CN109142190A - 一种沥青路面渗水系数的密封材料 - Google Patents
一种沥青路面渗水系数的密封材料 Download PDFInfo
- Publication number
- CN109142190A CN109142190A CN201811077067.XA CN201811077067A CN109142190A CN 109142190 A CN109142190 A CN 109142190A CN 201811077067 A CN201811077067 A CN 201811077067A CN 109142190 A CN109142190 A CN 109142190A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- bentonite
- sealing material
- bituminous pavement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青18‑25份、VAE0.5‑2份、膨润土15‑22份、硼砂2‑5份、木质磺酸钠5‑8份、硅烷偶联剂1‑5份；组分B由以下重量配比的原料:粉煤灰15‑22份、VAE0.5‑2份、膨润土18‑25份、甲基纤维素醚0.2‑1.5份。该密封材料具有良好的防水抗渗的效果，与沥青路面的表面有良好的结合和密封性能，易回收，不会对路面造成污染。
Description
技术领域
本发明属于交通道路试验领域，具体涉及一种沥青路面渗水系数的密封材料。
背景技术
沥青路面渗水系数是反映路面沥青混合料级配和水稳定性的一个重要指标。如果整个沥青面层均透水，则水势必进入基层或路基，使路面承载力降低，相反如果沥青面层中有一层不透水，而表面层能很快透水，则不致形成水膜，对抗滑性能有很大的好处。所以路面渗水已成为评价路面使用性能的一个重要的指标。
一般传统的沥青路面渗水系数试验，首先是用油灰或橡皮泥对环装密封区域进行密封处理，然后将搓成拇指粗细的条状密封材料摞在环状密封区域中央并且摞成一圈，将渗水仪放在试件路面表面的测点上，然后略微使劲将渗水仪压在条状油灰或橡皮泥表面，再将配重加上以防压力水从底座与路面间流出，而这时往往由于油灰或橡皮泥粘性不够与渗水仪和路面密封不好，使水从渗水仪的边沿渗出，造成试验失败。重换材料重新试验，给试验工作带来很大的困难。
发明内容
为解决上述问题，本发明提供了一种沥青路面渗水系数的密封材料，该密封材料具有良好的防水抗渗的效果，与沥青路面的表面有良好的结合和密封性能，易回收，不会对路面造成污染。
本发明是通过以下技术方案实现的：
一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青18-25份、VAE0.5-2份、膨润土15-22份、硼砂2-5份、木质磺酸钠5-8份、硅烷偶联剂1-5份；组分B由以下重量配比的原料:粉煤灰15-22份、VAE0.5-2份、膨润土18-25份、甲基纤维素醚0.2-1.5份。
优选地，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青22份、VAE0.8份、膨润土20份、硼砂2.5份、木质磺酸钠6份、硅烷偶联剂2份；组分B由以下重量配比的原料:粉煤灰20份、VAE1份、膨润土20份、甲基纤维素醚1份。
优选地，改性乳化沥青的制备方法为：将沥青加热至180-190℃，备用，将十二烷基苯磺酸钠与异十三醇聚氧乙烯醚及膨润土溶于水中，三种成分与水的质量比1:1-2:0.5-3：100，待充分溶解后，加热至65-70℃，介入氯化钙与氯化钠，再与沥青混合，搅拌均匀，再加入丙三醇，研磨均匀后，降温得到改性乳化沥青。
更优选地，水与沥青、氯化钠、氯化钙、丙三醇的质量比为：10:10-15：0.05-2:0.05-2：3-4。
上述所述的沥青路面渗水系数的密封材料的施工方法，包括以下步骤：
（1）将组分A中的改性乳化沥青、VAE、膨润土、硼砂、木质磺酸钠、硅烷偶联剂混合均匀后，均匀涂敷于地面，厚度为0.2-0.5cm，静置晾晒5-10分钟；
（2）将组分B中的粉煤灰、VAE、膨润土、甲基纤维素醚与适量的水混合均匀后，调成沉入度10厘米膏状，涂抹在组分A上面，保证渗水仪边缘涂抹均匀即可。
有益效果
本发明公开了一种沥青路面渗水系数的密封材料，该密封材料由组分A和组份B组成，施工时组份A直接涂敷于地面，既能与沥青地面紧密粘合在一起，又能与组份B的成分很好的密封，而且组份A涂敷于沥青地面的厚度较薄，施工完毕后不需要清除，节约了时间和资源；组份B能够与组份A紧密结合在一起，密封性好、易存放、不粘手、易回收，永不变干、不会对沥青路面产生污染，同时产品环保，无毒无害，操作性强。
具体实施方式
下面对本发明的实施例作详细说明，本实施例在以本发明技术方案为前提下进行实施，给出了详细的实施方式和具体的操作过程，但本发明的保护范围不限于下述的实施例。
实施例1
一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青22份、VAE0.8份、膨润土20份、硼砂2.5份、木质磺酸钠6份、硅烷偶联剂2份；组分B由以下重量配比的原料:粉煤灰20份、VAE1份、膨润土20份、甲基纤维素醚1份。
改性乳化沥青的制备方法：将沥青加热至180-190℃，备用，将十二烷基苯磺酸钠与异十三醇聚氧乙烯醚及膨润土溶于水中，三种成分与水的质量比1:1.2:1：100，待充分溶解后，加热至65℃，介入氯化钙与氯化钠，再与沥青混合，搅拌均匀，再加入丙三醇，研磨均匀后，降温得到改性乳化沥青。水与沥青、氯化钠、氯化钙、丙三醇的质量比为：10:12：0.1:0.1：3。
所述的沥青路面渗水系数的密封材料的施工方法，包括以下步骤：
（1）将组分A中的改性乳化沥青、VAE、膨润土、硼砂、木质磺酸钠、硅烷偶联剂混合均匀后，均匀涂敷于地面，厚度为0.2cm，静置晾晒5-10分钟；
（2）将组分B中的粉煤灰、VAE、膨润土、甲基纤维素醚与适量的水混合均匀后，调成沉入度10厘米膏状，涂抹在组分A上面，保证渗水仪不漏水即可。
实施例2
一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青18份、VAE0.5份、膨润土15份、硼砂2份、木质磺酸钠5份、硅烷偶联剂1份；组分B由以下重量配比的原料:粉煤灰15份、VAE0.5份、膨润土18份、甲基纤维素醚0.2份。
改性乳化沥青的制备方法：将沥青加热至180℃，备用，将十二烷基苯磺酸钠与异十三醇聚氧乙烯醚及膨润土溶于水中，三种成分与水的质量比1:1:0.5：100，待充分溶解后，加热至65℃，介入氯化钙与氯化钠，再与沥青混合，搅拌均匀，再加入丙三醇，研磨均匀后，降温得到改性乳化沥青。水与沥青、氯化钠、氯化钙、丙三醇的质量比为：10:10：0.05:0.05：3。
施工方法同实施例1。
实施例3
一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青25份、VAE2份、膨润土22份、硼砂5份、木质磺酸钠8份、硅烷偶联剂5份；组分B由以下重量配比的原料:粉煤灰22份、VAE2份、膨润土25份、甲基纤维素醚1.5份。
改性乳化沥青的制备方法：将沥青加热至190℃，备用，将十二烷基苯磺酸钠与异十三醇聚氧乙烯醚及膨润土溶于水中，三种成分与水的质量比1:2:3：100，待充分溶解后，加热至65℃，介入氯化钙与氯化钠，再与沥青混合，搅拌均匀，再加入丙三醇，研磨均匀后，降温得到改性乳化沥青。水与沥青、氯化钠、氯化钙、丙三醇的质量比为：10:15：2:2：3-4。
施工方法同实施例1。
对比例1
将实施例1中的改性乳化沥青替换为普通沥青，即为：
一种沥青路面渗水系数的密封材料，包括组分A和组分B，其中组分A由以下重量配比的原料组成:沥青22份、VAE0.8份、膨润土20份、硼砂2.5份、木质磺酸钠6份、硅烷偶联剂2份；组分B由以下重量配比的原料:粉煤灰20份、VAE1份、膨润土20份、甲基纤维素醚1份。
施工方法同实施例1。
对比例2
一种沥青路面渗水系数的密封材料，由以下重量配比的原料:粉煤灰20份、VAE1份、膨润土20份、甲基纤维素醚1份。
密封材料的施工方法，将粉煤灰、VAE、膨润土、甲基纤维素醚与适量的水混合均匀后，调成沉入度10厘米膏状，涂抹在渗水仪边缘即可。
对比例3
一种沥青路面渗水系数的密封材料，由以下重量成分的原料制成：碳酸钙60g，矿物质基础油36g，锂基脂0.5g，高岭土2.5g，二氧化硅0.45g，檀香香精0.1g，季铵盐类抗菌剂0.25g，染色剂0.1g，所述碳酸钙为100目的碳酸钙粉末。
将配方量的各组分混合，搅拌均匀后在40℃条件下皂化6h制备得到密封材料成品。
将实施例及对比例制成的密封材料应用于渗水试验，选取同样施工工艺的路面进行渗水试验，排除人为因素，其结果如下：
实施例中的密封材料在本标段沥青路面中做了20处的沥青路面渗水试验，没有发生一处密封材料渗水形现象，沥青路面渗水试验一次检测成功率为100％。
Claims (5)
1.一种沥青路面渗水系数的密封材料，其特征在于，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青18-25份、VAE0.5-2份、膨润土15-22份、硼砂2-5份、木质磺酸钠5-8份、硅烷偶联剂1-5份；组分B由以下重量配比的原料:粉煤灰15-22份、VAE0.5-2份、膨润土18-25份、甲基纤维素醚0.2-1.5份。
2.根据权利要求1所述的沥青路面渗水系数的密封材料，其特征在于，包括组分A和组分B，其中组分A由以下重量配比的原料组成:改性乳化沥青22份、VAE0.8份、膨润土20份、硼砂2.5份、木质磺酸钠6份、硅烷偶联剂2份；组分B由以下重量配比的原料:粉煤灰20份、VAE1份、膨润土20份、甲基纤维素醚1份。
3.根据权利要求1-2之一所述的沥青路面渗水系数的密封材料，其特征在于，改性乳化沥青的制备方法为：将沥青加热至180-190℃，备用，将十二烷基苯磺酸钠与异十三醇聚氧乙烯醚及膨润土溶于水中，三种成分与水的质量比1:1-2:0.5-3：100，待充分溶解后，加热至65-70℃，介入氯化钙与氯化钠，再与沥青混合，搅拌均匀，再加入丙三醇，研磨均匀后，降温得到改性乳化沥青。
4.根据权利要求3所述的密封材料，其特征在于，水与沥青、氯化钠、氯化钙、丙三醇的质量比为：10:10-15：0.05-2:0.05-2：3-4。
5.一种权利要求1-4之一所述的沥青路面渗水系数的密封材料的施工方法，其特征在于，包括以下步骤：
（1）将组分A中的改性乳化沥青、VAE、膨润土、硼砂、木质磺酸钠、硅烷偶联剂混合均匀后，均匀涂敷于地面，厚度为0.2-0.5cm，静置晾晒5-10分钟；
（2）将组分B中的粉煤灰、VAE、膨润土、甲基纤维素醚与适量的水混合均匀后，调成沉入度10厘米膏状，涂抹在组分A上面，保证渗水仪边缘涂抹均匀即可。