CN105586682A - Spandex core-spun yarn formed by cotton fibers and negative ion polyester fibers in siro spinning mode - Google Patents
Spandex core-spun yarn formed by cotton fibers and negative ion polyester fibers in siro spinning mode Download PDFInfo
- Publication number
- CN105586682A CN105586682A CN201610056757.1A CN201610056757A CN105586682A CN 105586682 A CN105586682 A CN 105586682A CN 201610056757 A CN201610056757 A CN 201610056757A CN 105586682 A CN105586682 A CN 105586682A
- Authority
- CN
- China
- Prior art keywords
- fiber
- anion terylene
- spun yarn
- anion
- siro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses spandex core-spun yarn formed by cotton fibers and negative ion polyester fibers in a siro spinning mode. The spandex core-spun yarn is manufactured with, by weight, 30-60 parts of the cotton fibers and 25-50 parts of the negative ion polyester fibers, and the siro spinning process is adopted to spin the cotton fibers and the negative ion polyester fibers into the spandex core-spun yarn. A mechanical property, an antibacterial property and negative ion release durability of the yarn are excellent.
Description
Technical field
The present invention relates to siro-spinning spandex core-spun yarn technical field, relate in particular to a kind of cotton fiber, anion is washedSynthetic fibre fibre sirospun spandex core-spun yarn.
Background technology
To spin be by the two parallel introducing spinning frame of rove draw zones to match network, after drawing-off respectively from sieve of spinning frameDraw vice mouth out converges, and due to the effect of the twist, two single thread self are coupled with certain twist, and twoRoot single thread also has the twist after converging between them, completed the twisting of single thread, strand simultaneously and closed, roll upAround work. Covering yarn is made up of core silk (yarn) and outer wrapping fiber, its outer wrapping fiber when spinning Siro Core-spun YarnBe two, match network and spin two yarns, spandex continuous yarn under the control of core silk take-off device, by with the speed of front rollerDegree is poor gives core silk certain pre-draft multiple, feeds people by godet roller from front roller. Match network spins two roveFeed people's device by the rove necessarily spacing and feed people from rear roller, after the drawing-off of certain multiple, export at front rollerPlace and spandex core silk twisted, have certain flexible siro-spinning spandex core-spun yarn thereby form.
Anion refers to the small ion cluster with unnecessary negative electrical charge in air, and diameter is between 0.16-3nm, negativeIon polyster fibre in use can discharge a certain amount of anion in air, has the cytoactive of makingChange, eliminate human-body fatigue, stablize automatic nervous system, strengthen human body resistance against diseases, resist electromagnetic radiation,The effects such as analgesia, have special health care; But contain at present the siro-spinning spandex bag of anion terylene fiberMechanical property, antibiotic property and the anion of heart yarn discharges persistence and also can not meet demand.
Summary of the invention
The present invention proposes a kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, mechanical property,It is very excellent that antibiotic property and anion discharge persistence.
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn that the present invention proposes, its raw material is pressedWeight portion comprises: cotton fiber 30-60 part, and anion terylene fiber 25-50 part, and adopt match network spinning processBe spun into spandex core-spun yarn.
Preferably, described cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material is by heavyAmount part comprises: cotton fiber 50-58 part, anion terylene fiber 30-36 part.
Preferably, described cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, anion teryleneFiber adopts following technique preparation: zirconium dioxide, silica and titanium dioxide are mixed to rear sintering,Obtaining particle diameter is the first prefabricated material of 0.1-0.8 micron; By the coptis, radix bupleuri, the root of Dahurain angelica, honeysuckle, fish raw meatGrass boiling, adds the first prefabricated material, coupling agent, flax fiber to soak, and filters, and adds anion to washSynthetic fibre mixes, extrudes, and section, melting, extruding, spray silk, obtains anion terylene fiber.
Preferably, the weight ratio of zirconium dioxide, silica and titanium dioxide is 20-30:5-15:10-18.
Preferably, the weight ratio of the coptis, radix bupleuri, the root of Dahurain angelica, honeysuckle, cordate houttuynia is 1-5:1-4:2-6:1-4:1-3。
Preferably, the weight ratio of flax fiber, terylene, coupling agent is 10-20:50-100:0.2-0.8.
Preferably, anion terylene fiber adopts following technique preparation: by weight by 20-30 part titanium dioxideZirconium, 5-15 part silica and 10-18 part titanium dioxide mix rear sintering, and obtaining particle diameter is 0.1-0.8The first prefabricated material of micron; By 1-5 part coptis, 1-4 part radix bupleuri, 2-6 part root of Dahurain angelica, 1-4 part honeysuckle,1-3 part cordate houttuynia boiling 5-10h, adds the first prefabricated material, 0.2-0.8 part coupling agent, 10-20 partFlax fiber soaks 10-20h, filters, and adds 50-100 part anion terylene to mix, extrude, and section,Melting, extruding, spray silk, obtains anion terylene fiber.
In the present invention, anion terylene fiber is a kind of physics chemical modification polyester fiber of holding concurrently, not only can be efficientSustained release anion, can make body local produce thermogenetic effect, stimulates circulation, the coptis that adds,Radix bupleuri, the root of Dahurain angelica, honeysuckle, cordate houttuynia can effectively suppress tubercle bacillus, Bacillus influenzae, vaccinia virus, andCan kill plasmodium, has a broad antifungal spectrum, and have long-lastingly, the coupling agent adding in addition, can strengthen first pre-System material and terylene compatibility, promote anion effect, and cotton fiber moisture absorption and good permeability are soft and warming,But mechanical strength is poor, cotton fiber and anion terylene fiber blending, anion terylene fiber blending transversalFace is cross, has many groove structures, not only can make up the defect of cotton fiber poor mechanical property, and bothSynergy, goods moisture absorption, permeability be through an enhancing, and can further stimulate circulation, and makes skinSkin keeps snugness.
Detailed description of the invention
Below, by specific embodiment, technical scheme of the present invention is elaborated.
Embodiment 1
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material comprises by weight:30 parts, cotton fiber, 50 parts of anion terylene fibers, and adopt match network spinning process to be spun into spandex core-spun yarn.
Embodiment 2
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material comprises by weight:60 parts, cotton fiber, 25 parts of anion terylene fibers, and adopt match network spinning process to be spun into spandex core-spun yarn.
Embodiment 3
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material comprises by weight:50 parts, cotton fiber, 36 parts of anion terylene fibers, and adopt match network spinning process to be spun into spandex core-spun yarn.
Anion terylene fiber adopts following technique preparation: by weight by 20 parts of zirconium dioxides, 15 parts of dioxiesSiClx and 10 parts of titanium dioxide mix rear sintering, and obtaining particle diameter is the first prefabricated material of 0.1-0.8 micron;By 5 portions of coptiss, 1 part of radix bupleuri, 6 parts of roots of Dahurain angelica, 1 portion of honeysuckle, 3 parts of cordate houttuynia boiling 5h, addThe first prefabricated material, 0.2 part of coupling agent, 20 parts of flax fibers soak 10h, filter, and add 100 parts of anionsTerylene mixes, extrudes, and section, melting, extruding, spray silk, obtains anion terylene fiber.
Embodiment 4
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material comprises by weight:58 parts, cotton fiber, 30 parts of anion terylene fibers, and adopt match network spinning process to be spun into spandex core-spun yarn.
Anion terylene fiber adopts following technique preparation: by weight by 30 parts of zirconium dioxides, 5 parts of dioxiesSiClx and 18 parts of titanium dioxide mix rear sintering, and obtaining particle diameter is the first prefabricated material of 0.1-0.8 micron;By 1 portion of coptis, 4 parts of radix bupleuri, 2 parts of roots of Dahurain angelica, 4 portions of honeysuckles, 1 part of cordate houttuynia boiling 10h, addThe first prefabricated material, 0.8 part of coupling agent, 10 parts of flax fibers soak 20h, filter, and add 50 parts of anionsTerylene mixes, extrudes, and section, melting, extruding, spray silk, obtains anion terylene fiber.
Embodiment 5
A kind of cotton fiber, anion terylene fiber siro-spinning spandex core-spun yarn, its raw material comprises by weight:54 parts, cotton fiber, 33 parts of anion terylene fibers, and adopt match network spinning process to be spun into spandex core-spun yarn.
Anion terylene fiber adopts following technique preparation: by weight by 26 parts of zirconium dioxides, 12 parts of dioxiesSiClx and 15 parts of titanium dioxide mix rear sintering, and obtaining particle diameter is the first prefabricated material of 0.1-0.8 micron;By 3 portions of coptiss, 2 parts of radix bupleuri, 5 parts of roots of Dahurain angelica, 2 portions of honeysuckles, 2 parts of cordate houttuynia boiling 8h, addThe first prefabricated material, 0.6 part of coupling agent, 18 parts of flax fibers soak 14h, filter, and add 88 parts of anionsTerylene mixes, extrudes, and section, melting, extruding, spray silk, obtains anion terylene fiber.
The above, be only preferably detailed description of the invention of the present invention, but not office of protection scope of the present inventionBe limited to this, any be familiar with those skilled in the art the present invention disclose technical scope in, according to thisThe technical scheme of invention and inventive concept thereof are equal to replaces or changes, and all should be encompassed in protection of the present inventionWithin scope.
Claims (7)
1. cotton fiber, an anion terylene fiber siro-spinning spandex core-spun yarn, is characterized in that, its raw materialComprise by weight: cotton fiber 30-60 part, anion terylene fiber 25-50 part, and adopt match network to spin workSkill is spun into spandex core-spun yarn.
2. cotton fiber according to claim 1, anion terylene fiber siro-spinning spandex core-spun yarn, itsBe characterised in that, its raw material comprises by weight: cotton fiber 50-58 part, anion terylene fiber 30-36 part.
3. cotton fiber according to claim 1, anion terylene fiber siro-spinning spandex core-spun yarn, itsBe characterised in that, anion terylene fiber adopts following technique preparation: by zirconium dioxide, silica and dioxyChange titanium and mix rear sintering, obtaining particle diameter is the first prefabricated material of 0.1-0.8 micron; By the coptis, radix bupleuri,The root of Dahurain angelica, honeysuckle, cordate houttuynia boiling, add the first prefabricated material, coupling agent, flax fiber to soak,Filter, add anion terylene to mix, extrude, section, melting, extruding, spray silk, obtain bearing fromSub-polyster fibre.
4. cotton fiber according to claim 3, anion terylene fiber siro-spinning spandex core-spun yarn, itsBe characterised in that, the weight ratio of zirconium dioxide, silica and titanium dioxide is 20-30:5-15:10-18.
5. according to the cotton fiber described in claim 3 or 4, anion terylene fiber siro-spinning spandex core-spun yarn,It is characterized in that, the weight ratio of the coptis, radix bupleuri, the root of Dahurain angelica, honeysuckle, cordate houttuynia is 1-5:1-4:2-6:1-4:1-3。
6. according to the cotton fiber described in claim 3-5 any one, anion terylene fiber siro-spinning spandex bagHeart yarn, is characterized in that, the weight ratio of flax fiber, terylene, coupling agent is 10-20:50-100:0.2-0.8.
7. according to the cotton fiber described in claim 3-6 any one, anion terylene fiber siro-spinning spandex bagHeart yarn, is characterized in that, anion terylene fiber adopts following technique preparation: by weight by 20-30 partZirconium dioxide, 5-15 part silica and 10-18 part titanium dioxide mix rear sintering, obtain particle diameter and areThe first prefabricated material of 0.1-0.8 micron; By 1-5 part coptis, 1-4 part radix bupleuri, 2-6 part root of Dahurain angelica, 1-4 partHoneysuckle, 1-3 part cordate houttuynia boiling 5-10h, add the first prefabricated material, 0.2-0.8 part coupling agent,10-20 part flax fiber soaks 10-20h, filters, and adds 50-100 part anion terylene to mix, and squeezesGo out, section, melting, extruding, spray silk, obtains anion terylene fiber.