CN108299956A - One kind is except aldehyde ordor removing sealer and preparation method thereof - Google Patents

One kind is except aldehyde ordor removing sealer and preparation method thereof Download PDF

Info

Publication number
CN108299956A
CN108299956A CN201710785340.3A CN201710785340A CN108299956A CN 108299956 A CN108299956 A CN 108299956A CN 201710785340 A CN201710785340 A CN 201710785340A CN 108299956 A CN108299956 A CN 108299956A
Authority
CN
China
Prior art keywords
ordor removing
sealer
aldehyde ordor
enzyme
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710785340.3A
Other languages
Chinese (zh)
Other versions
CN108299956B (en
Inventor
李浪
胡朝建
张金明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beiken (Zhejiang) Technology Development Co.,Ltd.
Original Assignee
Suzhou Baiyi Beiken New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Baiyi Beiken New Mstar Technology Ltd filed Critical Suzhou Baiyi Beiken New Mstar Technology Ltd
Priority to CN201710785340.3A priority Critical patent/CN108299956B/en
Publication of CN108299956A publication Critical patent/CN108299956A/en
Application granted granted Critical
Publication of CN108299956B publication Critical patent/CN108299956B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provides one kind except aldehyde ordor removing sealer and preparation method thereof.The present invention's removes aldehyde ordor removing sealer, by mass percentage, including following substance:4~20% film forming agent, 0.1~5% nanometer anion powder, 0.5~5% benzene homologues catabolic enzyme, 0.5~5% ester catabolic enzyme, 0.5~5% Formaldehyde decomposition enzyme, 0.03~0.05% activator, 0.1~2% stabilization moisturizer and the water of surplus, wherein, the film forming agent is water soluble chitosan.The present invention prepares raw material and proportioning by rationally control, and what is obtained removes aldehyde ordor removing sealer safety and environmental protection, and to the good purification of indoor pollution air, clean-up effect is lasting.Preparation process of the present invention is simple, obtained except aldehyde ordor removing sealer can be brushed directly, be sprayed at the base materials such as furniture, wallpaper, abatvoix, carpet, floor, adsorbs and decomposes the polluted gas such as the formaldehyde in air, TVOC.

Description

One kind is except aldehyde ordor removing sealer and preparation method thereof
Technical field
The invention belongs to technical field of air purification, are related to a kind of except aldehyde ordor removing sealer and preparation method thereof.
Background technology
In recent years, indoor pollution has become the important threat lived to people's house and health, Environment Protect in China association Related data statistics shows:Once luxurious finishing was carried out in 90% leukemia children man, annual 2100000 children die of luxurious coating It repaiies;80% house decoration formaldehyde;70% pregnant woman miscarriage is related with environmental pollution;Annual China draws because of indoor environmental pollution The death toll risen is up to 11.1 ten thousand people, and average daily 304 people is dead.Indoor environmental pollution, which has become, seriously affects modern One of the killer of class health.Indoors in fitment process, all more or less contain first in plank, glue, wall covering, furniture The harmful substances such as aldehyde, benzene homologues several years after finishing even all can be distributed gradually in many decades, to influence health.
In order to solve the pollution problem of room air, currently, including in the market having using more air clearing product The water paint of air-cleaning function, such as light-catalyst pigment for internal-wall, the air purification paint comprising nano-negative ion, environmentally friendly latex Paint etc.;Further include the air clearing products such as air filter, activated carbon.But the dirt of air clearing product in the prior art Dye object clean-up effect is to be improved, and clean-up effect persistence is bad.
CN105969007A discloses a kind of acrylic latex coating and preparation method thereof with air-cleaning function.The breast Shellac varnish includes the component of following mass parts:45-55 parts of acrylic emulsion, 4-6 parts of silica flour, 1-2 parts of phenoxy resin, bletilla striata powder 2- 4 parts, 1-3 parts of cornstarch, 0.25-0.75 parts of glutaraldehyde, 2-4 parts of air purification particle, 0.04-0.06 parts of antifoaming agent, dispersion 0.04-0.06 parts of agent, 30-40 parts of water.The acrylic latex coating of the invention has preferable film forming and resistance to soiling, adsorption capacity Greatly, but its raw material propylene yogurt liquid not environmentally, the effect and persistence of air purification are to be improved.
CN1803949A discloses a kind of building coating material and preparation method thereof with air purification function, the coating Material is mainly made of photochemical catalyst, film forming matter, color stuffing, auxiliary agent and water;Various substances and its weight percent content are such as Under:Photochemical catalyst TiO2-XNX1~3%, film forming matter polyacrylate dispersion 15~25%, dispersants ammonium polyacrylate salt 0.8~2.0%, wetting agent 0.2~0.5%, 0.1~0.2% antifoaming agent 0.6~0.8% of hydroxyethyl cellulose, pigment titanium white 7~9%, filler powdered whiting 25~30%, kaolin 8~10%, talcum powder 4~5%, coalescents 0.8~1.0%, Propylene glycol 1.8~2.0%, thickener 0.5~1.0%, aqueous solvent 20~30%, the building coating material of the invention coated on After material surface film forming, the polluter in the surrounding air that can effectively degrade is organic to indoor formaldehyde-phenol etc. small point harmful Son is degraded, but film forming matter polyacrylate dispersion is not environmentally in its constitutive material, the effect of air purification and purification Persistence it is to be improved.
CN104874286A discloses a kind of immobilised enzymes and removes aldehyde environmental protection coating agent, formula include complex enzyme, chitin, Fixation support material, water, activator can be coated on timber, plank, leather, plastics, glass, walling, non-woven fabrics or papery material Material adsorbs simultaneously these aldehydes persistent organic pollutants of degradation of formaldehyde, benzene,toluene,xylene, PM2.5, ammonia and TVOC, reaches Purify the purpose of air.But the long-term effect of the complex enzyme of the invention is to be improved.
Invention content
In view of the deficiencies of the prior art, one of the objects of the present invention is to provide one kind removing aldehyde ordor removing sealer, safety collar It protects, can effectively adsorb and decompose the pollutants such as the formaldehyde in air and TVOC, clean-up effect is more longlasting.
For this purpose, the present invention uses following technical scheme:
One kind removing aldehyde ordor removing sealer, by mass percentage, including following substance:
Wherein, the film forming agent is water soluble chitosan.
The present invention except aldehyde ordor removing sealer raw material and proportioning, can be specific as follows:
The mass percentage of water soluble chitosan is 4~20%, such as the mass percentage of water soluble chitosan is 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, preferably 5~8%;
The mass percentage of nanometer anion powder is 0.1~5%, such as the mass percentage of nanometer anion powder is 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, preferably 1~1.5%;
The mass percentage of benzene homologues catabolic enzyme is 0.5~5%, such as the mass percentage of benzene homologues catabolic enzyme is 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, it is excellent It is selected as 2~3%;
The mass percentage of ester catabolic enzyme be 0.5~5%, such as ester catabolic enzyme mass percentage be 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, preferably 1~ 2%;
The mass percentage of Formaldehyde decomposition enzyme is 0.5~5%, such as the mass percentage of Formaldehyde decomposition enzyme is 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, it is excellent It is selected as 1~2%;
The mass percentage of activator be 0.03~0.05%, such as activator mass percentage be 0.03%, 0.035%, 0.04%, 0.045%, 0.05%;
The mass percentage for stablizing moisturizer is 0.1~2%, such as the mass percentage of stable moisturizer is 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, preferably 0.8 ~1%;
Surplus is water.
Preferably, described to remove aldehyde ordor removing sealer, by mass percentage, including following substance:
The present invention has a large amount of amino can be with formaldehyde using water soluble chitosan as film forming agent in the structure of water soluble chitosan Reaction, can effectively remove the formaldehyde in pollution air, and compared with the existing technology in common esters of acrylic acid film forming agent, have Safe and environment-friendly advantage.Water soluble chitosan is a kind of derivative of chitosan, under alkaline condition generally by monoxone And chitosan reaction, by-CH2COOH is connected to the-NH of chitosan2Or on-OH, carboxymethyl chitosan is water-soluble very well.Chitosan Water solubility and the deacetylation and the molecular weight of chitosan of chitosan have relationship.In general, deacetylation is higher, water-soluble Property is better;Molecular weight becomes apparent water-soluble influence, and the chitosan of low molecular weight is water-soluble very well.The shell of high molecular weight is poly- Sugared dissolubility is bad, and acid condition is needed to dissolve.Preferably, the molecular weight of the water soluble chitosan of the invention is 20000 ~40000, such as the molecular weight of the water soluble chitosan is 20000,25000,30000,35000,40000.
The water soluble chitosan is carboxymethyl chitosan and/or chitosan quaternary ammonium salt.
Nanometer anion powder is also known as tourmaline anion powder, and ingredient is aluminium, sodium, iron, the lithium ring characterized by boracic The silicate material of shape structure has very strong oxidation also because the negative oxygen ion generated in anion powder has higher activity Original work are used, and the thorns such as benzene, formaldehyde, ketone, the ammonia that the art work used in fitment process indoors evaporates can be effectively eliminated Property gas is swashed, to be effectively improved pollution air.
The grain size of the nanometer anion powder is 1500~4000 mesh, such as the grain size of the nanometer anion powder is 1500、2000、2500、3000、3500、4000。
The mixture of the one kind or at least two of the ester catabolic enzyme in pectase, carboxy-lesterase and lipase.Institute State the mixture that the typical but unrestricted embodiment of mixture is two kinds of ester catabolic enzymes, for example, the ester catabolic enzyme be pectase and The mixture of the mixture of the mixture of carboxy-lesterase, carboxy-lesterase and lipase, pectase and lipase;The mixture is also It can be the mixture of three kinds of ester catabolic enzymes, such as the mixture that the ester catabolic enzyme is pectase, carboxy-lesterase and lipase.
The Formaldehyde decomposition enzyme is formaldehyde dehydrogenase.
The activator is glutathione.
The stable moisturizer is tween and/or glycerine.
Water soluble chitosan and nanometer anion powder and benzene homologues catabolic enzyme, ester catabolic enzyme, Formaldehyde decomposition in the present invention Act synergistically between the biological enzyme such as enzyme, it is adsorbable and decompose pollution air in formaldehyde, TVOC (Total Volatile The abbreviation of Organic Compounds, volatile organic matter) etc. polluted gas, activator and stablize moisturizer addition increase The long-term effect of enzyme.
The second object of the present invention is to provide a kind of preparation method except aldehyde ordor removing sealer, and the preparation method includes Following steps:By mass percentage, 4~20% water soluble chitosan is soluble in water, 0.1~5% is added into solution Nanometer anion powder stirring and dissolving, add 0.5~5% benzene homologues catabolic enzyme, 0.5~5% ester catabolic enzyme, 0.5~ 5% Formaldehyde decomposition enzyme, 0.03~0.05% activator and 0.1~2% stabilization moisturizer and the water of surplus continue to stir, It is made described and removes aldehyde ordor removing sealer.
Compared with prior art, beneficial effects of the present invention are:
(1) present invention prepares raw material and proportioning by rationally control, and what is obtained removes aldehyde ordor removing sealer to indoor pollution sky The good purification of gas, the removal rate of the polluted gas such as PARA FORMALDEHYDE PRILLS(91,95), TVOC is up to 96% or more after use for 24 hours;Clean-up effect is lasting, The removal rate of the polluted gas such as PARA FORMALDEHYDE PRILLS(91,95), TVOC is still up to 93% or more after being used 28 days except aldehyde ordor removing sealer.
(2) preparing for the present invention does not contain esters of acrylic acid, safety and environmental protection in raw material.
(3) of the invention except the preparation process of aldehyde ordor removing sealer is simple, the aldehyde ordor removing sealer obtained that removes can be brushed directly It applies, be sprayed at the base materials such as furniture, wallpaper, abatvoix, carpet, floor, adsorb and decompose the contamination gases such as the formaldehyde in air, TVOC Body.
Specific implementation mode
The technical solution further illustrated the present invention below by specific implementation mode.
Unless specific instructions, various raw materials of the invention are commercially available buys, or is prepared according to the conventional method of this field It obtains.
Embodiment 1
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 4% Carboxymethyl chitosan is soluble in water, and the grain size that 0.1% is added into solution is the nanometer anion powder stirring and dissolving of 1500 mesh, then Be added 0.5% benzene homologues catabolic enzyme, 0.5% pectase, the mixture of carboxy-lesterase, 1% formaldehyde dehydrogenase, 0.03% Glutathione and 0.1% tween and the water of surplus continue to stir, be made and remove aldehyde ordor removing sealer.
Embodiment 2
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 5% Chitosan quaternary ammonium salt is soluble in water, and the grain size that 0.6% is added into solution is the nanometer anion powder stirring and dissolving of 3000 mesh, then 1% benzene homologues catabolic enzyme, 1% carboxy-lesterase, 0.8% formaldehyde dehydrogenase, 0.04% glutathione and 0.5% is added Glycerine and the water of surplus continue to stir, be made and remove aldehyde ordor removing sealer.
Embodiment 3
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 8% Carboxymethyl chitosan is soluble in water, and the grain size that 1% is added into solution is the nanometer anion powder stirring and dissolving of 3500 mesh, then adds Enter the mixture of 2% benzene homologues catabolic enzyme, 1.5% carboxy-lesterase and lipase, 1.3% formaldehyde dehydrogenase, 0.05% Glutathione and 0.8% glycerine and the water of surplus continue to stir, be made and remove aldehyde ordor removing sealer.
Embodiment 4
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 10% Carboxymethyl chitosan is soluble in water, and the grain size that 1.5% is added into solution is the nanometer anion powder stirring and dissolving of 4000 mesh, then Be added 3% benzene homologues catabolic enzyme, 2% pectase, the mixture of carboxy-lesterase and lipase, 1.8% formaldehyde dehydrogenase, 0.04% glutathione and 1% glycerine and the water of surplus continue to stir, and are made and remove aldehyde ordor removing sealer.
Embodiment 5
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 15% Carboxymethyl chitosan is soluble in water, and the grain size that 3% is added into solution is the nanometer anion powder stirring and dissolving of 3000 mesh, then adds Enter the mixture of 4% benzene homologues catabolic enzyme, 4% pectase, carboxy-lesterase and lipase, 3% formaldehyde dehydrogenase, 0.03% glutathione and 1.5% tween and the water of surplus continue to stir, and are made and remove aldehyde ordor removing sealer.
Embodiment 6
The present embodiment by adjusting raw material composition and ratio, as follows:By mass percentage, by 20% The mixture of carboxymethyl chitosan and chitosan quaternary ammonium salt is soluble in water, and the grain size that 5% is added into solution is that 3000 purposes are received Rice negative ion powder stirring and dissolving, add 3% benzene homologues catabolic enzyme, the mixture of 5% lipase, 2% formaldehyde dehydrogenation Enzyme, 0.02% glutathione and 2% glycerine and the water of surplus continue to stir, and are made and remove aldehyde ordor removing sealer.
Comparative example 1
This comparative example by adjusting raw material composition and ratio, as follows:By mass percentage, by 8% Carboxymethyl chitosan is soluble in water, and 2% benzene homologues catabolic enzyme, 1.5% carboxy-lesterase and lipase are added into solution Mixture, 1.3% formaldehyde dehydrogenase, 0.05% glutathione and 0.8% glycerine and the water of surplus continue to stir, and are made Except aldehyde ordor removing sealer.
Comparative example 2
This comparative example by adjusting raw material composition and ratio, as follows:By mass percentage, by 8% Carboxymethyl chitosan is soluble in water, and the grain size that 1% is added into solution is the nanometer anion powder stirring and dissolving of 3500 mesh, then adds Enter 0.05% glutathione and 0.8% glycerine and the water of surplus continues to stir, is made and removes aldehyde ordor removing sealer.
Comparative example 3
This comparative example by adjusting raw material composition and ratio, as follows:By mass percentage, by 8% Carboxymethyl chitosan is soluble in water, and the grain size that 1% is added into solution is the nanometer anion powder stirring and dissolving of 3500 mesh, then adds Enter the mixture of 2% benzene homologues catabolic enzyme, 1.5% carboxy-lesterase and lipase, 1.3% formaldehyde dehydrogenase, 0.8% Glycerine and the water of surplus continue to stir, and are made and remove aldehyde ordor removing sealer.
Comparative example 4
This comparative example by adjusting raw material composition and ratio, as follows:By mass percentage, by 8% Carboxymethyl chitosan is soluble in water, and the grain size that 1% is added into solution is the nanometer anion powder stirring and dissolving of 3500 mesh, then adds Enter the mixture of 2% benzene homologues catabolic enzyme, 1.5% carboxy-lesterase and lipase, 1.3% formaldehyde dehydrogenase, 0.05% Glutathione and the water of surplus continue to stir, be made and remove aldehyde ordor removing sealer.
With reference to JCT-1074-2008《Function of purifying indoor air coating material purifying property》Standard to the present invention reality It is obtained except aldehyde ordor removing sealer is tested for the property to apply a 1-6 and comparative example 1-4, spray for 24 hours with 28 days after respectively to gas Component content is measured, and the results are shown in Table 1 for the removal rate of each polluted gas ingredient.
Table 1
The present invention prepares raw material and proportioning by rationally control, obtain except aldehyde ordor removing sealer is to indoor pollution air Good purification, the removal rate of the polluted gas such as PARA FORMALDEHYDE PRILLS(91,95), TVOC is up to 96% or more after use for 24 hours;Clean-up effect is lasting, removes Aldehyde ordor removing sealer is using the removal rate of the polluted gas such as PARA FORMALDEHYDE PRILLS(91,95), TVOC after 28 days still up to 93% or more.The present invention's It is obtained to remove aldehyde ordor removing sealer safety and environmental protection except the preparation process of aldehyde ordor removing sealer is simple, it can directly brush, be sprayed at house The base materials such as tool, wallpaper, abatvoix, carpet, floor adsorb and decompose the polluted gas such as the formaldehyde in air, TVOC.
Applicant states that the present invention illustrates detailed process equipment and the technological process of the present invention by above-described embodiment, But the invention is not limited in above-mentioned detailed process equipment and technological processes, that is, it is above-mentioned detailed not mean that the present invention has to rely on Process equipment and technological process could be implemented.Person of ordinary skill in the field it will be clearly understood that any improvement in the present invention, The addition of equivalence replacement and auxiliary element to each raw material of product of the present invention, the selection etc. of concrete mode all fall within the present invention's Within protection domain and the open scope.

Claims (10)

1. one kind removing aldehyde ordor removing sealer, which is characterized in that by mass percentage, including following substance:
Wherein, the film forming agent is water soluble chitosan.
2. according to claim 1 remove aldehyde ordor removing sealer, which is characterized in that by mass percentage, including following object Matter:
3. according to claim 1 or 2 remove aldehyde ordor removing sealer, which is characterized in that the molecule of the water soluble chitosan Amount is 20000~40000.
4. removing aldehyde ordor removing sealer according to one of claim 1-3, which is characterized in that the water soluble chitosan is carboxylic Methyl chitosan and/or chitosan quaternary ammonium salt.
5. removing aldehyde ordor removing sealer according to one of claim 1-4, which is characterized in that the grain of the nanometer anion powder Diameter is 1500~4000 mesh.
6. removing aldehyde ordor removing sealer according to one of claim 1-5, which is characterized in that the ester catabolic enzyme is selected from pectin One kind in enzyme, carboxy-lesterase and lipase or at least two mixture.
7. removing aldehyde ordor removing sealer according to one of claim 1-6, which is characterized in that the Formaldehyde decomposition enzyme is formaldehyde Dehydrogenase.
8. removing aldehyde ordor removing sealer according to one of claim 1-7, which is characterized in that the activator is gluathione Peptide.
9. removing aldehyde ordor removing sealer according to one of claim 1-8, which is characterized in that the stable moisturizer is tween And/or glycerine.
10. it is a kind of as described in one of claim 1-9 except aldehyde ordor removing sealer preparation method, which is characterized in that the system Preparation Method includes the following steps:By mass percentage, 4~20% water soluble chitosan is soluble in water, add into solution The nanometer anion powder stirring and dissolving for entering 0.1~5% adds 0.5~5% benzene homologues catabolic enzyme, 0.5~5% ester point Solve enzyme, 0.5~5% Formaldehyde decomposition enzyme, 0.03~0.05% activator and 0.1~2% stabilization moisturizer and surplus Water continues to stir, and is made described and removes aldehyde ordor removing sealer.
CN201710785340.3A 2017-09-04 2017-09-04 Formaldehyde-removing odor-removing sealing agent and preparation method thereof Active CN108299956B (en)