CN108947301A - 一种复配型抗泥牺牲剂及其制备方法 - Google Patents

一种复配型抗泥牺牲剂及其制备方法 Download PDF

Info

Publication number
CN108947301A
CN108947301A CN201811137164.3A CN201811137164A CN108947301A CN 108947301 A CN108947301 A CN 108947301A CN 201811137164 A CN201811137164 A CN 201811137164A CN 108947301 A CN108947301 A CN 108947301A
Authority
CN
China
Prior art keywords
mud
agent
sodium
compositional type
sacrifice
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811137164.3A
Other languages
English (en)
Inventor
朱建民
董振鹏
刘兆滨
王树博
潘阳
李成剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Oak Chemical Co Ltd
Original Assignee
Wuhan Oak Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Oak Chemical Co Ltd filed Critical Wuhan Oak Chemical Co Ltd
Priority to CN201811137164.3A priority Critical patent/CN108947301A/zh
Publication of CN108947301A publication Critical patent/CN108947301A/zh
Pending legal-status Critical Current

Abstract

本发明提出了一种复配型抗泥牺牲剂及其制备方法，采用主抗泥剂、助抗泥剂复配的方法，主抗泥剂选用阳离子表面活性剂，助抗泥剂选用低成本并具有一定抗泥作用的助剂，该复配型抗泥牺牲剂可以提高聚羧酸减水剂的抗泥性能，改善聚羧酸减水剂的适用性能。

Description

一种复配型抗泥牺牲剂及其制备方法
技术领域
本发明涉及混凝土外加剂领域，尤其涉及一种复配型抗泥牺牲剂及其制备方法。
背景技术
目前，聚羧酸高性能减水剂具有生产工艺成熟、水泥适应性好、坍落度损失较小等特点，但是聚羧酸高性能减水剂直接应用于混凝土时，由于混凝土砂石料含泥较多，经常出现适应性不好、混凝土坍落度损失大、混凝土和易性差等问题，难以满足实际工程的施工要求，且随着用于拌制混凝土的高质量的砂石越来越少，一些地方不得采用劣等的砂石。这些劣等砂石往往含有较多的粘土矿物，严重影响聚羧酸减水剂的功能。
发明内容
有鉴于此，本发明提出了一种具有良好抗泥性能的复配型抗泥牺牲剂及其制备方法。
本发明的技术方案是这样实现的：本发明提供了一种复配型抗泥牺牲剂，所述复配型抗泥牺牲剂包括主抗泥剂和助抗泥剂，主抗泥剂：助抗泥剂的质量比为3∶(4-6)。
在以上技术方案的基础上，优选的，所述主抗泥剂为十六烷基三甲基溴化铵、十二烷基三甲基氯化铵、四乙基溴化铵、四甲基溴化铵、十二烷基二甲基胺乙内酯、聚丙烯酸钠、聚二甲基二烯丙基氯化铵和二甲基二烯丙基氯化铵-丙烯酰胺中的一种。
在以上技术方案的基础上，优选的，所述聚丙烯酸钠的分子量为2000～5000。
在以上技术方案的基础上，优选的，所述助抗泥剂为醋酸铵、PEG-700、PEG-2000、三聚磷酸钠、尿素、木质素磺酸钠、对氨基苯磺酸钠、磷酸二氢钾、焦亚硫酸钠、葡萄糖酸钠、亚硫酸氢钠、硫酸亚铁、木质素磺酸钠、木质素磺酸钙和聚合硫酸铁中的一种或两种的混合物。
更进一步优选的，当助抗泥剂包括助抗泥剂1和助抗泥剂2时，所述主抗泥剂∶助抗泥剂1∶助抗泥剂2的质量比为6∶(6-7)∶(1-2)。
在以上技术方案的基础上，优选的，一种复配型抗泥牺牲剂的制备方法，其特征在于，包括如下步骤：
按质量比称量主抗泥剂和助抗泥剂，混合，在20～30℃下搅拌5～10分钟得到复配型抗泥牺牲剂。
本发明的一种复配型抗泥牺牲剂及其制备方法相对于现有技术具有以下有益效果：
通过本发明的制备方法制备的复配型抗泥牺牲剂能够解决聚羧酸减水剂应用在含泥量较多的混凝土砂石料中存在的问题，具有适应性好、混凝土坍落度损失小、和易性好的特点。
具体实施方式
下面将结合本发明实施方式，对本发明实施方式中的技术方案进行清楚、完整地描述，显然，所描述的实施方式仅仅是本发明一部分实施方式，而不是全部的实施方式。基于本发明中的实施方式，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施方式，都属于本发明保护的范围。
聚羧酸减水剂制备方法
实施例1
将3kg十六烷基三甲基溴化铵和4kg醋酸铵混合，加热至20℃，搅拌5分钟，搅拌得到抗泥牺牲剂。
实施例2
将3kg十二烷基三甲基氯化铵和5kgPEG-700混合，加热至25℃，搅拌6分钟，搅拌得到抗泥牺牲剂。
实施例3
将3kg四乙基溴化铵和6kg PEG-2000混合，加热至30℃，搅拌7分钟，搅拌得到抗泥牺牲剂。
实施例4
将6kg四甲基溴化铵与6kg三聚磷酸钠和1kg尿素混合，加热至20℃，搅拌8分钟，搅拌得到抗泥牺牲剂。
实施例5
将6kg十二烷基二甲基胺乙内酯与7kg木质素磺酸钠和2kg对氨基苯磺酸钠混合，加热至25℃，搅拌9分钟，搅拌得到抗泥牺牲剂。
实施例6
将6kg聚丙烯酸钠与6kg磷酸二氢钾和2kg焦亚硫酸钠混合，加热至30℃，搅拌10分钟，搅拌得到抗泥牺牲剂。
水泥净浆流动性测试实验
依照GB/T 8077-2012《混凝土外加剂匀质性试验方法》进行，297g水泥(华新P.O42.5)、3g钠基膨润土、聚羧酸减水剂1g、抗泥牺牲剂0.15g和水87g，立即搅拌混合，慢速搅拌120s，停15s，快速搅拌120s，抗泥牺牲剂为实施例1-6所制备。
混凝土性能测试实验
依照GB 8076-2008《混凝土外加剂》和GB/T 50080-2002《普通混凝土拌合物性能试验方法标准》进行，混凝土适配如下：380kg/m3水泥(华新P.O42.5)、177g/m3抗泥牺牲剂、750kg/m3沙、695kg/m3大石、375kg/m3小石、185Kg/m3水，聚羧酸减水剂掺量为0.3％(固含量40％)(相对于水泥掺量)
水泥净浆流动性测试结果：
所用抗泥牺牲剂 初始流动性/(mm) 30min后流动性/(mm)
聚羧酸减水剂 205 163
实施例1 228 213
实施例2 231 225
实施例3 223 209
实施例4 220 203
实施例5 225 222
实施例6 219 205
混凝土性能测试结果：
以上所述仅为本发明的较佳实施方式而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种复配型抗泥牺牲剂，其特征在于，包括主抗泥剂和助抗泥剂，所述主抗泥剂∶助抗泥剂的质量比为3∶(4-6)。
2.如权利要求1所述的一种复配型抗泥牺牲剂，其特征在于，所述主抗泥剂为十六烷基三甲基溴化铵、十二烷基三甲基氯化铵、四乙基溴化铵、四甲基溴化铵、十二烷基二甲基胺乙内酯、聚丙烯酸钠、聚二甲基二烯丙基氯化铵和二甲基二烯丙基氯化铵-丙烯酰胺共聚物中的一种。
3.如权利要求2所述的一种复配型抗泥牺牲剂，其特征在于，所述聚丙烯酸钠的重均分子量为2000～5000。
4.如权利要求1所述的一种复配型抗泥牺牲剂，其特征在于，所述助抗泥剂为醋酸铵、PEG-700、PEG-2000、三聚磷酸钠、尿素、木质素磺酸钠、对氨基苯磺酸钠、磷酸二氢钾、焦亚硫酸钠、葡萄糖酸钠、亚硫酸氢钠、硫酸亚铁、木质素磺酸钠、木质素磺酸钙和聚合硫酸铁中的一种或两种的混合物。
5.如权利要求4所述的一种复配型抗泥牺牲剂，其特征在于，当助抗泥剂包括助抗泥剂1和助抗泥剂2时，所述主抗泥剂∶助抗泥剂1∶助抗泥剂2的质量比为6∶(6-7)∶(1-2)。
6.如权利要求1所述的一种复配型抗泥牺牲剂的制备方法，其特征在于，包括如下步骤：
按质量比称量主抗泥剂和助抗泥剂，混合，在20～30℃下搅拌5～10分钟得到复配型抗泥牺牲剂。
CN201811137164.3A 2018-09-27 2018-09-27 一种复配型抗泥牺牲剂及其制备方法 Pending CN108947301A (zh)