CN108973491A - 模具表面可抗喷砂的激光雕刻工艺 - Google Patents

模具表面可抗喷砂的激光雕刻工艺 Download PDF

Info

Publication number
CN108973491A
CN108973491A CN201810936171.3A CN201810936171A CN108973491A CN 108973491 A CN108973491 A CN 108973491A CN 201810936171 A CN201810936171 A CN 201810936171A CN 108973491 A CN108973491 A CN 108973491A
Authority
CN
China
Prior art keywords
identified areas
laser engraving
protective coating
mold
sandblasting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810936171.3A
Other languages
English (en)
Inventor
任志同
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MOLD TECH (DONGGUAN) CO LTD
Original Assignee
MOLD TECH (DONGGUAN) CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MOLD TECH (DONGGUAN) CO LTD filed Critical MOLD TECH (DONGGUAN) CO LTD
Priority to CN201810936171.3A priority Critical patent/CN108973491A/zh
Publication of CN108973491A publication Critical patent/CN108973491A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种模具表面可抗喷砂的激光雕刻工艺，包括有以下步骤：（1）在模具的镜面上形成标识区域，该标识区域内的线宽＜0.8mm；（2）在模具的镜面上喷保护涂层，使得保护涂层完全覆盖住标识区域；（3）进行激光雕刻将标识区域之外的保护涂层去除；（4）对模具进行常规的晒纹操作，以使得在镜面上形成纹路；（5）将覆盖标识区域上的保护涂层去除，以使得标识区域上呈现高光效果。通过在标识区域喷保护涂层，并配合激光雕刻，使得标识区域得到精准及可靠的保护，使得模具表面的纹理类型的选择不受限制，喷砂处理后，模具表面纹理更加的均匀，并且光泽度可任意调整，同时也使得模具日常保养更加的简单和方便。

Description

模具表面可抗喷砂的激光雕刻工艺
技术领域
本发明涉及模具表面加工领域技术，尤其是指一种模具表面可抗喷砂的激光雕刻工艺。
背景技术
模具在生产制造过程中，其表面上均设置各种各样的标识，如字符或LOGO等等。现有技术中，当字符或LOGO线宽小于0.8mm晒纹后要求其保持镜面时，由于常规晒纹无法保证到字符或LOGO镜面，所以晒纹后模具无法喷砂处理会导致以下问题：1、产品表面纹理不均匀；2、产品表面光泽度无法调整；3、模具表面极易生锈；4、模具日常保养困难。
发明内容
有鉴于此，本发明针对现有技术存在之缺失，其主要目的是提供一种模具表面可抗喷砂的激光雕刻工艺，其能有效解决现有之模具在晒纹后无法进行喷砂处理的问题。
为实现上述目的，本发明采用如下之技术方案：
一种模具表面可抗喷砂的激光雕刻工艺，包括有以下步骤：
（1）在模具的镜面上形成标识区域，该标识区域内的线宽＜0.8mm；
（2）在模具的镜面上喷保护涂层，使得保护涂层完全覆盖住标识区域；
（3）进行激光雕刻将标识区域之外的保护涂层去除；
（4）对模具进行常规的晒纹操作，以使得在镜面上形成纹路；
（5）将覆盖标识区域上的保护涂层去除，以使得标识区域上呈现高光效果。
作为一种优选方案，所述步骤（3）中采用五轴激光雕刻机进行激光雕刻。
作为一种优选方案，所述保护涂层由以下质量百分比原料制成：固化剂10%-15%、增粘剂8%-10%、黑粉3%-7%，其余为红胶。
作为一种优选方案，所述步骤（5）中采用脱脱模剂将覆盖标识区域上的保护涂层去除。
本发明与现有技术相比具有明显的优点和有益效果，具体而言，由上述技术方案可知：
通过在标识区域喷保护涂层，并配合激光雕刻，使得标识区域得到精准及可靠的保护，使得模具表面的纹理类型的选择不受限制，喷砂处理后，模具表面纹理更加的均匀，并且光泽度可任意调整，同时也使得模具日常保养更加的简单和方便。
附图说明
图1是本发明之较佳实施例加工过程的第一状态示意图；
图2是本发明之较佳实施例加工过程的第二状态示意图；
图3是本发明之较佳实施例加工过程的第三状态示意图；
图4是本发明之较佳实施例加工过程的第四状态示意图；
图5是本发明之较佳实施例加工过程的第五状态示意图。
附图标识说明：
10、模具 11、标识区域
12、纹路 20、保护涂层。
具体实施方式
本发明揭示了一种模具表面可抗喷砂的激光雕刻工艺，包括有以下步骤：
（1）如图1所示，在模具10的镜面上形成标识区域11，该标识区域11内的线宽＜0.8mm。
（2）如图2所示，在模具10的镜面上喷保护涂层20，使得保护涂层20完全覆盖住标识区域11。所述保护涂层20由以下质量百分比原料制成：固化剂10%-15%、增粘剂8%-10%、黑粉3%-7%，其余为红胶，使得保护涂层20的可靠性更强。
（3）进行激光雕刻将标识区域11之外的保护涂层20去除，如图3所示。在本实施例中，采用五轴激光雕刻机进行激光雕刻，使得保护位置精准度更高。
（4）对模具10进行常规的晒纹操作，以使得在镜面上形成纹路12，如图4所示。
（5）将覆盖标识区域11上的保护涂层20去除，以使得标识区域11上呈现高光效果，如图5所示。在本实施例中，采用脱脱模剂将覆盖标识区域11上的保护涂层20去除。
本发明的设计重点在于：通过在标识区域喷保护涂层，并配合激光雕刻，使得标识区域得到精准及可靠的保护，使得模具表面的纹理类型的选择不受限制，喷砂处理后，模具表面纹理更加的均匀，并且光泽度可任意调整，同时也使得模具日常保养更加的简单和方便。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术范围作任何限制，故凡是依据本发明的技术实质对以上实施例所作的任何细微修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (4)

1.一种模具表面可抗喷砂的激光雕刻工艺，其特征在于：包括有以下步骤：
（1）在模具的镜面上形成标识区域，该标识区域内的线宽＜0.8mm；
（2）在模具的镜面上喷保护涂层，使得保护涂层完全覆盖住标识区域；
（3）进行激光雕刻将标识区域之外的保护涂层去除；
（4）对模具进行常规的晒纹操作，以使得在镜面上形成纹路；
（5）将覆盖标识区域上的保护涂层去除，以使得标识区域上呈现高光效果。
2.根据权利要求1所述的模具表面可抗喷砂的激光雕刻工艺，其特征在于：所述步骤（3）中采用五轴激光雕刻机进行激光雕刻。
3.根据权利要求1所述的模具表面可抗喷砂的激光雕刻工艺，其特征在于：所述保护涂层由以下质量百分比原料制成：固化剂10%-15%、增粘剂8%-10%、黑粉3%-7%，其余为红胶。
4.根据权利要求1所述的模具表面可抗喷砂的激光雕刻工艺，其特征在于：所述步骤（5）中采用脱脱模剂将覆盖标识区域上的保护涂层去除。
CN201810936171.3A 2018-08-16 2018-08-16 模具表面可抗喷砂的激光雕刻工艺 Pending CN108973491A (zh)