CN108866722A - The production technology of Tai Ji stone blend polyester spandex yarn - Google Patents
The production technology of Tai Ji stone blend polyester spandex yarn Download PDFInfo
- Publication number
- CN108866722A CN108866722A CN201810892384.0A CN201810892384A CN108866722A CN 108866722 A CN108866722 A CN 108866722A CN 201810892384 A CN201810892384 A CN 201810892384A CN 108866722 A CN108866722 A CN 108866722A
- Authority
- CN
- China
- Prior art keywords
- tai
- cotton
- spandex yarn
- mineral wool
- cotton fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production technologies of Tai Ji stone blend polyester spandex yarn, use Tai Ji mineral wool fabric and cotton fiber for raw material, the quality accounting of Tai Ji mineral wool fabric is 60~80%, the quality accounting of cotton fiber is 40~20%, the specific technological process of production is that cotton roll is respectively prepared by blowing process in two kinds of raw materials, then two kinds of cotton rolls are respectively prepared by the carded sliver by cotton carding, two kinds of carded slivers are by setting ratio and close after half ripe bar is made in drawing-off ripe bar is made again, most afterwards through spinning process such as rove, spun yarn and winders, the spandex yarn that is spun into.The wearability that clothes made by spandex yarn obtained by this kind of technique have release far infrared, promote blood circulation, improve the health-care efficacies such as sleep and natural environmental-protective, soft comfortable.
Description
Technical field
The present invention relates to technical field of textile manufacture, and in particular to the production technology of Tai Ji stone blend polyester spandex yarn.
Background technique
Tai Ji stone is a kind of natural silicon crystal quartz mine, bulk composition SiO2, and rich in the lot of trace such as titanium, potassium, germanium gold
Belong to mineral element.Tai Ji stone material clothing is to be made into natural Tai Ji stone using nanotechnology master batch is made, resolidification to fibre
It is formed by weaving in dimension and with yarn, has the excellent far infrared function of Tai Ji stone and is generated with the hydrone in human body cell
Resonant interaction enhances blood cell kinetic energy, refines hydrone, promotes blood of human body microcirculation, has to joint pain etc. is alleviated
Certain health-care effect.
Summary of the invention
For above situation, the present invention provides a kind of production technologies of Tai Ji stone blend polyester spandex yarn, with Tai Ji stone
Clothes made by fiber and cotton blend spandex yarn have more release far infrared, promote blood circulation, improve the health cares such as sleep
The wearability of effect and natural environmental-protective, soft comfortable.
The present invention solves the above problems by the following technical programs:The production work of Tai Ji stone blend polyester spandex yarn
Skill uses Tai Ji mineral wool fabric and cotton fiber for raw material, and the specific technological process of production of blend polyester spandex yarn is:
(1)Blowing:Cotton roll is made by mixing, shredding, dedoping step in Tai Ji mineral wool fabric;
(2)Cotton carding:To step(1)In cotton roll combed, cleaning is made the Tai Ji mineral wool carded sliver;
(3)According to step(1)And step(2)Production technology the cotton fiber carded sliver is made in cotton fiber;
(4)Head is simultaneously:By step(2)And step(3)The obtained Tai Ji mineral wool carded sliver and the cotton fiber carded sliver is according to setting ratio
It carries out and closes, half ripe bar is made in drawing-off;
(5)Two simultaneously:By eight steps(4)In obtained half ripe bar is carried out and is closed, ripe bar is made in drawing-off;
(6)Rove:By step(5)In made ripe bar drawing-off, twisting rove is made and respins into spun yarn, using post-processing work
Required spandex yarn is made in sequence.
Preferably, step(6)In joined during spun yarn processed it is spandex core-covered.
Preferably, the quality accounting of the Tai Ji mineral wool fabric is 60~80%, the quality accounting of the cotton fiber is
40~20%.
Beneficial effects of the present invention are:Tai Ji mineral wool fabric and cotton fiber are mixed again according to specific ratio by adding
Enter it is spandex core-covered made of Tai Ji stone blend polyester spandex yarn, clothes made by this kind of spandex yarn have release far infrared,
Promote blood circulation, improve sleep etc. health-care efficacies, the wearability of natural environmental-protective, soft comfortable, the spandex of addition to take
Dress is more elastic and cultivates one's moral character, the effect of fashion.
Detailed description of the invention
Fig. 1 is process flow diagram of the invention.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, right below in conjunction with specific embodiments and the drawings
Technical solution of the present invention is more clearly and completely described, it is clear that described embodiment is that a part of the invention is real
Example is applied, instead of all the embodiments.
The production technology of Tai Ji stone blend polyester spandex yarn, uses Tai Ji mineral wool fabric and cotton fiber for raw material, and Tai Ji stone is fine
The quality accounting for tieing up fabric is 60~80%, and the quality accounting of cotton fiber is 40~20%, the specific production of blend polyester spandex yarn
Process flow is:
(1)Blowing:Cotton roll is made by mixing, shredding, dedoping step in Tai Ji mineral wool fabric;
(2)Cotton carding:To step(1)In cotton roll combed, cleaning is made the Tai Ji mineral wool carded sliver;
(3)According to step(1)And step(2)Processing step the cotton fiber carded sliver is made in cotton fiber;
(4)Head is simultaneously:By step(2)And step(3)The obtained Tai Ji mineral wool carded sliver and the cotton fiber carded sliver is according to setting ratio
It carries out and closes, half ripe bar is made in drawing-off;
(5)Two simultaneously:By eight steps(4)In obtained half ripe bar is carried out and is closed, ripe bar is made in drawing-off;
(6)Rove:By step(5)In made ripe bar carries out drawing-off, rove is made in twisting;
(7)Spun yarn:Rove is subjected to drawing-off, twisting, spandex is added from front upper roller, is spun into spun yarn;
(8)Winder:Spun yarn is removed into yarn defect, connection coil by electronic yarn clearer, cylinder yarn, as required spandex yarn is made.
Claims (3)
1. the production technology of Tai Ji stone blend polyester spandex yarn, it is characterised in that:Use Tai Ji mineral wool fabric and cotton fiber for
The specific technological process of production of raw material, blend polyester spandex yarn is:
(1)Blowing:Cotton roll is made by mixing, shredding, dedoping step in Tai Ji mineral wool fabric;
(2)Cotton carding:To step(1)In cotton roll combed, cleaning is made the Tai Ji mineral wool carded sliver;
(3)According to step(1)And step(2)Production technology the cotton fiber carded sliver is made in cotton fiber;
(4)Head is simultaneously:By step(2)And step(3)The obtained Tai Ji mineral wool carded sliver and the cotton fiber carded sliver is according to setting ratio
It carries out and closes, half ripe bar is made in drawing-off;
(5)Two simultaneously:By eight steps(4)In obtained half ripe bar is carried out and is closed, ripe bar is made in drawing-off;
(6)Rove:By step(5)In made ripe bar drawing-off, twisting rove is made and respins into spun yarn, using post-processing work
Required spandex yarn is made in sequence.
2. the production technology of Tai Ji stone blend polyester spandex yarn according to claim 1, it is characterised in that:Step(6)In
It joined in the preparation process of the spun yarn processed spandex core-covered.
3. the production technology of Tai Ji stone blend polyester spandex yarn according to claim 1, the Tai Ji mineral wool fabric
Quality accounting is 60~80%, and the quality accounting of the cotton fiber is 40~20%.