CN108867073A - A kind of long vehicle pre-treating method of fiber - Google Patents
A kind of long vehicle pre-treating method of fiber Download PDFInfo
- Publication number
- CN108867073A CN108867073A CN201711176775.4A CN201711176775A CN108867073A CN 108867073 A CN108867073 A CN 108867073A CN 201711176775 A CN201711176775 A CN 201711176775A CN 108867073 A CN108867073 A CN 108867073A
- Authority
- CN
- China
- Prior art keywords
- raw material
- chemical raw
- processing
- cbb
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of long vehicle pre-treating method of fiber, including fiber is subjected to processing of singing；Carry out the processing of cold dome alkali oxygen：The first chemical raw material is added in bottom water, while uniformly adding the first chemical raw material during along clot；Short steaming oxygen bleaching is carried out using desizing machine to handle：The second chemical raw material is added in bottom water, while the uniformly additional third chemical raw material more suitable or bigger than each constituent concentration in the second chemical raw material during along clot；Tentering and preshrunk processing are carried out, to realize continuous production, shortens production cycle completion date, guarantees the friendship phase, color difference before and after product is avoided while improving elongation.
Description
Technical field
The present invention relates to textile process manufacturing fields, and in particular to a kind of long vehicle pre-treating method of fiber.
Background technique
Tencel is a kind of cellulose fibre, also referred to as Tencel fiber, is wood pulp, water and solvent oxygen based on coniferous tree
Change amine mixing, is heated to being completely dissolved, any derivative and chemical action will not be generated in course of dissolution, using solvent spinning
Technology does by force slightly below terylene, but is apparently higher than general viscose rayon, wet to improve significantly than viscose glue by force, has very
High rigidity, good washing dimensional stability (washing shrinkage is only 2-3%), hygroscopicity with higher, fiber cross section are
Round or ellipse, gloss is graceful, and soft, drapability is good, and elegant property is good.In general：Tencel has：1. there is the soft of cotton
It is soft；2. there is the high-tenacity of terylene；3. the warmth retention property of hairiness, but it is easy to be hardened under conditions of damp and hot.
Tencel fiber can decompose completely in soil, no pollution to the environment；In addition, amine oxide used in production is molten
Agent is completely harmless to human body, can almost recycle, can Reusability, cellulosic molecule contained by material pulp does not rise in production
Chemical change, no coupling product, no waste are discharged outside factory, are environmental protection or green fiber.The fabric has good moisture absorption
Property, comfort, drapability and stiffness and dyeability is good.Tencel (Tencel) is a kind of solvent type cellulose fibre, is Britain
Acordis company was developed by 10 years, until last century the nineties just complete business application, it is most typical environmentally protective fibre
Dimension.In May, 2004 is produced by unified after Lenzin company amalgamation.Its environmentally friendly feature：Raw material come from timber, can continuous Natural re generation,
Wood pulp is made in timber, using (NMMO) spinning technique, wood pulp is dissolved in amine-oxides solvent direct fabrics, is made completely in physics
With lower completion, amine-oxides solvent is recycled, and the rate of recovery can give birth to after nontoxic, pollution-free, tencel product use up to 99% or more
Change degradation, not can cause environmental pollution.Therefore it is referred to as " 21st century green fiber ", and obtain international environmentally protective card
Book.In a wet state, it is the cellulose fibre that the first wet strength outclass cotton.A hundred percent natural material, in addition
The manufacturing process of environmental protection allows life style, for this, to cater to the demand of modern consumer completely with conservation of nature environment.However at present
Complicated for the process flow of tencel, the production cycle is long, and can generate color difference.
Summary of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of long vehicle pre-treating methods of fiber, can
It realizes continuous production, shortens production cycle completion date, guarantee the friendship phase, color before and after product is avoided while improving elongation
Difference.
The present invention provides a kind of long vehicle pre-treating methods of fiber, include the following steps：
(1) fiber is subjected to processing of singing；
(2) processing of cold dome alkali oxygen is carried out：The first chemical raw material is added in bottom water, while during along clot uniformly
Additional first chemical raw material；
(3) short steaming oxygen bleaching is carried out using desizing machine to handle：The second chemical raw material is added in bottom water, while along clot
The third chemical raw material more suitable or bigger than each constituent concentration in the second chemical raw material is uniformly added in the process；
(4) tentering and preshrunk processing are carried out.
Preferably, first chemical raw material include chelated dispersants H, NAOH, scouring agent 6#, stabilizer P-CBB and
H2O2, or including oxalic acid, or include chelating agent H, CG and enzyme 2000L.
Preferably, chelated dispersants H, NAOH in the first chemical raw material, scouring agent 6#, stabilizer P-CBB and H2O2It is dense
Degree is respectively that the concentration of oxalic acid in 1.5g/L, 20-22g/L, 6g/L, 8g/L and 5-6g/L or the first chemical raw material is 8g/L,
Or it is respectively 1.5kg, 500g, 3kg in every 550L that first chelating agent H, CG and enzyme 2000L in chemical raw material, which is,.
Preferably, second and third described chemical raw material all includes chelated dispersants CM-5, DX-1099A, DX-1099B, stabilization
Agent P-CBB and H2O2。
Preferably, chelated dispersants CM-5, DX-1099A in second chemical raw material, DX-1099B, stabilizer P-
CBB and H2O2Concentration be respectively 1g/L, 12g/L, 6g/L, 6g/L, 2 and 5-3g/L.
Preferably, chelated dispersants CM-5, DX-1099A in the third chemical raw material, DX-1099B, stabilizer P-
CBB and H2O2Concentration be respectively 1g/L, 48g/L, 24g/L, 24g/L, 2 and 5-3g/L.
The process flow of the specialty fibers such as existing tencel, Modal is：Singe → roll up pre-treatment → drying → tentering →
Preshrunk, wherein package is suitble to processing small lot production, package in 10 hours handles 1800 meters or so, and (such as 8 produce simultaneously
14400 meters), and 24000 meters can be handled within long vehicle desizing machine 10 hours, high-efficient 66.7%.
Process flow is improved to by the present invention by process modification：It singes → short steaming the oxygen bleaching of cold dome enzymatic treatment → desizing machine
→ tentering → preshrunk shortens production cycle completion date to realize continuous production, guarantees the friendship phase, improves the same of elongation
When avoid color difference before and after product.
Specific embodiment
The following detailed description of specific implementation of the invention, it is necessary to it is indicated herein to be, implement to be only intended to this hair below
Bright further explanation, should not be understood as limiting the scope of the invention, and field person skilled in the art is according to above-mentioned
Some nonessential modifications and adaptations that summary of the invention makes the present invention, still fall within protection scope of the present invention.
Following problems can be faced by being handled using long vehicle：
(1) long vehicle processing reduced amplitude degree is big, the narrow difficult preshrunk of breadth；
(2) alkali oxygen concentration is high easily goes out broken hole, and cold dome selects alkali-free technique, washes (to remove cotton seed hulls)；
(3) equipment state difference quality measurement is unsecured, and special line is needed to do；
(4) steam box axis is few, and a distance tension little Yi goes out wrinkle；
(5) strength reduces, and is easy to stretch disconnected cloth；
(6) specialty fibers can first make 300-500 meters of samples；
(7) more serious problem is that cloth padding machine fold occurs in desizing machine, is difficult to remove once generating.
On this basis, the present invention improves parameter and technique, specifically overcomes tradition in the following manner
The shortcomings that technique, and at the same time overcoming using the above problem that may be faced when long vehicle, specifically the invention discloses one kind
The long vehicle pre-treating method of fiber, includes the following steps：
Embodiment one：
(1) it singes → cold dome alkali oxygen (enzyme) processing → (desizing machine) short steaming oxygen bleaching (2.5-3g/L) → post-processing
Wherein cold dome alkali oxygen, which is handled, is：
Speed：70±2m/min；
Chemical raw material：25 ± 5 DEG C of temperature, while uniformly adding chemical raw material；
Along clot direction：It rotates clockwise 10 ± 1 hours and banks up, 6-8 revs/min；
First technology preparation is as shown in following table 1-1：
| Chemical raw material | Bottom water | It is additional |
| 1. chelated dispersants H | 1.5g/l | 1.5g/l |
| ②NAOH | 20-22g/l | 20-22g/l |
| 3. scouring agent 6# | 6g/l | 6g/l |
| 4. stabilizer P-CBB | 8g/l | 8g/l |
| ⑤H2O2 | 5-6g/l | 5-6g/l |
| Total amount | /550L | /550L |
Table 1-1 cold dome alkali oxygen technology preparation
Wherein short steaming oxygen bleaching, which is handled, is：
Desizing machine speed：40±2m/min；
Temperature:101±1℃；
Configuration：Crawler belt is not worn, cloth beam is only perforated.
Rear car list is opened：The washing of 9 65 ± 3 DEG C of lattice；10 80 ± 3 DEG C of lattice hot water wash, 11 93 ± 3 DEG C of lattice hot water wash, flat wash trough add
Water guarantees liquid level room temperature, the washing of 12 80-85 DEG C of lattice, the washing of 13 85-90 DEG C of lattice, the washing of 14 90-95 DEG C of lattice, 15 85-90 DEG C of lattice water
It washes, 16 80 ± 85 DEG C of lattice hot water wash, No. 16 slots add water to form circulation spinner flowmeter flow control in 2.0 ± 0.3m3/h.
Height is 35 ± 5 DEG C to liquid material bath temperature degree, and chemical raw material temperature is 30 ± 5 DEG C, and 15# high is not added to the self weight of liquid mangle roller
Pressure, 11#-13# roll north and south 0.2 ± 0.02MPa of pressure, 14# high-capacity squeezer roll north and south 0.5 ± 0.02Mpa of pressure, 16#-
19# roll north and south 0.2 ± 0.02MPa of pressure, 20# high-capacity squeezer north and south 0.5 ± 0.02Mpa of pressure, each cropping wet cloth clot pressure
Power：0.5±0.1MPa.
| Technology preparation | Bottom water | It is additional |
| 1. chelating dispersing agent CM-5 | 1g/L | 1g/L |
| ②DX-1099A | 12g/L | 48g/L |
| ③DX-1099B | 6g/L | 24g/L |
| 4. stabilizer P-CBB | 6g/L | 24g/L |
| ⑤H2O2 | 2.5-3g/L | 2.5-3g/L |
| Total amount | /1000L | /1000L |
The short steaming oxygen bleaching treatment process prescription of table 1-2
Embodiment two：
(2) it singes → cold dome alkali oxygen (enzyme) processing → (desizing machine) short steaming oxygen bleaching (2.5-3g/L) → post-processing
Wherein cold dome alkali oxygen, which is handled, is：
Speed：70±2m/min；
Chemical raw material：45 ± 5 DEG C of temperature, while uniformly adding chemical raw material；
Along clot direction：It rotates clockwise 10 ± 1 hours and banks up, 6-8 revs/min；
Second technology preparation is as shown in following table 2-1：
Table 2-1 cold dome alkali oxygen technology preparation
Wherein short steaming oxygen bleaching, which is handled, is：
Desizing machine speed：40±2m/min；
Temperature:101±1℃；
Configuration：Crawler belt is not worn, cloth beam is only perforated.
Rear car list is opened：The washing of 9 65 ± 3 DEG C of lattice；10 80 ± 3 DEG C of lattice hot water wash, 11 93 ± 3 DEG C of lattice hot water wash, flat wash trough add
Water guarantees liquid level room temperature, the washing of 12 80-85 DEG C of lattice, the washing of 13 85-90 DEG C of lattice, the washing of 14 90-95 DEG C of lattice, 15 85-90 DEG C of lattice water
It washes, 16 80 ± 85 DEG C of lattice hot water wash, No. 16 slots add water to form circulation spinner flowmeter flow control in 2.0 ± 0.3m3/h.
Height gives 35 ± 5 DEG C of liquid material bath temperature degree, 30 ± 5 DEG C of materials.15# high is not pressurized to the self weight of liquid mangle roller, and 11#-13# rolls
Roller north and south 0.2 ± 0.02MPa of pressure, 14# high-capacity squeezer roll north and south 0.5 ± 0.02Mpa of pressure, 16#-19# roll north and south pressure
Power 0.2 ± 0.02MPa, 20# high-capacity squeezer north and south 0.5 ± 0.02Mpa of pressure, each cropping wet cloth clot pressure：0.5±
0.1MPa。
| Technology preparation | Bottom water | It is additional |
| 1. chelating dispersing agent CM-5 | 1g/L | 1g/L |
| ②DX-1099A | 12g/L | 48g/L |
| ③DX-1099B | 6g/L | 24g/L |
| 4. stabilizer P-CBB | 6g/L | 24g/L |
| ⑤H2O2 | 2.5-3g/L | 2.5-3g/L |
| Total amount | /1000L | /1000L |
The short steaming oxygen bleaching treatment process prescription of table 2-2
Embodiment three：
(3) it singes → cold dome alkali oxygen (enzyme) processing → (desizing machine) short steaming oxygen bleaching (5 ± 0.2g/L) → post-processing
Wherein cold dome alkali oxygen, which is handled, is：
Speed：70±2m/min；
Chemical raw material：60 ± 5 DEG C of temperature, 60 ± 5 DEG C of hopper temperature, while uniformly adding chemical raw material；
Along clot direction：It rotates clockwise 6 ± 1 hours and banks up, 6-8 revs/min；
Third technology preparation is as shown in following table 3-1：
| Materials | Bottom water | It is additional |
| Chelating agent H | 1.5kg | 1.5kg |
| CG | 500g | 500g |
| Enzyme 2000L | 3kg | 3kg |
| Total amount | /550L | /550L |
Table 3-1 cold dome alkali oxygen technology preparation
Wherein short steaming oxygen bleaching processing is (1# back segment list opens short steaming oxygen bleaching)：
Desizing machine speed：40±2m/min；
Temperature:101±1℃；
Configuration：Crawler belt is not worn, cloth beam is only perforated.
Rear car list is opened：The washing of 9 65 ± 3 DEG C of lattice；10 80 ± 3 DEG C of lattice hot water wash, 11 93 ± 3 DEG C of lattice hot water wash, flat wash trough add
Water guarantees liquid level room temperature, the washing of 12 80-85 DEG C of lattice, the washing of 13 85-90 DEG C of lattice, the washing of 14 90-95 DEG C of lattice, 15 85-90 DEG C of lattice water
It washes, 16 80 ± 85 DEG C of lattice hot water wash, No. 16 slots add water to form circulation spinner flowmeter flow control in 2.0 ± 0.3m3/h.
Height gives 35 ± 5 DEG C of liquid material bath temperature degree, 30 ± 5 DEG C of materials.15# high is not pressurized to the self weight of liquid mangle roller, and 11#-13# rolls
Roller north and south 0.2 ± 0.02MPa of pressure, 14# high-capacity squeezer roll north and south 0.5 ± 0.02Mpa of pressure, 16#-19# roll north and south pressure
Power 0.2 ± 0.02MPa, 20# high-capacity squeezer north and south 0.5 ± 0.02Mpa of pressure, each cropping wet cloth clot pressure：0.5±
0.1MPa。
| Technology preparation | Bottom water | It is additional |
| 1. chelating dispersing agent CM-5 | 2kg | 2kg |
| ②DX-1099A | 12kg | 48kg |
| ③DX-1099B | 4kg | 16kg |
| 4. stabilizer P-CBB | 4kg | 16kg |
| ⑤H2O2 | 5±0.2g/L | 20±1g/L |
| Total amount | /1000L | /1000L |
The short steaming oxygen bleaching treatment process prescription of table 3-2
It should be noted that keeping following condition in above-described embodiment：
(1) desizing machine tension adjustment reduces tension bracket tension, keeps 0.15-0.2Mpa；
(2) hardness of rubber roll 65-70 drops in padding machine pressure reduction；
(3) hygienic cleaning, flower hair, the end of a thread, sundries are cleaned out；
(4) electric appliance is synchronous；
(5) drying cylinder tension, which is incremented by, reduces wrinkle；
(6) there cannot be cloth guiding axle do not rotate and not flexible；
Long vehicle experimental result:
Determine production procedure：Singe → cold dome rolls enzymatic treatment → 3 ± 0.5g/L of short steaming oxygen bleaching → post-processing；
Material selects 100% tencel, having a size of 60*60,190*119,97/90 (unit：cm).
1. breadth changes
2. package processing and long vehicle processing elongation comparison
3. index after long vehicle pre-treatment
Status level in kind is tracked by scene and all data index analysis, long vehicle pre-treatment fully achieve
Customer requirement.The specialty fibers long vehicle pre-treating technology such as tencel is succeeded in developing, and is solved high-volume and is handed over phase pressure, and guarantees
Dyeing front and back color difference stability.Row yielding long vehicle is higher by 1% or so than being wrapped, and improves income effect.
Although for illustrative purposes, it has been described that exemplary embodiments of the present invention, those skilled in the art
Member it will be understood that, can be in form and details in the case where the scope and spirit for not departing from invention disclosed in appended claims
On the change that carry out various modifications, add and replace etc., and all these changes all should belong to appended claims of the present invention
Protection scope, and each step in the claimed each department of product and method, can in any combination
Form is combined.Therefore, to disclosed in this invention the description of embodiment be not intended to limit the scope of the invention,
But for describing the present invention.Correspondingly, the scope of the present invention is not limited by embodiment of above, but by claim or
Its equivalent is defined.
Claims (6)
1. a kind of long vehicle pre-treating method of fiber, which is characterized in that include the following steps：
(1) fiber is subjected to processing of singing；
(2) processing of cold dome alkali oxygen is carried out：The first chemical raw material is added in bottom water, while uniformly being added during along clot
First chemical raw material；
(3) short steaming oxygen bleaching is carried out using desizing machine to handle：The second chemical raw material is added in bottom water, while in the process along clot
In the uniform additional third chemical raw material more suitable or bigger than each constituent concentration in the second chemical raw material；
(4) tentering and preshrunk processing are carried out.
2. the method as described in claim 1, it is characterised in that：First chemical raw material include chelated dispersants H, NAOH,
Scouring agent 6#, stabilizer P-CBB and H2O2, or including oxalic acid, or include chelating agent H, CG and enzyme 2000L.
3. the method as described in claim 1, it is characterised in that：Chelated dispersants H, NAOH in first chemical raw material, boiling-off
Agent 6#, stabilizer P-CBB and H2O2Concentration be respectively 1.5g/L, 20-22g/L, 6g/L, 8g/L and 5-6g/L or first change
Learn that the concentration of oxalic acid in raw material be 8g/L or chelating agent H, CG in the first chemical raw material and enzyme 2000L are to divide in every 550L
It Wei not 1.5kg, 500g, 3kg.
4. the method according to claim 1, it is characterised in that：Second and third described chemical raw material all includes chelating
Dispersing agent C M-5, DX-1099A, DX-1099B, stabilizer P-CBB and H2O2。
5. method as claimed in claim 4, it is characterised in that：Chelated dispersants CM-5, DX- in second chemical raw material
1099A, DX-1099B, stabilizer P-CBB and H2O2Concentration be respectively 1g/L, 12g/L, 6g/L, 6g/L, 2 and 5-3g/L.
6. method as claimed in claim 5, it is characterised in that：Chelated dispersants CM-5, DX- in the third chemical raw material
1099A, DX-1099B, stabilizer P-CBB and H2O2Concentration be respectively 1g/L, 48g/L, 24g/L, 24g/L, 2 and 5-3g/L.