.6 part of coalescing agent, 2 parts of visible light catalyst, 0.1 part of silane coupling agent,
2 parts of nanometer anion powder, 0.2 part of substrate wetting agents, 0.5 part of Nano silver solution, 0.2 part of defoaming agent, 0.3 part of dispersing agent and water 75
Part, Nano silver solution is the aqueous solution of nano silver.The water-soluble resin is water-soluble styrene-acrylic resin, soluble polyurethane and water
At least one of dissolubility fluorocarbon resin, the coalescing agent be Lauryl Alcohol ester, butyl glycol ether, propylene glycol phenylate and oneself two
At least one of alcohol monobutyl ether acetate, the visible light catalyst are nano-titanium dioxide, and the silane coupling agent is methyl
At least one of acryloxy silane, silicon ester, amino silane and epoxy radicals silicone hydride, the partial size of the nanometer anion powder
Less than 50nm, anion burst size is greater than 5000ions/cm3, the content of nano silver is greater than in the Nano silver solution
3000ppm。
0.05 part of silane coupling agent is added in 15 parts of water, adds 0.05 part of defoaming agent and 0.1 part of dispersion
Agent stirs evenly, and is then slowly added into 2 parts of visible light catalyst, stirs under ultrasonication, and catalysis slurry is prepared,
It is spare；
0.05 part of silane coupling agent is added in 15 parts of water, adds 0.05 part of defoaming agent and 0.1 part of dispersion
Agent stirs evenly, and is then slowly added into 2 parts of nanometer anion powder, stirs under ultrasonication, and anion slurry is prepared
Material, it is spare；
35 parts of water, 0.1 part of dispersing agent, 0.2 part of substrate wetting agents, 0.1 part of defoaming agent are sequentially added into stirring
In cylinder, 15 parts of water-soluble resin is then added, stirs at low speed, is then slowly added into 0.6 part of coalescing agent, fills each component
Divide and be uniformly mixed, obtains resin slurry, it is spare；
Holding stirs at low speed, and catalysis slurry and anion slurry is slowly added in resin slurry, after mixing evenly again
Be slowly added into 0.5 part of Nano silver solution, be added remaining water, adjust pH value to 7~8, be then successively filtered with it is canned,
Obtain air purifying preparation.
It verifies through practice of construction, can directly be sprayed after the air purifying preparation that embodiment one is prepared to embodiment three is filling
It is applied on metope, ceiling, furniture and curtain, it is colorless and transparent after film forming, the appearance and color of coated article are not influenced.
The air purifying preparation that embodiment one to embodiment three obtains is subjected to purifying formaldehyde efficiency, purifying formaldehyde efficiency respectively
Persistence, antibacterium rate, antibacterium endurance quality, Anti-mildew capability, antifungi endurance quality and the test of anion burst size, are surveyed
Test result is as shown in table 1.
The performance test results of 1 air purifying preparation of table
As known from Table 1, the purifying formaldehyde for the air purifying preparation being prepared is high-efficient, and persistence is good, antibacterial effect
It is good, a large amount of anion can be discharged, indoor air quality can be substantially improved.
In conclusion a kind of air purifying preparation provided by the invention and preparation method thereof, the purification of air purifying preparation PARA FORMALDEHYDE PRILLS(91,95)
It is high-efficient, and persistence is good, good anti-bacterial effect, can discharge a large amount of anion, can substantially improve indoor air quality, preparation
Process is simple, is easy to construct.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalents made by bright description are applied directly or indirectly in relevant technical field, are similarly included in this hair
In bright scope of patent protection.
Claims (10)
1. a kind of air purifying preparation, which is characterized in that prepare raw material including following parts by weight: 10~20 parts of water-soluble resin,
0.2~1 part of coalescing agent, 1~3 part of visible light catalyst, 0.1~0.8 part of silane coupling agent, 1~3 part of nanometer anion powder,
0.2~0.6 part of substrate wetting agents, 0.5~2 part of Nano silver solution, 0.2~0.8 part of defoaming agent, 0.3~1 part of dispersing agent and water 70
~80 parts.
2. air purifying preparation according to claim 1, which is characterized in that the water-soluble resin is water-soluble phenylpropyl alcohol tree
At least one of rouge, soluble polyurethane and water-soluble fluorine carbon resin.
3. air purifying preparation according to claim 1, which is characterized in that the coalescing agent is Lauryl Alcohol ester, second two
At least one of alcohol butyl ether, propylene glycol phenylate and hexylene glycol monobutyl ether acetate.
4. air purifying preparation according to claim 1, which is characterized in that the visible light catalyst is nanometer titanium dioxide
Titanium.
5. air purifying preparation according to claim 1, which is characterized in that the silane coupling agent is methacryloxy
At least one of silane, silicon ester, amino silane and epoxy radicals silicone hydride.
6. air purifying preparation according to claim 1, which is characterized in that the partial size of the nanometer anion powder is less than
50nm, anion burst size are greater than 5000ions/cm3。
7. air purifying preparation according to claim 1, which is characterized in that the content of nano silver is big in the Nano silver solution
In 3000ppm.
8. a kind of preparation method of air purifying preparation, which is characterized in that by air cleaning described in claim 1-7 any one
The parts by weight of agent, fetch water respectively soluble resin, coalescing agent, visible light catalyst, silane coupling agent, nanometer anion powder, base
Material wetting agent, Nano silver solution, defoaming agent, dispersing agent and water；By 0.1~0.5 part of silane coupling agent, 10~20 parts of water,
0.1~0.2 part of defoaming agent, 0.1~0.4 part of dispersing agent and visible light catalyst are mixed, and catalysis slurry is obtained；It will remain
Remaining silane coupling agent, 10~15 parts of water, 0.1~0.2 part of defoaming agent, 0.1~0.4 part of dispersing agent and nano-negative ion
Powder is mixed, and anion slurry is obtained；By substrate wetting agents, water-soluble resin, coalescing agent, 10~20 parts of water, residue
Dispersing agent and remaining defoaming agent mixed, obtain resin slurry；Will catalysis slurry, anion slurry and resin slurry into
Row mixing, is then added Nano silver solution and remaining water, obtains the air purifying preparation.
9. the preparation method of air purifying preparation according to claim 8, which is characterized in that further include adjusting air purifying preparation
PH value to 7~8.
10. the preparation method of air purifying preparation according to claim 8, which is characterized in that further include successively to the sky
Gas cleanser be filtered with it is filling.