CN109016736B - 装饰片 - Google Patents
装饰片 Download PDFInfo
- Publication number
- CN109016736B CN109016736B CN201810670871.2A CN201810670871A CN109016736B CN 109016736 B CN109016736 B CN 109016736B CN 201810670871 A CN201810670871 A CN 201810670871A CN 109016736 B CN109016736 B CN 109016736B
- Authority
- CN
- China
- Prior art keywords
- layer
- decorative sheet
- pet
- height
- texture structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种装饰片，其包括：透明基层，其包括相对设置的第一表面和第二表面；固化胶层，其包括相对设置的第一侧面和第二侧面，所述第一侧面与所述第一表面相接触，所述第二侧面设有凹和/或凸的纹理结构；标记块，嵌设于所述第一侧面内并与所述第一表面相贴合；镀膜层，设置于所述第二侧面并覆盖所述纹理结构；打底层，覆盖于所述镀膜层远离所述固化胶层的一侧。使得装饰片具有标记又有装饰的纹理结构，标记清晰明了，纹理结构能产生光学效果，使装饰片具有较好的质感。
Description
技术领域
本发明涉及光学装饰领域，尤其涉及一种装饰片。
背景技术
随着消费类电子产品的日新月异，各品牌的产品竞争激烈，消费者对于消费类电子产品的要求也越来越高，除了电子产品的硬件规格(例如处理器、屏幕尺寸与像素、网络制式、相机像素等)，消费者也非常看重电子产品的外观设计。电子产品的前盖或者后盖，除了对颜色的需求外，更对质感提高到前所未有的高度，而显然，现有的电子产品的前盖或后盖均不符合要求。
鉴于此，本发明通过改善盖板以解决所存在的技术问题。
发明内容
基于此，有必要提供一种装饰元件以解决上述的技术问题。
本发明的一个技术方案是：
一种装饰片，其包括：
透明基层，其包括相对设置的第一表面和第二表面；
固化胶层，其包括相对设置的第一侧面和第二侧面，所述第一侧面于所述第一表面相接触，所述第二侧面设有凹和/或凸的纹理结构；
标记块，嵌设于所述第一侧面内并与所述第一表面相贴合；
镀膜层，设置于所述第二侧面并覆盖所述纹理结构；
打底层，覆盖于所述镀膜层远离所述固化胶层的一侧。
在其中一实施例中，所述标记块在所述第一表面的高度为1-10μm。
在其中一实施例中，所述标记块在所述第一表面的高度为4-5μm。
在其中一实施例中，所述标记块的材料为镜面银或油墨。
在其中一实施例中，所述标记块的材料为彩色油墨。
在其中一实施例中，所述标记块显示为logo、图案、文字、符号、数字中的一种或多种。
在其中一实施例中，所述标记块采用丝印工艺印刷而成。
在其中一实施例中，所述固化胶层在所述第一表面的高度为10-22μm。
在其中一实施例中，所述固化胶层在所述第一表面的高度为15-20μm。
在其中一实施例中，所述纹理结构为直线型柱面镜、曲线型柱面镜、CD纹、微透镜、蛾眼结构、小短线或拉丝纹，所述纹理结构的截面形状为三角形、矩形、梯形或弓形。
在其中一实施例中，所述固化胶层采用彩色UV胶压印并固化而成。
在其中一实施例中，所述镀膜层为蒸镀层。
在其中一实施例中，所述打底层为黑色油墨层、彩色油墨层或彩色UV胶层。
在其中一实施例中，所述透明基层为PET层，所述PET层包括彩色PET，或者所述PET层包括PET及贴附于所述PET上的彩色膜。
在其中一实施例中，所述透明基层为PET层，所述PET层包括位于所述第二表面的粘结层。
在其中一实施例中，还包括玻璃层，所述粘结层与所述玻璃层相粘结。
在其中一实施例中，所述透明基层为玻璃层。
在其中一实施例中，所述玻璃层的第二表面设置有抗反射膜、防指纹膜、硬化膜中的至少一种。
本发明的有益效果：本发明的装饰片具有嵌设于第一侧面内并与第一表面相贴合的标记块，固化胶层的第二侧面凹和/或凸设有纹理结构，纹理结构上覆设有镀膜层和打底层，使得装饰片具有标记又有装饰的纹理结构，标记清晰明了，纹理结构能产生光学效果，使装饰片具有较好的质感。
附图说明
图1为本发明装饰片的平面结构示意图；
图2为图1沿A-A线的剖面结构示意图；
图3为本发明装饰片的另一种剖面结构示意图；
图4为本发明装饰片的又一种平面结构示意图。
具体实施方式
为了便于理解本发明，下面将参照相关附图对本发明进行更全面的描述。附图中给出了本发明的较佳实施方式。但是，本发明可以通过许多不同的形式来实现，并不限于下面所描述的实施方式。相反地，提供这些实施方式的目的是使对本发明的公开内容理解的更加透彻全面。
除非另有定义，本文所使用的所有的技术和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同。本文中在本发明的说明书中所使用的术语只是为了描述具体的实施方式的目的，不是旨在于限制本发明。本文所使用的术语“和/或”包括一个或多个相关的所列项目的任意的和所有的组合。
请参图1和图2，本发明一种实施方式揭示了一种装饰片，可应用于电子产品的壳体，比如前盖或后盖。装饰片可贴覆于前盖或后盖上，也可以装饰片直接为前盖或后盖。这些电子产品包括但不限于手机、相机、平板电脑、终端显示器等。
本实施例中，装饰片包括透明基层1、固化胶层2、标记块3、镀膜层4和打底层5。
透明基层1所述相对设置的第一表面11和第二表面12。透明基层1为透明PET层，第一表面11为朝向电子产品内部的表面，第二表面12为朝向使用者观看方向的表面，从第二表面12可观察到第一表面11及设置于第一表面11上的部分结构。优选的，PET层包括彩色PET，或者PET层包括PET及贴附于PET上的彩色膜，可为装饰片提供色彩。这里所述说的透明是指可以从第二表面12观察到第一表面11上的结构、颜色等，或者说该透明是指透过率大于70％的情况。
在其他实施例中，透明基层1为玻璃层。固化胶层2和标记块3直接形成于玻璃层的第一表面11上。另可以根据电子产品的防反射、防指纹等需求，在透明基层1的第二表面12上设置抗反射膜、防指纹膜等功能膜层。此外，还可以对玻璃层进行强化处理。
固化胶层2，其包括相对设置的第一侧面21和第二侧面22。第一侧面21于第一表面11相接触，第二侧面22凹设有纹理结构23。第一侧面21一部分与标记块3接触，另一部分与第一表面11接触。固化胶层2在第一表面11的高度为10-22μm，也即固化胶层2最高点至第一表面的距离H的范围为10-22μm，优选的范围为15-20μm，比如H＝15μm。
固化胶层2的纹理结构23为凹陷结构且间隔设置，凹陷结构的高度d为3-10μm，宽度w为5-100μm，间隙的宽度x为3-100μm。比如d＝5μm，w＝20μm，x＝5μm。凹陷结构的截面形状为弓形，优选为劣弧弓。其他实施例中，纹理结构截面形状还可以为三角形、矩形、梯形或弓形。纹理结构23为直线型柱面镜规律间隙排列成一排。在复合光源下，可使装饰片颜色更加靓丽，更具质感。在单光源下，还可呈现光影条纹，并随着观察角度的移动，光影亮纹随之移动，从而具有较好的装饰效果。
标记块3嵌设于第一侧面21内并与第一表面11相贴合。标记块3在第一表面11的高度h为1-10μm，优选的范围为4-5μm。比如，h＝4μm。标记块3采用丝印工艺印刷而成，即用镜面银或油墨丝印在透明基层1的第一表面上。优选的，可选用彩色油墨丝印。印刷完成后，从第二表面侧观察，标记块3显示为logo、图案、文字、符号、数字等中的一种或多种。比如，装饰片应用于手机后盖时，标记块3即为logo，并且可以为金色logo等。
固化胶层2为UV固化胶压印固化而成。即在第一表面11上涂覆流质状UV固化胶，UV固化胶完全覆盖早已丝印好的标记块3。然后采用模具对流质状UV固化胶进行压印后固化，脱模后形成需要的纹理结构23。如此，标记块3将嵌设于第一侧面21内，纹理结构23形成于第二侧面22上。在具有高度h的标记块3上，涂覆具有高度H的UV固化胶，h的范围为2-6μm，H的范围为10-22μm。同时，满足2h≤H≤6h；优选的，H≈4h。在此范围内，可形成质量较好的标记，固化胶层2具有适当的厚度，既不会因为太薄而影响标记的显示(比如，UV固化胶过薄，会使标记周围出现黑晕)，又不会因为太厚而影响UV固化胶在透明基层1的第一表面11的粘附性能，从而使装饰片具有显眼的标记，且在标记外具有纹理结构，能产生光影效果，增加装饰片的质感，具有较好的装饰效果。装饰片应用于电子产品时，使电子产品具有较好的外观设计。
优选的，固化胶层2还可以采用彩色UV固化胶压印并固化而成。采用自带颜色的UV固化胶直接压印成型，由彩色UV固化胶为装饰片提供颜色，无需增加其他的颜色层，颜色可多选择性。或者，彩色UV固化胶与彩色PET配合显色，使得颜色更加丰富。
镀膜层4设置于第二侧面22并覆盖纹理结构23。镀膜层4可为蒸镀层，通过蒸镀工艺覆盖至UV纹理层3上。镀膜层4选自氧化铝层、氧化铌层、氧化钛层、氧化钒层、氧化钨层、氧化硅层、氮化硅层中的一种或多种。
打底层5，覆盖于镀膜层4远离固化胶层2的一侧。打底层5为黑色油墨层、彩色油墨层或彩色UV胶层。打底层5具有遮光的作用，一是保护电子产品内部结构，二是从第二表面12观察时，使第一表面11上的颜色层的显色效果更佳。打底层5还具有显色、调色作用，可与镀膜层4一起为装饰片提供色彩，或者为彩色PET或彩色UV固化胶的颜色起调色作用。
请参图3，装饰片还可包括玻璃层6。此时，透明基层1为PET层，且PET层的第二表面12包括粘结层13。粘结层13与玻璃层6相粘结。
请参图4，固化胶层2’的纹理结构23’为曲线型柱面镜。曲线型柱面镜可使预定方向的纹理结构23’呈现变化，从而使得在自然光下，装饰片即可呈现光影亮纹，且该光影亮纹随视线移动而移动，光影效果更具突出。其他实施例中，纹理结构还可以为CD纹、微透镜、蛾眼结构、小短线或拉丝纹等，可以为其中一种或者是两种以上的组合或叠加。
本发明的装饰片具有嵌设于第一侧面内并与第一表面相贴合的标记块，固化胶层的第二侧面凹和/或凸设有纹理结构，纹理结构上覆设有镀膜层和打底层，使得装饰片具有标记又有装饰的纹理结构，标记清晰明了，纹理结构能产生光学效果，使装饰片具有较好的质感。
为使本发明的上述目的、特征和优点能够更加明显易懂，上面结合附图对本发明的具体实施方式做详细的说明。在上面的描述中阐述了很多具体细节以便于充分理解本发明。但是本发明能够以很多不同于上面描述的其它方式来实施，本领域技术人员可以在不违背本发明内涵的情况下做类似改进，因此本发明不受上面公开的具体实施例的限制。并且，以上所述实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (11)
1.一种装饰片，其特征在于包括：
透明基层，其包括相对设置的第一表面和第二表面，所述透明基层为PET层，所述PET层包括位于所述第二表面的粘结层；
固化胶层，其包括相对设置的第一侧面和第二侧面，所述第一侧面与所述第一表面相接触，所述第二侧面设有凹和/或凸的纹理结构；
标记块，嵌设于所述第一侧面内并与所述第一表面相贴合；
镀膜层，设置于所述第二侧面并覆盖所述纹理结构；
打底层，覆盖于所述镀膜层远离所述固化胶层的一侧；
其中，所述标记块在所述第一表面的高度为1-10μm；所述固化胶层的高度为H，所述标记块的高度为h，则，2h≤H≤6h。
2.根据权利要求1所述的装饰片，其特征在于，所述标记块在所述第一表面的高度为4-5μm。
3.根据权利要求1所述的装饰片，其特征在于，所述标记块的材料为镜面银或油墨。
4.根据权利要求3所述的装饰片，其特征在于，所述标记块的材料为彩色油墨。
5.根据权利要求1所述的装饰片，其特征在于，所述标记块显示为logo、图案、文字、符号、数字中的一种或多种。
6.根据权利要求1所述的装饰片，其特征在于，所述固化胶层在所述第一表面的高度为10-22μm。
7.根据权利要求6所述的装饰片，其特征在于，所述固化胶层在所述第一表面的高度为15-20μm。
8.根据权利要求1所述的装饰片，其特征在于，所述纹理结构为直线型柱面镜、曲线型柱面镜、CD纹、微透镜、蛾眼结构、小短线或拉丝纹，所述纹理结构的截面形状为三角形、矩形、梯形或弓形。
9.根据权利要求1所述的装饰片，其特征在于，所述固化胶层采用彩色UV胶压印并固化而成。
10.根据权利要求1所述的装饰片，其特征在于，所述打底层为黑色油墨层、彩色油墨层或彩色UV胶层。
11.根据权利要求1所述的装饰片，其特征在于，所述透明基层为PET层，所述PET层包括彩色PET，或者所述PET层包括PET及贴附于所述PET上的彩色膜。