CN108947455A - A kind of color slurry sealing and preparation method thereof - Google Patents
A kind of color slurry sealing and preparation method thereof Download PDFInfo
- Publication number
- CN108947455A CN108947455A CN201810944135.1A CN201810944135A CN108947455A CN 108947455 A CN108947455 A CN 108947455A CN 201810944135 A CN201810944135 A CN 201810944135A CN 108947455 A CN108947455 A CN 108947455A
- Authority
- CN
- China
- Prior art keywords
- parts
- solid powder
- resin emulsion
- color slurry
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of color slurry sealings, it is characterised in that: including 100 parts of solid powder, 16 ~ 24 parts and 5 ~ 15 parts of water of resin emulsion；The solid powder include weight ratio be 8% white superfine calcined kaolin, 64% white fused alumina antiskid aggregate, 13% metakaolin, 8% sodium metasilicate, 4.5% weather-proof pigment and 1.5% curing agent p-methyl benzenesulfonic acid；The resin emulsion includes silicone acrylic emulsion 95% and fluorocarbon resin lotion 5%.The present invention has the advantages that the technical program early strength with higher and bend-press ratio: 3d compression strength is more than 15MPa；3d flexural strength is more than 5MPa；Have good adhesion strength to bituminous pavement and cement concrete pavement under the conditions of air drying: the adhesion strength of 3d age bituminous pavement is more than 0.6MPa；The adhesion strength of 28d age bituminous pavement is more than 0.9MPa.
Description
Technical field
The present invention relates to a kind of color slurry sealing, especially a kind of color slurry sealing and preparation method thereof.
Background technique
Along with the quick fast development of China's economic society and transportation business, people are to require road to have basic
While sensible function, higher requirement is proposed to functions such as landscape, the identification warnings of road.Colored road surface is as road
The carrier of road landscape or communication function, increasingly finds broad application.Currently, colored road surface main Types include color asphalt road
Face, resin-bonded colored aggregate road surface.Many years application practice shows Colorful Asphalt Pavement due to being difficult to find that hard, wear-resistant, gluing
Attached performance is excellent and color and road surface color similar in building stones, in use process, asphalt membrane is easily worn and exposes building stones sheet
Color, color durability are poor.Resin-bonded colored aggregate road surface, as antiskid aggregate, can be used poly- using colored ceramic particle
The oiliness binder such as urethane resin, acrylic resin, epoxy resin, by playing the adhesive property of resin material for chromatic ceramics
Particle is adhered to road surface, and forms colored road surface, to meet useful life longevity requirement, such used resin gluing in road surface
The material prices such as agent, chromatic ceramics aggregate are expensive, and cost is high, such road surface due to resin material leakproofness, in rain
After water immerses lower part asphalt surface course, then damage is easily generated.For current common color road surface, the present invention
It is proposed that a kind of entire body is of the same colour, intensity is high, wearability is good, a kind of color slurry sealing mixing of good permeability, color tunable, construction is simple
Material and preparation method thereof, to meet the growth requirement of the growing beautiful traffic of the people, humane traffic.
Summary of the invention
It is an object of the invention to provide a kind of color slurry sealings and preparation method thereof, solve one in above-mentioned prior art problem
Or it is multiple.
In order to solve the above technical problems, the technical solution of the present invention is as follows: a kind of color slurry sealing, innovative point are: including
100 parts of solid powder, 16 ~ 24 parts and 5 ~ 15 parts of water of resin emulsion；Solid powder includes that weight ratio is superfine calcinated for 8% white
Kaolin, 64% white fused alumina antiskid aggregate, 13% metakaolin, 8% sodium metasilicate, 4.5% weather-proof pigment and 1.5%
Curing agent p-methyl benzenesulfonic acid；Resin emulsion includes silicone acrylic emulsion 95% and fluorocarbon resin lotion 5%.
In some embodiments, weather-proof pigment is that iron oxide red or iron are green.
In some embodiments, water is drinkable water.
A kind of preparation method of color slurry sealing, innovative point are: including the following steps:
1) firstly, successively by white superfine calcined kaolin, metakaolin, sodium metasilicate, weather-proof pigment, curing agent, white fused alumina
Antiskid aggregate stirs evenly；
2) secondly, silicone acrylic emulsion and fluorocarbon resin lotion are stirred evenly in a sealed meter environment；
3) it weighs resin emulsion in proportion again and is placed in container with water and stir evenly；
4) finally weigh in proportion in the resin emulsion after solid powder pours into dilution can be used after mixing evenly.
The present invention has the advantages that the technical program early strength with higher and bend-press ratio: 3d compression strength is more than
15MPa；3d flexural strength is more than 5MPa；Have under the conditions of air drying to bituminous pavement and cement concrete pavement good viscous
Attached power: the adhesion strength of 3d age bituminous pavement is more than 0.6MPa；The adhesion strength of 28d age bituminous pavement is more than 0.9MPa.
Specific embodiment
A kind of color slurry sealing, including 100 parts of solid powder, 16 ~ 24 parts and 5 ~ 15 parts of water of resin emulsion；Solid powder includes
Weight ratio be 8% white superfine calcined kaolin, 64% white fused alumina antiskid aggregate, 13% metakaolin, 8% sodium metasilicate,
4.5% weather-proof pigment and 1.5% curing agent p-methyl benzenesulfonic acid；Resin emulsion includes silicone acrylic emulsion 95% and fluorocarbon resin
Lotion 5%.
100 parts of solid powder: white superfine calcined kaolin 8%, 400 mesh ~ 800 mesh, white fused alumina antiskid aggregate 64%, granularity
Each half of 0 ~ 0.6mm, 0.6 ~ 1.18mm, metakaolin 13%, 800 mesh ~ 1200 mesh, sodium metasilicate 8% are 800 mesh ~ 1200 mesh, weather-proof
Type pigment 4.5%, can for iron oxide red, iron green etc., curing agent p-methyl benzenesulfonic acid 1.5%；16 ~ 24 parts of resin emulsion: silicone acrylic emulsion 95%,
PH value is 7 ~ 10, and glass transition temperature is 10 ~ 20 DEG C, 0 DEG C of minimum film formation temperature, fluorocarbon resin lotion 5%.
In some embodiments, weather-proof pigment is that iron oxide red or iron are green.
In some embodiments, water is drinkable water.
A kind of preparation method of color slurry sealing, includes the following steps:
1) firstly, successively by white superfine calcined kaolin, metakaolin, sodium metasilicate, weather-proof pigment, curing agent, white fused alumina
Antiskid aggregate stirs evenly；
2) secondly, silicone acrylic emulsion and fluorocarbon resin lotion are stirred evenly in a sealed meter environment；
3) it weighs resin emulsion in proportion again and is placed in container with water and stir evenly；
4) finally weigh in proportion in the resin emulsion after solid powder pours into dilution can be used after mixing evenly.
The present invention has the advantages that the technical program early strength with higher and bend-press ratio: 3d compression strength is more than
15MPa；3d flexural strength is more than 5MPa；Have under the conditions of air drying to bituminous pavement and cement concrete pavement good viscous
Attached power: the adhesion strength of 3d age bituminous pavement is more than 0.6MPa；The adhesion strength of 28d age bituminous pavement is more than 0.9MPa.This hair
Bright claimed range is defined by the appending claims and its equivalent thereof.The above is only preferred embodiment of the invention,
It should be pointed out that those skilled in the art, without departing from the concept of the premise of the invention, can also make
Several similar modification and improvement, within these also should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of color slurry sealing, it is characterised in that: including 100 parts of solid powder, 16 ~ 24 parts and 5 ~ 15 parts of water of resin emulsion；Institute
State solid powder include weight ratio be 8% white superfine calcined kaolin, 64% white fused alumina antiskid aggregate, 13% higher ridge
Soil, 8% sodium metasilicate, 4.5% weather-proof pigment and 1.5% curing agent p-methyl benzenesulfonic acid；The resin emulsion includes silicon third
Lotion 95% and fluorocarbon resin lotion 5%.
2. a kind of color slurry sealing according to claim 1, it is characterised in that: the weather-proof pigment is that iron oxide red or iron are green.
3. a kind of color slurry sealing according to claim 1, it is characterised in that: the water is drinkable water.
4. a kind of preparation method of color slurry sealing, characterized by the following steps:
Firstly, successively white superfine calcined kaolin, metakaolin, sodium metasilicate, weather-proof pigment, curing agent, white fused alumina are prevented
Sliding aggregate stirs evenly；
Secondly, silicone acrylic emulsion and fluorocarbon resin lotion are stirred evenly in a sealed meter environment；
It weighs resin emulsion in proportion again and is placed in container with water and stirred evenly；
Finally weigh in proportion in the resin emulsion after solid powder pours into dilution can be used after mixing evenly.