CN107904722A - A kind of manufacture craft of mercerized cotton yarn - Google Patents

A kind of manufacture craft of mercerized cotton yarn Download PDF

Info

Publication number
CN107904722A
CN107904722A CN201711207376.XA CN201711207376A CN107904722A CN 107904722 A CN107904722 A CN 107904722A CN 201711207376 A CN201711207376 A CN 201711207376A CN 107904722 A CN107904722 A CN 107904722A
Authority
CN
China
Prior art keywords
yarn
completion
cotton
manufacture craft
mercerized cotton
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711207376.XA
Other languages
Chinese (zh)
Inventor
王文元
张永辉
刘海瑞
孙亚楠
朱枝群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU MINGYUAN TEXTILE CO Ltd
Original Assignee
JIANGSU MINGYUAN TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU MINGYUAN TEXTILE CO Ltd filed Critical JIANGSU MINGYUAN TEXTILE CO Ltd
Priority to CN201711207376.XA priority Critical patent/CN107904722A/en
Publication of CN107904722A publication Critical patent/CN107904722A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of manufacture craft of mercerized cotton yarn, comprise the following steps that：Choose long-staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, the process weaving of rove, spun yarn is into raw yarn；Raw yarn is placed on gas singeing machine and singed, wherein when singing, the temperature of the burner of gas singeing machine keep at 980~1030 DEG C, 700~750m/min of speed.The raw material of present invention process is easy to get, it is easy to operate, solves the problems, such as the generation of mercerized cotton yarn electrostatic, facilitate user and wear the clothing that mercerized cotton yarn is made, in addition the disposal molding rate of mercerising of the mercerized cotton yarn in mercerizing process is improved, the time is saved, improves work efficiency, reduces the cost of production.

Description

A kind of manufacture craft of mercerized cotton yarn
Technical field
The invention belongs to textile technology field, more particularly to a kind of manufacture craft of mercerized cotton yarn.
Background technology
Mercerized cotton also known as " ice silk flosssilk wadding ＂, high weaving yarn is made through spinning, then through singing, the special manufacturing procedure such as mercerising, system Into bright and clean beautiful, soft crease-resistant high-quality mercerized yarn.Fabric is knitted with high-quality made of this raw material, is not only protected completely The natural characteristic that raw cotton is excellent has been stayed, and there is soyeux gloss, fabrics feel soft.Mercerising cotton Products are good because of its Good moisture pick-up properties, soft feel and comfortable sense of touch during with human contact, enjoy liking for people always for a long time, Easily go wrong in mercerized cotton yarn mercerizing process, may not once be molded, although in addition, relative to dacron in pure cotton For, the probability that electrostatic produces is smaller, but the phenomenon of electrostatic, the life band to wearer are still had in actual life Inconvenience is carried out, in consideration of it, needing to be improved the production technology of fabric.
The content of the invention
To solve the deficiencies in the prior art, the present invention carries raw material and is easy to get, and solves mercerising veil produces electrostatic problem one The manufacture craft of kind mercerized cotton yarn.
The technical solution adopted in the present invention is：A kind of manufacture craft of mercerized cotton yarn, comprises the following steps that：
Step A raw yarns：Choose long-staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, the process of rove, spun yarn Weave into raw yarn；
Step B singes：Raw yarn is placed on gas singeing machine and singed, wherein when singing, the fire of gas singeing machine Mouthful temperature keep at 980~1030 DEG C, 700~750m/min of speed；
Step C reeling：The raw yarn that completion is singed, carries out reeler's sequence on reeling frame；
Step D mercerisings：NAOH is selected the raw yarn for completion of singing to be carried out mercerization finish, in the mistake of mercerising as mercerizing agent Cheng Zhong, when the cotton yarn for carrying out mercerization finish is leaving caustic dip groove into before water wash zone, will roll unnecessary lye；
Step E：The yarn bundling that mercerization finish is completed is put into dedicated staining jar and is soaked, the yarn for soaking completion is carried out Drift and dyeing process are boiled, the yarn completed is contaminated and is first dehydrated, dried, dried, the yarn for drying completion is put into mixing Soaked in agent, the drying yarn of completion will be soaked, the yarn of completion is then subjected to winding procedure, is packed after the completion of last winder Into case.
As the further preferred of the method for the present invention, the long-staple cotton is Xinjiang Long staple cotton.
As the further preferred of the method for the present invention, the intermixture in the step E is included according to the anti-of mass ratio 1: 4 Electrostatic agent and water.
As the further preferred of the method for the present invention, the antistatic additive include 3~5 parts of Jasmine extracting solution, go from 3~5 parts of sub- 10~15 parts of water, 10~15 parts of organic solvent, 5~8 parts of sodium sulfocyanate, 15~20 parts of polyethylene glycol and toluene.
As the further preferred of the method for the present invention, the organic solvent is methyl acetate or espeleton.
As the further preferred of the method for the present invention, the concentration of the mercerizing agent in the step D is 260~280g/L.
As the further preferred of the method for the present invention, the temperature dried in the step E is 85~95 DEG C.
As the further preferred of the method for the present invention, the alkali temperature in mercerizing process in the step D is 20~22 ℃。
The beneficial effects of the present invention are：The raw material of present invention process is easy to get, easy to operate, solves mercerized cotton yarn electrostatic The problem of generation, facilitate user and wear the clothing that mercerized cotton yarn is made, in addition improve mercerized cotton yarn in mercerizing process Mercerising disposal molding rate, save the time, improve work efficiency, reduce the cost of production.
Embodiment：
Specific introduction is done to the present invention with reference to embodiment.
Embodiment 1
A kind of manufacture craft of mercerized cotton yarn, comprises the following steps that：
Step A raw yarns：Choose Xinjiang Long staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, rove, spun yarn Process is weaved into raw yarn；
Step B singes：Raw yarn is placed on gas singeing machine and singed, wherein when singing, the fire of gas singeing machine Mouthful temperature keep at 980 DEG C, speed 700m/min；
Step C reeling：The raw yarn that completion is singed, carries out reeler's sequence on reeling frame；
Step D mercerisings：NAOH is selected the raw yarn for completion of singing to be carried out mercerization finish, in the mistake of mercerising as mercerizing agent Cheng Zhong, when the cotton yarn for carrying out mercerization finish is leaving caustic dip groove into before water wash zone, will roll unnecessary lye；
Step E：The yarn bundling that mercerization finish is completed is put into dedicated staining jar and is soaked, the yarn for soaking completion is carried out Drift and dyeing process are boiled, the yarn completed is contaminated and is first dehydrated, dried, dried, the yarn for drying completion is put into mixing Soaked in agent, wherein intermixture includes the antistatic additive and water according to mass ratio 1: 4, will soak the drying yarn of completion, then The yarn of completion is subjected to winding procedure, case is packaged into after the completion of last winder.
Antistatic additive includes 3 parts of Jasmine extracting solution, 10 parts of deionized water, 10 parts of methyl acetate, sulphur cyanogen in the present embodiment 3 parts of sour 5 parts of sodium, 15 parts of polyethylene glycol and toluene.
The concentration of the mercerizing agent in step D in the present embodiment is 260g/L.
The temperature dried in step E in the present embodiment is 85 DEG C.
The alkali temperature in the mercerizing process in step D in the present embodiment is 20 DEG C.
Embodiment 2
A kind of manufacture craft of mercerized cotton yarn, comprises the following steps that：
Step A raw yarns：Choose Xinjiang Long staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, rove, spun yarn Process is weaved into raw yarn；
Step B singes：Raw yarn is placed on gas singeing machine and singed, wherein when singing, the fire of gas singeing machine Mouthful temperature keep at 1000 DEG C, speed 725m/min；
Step C reeling：The raw yarn that completion is singed, carries out reeler's sequence on reeling frame；
Step D mercerisings：NAOH is selected the raw yarn for completion of singing to be carried out mercerization finish, in the mistake of mercerising as mercerizing agent Cheng Zhong, when the cotton yarn for carrying out mercerization finish is leaving caustic dip groove into before water wash zone, will roll unnecessary lye；
Step E：The yarn bundling that mercerization finish is completed is put into dedicated staining jar and is soaked, the yarn for soaking completion is carried out Drift and dyeing process are boiled, the yarn completed is contaminated and is first dehydrated, dried, dried, the yarn for drying completion is put into mixing Soaked in agent, wherein intermixture includes the antistatic additive and water according to mass ratio 1: 4, will soak the drying yarn of completion, then The yarn of completion is subjected to winding procedure, case is packaged into after the completion of last winder.
Antistatic additive includes 4 parts of Jasmine extracting solution, 12 parts of deionized water, 13 parts of methyl acetate, sulphur cyanogen in the present embodiment 4 parts of sour 7 parts of sodium, 18 parts of polyethylene glycol and toluene.
The concentration of the mercerizing agent in step D in the present embodiment is 270g/L.
The temperature dried in step E in the present embodiment is 90 DEG C.
The alkali temperature in the mercerizing process in step D in the present embodiment is 21 DEG C.
Embodiment 3
A kind of manufacture craft of mercerized cotton yarn, comprises the following steps that：
Step A raw yarns：Choose Xinjiang Long staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, rove, spun yarn Process is weaved into raw yarn；
Step B singes：Raw yarn is placed on gas singeing machine and singed, wherein when singing, the fire of gas singeing machine Mouthful temperature keep at 1030 DEG C, speed 750m/min；
Step C reeling：The raw yarn that completion is singed, carries out reeler's sequence on reeling frame；
Step D mercerisings：NAOH is selected the raw yarn for completion of singing to be carried out mercerization finish, in the mistake of mercerising as mercerizing agent Cheng Zhong, when the cotton yarn for carrying out mercerization finish is leaving caustic dip groove into before water wash zone, will roll unnecessary lye；
Step E：The yarn bundling that mercerization finish is completed is put into dedicated staining jar and is soaked, the yarn for soaking completion is carried out Drift and dyeing process are boiled, the yarn completed is contaminated and is first dehydrated, dried, dried, the yarn for drying completion is put into mixing Soaked in agent, wherein intermixture includes the antistatic additive and water according to mass ratio 1: 4, will soak the drying yarn of completion, then The yarn of completion is subjected to winding procedure, case is packaged into after the completion of last winder.
Antistatic additive includes 5 parts of Jasmine extracting solution, 15 parts of deionized water, 15 parts of methyl acetate, sulphur cyanogen in the present embodiment 5 parts of sour 8 parts of sodium, 20 parts of polyethylene glycol and toluene.
The concentration of the mercerizing agent in step D in the present embodiment is 280g/L.
The temperature dried in step E in the present embodiment is 95 DEG C.
The alkali temperature in the mercerizing process in step D in the present embodiment is 22 DEG C.
The beneficial effects of the present invention are：The raw material of present invention process is easy to get, easy to operate, solves mercerized cotton yarn electrostatic The problem of generation, facilitate user and wear the clothing that mercerized cotton yarn is made, in addition improve mercerized cotton yarn in mercerizing process Mercerising disposal molding rate, save the time, improve work efficiency, reduce the cost of production.
The above is only the preferred embodiment of patent of the present invention, it is noted that for the common skill of the art For art personnel, on the premise of patent principle of the present invention is not departed from, some improvements and modifications can also be made, these improve and Retouching also should be regarded as the protection domain of patent of the present invention.

Claims (8)

  1. A kind of 1. manufacture craft of mercerized cotton yarn, it is characterised in that：Comprise the following steps that：
    Step A raw yarns：Choose long-staple cotton, by long-staple cotton by blowing, cotton carding, head simultaneously, two simultaneously, the process of rove, spun yarn weaves Into raw yarn；
    Step B singes：Raw yarn is placed on gas singeing machine and singed, wherein when singing, the burner of gas singeing machine Temperature keep at 980~1030 DEG C, 700~750m/min of speed；
    Step C reeling：The raw yarn that completion is singed, carries out reeler's sequence on reeling frame；
    Step D mercerisings：NAOH is selected to be used as mercerizing agent, by the raw yarn of completion of singing progress mercerization finish, during mercerising, When the cotton yarn for carrying out mercerization finish is leaving caustic dip groove into before water wash zone, unnecessary lye is rolled；
    Step E：The yarn bundling that mercerization finish is completed is put into dedicated staining jar and is soaked, the yarn for soaking completion is carried out boiling drift And dyeing process, contaminate the yarn completed and be first dehydrated, dried, dried, the yarn for drying completion is put into intermixture Immersion, will soak the drying yarn of completion, and the yarn of completion then is carried out winding procedure, is packaged into after the completion of last winder Case.
  2. 2. the manufacture craft of a kind of mercerized cotton yarn according to claim 1, it is characterised in that the long-staple cotton is Xinjiang Long-staple cotton.
  3. 3. the manufacture craft of a kind of mercerized cotton yarn according to claim 1, it is characterised in that mixed in the step E Mixture is included according to mass ratio 1：4 antistatic additive and water.
  4. 4. the manufacture craft of a kind of mercerized cotton yarn according to claim 3, it is characterised in that the antistatic additive includes 3~5 parts of Jasmine extracting solution, 10~15 parts of deionized water, 10~15 parts of organic solvent, 5~8 parts of sodium sulfocyanate, polyethylene glycol 15~20 parts and 3~5 parts of toluene.
  5. 5. the manufacture craft of a kind of mercerized cotton yarn according to claim 4, it is characterised in that the organic solvent is vinegar Sour methyl esters or espeleton.
  6. A kind of 6. manufacture craft of mercerized cotton yarn according to claim 1, it is characterised in that the silk in the step D The concentration of photo etching is 260~280g/L.
  7. 7. the manufacture craft of a kind of mercerized cotton yarn according to claim 1, it is characterised in that dried in the step E Temperature be 85~95 DEG C.
  8. A kind of 8. manufacture craft of mercerized cotton yarn according to claim 1, it is characterised in that the silk in the step D Alkali temperature in light process is 20~22 DEG C.
CN201711207376.XA 2017-11-27 2017-11-27 A kind of manufacture craft of mercerized cotton yarn Pending CN107904722A (en)