CN109110836A - 一种从蛇纹石中提取复合硅酸盐净水剂的方法及其应用 - Google Patents
一种从蛇纹石中提取复合硅酸盐净水剂的方法及其应用 Download PDFInfo
- Publication number
- CN109110836A CN109110836A CN201811089109.1A CN201811089109A CN109110836A CN 109110836 A CN109110836 A CN 109110836A CN 201811089109 A CN201811089109 A CN 201811089109A CN 109110836 A CN109110836 A CN 109110836A
- Authority
- CN
- China
- Prior art keywords
- serpentine
- purifying agent
- water purifying
- silicate salt
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种从蛇纹石中提取复合硅酸盐净水剂的方法，包括步骤：（1）采用颚式破碎机将蛇纹石破碎得到破碎颗粒；（2）将得到的破碎颗粒用球磨机加水进行研磨，直至至少90%的颗粒直径小于等于200目，然后用气体重选机将含金属杂质部分选出；（3）将步骤（2）中所得材料采用6000GS湿式磁选出各类金属杂质，得到无杂质成品；（4）将步骤（3）所得无杂质成品送入回转窑内焙烧。与现有技术相比，本发明具有如下的有益效果：本发明大大降低了污水处理产品的生产成本，现有常规应用的污水处理剂例如PAM（聚丙烯酰胺）、PAC等产品造价高，对水体中有机物处理能力有限，远远达不到高效水处理的效果。
Description
技术领域
本发明涉及净水剂技术领域，具体涉及一种从蛇纹石中提取复合硅酸盐净水剂的方法及其应用。
背景技术
蛇纹石属超基性岩，硅量小于45%，几乎全部由蛇纹岩矿物如叶蛇纹石和纤蛇纹石组成，常见残余橄榄石，其他有铁镁矿物石榴子石、辉石、角闪石，常含云母，此外有铬铁矿或铬尖晶石，色深，呈黑、绿、红色，其理论化学成分(Mg，Fe，Ni)3Si2O5(OH)4、化学式Mg6[Si4O10](OH)8、成分含量：MgO43.6%、SiO243.6%、H2O13.1%。蛇纹石中除含复合硅酸盐外，还含有镍Ni、铬Cr、钴Co、铁Fe、铜Cu、金Au、银Ag、钙Ca、镁Mg、铝Al、铅Pb、锌Zn、钾K、纳Na、锰Mn、钛Ti、锡Sn、锶Sr、铀U、硅Si、硫S、磷P等。
蛇纹石资源丰富，国内众多相关发明对蛇纹石的利用率低，实际应用可能性小，可以大规模应用蛇纹石，有效利用蛇纹石这一自然资源，利用其中的元素作为净水剂来使用；而常规应用的污水处理剂例如PAM（聚丙烯酰胺）等产品造价高，对水体中有机物处理能力有限，远远达不到高效水处理的效果。
发明内容
本发明的目的在于提供一种从蛇纹石中提取复合硅酸盐净水剂的方法及其应用，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
本发明提供了一种从蛇纹石中提取复合硅酸盐净水剂的方法，包括步骤：
（1）采用颚式破碎机将蛇纹石破碎得到破碎颗粒；
（2）将得到的破碎颗粒用球磨机加水进行研磨，直至至少90%的颗粒直径小于等于200目，然后用气体重选机将含金属杂质部分选出；
（3）将步骤（2）中所得材料采用6000GS湿式磁选出各类金属杂质，得到无杂质成品；
（4）将步骤（3）所得无杂质成品送入回转窑内焙烧；
（5）将步骤（4）所得材料继续经球磨机研磨直至90%的颗粒直径小于等于600目；
（6）将步骤（5）所得材料与聚丙烯酰胺按照10：1的比例调配，最终得到复合硅酸盐净水剂。
作为本发明的进一步技术方案是：在步骤（1）中，蛇纹石的破碎粒度≤4mm；
作为本发明的再进一步技术方案是：在步骤（4）中，所述回转窑的温度为400℃。
作为本发明的再进一步技术方案是：在步骤（4）中，在回转窑中的焙烧时间为10分钟。
一种从蛇纹石中提取复合硅酸盐净水剂在污水处理上的应用。
与现有技术相比，本发明具有如下的有益效果：本发明大大降低了污水处理产品的生产成本，现有常规应用的污水处理剂例如PAM（聚丙烯酰胺）、PAC等产品造价高，对水体中有机物处理能力有限，远远达不到高效水处理的效果。本发明廉价高效，将在河流、胡泊、工业污水、矿山尾矿回水等方面全面代替传统水处理剂。
具体实施方式
下面结合具体实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种从蛇纹石中提取复合硅酸盐净水剂的方法，包括步骤：
（1）采用颚式破碎机将蛇纹石破碎得到破碎颗粒；
（2）将得到的破碎颗粒用球磨机加水进行研磨，直至至少90%的颗粒直径小于等于200目，然后用气体重选机将含金属杂质部分选出；
（3）将步骤（2）中所得材料采用6000GS湿式磁选出各类金属杂质，得到无杂质成品；
（4）将步骤（3）所得无杂质成品送入回转窑内焙烧，对材料进行改性，并使材料含水率小于8%；
（5）将步骤（4）所得材料继续经球磨机研磨直至90%的颗粒直径小于等于600目；
（6）将步骤（5）所得材料与聚丙烯酰胺按照10：1的比例调配，最终得到复合硅酸盐净水剂。
在步骤（1）中，蛇纹石的破碎粒度≤4mm；
在步骤（4）中，所述回转窑的温度为400℃。
在步骤（4）中，在回转窑中的焙烧时间为10分钟。
一种从蛇纹石中提取复合硅酸盐净水剂在污水处理上的应用。
在使用过程中采用干粉喷药器将复合硅酸盐净水剂在污水中直接喷撒，也可在污水沉淀池内定量投撒。
本发明中的复合硅酸盐净水剂实际应用案例：
案例1：
在湖泊污水处理中，全面抽取湖水底泥，在沉淀池中每吨泥水中添加1-5公斤本发明的复合硅酸盐净水剂，30分钟后泥水分离，达到相应的处理效果，与目前常规工艺效率提高约50%，成本降低约70%。
案例2
河道污水断面考核处理中，采用固粉风力撒药机直接喷洒方式，每吨水添加5公斤本发明的复合硅酸盐净水剂，1000-至2000米后水体断面考核效果提升，由V类水体提升至IV类水体，与目前常规工艺效率提高约40%，成本降低约70%。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种从蛇纹石中提取复合硅酸盐净水剂的方法，其特征在于，包括步骤：
（1）采用颚式破碎机将蛇纹石破碎得到破碎颗粒；
（2）将得到的破碎颗粒用球磨机加水进行研磨，直至至少90%的颗粒直径小于等于200目，然后用气体重选机将含金属杂质部分选出；
（3）将步骤（2）中所得材料采用6000GS湿式磁选出各类金属杂质，得到无杂质成品；
（4）将步骤（3）所得无杂质成品送入回转窑内焙烧；
（5）将步骤（4）所得材料继续经球磨机研磨直至90%的颗粒直径小于等于600目；
（6）将步骤（5）所得材料与聚丙烯酰胺按照10：1的比例调配，最终得到复合硅酸盐净水剂。
2.根据权利要求1所述的一种从蛇纹石中提取复合硅酸盐净水剂的方法，其特征在于，在步骤（1）中，蛇纹石的破碎粒度≤4mm。
3.根据权利要求1所述的一种从蛇纹石中提取复合硅酸盐净水剂的方法，其特征在于，在步骤（4）中，所述回转窑的温度为400℃。
4.根据权利要求3所述的一种从蛇纹石中提取复合硅酸盐净水剂的方法，其特征在于，在步骤（4）中，在回转窑中的焙烧时间为10分钟。
5.一种如权利要求1-4任一所述的从蛇纹石中提取复合硅酸盐净水剂在污水处理上的应用。