CN107022836A - A kind of preparation technology of the super soft fabric of warp knit pure cotton - Google Patents
A kind of preparation technology of the super soft fabric of warp knit pure cotton Download PDFInfo
- Publication number
- CN107022836A CN107022836A CN201610066127.2A CN201610066127A CN107022836A CN 107022836 A CN107022836 A CN 107022836A CN 201610066127 A CN201610066127 A CN 201610066127A CN 107022836 A CN107022836 A CN 107022836A
- Authority
- CN
- China
- Prior art keywords
- pure cotton
- fabric
- preparation technology
- cotton
- super soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is as follows the step of the preparation technology the invention discloses a kind of preparation technology of the super soft fabric of warp knit pure cotton：(1) braiding of the super soft fabric of pure cotton, from Quality Pure Cotton Yarn Production as raw material, then carries out high density weaving by KS4 types tricot machine, using the match close spinning process of network during spinning, and fabric finished product is concretely comprised the following steps：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn → winder → plying → resultant yarn；(2) postfinishing process of fabric, (2.1) pre-treatment, (2.2) dyeing processing, the drying of (2.3) overfeeding；(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine.The present invention is arranged postfinishing process, is developed a kind of super soft fabric of the warp knit pure cotton of suitable home textile using the match close spinning process of network and high density weaving process, airflow soft machine.
Description
Technical field
The present invention relates to a kind of preparation technology of super soft fabric, the preparation work of more particularly to a kind of super soft fabric of warp knit pure cotton
Skill.
Background technology
Constantly strengthen as people advocate natural theory, natural fiber extremely people favor, and among these, people are to cotton
Fiber is shown special preference to；For knitting product, pure cotton weft knitting product substantially rules all the land, and warp knit kind is few；Pure cotton is passed through
Compiling the intrinsic physical arrangement of product makes it in terms of elasticity, the dimensional stability peace property endured between weft-knitted fabric and woven
Between, and warp knitting technology can be readily formed simple pattern tissue, improve appearance of fabrics；Knitted fabric has good
Intrinsic characteristic and surface texture, laddering is small, light weight is wear-resisting, plentiful strong, is adapted to a textile fabric is made.
Warp knit pure cotton super-soft home textile fabric is deep always to be favored by consumer, but at present puzzlement enterprise the problem of, performance compared with
For it is prominent be washing shrinkage, the problems such as loosely organized, have a strong impact on product appearance and quality.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of preparation technology of the super soft fabric of warp knit pure cotton.
To reach above-mentioned purpose, technical scheme is as follows：
The step of a kind of preparation technology of the super soft fabric of warp knit pure cotton, preparation technology, is as follows：
(the braiding of the super soft fabric of (1) pure cotton
From Quality Pure Cotton Yarn Production as raw material, then spinned by the vertical set spinning machine of reaching of Switzerland, using match network during spinning
Close spinning process, specific spinning stage is：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn → winder → plying → resultant yarn；
Yarn qualities technological parameter：
Workshop temperature is 22~26+2 DEG C during above-mentioned spinning, and humidity is 68~72+5%
(2) postfinishing process of fabric, is arranged using airflow soft machine, comprised the following steps that：
(2.1) pre-treatment:
Boil cloth → oxygen bleaching → washing → dehydration；
(2.2) dyeing is handled,
Carry out dyeing → soaping → successively using common normal-temp. and-pressure dyeing machine and dry；
(2.3) overfeeding is dried, and temperature is 180 DEG C, and speed is 8~10m/min, and overfeed ratio is 1O%~15%；
(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine, and temperature is 160 DEG C, and speed is 15m/min, is surpassed
The amount of feeding is 5%~10%, and breadth is 25O~255cm.
In one embodiment of the invention, the formula used in the pre-treatment is scouring agent 1g/L, hydrogen peroxide 8g/L,
Caustic soda 2g/L, stabilizer 2.5g/L, dispersant 1g/L, defoamer 1g/L；Handle bath raio 1:15,95 DEG C of temperature, time:50min.
In one embodiment of the invention, stamp processing can also be carried out after step (2.4) thermal finalization.
By above-mentioned technical proposal, the beneficial effects of the invention are as follows：
The present invention solves the problems, such as the depilation of warp knit pure-cotton fabric using the match close spinning process of network and postfinishing process.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
The invention discloses a kind of preparation technology of the super soft fabric of warp knit pure cotton, it is characterised in that the preparation technology's
Step is as follows：
(1) braiding of the super soft fabric of pure cotton
From Quality Pure Cotton Yarn Production (70/30 long-staple cotton/combed cotton) as raw material, then carried out by the vertical set spinning machine of reaching of Switzerland
Spinning, using the match close spinning process of network during spinning, specific spinning stage is：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn →
Winder → plying → resultant yarn；
Yarn qualities technological parameter：
Workshop temperature is 22+2 DEG C during above-mentioned spinning, and humidity is 68+5%
During above-mentioned warping, using section warping and the method for axle；The tension stability of each warp thread can be controlled consistent, done
To each section of warp thread and the synchronism stability of each warp beam tension force, thoroughly change the broken needle because the irregular generation of tension force, skew of weft, cloth
The problems such as face out-of-flatness, while the waxing for ensureing every warp thread is fully, prevent warp thread cross-linked binder.
(2) postfinishing process of fabric, is arranged using airflow soft machine, comprised the following steps that：
(2.1) pre-treatment:
Boil cloth → oxygen bleaching → washing → dehydration (boiling cloth abundant, dark half floats).
(2.2) dyeing is handled；
Common normal-temp. and-pressure dyeing machine, which carries out dyeing → soaping → successively, dries
(2.3) overfeeding is dried, and temperature is 180 DEG C, and speed is 8m/min, and overfeed ratio is 1O%；Fabric can be controlled to shrink
Rate.
(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine, and temperature is 160 DEG C, and speed is 15m/min, is surpassed
The amount of feeding is 5%, and breadth is 25Ocm, it is ensured that reach required door width, while control meets washing shrinkage requirement.
The formula used in above-mentioned pre-treatment is scouring agent 1g/L, hydrogen peroxide 8g/L, caustic soda 2g/L, stabilizer 2.5g/L,
Dispersant 1g/L, defoamer 1g/L；Handle bath raio 1:15,95 DEG C of temperature, time:50min.
Embodiment 2
The invention discloses a kind of preparation technology of the super soft fabric of warp knit pure cotton, it is characterised in that the preparation technology's
Step is as follows：
(1) braiding of the super soft fabric of pure cotton
From Quality Pure Cotton Yarn Production (70/30 long-staple cotton/combed cotton) as raw material, then carried out by the vertical set spinning machine of reaching of Switzerland
Spinning, using the match close spinning process of network during spinning, specific spinning stage is：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn →
Winder → plying → resultant yarn；
Yarn qualities technological parameter：
Workshop temperature is 24+2 DEG C during above-mentioned spinning, and humidity is 70+5%
During above-mentioned warping, using section warping and the method for axle；The tension stability of each warp thread can be controlled consistent, done
To each section of warp thread and the synchronism stability of each warp beam tension force, thoroughly change the broken needle because the irregular generation of tension force, skew of weft, cloth
The problems such as face out-of-flatness, while the waxing for ensureing every warp thread is fully, prevent warp thread cross-linked binder.
(2) postfinishing process of fabric, is arranged using airflow soft machine, comprised the following steps that：
(2.1) pre-treatment:
Boil cloth → oxygen bleaching → washing → dehydration (boiling cloth abundant, dark half floats).
(2.2) dyeing is handled；
Common normal-temp. and-pressure dyeing machine, which carries out dyeing → soaping → successively, dries
(2.3) overfeeding is dried, and temperature is 180 DEG C, and speed is 9m/min, and overfeed ratio is 12%；Fabric can be controlled to shrink
Rate.
(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine, and temperature is 160 DEG C, and speed is 15m/min, is surpassed
The amount of feeding is 8%, and breadth is 252cm, it is ensured that reach required door width, while control meets washing shrinkage requirement.
The formula used in above-mentioned pre-treatment is scouring agent 1g/L, hydrogen peroxide 8g/L, caustic soda 2g/L, stabilizer 2.5g/L,
Dispersant 1g/L, defoamer 1g/L；Handle bath raio 1:15,95 DEG C of temperature, time:50min.
Embodiment 3
The invention discloses a kind of preparation technology of the super soft fabric of warp knit pure cotton, it is characterised in that the preparation technology's
Step is as follows：
(1) braiding of the super soft fabric of pure cotton
From Quality Pure Cotton Yarn Production (70/30 long-staple cotton/combed cotton) as raw material, then carried out by the vertical set spinning machine of reaching of Switzerland
Spinning, using the match close spinning process of network during spinning, specific spinning stage is：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn →
Winder → plying → resultant yarn；
Yarn qualities technological parameter：
Workshop temperature is 26+2 DEG C during above-mentioned spinning, and humidity is 72+5%
During above-mentioned warping, using section warping and the method for axle；The tension stability of each warp thread can be controlled consistent, done
To each section of warp thread and the synchronism stability of each warp beam tension force, thoroughly change the broken needle because the irregular generation of tension force, skew of weft, cloth
The problems such as face out-of-flatness, while the waxing for ensureing every warp thread is fully, prevent warp thread cross-linked binder.
(2) postfinishing process of fabric, is arranged using airflow soft machine, comprised the following steps that：
(2.1) pre-treatment:
Boil cloth → oxygen bleaching → washing → dehydration (boiling cloth abundant, dark half floats).
(2.2) dyeing is handled；
Common normal-temp. and-pressure dyeing machine, which carries out dyeing → soaping → successively, dries
(2.3) overfeeding is dried, and temperature is 180 DEG C, and speed is 10m/min, and overfeed ratio is 15%；Fabric can be controlled to shrink
Rate.
(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine, and temperature is 160 DEG C, and speed is 15m/min, is surpassed
The amount of feeding is 10%, and breadth is 255cm, it is ensured that reach required door width, while control meets washing shrinkage requirement.
The formula used in above-mentioned pre-treatment is scouring agent 1g/L, hydrogen peroxide 8g/L, caustic soda 2g/L, stabilizer 2.5g/L,
Dispersant 1g/L, defoamer 1g/L；Handle bath raio 1:15,95 DEG C of temperature, time:50min.
To ensure fabric bursting strength, broken hole problem takes " light kiering, middle oxygen bleaching " removal of impurities composition, and body is soft,
Cloth cover is clean, is that stamp and dyeing are ready below.
The present invention can also carry out stamp processing after thermal finalization, finally obtain finished product fabric, improve the aesthetics of product.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of preparation technology of the super soft fabric of warp knit pure cotton, it is characterised in that as follows the step of the preparation technology：
(1) braiding of the super soft fabric of pure cotton
From Quality Pure Cotton Yarn Production as raw material, then spinned by the vertical set spinning machine of reaching of Switzerland, it is close using match network during spinning
Spinning process, specific spinning stage is：Mixed cotton → cotton carding → 4 draftings → rove → spun yarn → winder → plying → resultant yarn；
Yarn qualities technological parameter：
Workshop temperature is 22~26+2 DEG C during above-mentioned spinning, and humidity is 68~72+5%
(2) postfinishing process of fabric, is arranged using airflow soft machine, comprised the following steps that：
(2.1) pre-treatment:
Boil cloth → oxygen bleaching → washing → dehydration；
(2.2) dyeing is handled：
Carry out dyeing → soaping → successively using common normal-temp. and-pressure dyeing machine and dry；
(2.3) overfeeding is dried, and temperature is 180 DEG C, and speed is 8~10m/min, and overfeed ratio is 1O%~15%；
(2.4) thermal finalization, thermal finalization is carried out using pin tentering forming machine, and temperature is 160 DEG C, and speed is 15m/min, overfeed ratio
For 5%~10%, breadth is 25O~255cm.
2. a kind of preparation technology of the super soft fabric of warp knit pure cotton according to claim 1, it is characterised in that the pre-treatment
The middle formula used is scouring agent 1g/L, hydrogen peroxide 8g/L, caustic soda 2g/L, stabilizer 2.5g/L, dispersant 1g/L, defoamer
1g/L；Handle bath raio 1:15,95 DEG C of temperature, time:50min.
3. the preparation technology of the super soft fabric of a kind of warp knit pure cotton according to claim 1, it is characterised in that in step
(2.4) stamp processing can also be carried out after thermal finalization.