CN109053174A - A kind of snowflake white sand ceramic tile and preparation method thereof - Google Patents
A kind of snowflake white sand ceramic tile and preparation method thereof Download PDFInfo
- Publication number
- CN109053174A CN109053174A CN201811243269.7A CN201811243269A CN109053174A CN 109053174 A CN109053174 A CN 109053174A CN 201811243269 A CN201811243269 A CN 201811243269A CN 109053174 A CN109053174 A CN 109053174A
- Authority
- CN
- China
- Prior art keywords
- parts
- white sand
- ceramic tile
- snowflake white
- snowflake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of snowflake white sand ceramic tiles and preparation method thereof, belong to tile material field.The snowflake white sand ceramic tile includes the raw material of following parts by weight: 80-110 parts of snowflake white sand, 25-33 parts of diatomite, 18-22 parts of silica flour, 48-56 parts of potassium feldspar, 7-9 parts of precipitated calcium carbonate, 12-16 parts of white clay, 15-19 parts of pyrophillite, 5-9 parts of nano-titanium dioxide, 13-15 parts of hollow glass micropearl, 2-4 parts of suspending agent, 3-5 parts of bonding agent.Snowflake white sand ceramic tile of the present invention and preparation method thereof increases wear-resisting property, improves freedom from cracking ability, reduces the breakage rate of product, improves material overall performance and use degree is wider.
Description
Technical field
A kind of tile material field of the present invention, and in particular to snowflake white sand ceramic tile and preparation method thereof.
Background technique
Ceramic tile is metal oxide and half-metal oxide with fire resisting, via grinding, mixing, compacting, glazing, sintering
And manufactured process, a kind of porcelain of acid and alkali-resistance of formation or stone matter etc., it is widely used in building or ornament materials, referred to as porcelain
Brick.Its raw material is mostly mixed by clay, quartz etc..With the rapid development of China's building tile industry, so that people
It is also higher and higher to the performance requirement of ceramic tile.For ceramic tile currently on the market there is wearing no resistance, use process is swollen
Easy frictional dissipation is very serious, highly shortened its service life, is unable to satisfy the market demand.
Snowflake white sand has excellent performance, it is to be process by pure quartz wedge through advanced extra-fine grinding technique,
It and is the extremely wide inorganic non-metallic material of purposes.Snowflake white sand is with dielectric properties are excellent, thermal expansion coefficient is low, thermally conductive
The advantages that coefficient is high, suspendability is good.Wherein, the dioxide-containing silica of snowflake white sand be 99.3%, 7 grades of hardness Mohs, whiteness
Greater than 91, size distribution is more satisfactory.Also very pure exquisiteness, glossiness height are often used in and build the texture of snowflake white sand
Build finishing, terrazzo aggregate, lacquer, sand texture coating etc..There are no the ceramic tiles using snowflake white sand as raw material currently on the market.
Summary of the invention
The purpose of the present invention is to provide a kind of snowflake white sand ceramic tiles and preparation method thereof, and which increase wear-resisting properties, mention
High freedom from cracking ability, reduces the breakage rate of product, improves material overall performance and use degree is wider.
To achieve the above object, the invention provides the following technical scheme:
A kind of snowflake white sand ceramic tile, the raw material including following parts by weight: 80-110 parts of snowflake white sand, 25-33 parts of diatomite,
18-22 parts of silica flour, 48-56 parts of potassium feldspar, 7-9 parts of precipitated calcium carbonate, 12-16 parts of white clay, 15-19 parts of pyrophillite, nanometer two
5-9 parts of titanium oxide, 13-15 parts of hollow glass micropearl, 2-4 parts of suspending agent, 3-5 parts of bonding agent.
Preferably, the snowflake white sand ceramic tile, the raw material including following parts by weight: 95 parts of snowflake white sand, 29 parts of diatomite,
It is 20 parts of silica flour, 52 parts of potassium feldspar, 8 parts of precipitated calcium carbonate, 14 parts of white clay, 17 parts of pyrophillite, 7 parts of nano-titanium dioxide, hollow
14 parts of glass microballoon, 3 parts of suspending agent, 4 parts of bonding agent.
Preferably, the preparation method of a kind of snowflake white sand ceramic tile, comprising the following steps:
(1) snowflake white sand, diatomite, silica flour, potassium feldspar, precipitated calcium carbonate, pyrophillite, nano-titanium dioxide are put into
It is ground to ball mill, obtains powder;
(2) white clay, suspending agent, bonding agent, hollow glass micropearl are mixed evenly under 10-13 DEG C of water-bath, are stirred
After time is 10-20min, temperature is gradually lowered to 0 DEG C, continues to stir 25-30min, is then placed in cracking axe and reacts 20-
30min is to get auxiliary material;
(3) powder and auxiliary material are mixed with water, are aided with microwave irradiation, then put into grinder and ground, obtained
To slurry;
(4) be atomized using spray tower slurry, drying and granulating, be then allowed to stand after aging 24-28h carry out base, glazing,
It fires, edging is to get the snowflake white sand ceramic tile.
Preferably, in the step (1), the partial size 500-600 mesh of powder.
Preferably, in the step (1), the revolving speed of ball mill is 165-185r/min, milling time 1-1.5h.
Preferably, in the step (2), the temperature for cracking axe is 400-450 DEG C.
Preferably, in the step (3), the revolving speed of grinder is 150-200r/min, milling time 30-45min.
Compared with prior art, the beneficial effects of the present invention are:
(1) raw material is wanted based on snowflake white sand, by adding diatomite, silica flour, pyrophillite, precipitated calcium carbonate, enhancing
The wear-resisting property of ceramic tile improves the overall performance of ceramic tile by adding potassium feldspar, nano-titanium dioxide.
(2) auxiliary material is made in white clay, suspending agent, bonding agent, hollow glass micropearl, improves the adhesive effect of powder, meanwhile,
The freedom from cracking ability of ceramic tile is improved, secondly, improving the sound-absorbing effect of ceramic tile.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiments of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is general
Logical technical staff every other embodiment obtained without making creative work belongs to what the present invention protected
Range.
Embodiment 1
A kind of snowflake white sand ceramic tile described in the present embodiment, the raw material including following parts by weight: 80 parts of snowflake white sand, silicon
25 parts of diatomaceous earth, 18 parts of silica flour, 48 parts of potassium feldspar, 7 parts of precipitated calcium carbonate, 12 parts of white clay, 15 parts of pyrophillite, nano-titanium dioxide
5 parts, 13 parts of hollow glass micropearl, 2 parts of suspending agent, 3 parts of bonding agent.
A kind of preparation method of the snowflake white sand ceramic tile, comprising the following steps:
(1) snowflake white sand, diatomite, silica flour, potassium feldspar, precipitated calcium carbonate, pyrophillite, nano-titanium dioxide are put into
It is ground to ball mill, the revolving speed of ball mill is 165r/min, milling time 1h, obtains powder, the partial size 500 of powder
Mesh;
(2) white clay, suspending agent, bonding agent, hollow glass micropearl are mixed evenly under 10 DEG C of water-baths, mixing time
After 10min, temperature is gradually lowered to 0 DEG C, continues to stir 25min, is then placed in cracking axe and reacts 20min, crack axe
Temperature be 400 DEG C to get auxiliary material;
(3) powder and auxiliary material are mixed with water, are aided with microwave irradiation, then put into grinder and ground, ground
The revolving speed of grinding machine is 150r/min, and milling time 30min obtains slurry;
(4) it is atomized using spray tower slurry, drying and granulating, is then allowed to stand and aging carries out base, glazing, burning afterwards for 24 hours
System, edging are to get the snowflake white sand ceramic tile.
Embodiment 2
A kind of snowflake white sand ceramic tile described in the present embodiment, the raw material including following parts by weight: 95 parts of snowflake white sand, silicon
29 parts of diatomaceous earth, 20 parts of silica flour, 52 parts of potassium feldspar, 8 parts of precipitated calcium carbonate, 14 parts of white clay, 17 parts of pyrophillite, nano-titanium dioxide
7 parts, 14 parts of hollow glass micropearl, 3 parts of suspending agent, 4 parts of bonding agent.
A kind of preparation method of the snowflake white sand ceramic tile, comprising the following steps:
(1) snowflake white sand, diatomite, silica flour, potassium feldspar, precipitated calcium carbonate, pyrophillite, nano-titanium dioxide are put into
It is ground to ball mill, the revolving speed of ball mill is 175r/min, milling time 1.2h, obtains powder, the partial size 550 of powder
Mesh;
(2) white clay, suspending agent, bonding agent, hollow glass micropearl are mixed evenly under 12 DEG C of water-baths, mixing time
After 15min, temperature is gradually lowered to 0 DEG C, continues to stir 27min, is then placed in cracking axe and reacts 25min, crack axe
Temperature be 425 DEG C to get auxiliary material;
(3) powder and auxiliary material are mixed with water, are aided with microwave irradiation, then put into grinder and ground, ground
The revolving speed of grinding machine is 175r/min, and milling time 38min obtains slurry;
(4) it is atomized using spray tower slurry, drying and granulating, carries out base, glazing, burning after being then allowed to stand aging 26h
System, edging are to get the snowflake white sand ceramic tile.
Embodiment 3
A kind of snowflake white sand ceramic tile described in the present embodiment, the raw material including following parts by weight: 110 parts of snowflake white sand,
33 parts of diatomite, 22 parts of silica flour, 56 parts of potassium feldspar, 9 parts of precipitated calcium carbonate, 16 parts of white clay, 19 parts of pyrophillite, nanometer titanium dioxide
9 parts of titanium, 15 parts of hollow glass micropearl, 4 parts of suspending agent, 5 parts of bonding agent.
A kind of preparation method of the snowflake white sand ceramic tile, comprising the following steps:
(1) snowflake white sand, diatomite, silica flour, potassium feldspar, precipitated calcium carbonate, pyrophillite, nano-titanium dioxide are put into
It is ground to ball mill, the revolving speed of ball mill is 185r/min, milling time 1.5h, obtains powder, the partial size 600 of powder
Mesh;
(2) white clay, suspending agent, bonding agent, hollow glass micropearl are mixed evenly under 13 DEG C of water-baths, mixing time
After 20min, temperature is gradually lowered to 0 DEG C, continues to stir 30min, is then placed in cracking axe and reacts 30min, crack axe
Temperature be 450 DEG C to get auxiliary material;
(3) powder and auxiliary material are mixed with water, are aided with microwave irradiation, then put into grinder and ground, ground
The revolving speed of grinding machine is 200r/min, and milling time 45min obtains slurry;
(4) it is atomized using spray tower slurry, drying and granulating, carries out base, glazing, burning after being then allowed to stand aging 28h
System, edging are to get the snowflake white sand ceramic tile.
Above content is only to structure of the invention example and explanation, affiliated those skilled in the art couple
Described specific embodiment does various modifications or additions or is substituted in a similar manner, without departing from the present invention
Structure or beyond the scope defined by this claim, be within the scope of protection of the invention.
Claims (7)
1. a kind of snowflake white sand ceramic tile, which is characterized in that the raw material including following parts by weight: 80-110 parts of snowflake white sand, diatom
25-33 parts native, 18-22 parts of silica flour, 48-56 parts of potassium feldspar, 7-9 parts of precipitated calcium carbonate, 12-16 parts of white clay, pyrophillite 15-19
Part, 5-9 parts of nano-titanium dioxide, 13-15 parts of hollow glass micropearl, 2-4 parts of suspending agent, 3-5 parts of bonding agent.
2. a kind of snowflake white sand ceramic tile according to claim 1, which is characterized in that the raw material including following parts by weight: snow
95 parts of grey sand, 29 parts of diatomite, 20 parts of silica flour, 52 parts of potassium feldspar, 8 parts of precipitated calcium carbonate, 14 parts of white clay, pyrophillite 17
Part, 7 parts of nano-titanium dioxide, 14 parts of hollow glass micropearl, 3 parts of suspending agent, 4 parts of bonding agent.
3. -2 described in any item a kind of preparation methods of snowflake white sand ceramic tile according to claim 1, which is characterized in that including with
Lower step:
(1) snowflake white sand, diatomite, silica flour, potassium feldspar, precipitated calcium carbonate, pyrophillite, nano-titanium dioxide are put into ball
Grinding machine is ground, and powder is obtained;
(2) white clay, suspending agent, bonding agent, hollow glass micropearl are mixed evenly under 10-13 DEG C of water-bath, mixing time
After 10-20min, temperature is gradually lowered to 0 DEG C, continues to stir 25-30min, is then placed in cracking axe and reacts 20-
30min is to get auxiliary material;
(3) powder and auxiliary material are mixed with water, are aided with microwave irradiation, then put into grinder and ground, starched
Material;
(4) it is atomized using spray tower slurry, drying and granulating, carries out base, glazing, burning after being then allowed to stand aging 24-28h
System, edging are to get the snowflake white sand ceramic tile.
4. a kind of preparation method of snowflake white sand ceramic tile according to claim 3, it is characterised in that: in the step (1),
The partial size 500-600 mesh of powder.
5. a kind of preparation method of snowflake white sand ceramic tile according to claim 3, it is characterised in that: in the step (1),
The revolving speed of ball mill is 165-185r/min, milling time 1-1.5h.
6. a kind of snowflake white sand ceramic tile according to claim 3 and preparation method thereof, it is characterised in that: the step (2)
In, the temperature for cracking axe is 400-450 DEG C.
7. a kind of snowflake white sand ceramic tile according to claim 3 and preparation method thereof, it is characterised in that: the step (3)
In, the revolving speed of grinder is 150-200r/min, milling time 30-45min.