CN109023656A - A kind of production method of black and white elastic galled twill printed fabric - Google Patents
A kind of production method of black and white elastic galled twill printed fabric Download PDFInfo
- Publication number
- CN109023656A CN109023656A CN201810948754.8A CN201810948754A CN109023656A CN 109023656 A CN109023656 A CN 109023656A CN 201810948754 A CN201810948754 A CN 201810948754A CN 109023656 A CN109023656 A CN 109023656A
- Authority
- CN
- China
- Prior art keywords
- black
- twill
- fabric
- white
- galled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production methods of black and white elastic galled twill printed fabric, after taking the yarn weaving being made of Hei Si and Bai Si to obtain black and white stretch twill fabric, continue on through debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp to get to finished product.Compared with prior art, fabric of the invention can obtain suitable length and lousiness fine and smooth enough, the soft hair partially of fabric hand feel, and visual effect is naturally comfortable etc..
Description
Technical field
The invention belongs to functional fabric preparation technical fields, are related to a kind of system of black and white elastic galled twill printed fabric
Make method.
Background technique
The appearance fabric of the products such as the existing men's clothing Buddhist nun of company overcomes, cotton clothes, jacket is generally using having metallic luster
Fabric, to show the luxurious of leather.But the appearance of this metallic luster is also easy to be difficult to meet partially comfortable due to high cold
The user of natural demand.
Summary of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of black and white elastic galleds
The production method of twill printed fabric is mainly coated 40D spandex by the compound space-variant fiber of terylene 75D black and white again and is tiltedly organized with herringbone
The top-weight fabric of intertexture, fabric is after desizing, fluffing, sizing, plucking arrange, and cloth cover is soft, and wool-like effect is good, and fabric turns through heat
After bat printing is spent, there are monochromatic lattice, polychrome to expire the flower pattern of the hair series partially such as bottom sieve frame type, plover gradual change.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of production method of black and white elastic galled twill printed fabric, takes the yarn weaving being made of Hei Si and Bai Si to obtain
To after black and white stretch twill fabric, debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp are continued on through to get to finished product.
Further, the compositely proportional of black silk and white silk is 1:1.1-1.3 in the yarn, is more than that this range is partially black
Or it is partially white.In addition, warp thread is the white silk ATY SD of the black silk+T-75D of T-75D, weft yarn T-75D in yarn of the present invention
The black white silk ATY SD+40D spandex machine packet of silk+T-75D, makes product show preferable coloured light sense and stereovision.
Further, the detailed process of Alkali reduction cleaning are as follows:
At 125 DEG C, the piece alkali for accounting for black and white stretch twill fabric weight 13-15% to be processed is taken to carry out according to bath raio 1:8
Decrement treatment.In this step, if concentration of caustic soda is low, temperature is low, fiber detaching can have a significant impact to ball woll with regard to insufficient,
If plucking is uneven, maula is not grown, and feel can harden.Excessive concentration, temperature height, fiber detaching are with regard to mistake.Fabric strength swashs
Poly- decline, and plucking is easy to pull out broken hole.
Further, the detailed process of fluffing are as follows:
It takes fabric to enter in the auxiliary agent pond for the raising agent FS-202 that content is 2.5-3%o.w.f, is handled at 50 DEG C
20min, it is therefore an objective to which fiber is more fluffy, is convenient for next procedure plucking.
Further, the process conditions of plucking are as follows: use 8 roller linkage process, the roller diameter of each plucking roller is
1500mm, revolving speed 120r/min, the cloth feeding speed for controlling fabric is 10m/min, and plucking repeats 2-3 times.Further, it draws
After hair, floating hair is also removed using washing, floating hair when to avoid stamp adheres at light color relatively and causes flaw.
Further, the process conditions of stamp are as follows: the diameter of stamp hot-rolling is 600-800mm, and roller revolving speed is 20-30r/
Min, printing temperature are 190-198 DEG C, and the cloth feeding speed of fabric is 10m/min.
Further, weaving of the invention can be divided into raw material → warping → starching → and axis → and wear silk → upper machine → weaving
Etc. processes, wherein and during axis, warp thread and axis pressure be 2.3kg, convoluting speed 320m/min；Weft yarn uses 80
Grid-connected drafting machine, and axis pressure 2.8kg, 3.5 times of spandex draft ratio, convoluting speed 320m/min.When specific weaving, on
Machine is always through number: 10540, looming weaving strength: 11kg, 3.2, Lian Su: 520 turns/min of water pump, nozzle: 75/20.Preferably,
Warp rebeaming machine can select TM-400 type, loom W-480 type.
Compared with prior art, the invention has the following advantages that
(1) all ATY fabric hand feel and style is relatively more unified currently on the market.The present invention using the black silk of terylene 75D and
Terylene 75D Bai Sisheng core carries out blowing by daily output ATY (B-501) space-variant machine, and it is mixed to obtain the black and white that visual effect shows unique characteristics
Plying, and then it is prominent to guarantee that fabric comes out color fastness.In addition, the present invention also the parameters such as tension in weaving process are carried out it is detailed
It limits, ensure that the twill fabric weaved has suitable elastic force.
(2) compared to conventional fabric, the present invention also further eliminates dyeing, soaps, fixation three process, not only saves
Process, while also effectively saving the discharge of wastewater etc. in process.
(3) present invention, using processes such as special Alkali reduction cleaning, sizing and pluckings, obtains after the completion of face weave
Suitable length and lousiness fine and smooth enough, it is ensured that fabric obtains the soft feel of inclined hair, visual effect is naturally comfortable,
Further, since fabric physical property is suitable for, it can choose packing paper thermal transfer printing, 198 DEG C of printing temperature, have monochromatic lattice, polychrome full
The flower pattern of the hair series partially such as bottom sieve frame type, plover gradual change.
Specific embodiment
The present invention is described in detail combined with specific embodiments below.The present embodiment is based on the technical solution of the present invention
Implemented, the detailed implementation method and specific operation process are given, but protection scope of the present invention be not limited to it is following
Embodiment.
In following embodiment, unless otherwise noted, then show used reagent treatment, treatment process (such as weaving)
For the reagent treatment or treatment process of yarn or fabric commonly used in the art.
Embodiment 1
A kind of production method of black and white elastic galled twill printed fabric, takes the yarn weaving being made of Hei Si and Bai Si to obtain
To after black and white stretch twill fabric, debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp are continued on through to get to finished product.
In the present embodiment, the compositely proportional of black silk and white silk is 1:1.2 in the yarn, in used yarn, warp
Yarn is the white silk ATY SD of the black silk+T-75D of T-75D, and weft yarn is the white silk ATY SD+40D spandex machine packet of the black silk+T-75D of T-75D, is made
Product has shown preferable coloured light sense and stereovision.
The detailed process of Alkali reduction cleaning are as follows:
At 125 DEG C, the piece alkali for accounting for black and white stretch twill fabric weight 14% to be processed is taken to be reduced according to bath raio 1:8
Processing.
The detailed process of fluffing are as follows:
It takes fabric to enter in the auxiliary agent pond for the raising agent FS-202 that content is 2.7%o.w.f, handles 20min at 50 DEG C.
The process conditions of plucking are as follows: use 8 roller linkage process, the roller diameter of each plucking roller is 1500mm, and revolving speed is
120r/min, the cloth feeding speed for controlling fabric is 10m/min, and plucking repeats 2-3 times.
The process conditions of stamp are as follows: the diameter of stamp hot-rolling is 700mm, and roller revolving speed is 25r/min, and printing temperature is
194 DEG C, the cloth feeding speed of fabric is 10m/min.
Finally, fabric end properties parameter obtained is as follows: Du≤4 grade Se Lao, rub resistance staining fastness are dry: 4-5 grades
It is wet: within 3-4 grades, moisture absorption 2 seconds, pliability 5.
Comparative example 1
Compared with Example 1, the overwhelming majority is all identical, in addition in the present embodiment Alkali reduction cleaning process, piece alkali additional amount
It is the 10% of black and white stretch twill fabric weight to be processed, temperature is changed to outside 90 DEG C, remaining is constant.
Comparative example 2
Compared with Example 1, the overwhelming majority is all identical, in addition in the present embodiment Alkali reduction cleaning process, piece alkali additional amount
It is the 20% of black and white stretch twill fabric weight to be processed, temperature is changed to outside 150 DEG C, remaining is constant.
It is respectively compared embodiment 1 and comparative example 1, comparative example 2 fabric of process that treated, it is found that embodiment 1 obtains face
The plucking of material uniformly, moderate length, and it is soft.And the partial region of the fabric of comparative example 1 does not have a plucking, and feel compared with
Firmly, the fabric of comparative example 2 then has after plucking parts against wear in small holes, and fabric is easy to rip damage after pullling.
Comparative example 3
Compared with Example 1, the overwhelming majority is all identical, in addition to the present embodiment eliminates fluffing process.
Fabric after comparing embodiment 1 and 3 working process of comparative example, compared to the fabric of embodiment 1, the face of comparative example 3
Plucking length on material is shorter, and partial region even has no obvious plucking, and feel is obviously hard.
Embodiment 2
A kind of production method of black and white elastic galled twill printed fabric, takes the yarn weaving being made of Hei Si and Bai Si to obtain
To after black and white stretch twill fabric, debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp are continued on through to get to finished product.
In the present embodiment, the compositely proportional of black silk and white silk is 1:1.1 in the yarn, in used yarn, warp
Yarn is the white silk ATY SD of the black silk+T-75D of T-75D, and weft yarn is the white silk ATY SD+40D spandex machine packet of the black silk+T-75D of T-75D, is made
Product has shown preferable coloured light sense and stereovision.
The detailed process of Alkali reduction cleaning are as follows:
At 125 DEG C, the piece alkali for accounting for black and white stretch twill fabric weight 13% to be processed is taken to be reduced according to bath raio 1:8
Processing.
The detailed process of fluffing are as follows:
It takes fabric to enter in the auxiliary agent pond for the raising agent FS-202 that content is 2.5%o.w.f, handles 20min at 50 DEG C.
The process conditions of plucking are as follows: use 8 roller linkage process, the roller diameter of each plucking roller is 1500mm, and revolving speed is
120r/min, the cloth feeding speed for controlling fabric is 10m/min, and plucking repeats 2-3 times.
The process conditions of stamp are as follows: the diameter of stamp hot-rolling is 600mm, and roller revolving speed is 20r/min, and printing temperature is
190 DEG C, the cloth feeding speed of fabric is 10m/min.
Finally, fabric end properties parameter obtained is as follows: Du≤4 grade Se Lao, rub resistance staining fastness are dry: 4-5 grades
It is wet: within 3-4 grades, moisture absorption 2 seconds, pliability 5.
Embodiment 3
A kind of production method of black and white elastic galled twill printed fabric, takes the yarn weaving being made of Hei Si and Bai Si to obtain
To after black and white stretch twill fabric, debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp are continued on through to get to finished product.
In the present embodiment, the compositely proportional of black silk and white silk is 1:1.3 in the yarn, in used yarn, warp
Yarn is the white silk ATY SD of the black silk+T-75D of T-75D, and weft yarn is the white silk ATY SD+40D spandex machine packet of the black silk+T-75D of T-75D, is made
Product has shown preferable coloured light sense and stereovision.
The detailed process of Alkali reduction cleaning are as follows:
At 125 DEG C, the piece alkali for accounting for black and white stretch twill fabric weight 15% to be processed is taken to be reduced according to bath raio 1:8
Processing.
The detailed process of fluffing are as follows:
It takes fabric to enter in the auxiliary agent pond for the raising agent FS-202 that content is 3%o.w.f, handles 20min at 50 DEG C.
The process conditions of plucking are as follows: use 8 roller linkage process, the roller diameter of each plucking roller is 1500mm, and revolving speed is
120r/min, the cloth feeding speed for controlling fabric is 10m/min, and plucking repeats 2-3 times.
The process conditions of stamp are as follows: the diameter of stamp hot-rolling is 800mm, and roller revolving speed is 30r/min, and printing temperature is
198 DEG C, the cloth feeding speed of fabric is 10m/min.
Finally, fabric end properties parameter obtained is as follows: Du≤4 grade Se Lao, rub resistance staining fastness are dry: 4-5 grades
It is wet: within 3-4 grades, moisture absorption 2 seconds, pliability 5.
The above description of the embodiments is intended to facilitate ordinary skill in the art to understand and use the invention.
Person skilled in the art obviously easily can make various modifications to these embodiments, and described herein general
Principle is applied in other embodiments without having to go through creative labor.Therefore, the present invention is not limited to the above embodiments, ability
Field technique personnel announcement according to the present invention, improvement and modification made without departing from the scope of the present invention all should be of the invention
Within protection scope.
Claims (6)
1. a kind of production method of black and white elastic galled twill printed fabric, which is characterized in that take and be made of Hei Si and Bai Si
After yarn weaving obtains black and white stretch twill fabric, continue on through debatching, Alkali reduction cleaning, fluffing, sizing, plucking, stamp to get
To finished product.
2. a kind of production method of black and white elastic galled twill printed fabric according to claim 1, which is characterized in that institute
The compositely proportional of black silk and white silk is 1:1.1-1.3 in the yarn stated.
3. a kind of production method of black and white elastic galled twill printed fabric according to claim 1, which is characterized in that alkali
It is reduced the detailed process of cleaning are as follows:
At 125 DEG C, the piece alkali for accounting for black and white stretch twill fabric weight 13-15% to be processed is taken to be reduced according to bath raio 1:8
Processing.
4. a kind of production method of black and white elastic galled twill printed fabric according to claim 1, which is characterized in that rise
The detailed process of hair are as follows:
It takes fabric to enter in the auxiliary agent pond for the raising agent FS-202 that content is 2.5-3%o.w.f, handles 20min at 50 DEG C.
5. a kind of production method of black and white elastic galled twill printed fabric according to claim 1, which is characterized in that draw
The process conditions of hair are as follows: use 8 roller linkage process, the roller diameter of each plucking roller is 1500mm, revolving speed 120r/min, control
The cloth feeding speed of base cloth is 10m/min, and plucking repeats 2-3 times.
6. a kind of production method of black and white elastic galled twill printed fabric according to claim 1, which is characterized in that print
Colored process conditions are as follows: the diameter of stamp hot-rolling is 600-800mm, and roller revolving speed is 20-30r/min, printing temperature 190-
198 DEG C, the cloth feeding speed of fabric is 10m/min.