CN109182623B - 一种磨花效应皮革产品的制备方法 - Google Patents
一种磨花效应皮革产品的制备方法 Download PDFInfo
- Publication number
- CN109182623B CN109182623B CN201811065835.XA CN201811065835A CN109182623B CN 109182623 B CN109182623 B CN 109182623B CN 201811065835 A CN201811065835 A CN 201811065835A CN 109182623 B CN109182623 B CN 109182623B
- Authority
- CN
- China
- Prior art keywords
- leather
- blank
- effect
- spray
- permeability detection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种磨花效应皮革产品的制备方法，包括皮坯的一次喷染步骤、磨革步骤、二次喷染步骤和后处理步骤，在所述一次喷染步骤前对皮坯进行渗透性检测，得到皮坯的渗透性检测值；所述一次喷染步骤中和二次喷染步骤中渗透剂总用量根据所述的渗透性检测值确定；本发明根据皮坯的渗透性检测值来控制渗透剂用量，可以达到控制喷染时染料水对皮坯层的渗透深度，从而实现控制磨革后磨花效应程度，使磨花效应自然，制得的磨花效应皮革皮张之间差异小，外观质量稳定。
Description
技术领域
本发明属于制革技术领域，具体涉及一种磨花效应皮革产品的制备方法。
背景技术
生活中，皮革制品我们随处可见，我们的皮鞋，皮衣、皮带、包包、沙发外面的皮革料子等等都是皮革制品。皮革是经过脱毛和鞣制等物理、化学加工所得到的已经变性不易腐烂的动物皮。皮革按表面处理方法不同分为全粒面革、轻磨面革、修面革、正绒革、反绒革等，而光面皮又被划分为漆皮、苯胺革、半苯胺革等。皮革的表面经常表现出不同的形状和花纹，这是由于其加工制作过程中，采用不同的表面处理方法，可以带来不同的产品品质和外观。磨花效应皮革是在对皮坯表面进行喷染着色后，再用砂纸磨革以获得磨花效果，存在的问题是，传统工艺中表面的颜色称之为面色，需要转鼓染色进行表染而得到，工艺要求染色时间短，颜色精确，当前工艺制得的磨花效应皮革不同批次之间或者同一批次不同皮张之间颜色差异大，制衣厂很难进行配色，从而影响使用，并且因其厚度、皮坯表面电荷等影响，染面色时染料的渗透程度差异大，其磨花效果自然千差万别。
发明内容
本发明的目的是提供一种磨花效应皮革产品的制备方法，以解决上述问题。本发明所采用的技术方案是：
一种磨花效应皮革产品的制备方法，包括皮坯的一次喷染步骤、磨革步骤、二次喷染步骤和后处理步骤，在所述一次喷染步骤前对皮坯进行渗透性检测，得到皮坯的渗透性检测值；所述一次喷染步骤中和二次喷染步骤中渗透剂总用量根据所述的渗透性检测值确定；
所述渗透性检测值是指皮坯表面的水滴接触角测试值X；所述渗透剂总用量Y＝48-(3/5)X。
进一步的，对皮坯进行渗透性检测后，选择水滴接触角测试值X为30～70的皮坯制备磨花效应皮革产品。
进一步的，所述后处理步骤包括固色处理，得到磨花效应皮革的绒面产品。
进一步的，所述后处理步骤包括封底、喷浆、熨平、喷浆、喷光油、熨平，得到磨花效应皮革的光面产品。
发明人发现磨花效果与喷染时的染料水在皮坯中的渗透情况有关。在传统工艺中，由于对皮坯的渗透性指标未作控制，也没有根据皮坯的渗透性指标对喷染时的配方进行相应调整，因此喷染时的染料水渗透深度完全不可控，磨革后颜色变化大，因此无法掌握磨花效果，也就无法得到稳定可控的磨花效应皮革产品。
本发明的有益点在于：本发明根据皮坯的渗透性检测值来控制渗透剂用量，可以达到控制喷染时染料水对皮坯层的渗透深度，从而实现控制磨革后磨花效应程度，使磨花效应自然，制得的磨花效应皮革皮张之间差异小，外观质量稳定。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明。
实施例1
一种磨花效应皮革产品的制备方法，包括以下步骤：
1)对皮坯进行渗透性检测，渗透性检测以水滴实验观察为准，检测时在皮坯上滴几滴清水，水珠保持15-30秒不浸湿皮面或不渗透进皮内部，1-2分钟皮坯表面稍有浸湿，测量水滴与皮坯表面的接触角，得到渗透性检测值为30，确定两次喷染的渗透剂总用量为30g/sf。
2)对皮坯进行一次喷染：
喷浆配方为
染料水40g/L
渗透剂700g/L
水600g/L
喷浆机大喷量，8枪8-12格喷3遍，低温烘干，
3)磨革，采用800#砂纸进行磨革，转笼，抛光。
修色：
4)对皮坯进行二次喷染，
喷浆配方为：
染料水10g/L
渗透剂800g/L
水400g/L
喷浆机小喷量，8枪6-8格1-2遍，低温烘干。
5)固色后得到具有磨花效应皮革的绒面产品，固色剂配方为：
水：3000g/L
消光聚氨酯：40g/L
绒面固色剂：100g/L
匀染渗透剂：50g/L。
实施例2
一种磨花效应皮革产品的制备方法，包括以下步骤：
1)对皮坯进行渗透性检测，渗透性检测以水滴实验观察为准，检测时在皮坯上滴几滴清水，水珠保持15-30秒不浸湿皮面或不渗透进皮内部，1-2分钟皮坯表面稍有浸湿，测量水滴与皮坯表面的接触角，得到渗透性检测值为60，确定两次喷染的渗透剂总用量为12g/sf。
2)对皮坯进行一次喷染：
喷浆配方为
染料水40g/L
渗透剂600g/L
水600g/L
喷浆机大喷量，8枪8-12格喷3遍，低温烘干，
3)磨革，采用800#砂纸进行磨革，转笼，抛光。
修色：
4)对皮坯进行二次喷染，
喷浆配方为：
染料水10g/L
渗透剂700g/L
水400g/L
喷浆机小喷量，8枪6-8格1-2遍，低温烘干。
5)固色后得到具有磨花效应皮革的绒面产品，固色剂配方为：
水：3000g/L
消光聚氨酯：40g/L
绒面固色剂：100g/L
匀染渗透剂：50g/L。
实施例3
一种磨花效应皮革产品的制备方法，包括以下步骤：
1)对皮坯进行渗透性检测，渗透性检测以水滴实验观察为准，检测时在皮坯上滴几滴清水，水珠保持15-30秒不浸湿皮面或不渗透进皮内部，1-2分钟皮坯表面稍有浸湿，测量水滴与皮坯表面的接触角，得到渗透性检测值为70，确定两次喷染的渗透剂总用量为6g/sf。
2)对皮坯进行一次喷染：
喷浆配方为
染料水40g/L
渗透剂400g/L
水600g/L
喷浆机大喷量，8枪8-12格喷3遍，低温烘干，
3)磨革，采用800#砂纸进行磨革，转笼，抛光。
修色：
4)对皮坯进行二次喷染，
喷浆配方为：
染料水10g/L
渗透剂600g/L
水400g/L
喷浆机小喷量，8枪6-8格1-2遍，低温烘干。
5)经过封底、喷浆、熨平、喷浆、喷光油、熨平，得到磨花效应皮革的光面产品。
Claims (4)
1.一种磨花效应皮革产品的制备方法，包括皮坯的一次喷染步骤、磨革步骤、二次喷染步骤和后处理步骤，其特征在于：在所述一次喷染步骤前对皮坯进行渗透性检测，得到皮坯的渗透性检测值；所述一次喷染步骤中和二次喷染步骤中渗透剂总用量根据所述的渗透性检测值确定；所述渗透性检测值是指皮坯表面的水滴接触角测试值X；所述渗透剂总用量Y＝48-(3/5)X。
2.根据权利要求1所述的磨花效应皮革产品的制备方法，其特征在于：对皮坯进行渗透性检测后，选择水滴接触角测试值X为30～70的皮坯制备磨花效应皮革产品。
3.根据权利要求1所述的磨花效应皮革产品的制备方法，其特征在于：所述后处理步骤包括固色处理，得到磨花效应皮革的绒面产品。
4.根据权利要求1所述的磨花效应皮革产品的制备方法，其特征在于：所述后处理步骤包括封底、喷浆、熨平、喷浆、喷光油、熨平，得到磨花效应皮革的光面产品。