CN109021623A - A kind of effectively insulating fire proof and thermo-insulation coating material formula - Google Patents
A kind of effectively insulating fire proof and thermo-insulation coating material formula Download PDFInfo
- Publication number
- CN109021623A CN109021623A CN201810488720.5A CN201810488720A CN109021623A CN 109021623 A CN109021623 A CN 109021623A CN 201810488720 A CN201810488720 A CN 201810488720A CN 109021623 A CN109021623 A CN 109021623A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermo
- agent
- coating material
- insulation coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of effectively insulating fire proof and thermo-insulation coating material formula, it is related to the exterior coating technical field of building.A kind of effectively insulating fire proof and thermo-insulation coating material formula is made of following raw material: water, defoaming agent, refractory fibre, inorganic bond, anticorrosion and bactericidal agent, propylene glycol, diatomite, titanium dioxide, silica solution, dispersing agent.Above-mentioned raw materials are taken to can be completed according to a kind of processing of effectively insulating fire proof and thermo-insulation coating material formula according to parts by weight.After adopting the above technical scheme, the invention has the following beneficial effects: this functional insulating mold coating, has had both insulation, purification air, anti-corrosion, the function of fire-proof high-temperature resistant.
Description
Technical field
The present invention relates to the exterior coating technical fields of building, and in particular to a kind of effectively insulating fire proof and thermo-insulation coating material is matched
Side.
Background technique
In the trend that the world today advocates energy-saving and emission-reduction and ecological ideas, heat-barrier material is just by based on industrial heat-insulation and heat-preservation
To changing based on building heat insulation.Country is vigorously advocating low-carbon energy-saving industry, advocates energy saving economizing type energy industry, institute
More pay attention to R&D and promotion application building heat insulation coating with us.
Heat insulating coatings are to brush that the coating of thermal insulation function can be played in building surface, by use occasion difference
It is divided into transparent heat-insulated thermal insulation coatings and nontransparent heat insulating coatings;Pacify heat-insulation and heat-preservation mechanism, barrier property heat-insulation and heat-preservation can be divided into
3 class of coating, reflective heat-insulation paint and radiation heat insulation thermal insulation coatings.Current coating is all the thermal insulation separation of single heat preservation correlated performance
Hot coating, he does not have as purified air, improves air quality, fireproof function, the heat-insulated guarantor of development and production composite multi-functional
Thermo-paint, that is, a kind of insulating mold coating not only have excellent thermal and insulating performance also and have other to environmentally friendly low-carbon section
The multifunctional thermal-insulation thermal insulation coatings of energy performance.
Summary of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of effectively insulating fireproof heat insulatings to apply
Material, this functional insulating mold coating have had both insulation, purification air, anti-corrosion, the function of fire-proof high-temperature resistant.
To achieve the above object, the present invention uses the following technical scheme to be: a kind of effectively insulating fire proof and thermo-insulation coating material by with
The raw material of lower parts by weight forms: 250-300 parts of water, 1.5-2 parts of defoaming agent, and 15-22 parts of refractory fibre, inorganic bond 15-
30 parts, 1-2 parts of anticorrosion and bactericidal agent, 10-15 parts of propylene glycol, 100-150 parts of diatomite, 100-125 parts of titanium dioxide, silica solution 250-
300 parts, 4-6 parts of dispersing agent.Its Recipe comprise the steps of: the first step first in stirring container be added water, titanium dioxide,
Refractory fibre is stirred;Inorganic bond, anticorrosion and bactericidal agent, propylene glycol, diatomite is added in second step in stirring container;The
Dispersing agent stirring is added in stirring container and carries out high speed dispersion for three steps;It is equal that silica solution stirring is added in 4th step in stirring container
It is even;Defoaming agent is added in stirring container and is stirred for 5th step.
It is stirred at room temperature 10-15 minutes after inorganic bond, diatomite is added in the container.
It is stirred at room temperature 25-30 minutes after defoaming agent is added in the container.
It is one to have excellent extension after adopting the above technical scheme, the invention has the following beneficial effects: diatomite used in it
Property, there is that higher impact strength, tensile strength, tearing strength, light soft interior mill property is good, good etc. the high-quality work that does Compressive Strength
With, be free of harmful chemical, in addition to have the characteristics that non-ignitable, sound insulation, waterproof, it is light-weight and heat-insulated other than, also dehumidify, remove
Smelly, the effects of purifying the air of a room, be excellent environment-friendly type indoor and outdoor decoration material;Silica solution, refractory fibre, high temperature resistant inorganic
The addition of adhesive, gelatification can not only be played by imparting, and be also equipped with excellent high temperature resistant and fire protecting performance.In summary each
Functional material characteristic, this functional insulating mold coating have had both the function of insulation, purification air, fire-proof high-temperature resistant
Energy.
Specific embodiment
Embodiment 1
The technical solution that the specific embodiment of the invention uses: a kind of effectively insulating fire proof and thermo-insulation coating material is by following parts by weight
Raw material composition: 275 parts of water, 100 parts of titanium dioxide, 18 parts of refractory fibre, 17 parts of inorganic bond, 1.5 parts of anticorrosion and bactericidal agent, the third two
14 parts of alcohol, 115 parts of diatomite, 4.5 parts of dispersing agent, 280 parts of silica solution, 1.8 parts of defoaming agent, its Recipe include following step
Rapid: the first step is first added water, titanium dioxide, refractory fibre in stirring container and is stirred;Second step is added in stirring container
Inorganic bond, anticorrosion and bactericidal agent, propylene glycol, diatomite;Dispersing agent stirring is added in stirring container and carries out high speed for third step
Dispersion;Silica solution is added in stirring container and stirs evenly for 4th step;Defoaming agent is added in stirring container and is stirred for 5th step
It mixes.
It is stirred at room temperature 10-15 minutes after inorganic bond, diatomite is added in the container.
It is stirred at room temperature 25-30 minutes after defoaming agent is added in the container.
The dispersing agent is one kind in the molecule while having lipophilic and two kinds of opposite natures of hydrophily interfaces living
Property agent.It uniform can disperse those to be poorly soluble in the inorganic of liquid, the solid and liquid particles of organic pigment, while can also prevent
The sedimentation and cohesion of particle, amphipathic reagent needed for forming stable suspension.
The silica solution is dispersion liquid of the nanoscale silica dioxide granule in water or in solvent, is used as various fire resistings
Material binder has the characteristics that cohesive force is strong, high temperature resistant, is used for coatings industry, coating can be made secured, but can dirt-resisting dustproof,
The functions such as ageing-resistant, fire prevention.
The refractory fibre is also known as ceramic fibre, the refractory material that thermal conductivity is minimum, insulating energy-saving effect is best, it has
There is the effect of light-weight, low heat conductivity, resistance to mechanical vibration.
The anticorrosion and bactericidal agent has sterilization, antibacterial efficient, wide spectrum, lasting effect long, with various emulsifiers, surface-active
Agent intermiscibility is good, has excellent compatibility, and property miscible with water is good, easy to use, not by temperature limiting, 80 DEG C the following are
It is good, 100 DEG C below efficient 90% or more.
The high temperature resistant inorganic adhesive be it is a kind of using inorganic nano material through high temperature resistant made of polycondensation reaction without
Machine nanocomposite binders, by the screening to composition proportion and preparation technology parameter, obtaining binder is pH value for neutrality
Suspension/dispersion, not only cohesive force is strong and non-corrosive to metallic matrix, but also can keep good viscous under high temperature again
Connect performance and corrosion resistance, long service life.
Embodiment 2
Difference of the present embodiment from embodiment 1 is that it is made of the raw material of following weight fraction: 290 parts of water, titanium dioxide 115
Part, 20 parts of refractory fibre, 25 parts of inorganic bond, 1 part of anticorrosion and bactericidal agent, 11 parts of propylene glycol, 130 parts of diatomite, dispersing agent 4
Part, 270 parts of silica solution, 1.7 parts of defoaming agent, other raw material compositions, parts by weight are same as Example 1.
Embodiment 3
Difference of the present embodiment from embodiment 1 is that it is made of the raw material of following weight fraction: 290 parts of water, titanium dioxide 115
Part, 20 parts of refractory fibre, 25 parts of inorganic bond, 1 part of anticorrosion and bactericidal agent, 11 parts of propylene glycol, 130 parts of diatomite, dispersing agent 4
Part, 270 parts of silica solution, 1.7 parts of defoaming agent, other raw material compositions, parts by weight are same as Example 1.
Embodiment 4
Difference of the present embodiment from embodiment 1 is that it is made of the raw material of following weight fraction: 275 parts of water, titanium dioxide 120
Part, 17 parts of refractory fibre, 20 parts of inorganic bond, 2 parts of anticorrosion and bactericidal agent, 13 parts of propylene glycol, 125 parts of diatomite, dispersing agent 5.5
Part, 295 parts of silica solution, 1.9 parts of defoaming agent, other raw material compositions, parts by weight are same as Example 1.
It is one to have excellent extension after adopting the above technical scheme, the invention has the following beneficial effects: diatomite used in it
Property, there is that higher impact strength, tensile strength, tearing strength, light soft interior mill property is good, good etc. the high-quality work that does Compressive Strength
With, be free of harmful chemical, in addition to have the characteristics that non-ignitable, sound insulation, waterproof, it is light-weight and heat-insulated other than, also dehumidify, remove
Smelly, the effects of purifying the air of a room, be excellent environment-friendly type indoor and outdoor decoration material;Silica solution, refractory fibre, high temperature resistant inorganic
The addition of adhesive, gelatification can not only be played by imparting, and be also equipped with excellent high temperature resistant and fire protecting performance.In summary each
Functional material characteristic, this functional insulating mold coating have had both the function of insulation, purification air, fire-proof high-temperature resistant
Energy.
The above is only used to illustrate the technical scheme of the present invention and not to limit it, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (7)
1. a kind of effectively insulating fire proof and thermo-insulation coating material, it is characterised in that it is made of the raw material of following parts by weight: water 250-300
Part, 1.5-2 parts of defoaming agent, 15-22 parts of refractory fibre, 15-30 parts of inorganic bond, 1-2 parts of anticorrosion and bactericidal agent, propylene glycol 10-
15 parts, 100-150 parts of diatomite, 100-125 parts of titanium dioxide, 250-300 parts of silica solution, 4-6 parts of dispersing agent.
2. a kind of effectively insulating fire proof and thermo-insulation coating material formula, it is characterised in that its Recipe is the following steps are included: the first step
Water, titanium dioxide, refractory fibre are first added in stirring container to be stirred;Inorganic bond is added in second step in stirring container
Agent, anticorrosion and bactericidal agent, propylene glycol, diatomite;Dispersing agent stirring is added in stirring container and carries out high speed dispersion for third step;4th
Silica solution is added in stirring container and stirs evenly for step;Defoaming agent is added in stirring container and is stirred for 5th step.
3. a kind of effectively insulating fire proof and thermo-insulation coating material according to claim 1, it is characterised in that it is by following weight fraction
Raw material composition: 275 parts of water, 100 parts of titanium dioxide, 18 parts of refractory fibre, 17 parts of inorganic bond, 1.5 parts of anticorrosion and bactericidal agent, third
14 parts of glycol, 115 parts of diatomite, 4.5 parts of dispersing agent, 280 parts of silica solution, 1.8 parts of defoaming agent.
4. a kind of effectively insulating fire proof and thermo-insulation coating material according to claim 1, it is characterised in that it is by following weight fraction
Raw material composition: 290 parts of water, 115 parts of titanium dioxide, 20 parts of refractory fibre, 25 parts of inorganic bond, 1 part of anticorrosion and bactericidal agent, the third two
11 parts of alcohol, 130 parts of diatomite, 4 parts of dispersing agent, 270 parts of silica solution, 1.7 parts of defoaming agent.
5. a kind of effectively insulating fire proof and thermo-insulation coating material according to claim 1, it is characterised in that it is by following weight fraction
Raw material composition: 275 parts of water, 120 parts of titanium dioxide, 17 parts of refractory fibre, 20 parts of inorganic bond, 2 parts of anticorrosion and bactericidal agent, the third two
13 parts of alcohol, 125 parts of diatomite, 5.5 parts of dispersing agent, 295 parts of silica solution, 1.9 parts of defoaming agent.
6. a kind of effectively insulating fire proof and thermo-insulation coating material formula according to claim 2, it is characterised in that in the container
It is stirred at room temperature 10-15 minutes after inorganic bond, diatomite is added.
7. a kind of effectively insulating fire proof and thermo-insulation coating material formula according to claim 2, it is characterised in that: in the container
It is stirred at room temperature 25-30 minutes after defoaming agent is added.