CN104531010A - Adhesive paste, and preparation method and application thereof - Google Patents
Adhesive paste, and preparation method and application thereof Download PDFInfo
- Publication number
- CN104531010A CN104531010A CN201510049766.3A CN201510049766A CN104531010A CN 104531010 A CN104531010 A CN 104531010A CN 201510049766 A CN201510049766 A CN 201510049766A CN 104531010 A CN104531010 A CN 104531010A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- sterilant
- cream
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an adhesive paste in building materials, particularly an adhesive paste, and a preparation method and application thereof. The adhesive paste comprises the following components in parts by weight: 75-370 parts of pure acrylic emulsion, 3-20 parts of hydroxypropyl methylcellulose, 0-200 parts of water, 400-650 parts of filler, 3-25 parts of redispersible latex powder and 0.2-3 parts of bactericide. The adhesive paste can be firmly attached to the cement wall and ground, is suitable for attaching wall and ground polished bricks, ceramic bricks and natural stones to cement surfaces, and can greatly lower the construction cost.
Description
Technical field
The present invention relates to the stickup cream of material of construction, particularly one pastes cream, preparation method and application.
Background technology
Current construction industry is pasted polished tile, is entirely thrown glaze, microlite, marble, Antique Imitation Tiles, rostone still with neat slurry or clay water distribution stickup on cement wall ground, this construction technology, because shrinking percentage when cement or clay solidify is comparatively large and the dried reason such as to expand with heat and contract with cold, wall ground Throwing light brick, is entirely thrown the easy hollowing of the stone material such as glaze, microlite, comes off, is tilted.
Find through retrieval, publication number is that the application for a patent for invention of CN102702908A discloses the anti-brick coating of a kind of environment-friendly type building exterior wall and preparation method, for skin surface decoration, overcome that existing ceramic tile system easily comes off, ceramic tile is from great, that cost is high deficiency.The cellulose ether aqueous solution, pure-acrylic emulsion, ethylene glycol, thickening material, film coalescence aid, defoamer, sanitas, pH value regulator, the multifunctional assistant that are 2% by the water of specified weight number ratio, titanium dioxide, color sand, dispersion agent, weight concentration form.
Publication number is that the application for a patent for invention of CN1211603 discloses a kind of binder for ceramics and stone and preparation method thereof, which overcome the defect that existing ceramic stone sand-cement slurry is pasted not strongly, be made up of polyvinyl alcohol, vinylformic acid, formaldehyde, iron trichloride, urea, water glass, sepiolite, calcium hydroxide, quartz sand, cement.
Publication number is that the application for a patent for invention of CN1064693 discloses a kind of wall brick and pavement adhesive specially, and each component weight ratio is ethene-vinyl acetate copolymer emulsion 100 parts, polyvinyl alcohol water solution (10% content) 5.0 ~ 30 parts, ethanol (or ethylene glycol) 5 ~ 30 parts, 20 ~ 120 parts, water, limestone powder 400 ~ 650 parts, Tritolyl Phosphate 0.2 ~ 3.0 part.But compression shear adhesive strength is all lower after its compression shear adhesive strength and thermal ageing.
Indoor and outdoor wall ground decoration requires more and more higher in recent years, and the artificial stone-like material's specific absorption produced is very low, therefore pastes a great problem firmly becoming industry for a long time with cement wall ground.
Summary of the invention
The object of this invention is to provide a kind of stickup cream, preparation method and application.
For achieving the above object, the technical scheme that concrete employing is following:
A kind of stickup cream, by weight, comprises pure-acrylic emulsion 75-370 part, Vltra tears 3-20 part, water 0-200 part, filler 400-650 part, redispersible latex powder 3-25 part, sterilant 0.2-3 part.
In order to make the cohesive force of tackiness agent stronger, described stickup cream by weight, comprises pure-acrylic emulsion 200-370 part, Vltra tears 5-10 part, water 1-50 part, filler 400-550 part, redispersible latex powder 5-15 part, sterilant 0.2-3 part.
Consider cohesive force and the cost of tackiness agent, described stickup cream by weight, comprises pure-acrylic emulsion 200 parts, Vltra tears 5 parts, 150 parts, water, filler 500 parts, redispersible latex powder 10 parts, 2 parts, sterilant.
In order to make above-mentioned tackiness agent better use at northern area, the special stickup cream of polished tile of the present invention, ceramic tile and lithotome also comprises ethanol or the ethylene glycol of 1-30 part.
Preferably, described ethanol or ethylene glycol are 5 parts.
In the inventive solutions, described filler is selected from one or more in water-ground limestone, light calcium carbonate, kaolin or grey calcium; Institute's sterilant is selected from one or more in Tritolyl Phosphate, formaldehyde or isothiazolinone.
In order to reach better bonding effect, preferably, described filler is selected from water-ground limestone; Institute's sterilant is selected from Tritolyl Phosphate.
The viscosity of Vltra tears of the present invention is 50000 ~ 200000mPa.s.
Dispersibility latex powder of the present invention can select commercially available all products, and the present invention does not make particular determination, the product that the companies such as such as Dalian, Taiwan chemistry, Germany watt gram WACKER VINNAPAS, Ke Laien chemical industry, open country, Guangzhou, Henan Tian Sheng group produce.
Pure-acrylic emulsion of the present invention can select commercially available all products.
Stickup cream provided by the invention and cement wall ground have the advantage of firm pasting.
Present invention also offers the preparation method of described stickup cream, specifically comprise the following steps:
(1) pure-acrylic emulsion and sterilant mix, obtain mixture 1, if needed, need in mixture 1 to add water, ethanol or ethylene glycol (namely when needing in raw material to add water, ethanol or ethylene glycol, adding water, ethanol or ethylene glycol in mixture 1);
(2) add to after stirring in mixture 1 after filler, hydroxypropylcellulose and dispersibility latex powder being stirred again and get final product.
Stickup cream of the present invention is applicable in wall, ground polished tile, ceramic tile and lithotome and cement surface are pasted.
Stickup cream of the present invention, bond strength is very high, toughness is very large, cause production cost also higher, so consider first to scrape layer of adhesive at the back face of stone that will paste, and then scrape one deck neat slurry or clay is pasted on wall ground again, concrete, stickup cream of the present invention is first scraped in polished tile, ceramic tile or lithotome back side 1-5mm, scrape neat slurry or clay again, and then be pasted on wall, ground.
It is very firmly that stickup cream directly sticks at stone material, it is very firmly that stickup cream bonds with neat slurry or clay when wet, it is again very firmly that neat slurry or clay and cement wall ground are pasted, and traditional construction technology will be cut at back face of stone, hook is fixed on the wall, although such construction technology does not drop, but also can hollowing, the present invention can reduce construction cost greatly compared with traditional construction technology.
Embodiment
Following examples for illustration of the present invention, but are not used for limiting the scope of the invention.If no special instructions, the material selected in embodiment is commercially available prod.
Embodiment 1
The starting material pasting cream in the present embodiment are composed of the following components: pure-acrylic emulsion 200g, Vltra tears 5g, water 150g, water-ground limestone 500g, redispersible latex powder 10g, Tritolyl Phosphate 2g.
Embodiment 2
The difference of the present embodiment and embodiment 1 is only also to comprise 5g ethanol or ethylene glycol.
Embodiment 3
The starting material pasting cream in the present embodiment are composed of the following components: pure-acrylic emulsion 370g, Vltra tears 10g, water 50g, water-ground limestone 400g, redispersible latex powder 20g, Tritolyl Phosphate 2g.
Embodiment 4
The starting material of the stickup cream in the present embodiment are composed of the following components: pure-acrylic emulsion 75g, Vltra tears 3g, light calcium carbonate 400g, redispersible latex powder 3g, isothiazolinone 0.2g.
Embodiment 5
The starting material pasting cream in the present embodiment are composed of the following components: pure-acrylic emulsion 370g, Vltra tears 20g, water 200g, kaolin 650g, redispersible latex powder 25g, formaldehyde 3g.
Embodiment 6
The present embodiment is the preparation method pasting cream in embodiment 1-5, specifically comprises the following steps:
(1) embodiment 1,3,5 is for mix pure-acrylic emulsion, water and sterilant, obtains mixture 1; Embodiment 2, for pure-acrylic emulsion, water, sterilant and ethanol (ethylene glycol) to be mixed, obtains mixture 1; Embodiment 4, for pure-acrylic emulsion and sterilant to be mixed, obtains mixture 1;
(2) add to after stirring in mixture 1 after filler, hydroxypropylcellulose and dispersibility latex powder being stirred again and get final product.
Comparative example 1
Take publication number as the embodiment 2 of the application for a patent for invention of 103214212A be comparative example 1.
Comparative example 2
Take publication number as the embodiment 4 of the application for a patent for invention of 103214212A be comparative example 2.
Comparative example 3
Take publication number as the embodiment of the application for a patent for invention of 1064693 be comparative example 3.
Experimental example:
Stickup cream the embodiment of the present application 1-embodiment 5 obtained is tested according to the standard of JC/T547-2005 " ceramic wall and floor bricks tackiness agent ", and test result is as follows:
In addition, stickup cream of the present invention is applied in actual production, and concrete application method is first scraped in polished tile, ceramic tile and lithotome back side 1-5mm for pasting cream, then scrapes neat slurry or clay, and then is pasted on wall, ground.Through practice test, stickup cream of the present invention and cement wall ground firm pasting, and there will not be hollowing, come off, tilt phenomenon, and greatly can reduce construction cost.
Although above the present invention is described in detail with a general description of the specific embodiments, on basis of the present invention, can make some modifications or improvements it, this will be apparent to those skilled in the art.Therefore, these modifications or improvements without departing from theon the basis of the spirit of the present invention, all belong to the scope of protection of present invention.
Claims (10)
1. paste a cream, it is characterized in that, by weight, comprise pure-acrylic emulsion 75-370 part, Vltra tears 3-20 part, water 0-200 part, filler 400-650 part, redispersible latex powder 3-25 part, sterilant 0.2-3 part.
2. stickup cream according to claim 1, is characterized in that, by weight, comprises pure-acrylic emulsion 200-370 part, Vltra tears 5-10 part, water 1-50 part, filler 400-550 part, redispersible latex powder 5-15 part, sterilant 0.2-3 part.
3. stickup cream according to claim 1, is characterized in that, by weight, comprises pure-acrylic emulsion 200 parts, Vltra tears 5 parts, 150 parts, water, filler 500 parts, redispersible latex powder 10 parts, 2 parts, sterilant.
4. the stickup cream according to any one of claim 1-3, is characterized in that, also comprises ethanol or the ethylene glycol of 1-30 part.
5. stickup cream according to claim 4, is characterized in that, described ethanol or ethylene glycol are 5 parts.
6. the stickup cream according to any one of claim 1-3, is characterized in that, described filler is selected from one or more in water-ground limestone, light calcium carbonate, kaolin or grey calcium; Institute's sterilant is selected from one or more in Tritolyl Phosphate, formaldehyde or isothiazolinone.
7. stickup cream according to claim 6, is characterized in that, described filler is selected from water-ground limestone, and institute's sterilant is selected from Tritolyl Phosphate.
8. paste the preparation method of cream described in any one of claim 1-7, it is characterized in that, comprise the following steps:
(1) pure-acrylic emulsion and sterilant mix, and obtain mixture 1, if needed, add water, ethanol or ethylene glycol in mixture 1;
(2) add to after stirring in mixture 1 after filler, hydroxypropylcellulose and dispersibility latex powder being stirred again and get final product.
9. described in any one of claim 1-7, paste the application of cream in wall, ground polished tile, ceramic tile and lithotome and cement surface are pasted.
10. paste the application of cream according to claim 9, it is characterized in that, described stickup cream is first scraped in polished tile, ceramic tile or lithotome back side 1-5mm, then scrapes neat slurry or clay, is then pasted on wall, ground.