CN109181445A - 一种水抗菌内墙乳胶漆及其制备和应用方法 - Google Patents

一种水抗菌内墙乳胶漆及其制备和应用方法 Download PDF

Info

Publication number
CN109181445A
CN109181445A CN201810856545.0A CN201810856545A CN109181445A CN 109181445 A CN109181445 A CN 109181445A CN 201810856545 A CN201810856545 A CN 201810856545A CN 109181445 A CN109181445 A CN 109181445A
Authority
CN
China
Prior art keywords
parts
emulsion
interior wall
latex paint
wall latex
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810856545.0A
Other languages
English (en)
Inventor
吕松春
余明
刘松新
陈晓文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingyuan Cheng Ming New Mstar Technology Ltd
Guangdong Hualan Automobile Material Research Institute
Original Assignee
Qingyuan Cheng Ming New Mstar Technology Ltd
Guangdong Hualan Automobile Material Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingyuan Cheng Ming New Mstar Technology Ltd, Guangdong Hualan Automobile Material Research Institute filed Critical Qingyuan Cheng Ming New Mstar Technology Ltd
Priority to CN201810856545.0A priority Critical patent/CN109181445A/zh
Publication of CN109181445A publication Critical patent/CN109181445A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水抗菌内墙乳胶漆及其制备和应用方法，包括以下重量组份：乳液40‑80份、水性环氧树脂5‑15份、轻质碳酸钙5‑15份、滑石粉5‑15份、绢云母粉5‑15份、成膜助剂1‑5份、消泡剂0.1‑0.5份、增稠剂0.1‑0.5份与纳米银5‑10份；包括以下步骤：S1：称量配比，将所有所需要的原料进行称量，S2：混合硅丙乳液、醋叔乳液与氟碳乳液制取乳液，S3：加热粉碎贝壳制取轻质碳酸钙，S4：将所有加入搅拌机进行混合，S5：混合搅拌完成后制得乳胶漆。本发明配方更加的科学合理，能够更好的提高该乳胶漆的抗菌效果，能够有效的保证使用者的身体健康不会受到损害，降低了该乳胶漆的制备成本，本发明的制备方法更加的简单，可以防止搅拌混合原料过程中原料洒落。

Description

一种水抗菌内墙乳胶漆及其制备和应用方法
技术领域
本发明涉及一种乳胶漆领域，具体为一种水抗菌内墙乳胶。
本发明涉及一种乳胶漆领域，具体为一种水抗菌内墙乳胶漆的制备方法。
本发明涉及一种乳胶漆领域，具体为一种水抗菌内墙乳胶漆的应用方法。
背景技术
乳胶漆又称乳胶涂料，是涂料的一种，乳胶漆具有干燥速度快，耐碱度效果好和调制方便的有点，其特点让乳胶漆的应用范围很广，现有的涂料配方复杂，生产工艺不够科学，并且含有较多的有害物质，使用后会给使用者的身体造成影响，在人们对健康日以注重的当下，传统的乳胶漆已经不能满足使用者的使用需求。
发明内容
本发明的目的在于提供一种水抗菌内墙乳胶漆及其制备和应用方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种水抗菌内墙乳胶漆，包括以下重量组份：乳液40-80份、水性环氧树脂5-15份、轻质碳酸钙5-15 份、滑石粉5-15份、绢云母粉5-15份、成膜助剂1-5份、消泡剂0.1-0.5 份、增稠剂0.1-0.5份与纳米银5-10份。
优选的，所述乳液包括硅丙乳液、醋叔乳液与氟碳乳液，且硅丙乳液、醋叔乳液与氟碳乳液的混合比例为6：1.5：3.5。
优选的，所述轻质碳酸钙由贝壳烧结后碾碎制成，所述消泡剂为YJG200 消泡剂或XPJ284消泡剂中的一种或两者等比混合物。
优选的，所述增稠剂为非缔合型碱溶胀增稠剂、缔合型碱溶胀增稠剂、聚氨酯增稠剂或疏水改性非聚氨酯增稠剂中的一种。
一种水抗菌内墙乳胶漆的制备方法，包括以下步骤：
S1:称量配比，将所有所需要的原料进行称量，按照一定的比例取用，并进行存储；
S2：将称取好的硅丙乳液、醋叔乳液与氟碳乳液按照6：1.5：3.5倒入到搅拌器中，将硅丙乳液、醋叔乳液与氟碳乳搅拌混合成乳液待用；
S3：将称取好的贝壳先进行烧结，烧结好后再对其粉碎，粉碎好的原料即为轻质碳酸钙；
S4：将S1中制取好的乳液、S2中制取好的轻质碳酸钙、滑石粉、绢云母粉、成膜助剂、消泡剂、增稠剂与纳米银倒入搅拌器中进行搅拌；
S5：搅拌完成后制得乳胶漆。
优选的，所述贝壳烧结时的温度不低于800℃，所述烧结好的贝壳需要被碾碎至500目。
优选的，所述S2中搅拌器的转速为1000-1200r/min，所述S4至少需要搅拌1h，所述搅拌器上安装了防护罩。
一种水抗菌内墙乳胶漆应用在建筑内墙的表面保护材料中。
与现有技术相比，本发明的有益效果是：本发明配方更加的科学合理，能够更好的提高该乳胶漆的抗菌效果，能够有效的保证使用者的身体健康不会受到损害，并且制配原料来源广泛，大大降低了该乳胶漆的制备成本，本发明的制备方法更加的简单，可以防止搅拌混合原料过程中原料洒落。
附图说明
图1为本实用发明的流程图。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
本发明提供一种技术方案：一种水抗菌内墙乳胶漆，包括以下重量组份：乳液50份、水性环氧树脂8份、轻质碳酸钙8份、滑石粉9份、绢云母粉10 份、成膜助剂2份、消泡剂0.2份、增稠剂0.2份与纳米银5份。
一种水抗菌内墙乳胶漆的制备方法，包括以下步骤：
S1:称量配比，将所有所需要的原料通过电子秤进行称量，按照一定的比例取用，将区号的原料放入储存设备中进行存储；
S2：将称取好的硅丙乳液、醋叔乳液与氟碳乳液按照6：1.5：3.5倒入到搅拌器中，开启搅拌器，将硅丙乳液、醋叔乳液与氟碳乳搅拌混合成乳液放置在储存罐中待用；
S3：将称取好的贝壳取出进行烧结，烧结好后使用粉碎研磨设备再对其进行粉碎，粉碎好的原料即为轻质碳酸钙；
S4：将S1中制取好的乳液、S2中制取好的轻质碳酸钙、滑石粉、绢云母粉、成膜助剂、消泡剂、增稠剂与纳米银倒入搅拌器中，将搅拌器打开对其进行搅拌；
S5：搅拌完成后制得乳胶漆，将乳胶漆封存进行运输。
一种水抗菌内墙乳胶漆应用在建筑内墙的表面保护材料中。
实施例二
本发明提供一种技术方案：一种水抗菌内墙乳胶漆，包括以下重量组份：乳液80份、水性环氧树脂14份、轻质碳酸钙8份、滑石粉9份、绢云母粉 10份、成膜助剂2份、消泡剂0.2份、增稠剂0.2份与纳米银15份。
一种水抗菌内墙乳胶漆的制备方法，包括以下步骤：
S1:称量配比，将所有所需要的原料通过电子秤进行称量，按照一定的比例取用，将区号的原料放入储存设备中进行存储；
S2：将称取好的硅丙乳液、醋叔乳液与氟碳乳液按照6：1.5：3.5倒入到搅拌器中，开启搅拌器，将硅丙乳液、醋叔乳液与氟碳乳搅拌混合成乳液放置在储存罐中待用；
S3：将称取好的贝壳取出进行烧结，烧结好后使用粉碎研磨设备再对其进行粉碎，粉碎好的原料即为轻质碳酸钙；
S4：将S1中制取好的乳液、S2中制取好的轻质碳酸钙、滑石粉、绢云母粉、成膜助剂、消泡剂、增稠剂与纳米银倒入搅拌器中，将搅拌器打开对其进行搅拌；
S5：搅拌完成后制得乳胶漆，将乳胶漆封存进行运输。
一种水抗菌内墙乳胶漆应用在建筑内墙的表面保护材料中。
本发明配方更加的科学合理，能够更好的提高该乳胶漆的抗菌效果，能够有效的保证使用者的身体健康不会受到损害，并且制配原料来源广泛，大大降低了该乳胶漆的制备成本，本发明的制备方法更加的简单，可以防止搅拌混合原料过程中原料洒落。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (8)

1.一种水抗菌内墙乳胶漆，其特征在于，包括以下重量组份：乳液40-80份、水性环氧树脂5-15份、轻质碳酸钙5-15份、滑石粉5-15份、绢云母粉5-15份、成膜助剂1-5份、消泡剂0.1-0.5份、增稠剂0.1-0.5份与纳米银5-10份。
2.根据权利要求1所述的一种水抗菌内墙乳胶漆，其特征在于:所述乳液包括硅丙乳液、醋叔乳液与氟碳乳液，且硅丙乳液、醋叔乳液与氟碳乳液的混合比例为6：1.5：3.5。
3.根据权利要求1所述的一种水抗菌内墙乳胶漆，其特征在于，所述轻质碳酸钙由贝壳烧结后碾碎制成，所述消泡剂为YJG200消泡剂或XPJ284消泡剂中的一种或两者等比混合物。
4.根据权利要求1所述的一种水抗菌内墙乳胶漆，其特征在于，所述增稠剂为非缔合型碱溶胀增稠剂、缔合型碱溶胀增稠剂、聚氨酯增稠剂或疏水改性非聚氨酯增稠剂中的一种。
5.一种如权利要求1所述的水抗菌内墙乳胶漆的制备方法，其特征在于，包括以下步骤：
S1:称量配比，将所有所需要的原料进行称量，按照一定的比例取用，并进行存储；
S2：将称取好的硅丙乳液、醋叔乳液与氟碳乳液按照6：1.5：3.5倒入到搅拌器中，将硅丙乳液、醋叔乳液与氟碳乳搅拌混合成乳液待用；
S3：将称取好的贝壳先进行烧结，烧结好后再对其粉碎，粉碎好的原料即为轻质碳酸钙；
S4：将S1中制取好的乳液、S2中制取好的轻质碳酸钙、滑石粉、绢云母粉、成膜助剂、消泡剂、增稠剂与纳米银倒入搅拌器中进行搅拌
S5：搅拌完成后制得乳胶漆。
6.根据权利要求5所述的水抗菌内墙乳胶漆的制备方法，其特征在于，所述贝壳烧结时的温度不低于800℃，所述烧结好的贝壳需要被碾碎至500目。
7.根据权利要求5所述的水抗菌内墙乳胶漆的制备方法,起特征在于，所述S2中搅拌器的转速为1000-1200r/min，所述S4至少需要搅拌1h，所述搅拌器上安装了防护罩。
8.一种如权利要求1所述的水抗菌内墙乳胶漆应用在建筑内墙的表面保护材料中。
CN201810856545.0A 2018-07-31 2018-07-31 一种水抗菌内墙乳胶漆及其制备和应用方法 Pending CN109181445A (zh)