CN105671716B - Alginate fibre produces the high-grade knitted method with yarn with combing medium staple cotton, long wool cotton blend - Google Patents
Alginate fibre produces the high-grade knitted method with yarn with combing medium staple cotton, long wool cotton blend Download PDFInfo
- Publication number
- CN105671716B CN105671716B CN201510594058.8A CN201510594058A CN105671716B CN 105671716 B CN105671716 B CN 105671716B CN 201510594058 A CN201510594058 A CN 201510594058A CN 105671716 B CN105671716 B CN 105671716B
- Authority
- CN
- China
- Prior art keywords
- cotton
- alginate fibre
- combing
- yarn
- staple cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of alginate fibre and combing medium staple cotton, long wool cotton blend to produce the high-grade knitted method with yarn, from alginate fibre and cotton fiber.Alginate fibre through blowing, cotton carding, it is pre- and after on drafting with combing medium staple cotton, long wool sliver and closing, then produce cylinder yarn through rove, spun yarn, winding procedure, blending rate is marine alga/combed long staple cotton fiber/combing fine fleece cotton fiber 50/30/20.Cylinder yarn produced by the invention, due to there is the addition of combing suede cotton, medium staple cotton, the cotton texture of fabric is added, the fabric filoplume being made into is few, anti-fluffing and anti-pilling performance is good, strength is high, fluffy, soft elastic, solves the easy wrinkle and dimensional stability problems of pure cotton fabric, snugness of fit and warmth retention property is set further to improve, the personal dress ornament such as underwear, vest, undershirt, shorts, T-shirt, nightwear is made with it, warmth retention property is good, also the effect of skin care moisturizing and health care.
Description
Technical field
The present invention relates to a kind of alginate fibre and combing medium staple cotton, combed long staple cotton blending to produce the high-grade knitted side with yarn
Method.
Background technology
Alginate fibre is using the alginic acid for extracting to obtain in some brown algae in ocean to be fine made from raw material
Dimension.During textile process, this fiber can with natural cotton or other fiber blends, product is rich in gloss, feel is soft and smooth,
Moisture absorption is ventilative, comfortableness is preferable.It may finally be used to manufacture clothes, household textiles, mattress etc..
Alginate fibre has some good characteristics as a kind of new environmental type cellulose fibre：First, marine alga is fine
Dimension has moisture-absorbing moisture-keeping function.Moisture pick-up properties can be played by the contact with skin in the fibre, actively discharge algae component,
The skin of wearer is made to absorb the vitamin and mineral of marine alga release.The clothes made not only summer wear it is comfortable, and
Can also antibacterial beneficial skin, play a part of beauty and health care.Second, alginate fibre has certain radiation-proof effect.Especially for low
Frequency electromagnetic waves effect is very good, can apply to maternity dress production.Third, the anti-flammability of alginate fibre is good, alginate fibre is in sky
Naked light will not be played in gas, Product Safety is good, can be used for producing protective garment, toy for children etc..Fourth, in biomedical aspect,
Due to containing substantial amounts of calcium ion in alginate fibre, can be imitated with the sodium ion exchange in blood so as to play good hemostasis
Fruit, promote wound healing.Therefore, alginate fibre material is particularly suitable for making high-grade gauze, dressing, operation suture thread, adhesive bandage
Deng.The various excellent properties of algae fiber have obtained extensive concern in field of textiles and medical domain, and alginate fibre will have
Broader market development prospect.
But there is problems with alginate fibre：Alginate fibre strength is low, larger, the marine alga in blending production process of wet elongation
Fiber is easily pulled off, and alginate fibre is also easy to produce slippage in drafting process, it is difficult to ensures yarn quality.Improve marine alga yarn kind
Strength is the difficult point of alginate fibre high-count yarn spun.Alginate fibre regain is big, needs to pay special attention in spinning process relative in workshop
The change and control of humidity.Performance difference between alginate fibre and combing medium staple cotton, combed long staple cotton is big, and spinning is difficult,
Reasonable arrangement blending rate.
The content of the invention
The purpose of the present invention is to be directed to above-mentioned present situation, it is desirable to provide a kind of dry and wet intensity is high, sucting wet air permeability is good, skin care,
Health care, fabric feeling are soft and smooth, bright color, the plentiful round and smooth alginate fibre of cloth covering weave and cotton blend produce high-grade knitted use
The method of yarn.
The implementation of the object of the invention is that a kind of alginate fibre produces high-grade pin with combed long staple cotton, fine fleece cotton blend
The method with yarn is knitted,
Alginate fibre：Dry fracture strength 1.6CN/dtex, wet breaking strength 1.1CN/dtex, dry elongation at break
10.3%th, wet elongation at break 16.8%, line density 1.7dtex, length 38mm, regain 9.7%.
Combed long staple cotton fiber：It is 2.0 grades of grade of distributing cotton, principal length 37.1mm, beam fibre fracture strength 43.0CN/tex, thin
Spend 1.35dtex, below 16mm short fiber contents are 22%, regain 9.44%, percentage of impurity 3.6%
Combing fine fleece cotton fiber：2.5 grades of grade of distributing cotton, principal length 29.2mm, fracture strength 28.8CN/tex, fineness
1.69dtex, below 16mm short fiber content are 15.8%, regain 9.67%, percentage of impurity 2%；
Alginate fibre through blowing, cotton carding, it is pre- and after on drafting with medium staple cotton, long-staple cotton yarn and close, then through rove,
Spun yarn, winding procedure produce cylinder yarn, and blending rate is marine alga/combed long staple cotton fiber/combing fine fleece cotton fiber 50/30/20；
Production comprises the following steps that：
1) alginate fibre cotton cleaning process
Griping cotton machine hired roughneck's decrease speed each 3mm, rotating speed 960r/min, rotary machinery speed 2.8r/min, blade stretch out
Rib 3mm, Beater Speed 800r/min, fan speed 950r/min, the gauge 12mm of hired roughneck and pedal roller, humiture 20-
25 DEG C of 55-65%；Lap roller speed 12r/min, alginate fibre cotton rolling quantity is 380g/m in production, and lap length is 36m.
Install rove device additional on blowing, 6 are added when coiled with the other rove of branch；
2) alginate fibre carding step
Feed plate raises 5mm, cylinder speed 330r/min, licker-in speed 785r/min, doffer speed 19r/min, cover plate
Speed 87.3mm/min, cylinder and the English silk of licker-in gauge 7, feed plate and the English silk of licker-in gauge 14, cylinder and the English of doffer's gauge 4
Silk, mote knife height are put down with machine frame, 90 ° of the knife back and machine frame horizontal plane angle, 20-25 DEG C of temperature, humidity 55-65%；
3) mixing in doubling step
Alginate fibre first passes through one in advance simultaneously, the quantitative 19g/5 rice of pre- and dry weight, then by three draftings and closes；Head is simultaneously adopted
With 6,3 alginate fibres, 2 combed long staple cotton bars and 1 combing fine fleece sliver simultaneously close；Head and the quantitative 17.5g/5 rice of dry weight,；
Two and 6 quantitative 17g/5 rice of root dry weight, three and 6 quantitative 16.8g/5 rice of root dry weight, Uster sliver control within 3.5%, temperature
20-25 DEG C of 55-65% of humidity；
4) Roving Frames
Roving twist 5 twists with the fingers/10cm, and roller gauge uses 22mm × 42mm, 1.21 times, nip gauge 6mm of back area draft,
The quantification of 4.20g/10 rice of rove dry weight, 8 times of weight drafting multiple, 8.24 times of mechanical commutation draft, front roller rotating speed 180r/min, return
Tide 9%, weight in wet base 4.58g/10m, special number 9.8tex, twist factor 107, front roller diameter 28mm, pressing device winding number 2 enclose, spindle top winding number
3/4 encloses, within Uster sliver 4.5%, 20-25 DEG C of 55-65% of humiture；
5) spinning process
46.7 times of total draft multiple, 47.5 times of weight drafting multiple, 49 times of mechanical commutation draft multiple, roller gauge be 17mm ×
40mm, back zone drafting multiple are 1.2 times, nip gauge 2.5mm, front roller diameter 25mm, spindle rotating speed 14000r/min, motor
The rotating speed 1460r/min twists 121 twist with the fingers/10cm, twist factor 380, rings model PG2/13851, wire loop model OSS120,
20-25 DEG C of temperature, humidity 55-65%；
6) winding procedure
Produced on automatic winder, using electronic yarn clearer and empty sth. made by twisting without knot technology, electronic yarn clearer parameter：NSL1：350%
0.4cm、NSL2：130%1.3cm, NSL3：100%4cm, NSL4：25%100cm, T1：- 46%3.6cm, T2：- 38%
9.5cm、T3：- 17%140cm, 20-25 DEG C of 55-65% of humiture, produce thin (50/30/20) 9.8tex's of HZ/J length/J
It is high-grade knitted to use yarn.
Alginate fibre through blowing, cotton carding, it is pre- and after on drafting with combing medium staple cotton, long wool sliver and close, then through rove,
Spun yarn, winding procedure produce cylinder yarn, and blending rate is marine alga/combed long staple cotton fiber/combing fine fleece cotton fiber 50/30/20.
Cylinder yarn produced by the invention, due to there is the addition of combing suede cotton, medium staple cotton, the cotton texture of fabric is added, the fabric being made into
Filoplume is few, and anti-fluffing and anti-pilling performance is good, and strength is high, and fluffy, soft elastic, the easy wrinkle and size for solving pure cotton fabric are steady
Qualitative question, snugness of fit and warmth retention property is further improved, underwear, vest, undershirt, shorts, T-shirt, nightwear are made with it
It is good etc. personal dress ornament, warmth retention property, the also effect of skin care moisturizing and health care.
Embodiment
The present invention be by alginate fibre through blowing, cotton carding, it is pre- and after on drafting with medium staple cotton, long-staple cotton yarn simultaneously
Close, then cylinder yarn is produced through rove, spun yarn, winding procedure.
Suitable alginate fibre, alginate fibre production line and long-staple cotton fiber, medium staple cotton fiberline are first selected, specifically
It is as follows：
Alginate fibre：Dry fracture strength 1.6CN/dtex, wet breaking strength 1.1CN/dtex, dry elongation at break
10.3%th, wet elongation at break 16.8%, line density 1.7dtex, length 38mm, regain 9.7%.
Alginate fibre cotton carding production line is using A002C types automatic plucker, A036B porcupine openers, the double cottons of A092A types
Case cotton feeder, A076C types lapper and A186D carding machines.
Cotton fiber condition：
Combed long staple cotton fiber：It is 2.0 grades of grade of distributing cotton, principal length 37.1mm, beam fibre fracture strength 43.0CN/tex, thin
Spend 1.35dtex, below 16mm short fiber contents are 22%, regain 9.44%, percentage of impurity 3.6%
Combing fine fleece cotton fiber：2.5 grades of grade of distributing cotton, principal length 29.2mm, fracture strength 28.8CN/tex, fineness
1.69dtex, below 16mm short fiber content are 15.8%, regain 9.67%, percentage of impurity 2%
The production line of cotton is using A002C types automatic plucker, A035C mixed cotton slitters, A036B porcupine openers, A092A types
Tandem feeder, A076C types lapper and A186D carding machines.On combing process due in the pure cotton carded sliver cotton junction impurity and
Below 16mm short flannel is more, and uses double combings, reduces short flannel and improves the regularity of fiber, the control of cotton noils rate
19% or so.Double combing flows：FA317A drawing frames are pre- for the first time simultaneously, FA356 bars and roll up joint, FA266 combing machines,
FA317A drawing frames second are pre- simultaneously, FA356 bars and roll up joint, FA266 combing.
Alginate fibre through blowing, cotton carding, it is pre- and after on drafting with medium staple cotton, long-staple cotton yarn and close, then through rove,
Spun yarn, winding procedure produce cylinder yarn, and blending rate is marine alga/combed long staple cotton fiber/combing fine fleece cotton fiber 50/30/20；
Production comprises the following steps that：
1) alginate fibre cotton cleaning process
Alginate fibre regularity is good, free from foreign meter, but fiber packing is close, according to these features in traditional technological process
On the basis of reduce A035C mixed cotton slitters this road technological processes, reduce the strike of A035C porcupines hired roughneck parallel with two, reduce
The damage of fiber.Improving griping cotton machine and hopper machinery running rate in process of production simultaneously, (general more than 85%), is suitably carried
High coiled fan speed, it is ensured that producing wound laps are good.Cotton efficiency is grabbed to improve disk, each 3mm of griping cotton machine hired roughneck's decrease speed,
Grab cotton hired roughneck rotating speed 960r/min, rotary machinery speed 2.8r/min, 20-25 DEG C of temperature, humidity 55-65%.Alginate fibre cotton
Pack tightly, blade stretches out rib 3mm, accomplishes that diligent grab is grabbed less, is sufficiently mixed fiber.It is more to install SXFZ-103 types on porcupine opener additional
Function is anti-to roll instrument, makes the instrument to stop wanting cotton when measuring hired roughneck's rotating speed and being less than setting value, sheet cotton is wound so as to prevent hired roughneck
And break dirt rod and produce rope silk.A076 synthesis Beater Speed 800r/min, fan speed 950r/min, hired roughneck and pedal roller
Gauge 12mm；Lap roller speed 12r/min, reduce the gauge of porcupine hired roughneck and comprehensive hired roughneck's dirt rod and dirt rod.In production
Alginate fibre cotton rolling quantity is 380g/m, and lap length is 36m, and lap elongation is controlled in 0.5-2.5%.A076C types into
Install rove device on volume machine additional, 6 are added when coiled with the other rove of branch；
Install the intelligent Homogeneous assay method systems of conventional FLT600 on lapper additional, this Homogeneous assay method system is set simply, first
Lap design weight (including weight containing skewer) is input to " input area ", after the completion of click on monitoring display, second is finished after driving
After complete lap, cotton rolling weight is weighed up, " weight is adjusted soon " input lap actual measurement weight, point " confirmation " on display screen is clicked on and opens
Car, then the cotton rolling weight driven are exactly qualified volume.By this Homogeneous assay method system, lap just volume rate is high, can improve cotton rolling weight
Irregular, cotton rolling weight irregularity is can be controlled within 1%.It is another to be especially stressed that the lap thickness shown on display screen
Less than 5mm, otherwise this Homogeneous assay method system can fail.Unclear influence carded sliver matter is easily layered when moving back and scratching in cotton carding for lap
Amount, thus install rove device additional on blowing, 6 are added when coiled with the other rove of branch, and increase the pressure of calender roller.
Alginate fibre carding process：
2) alginate fibre carding step
Due to alginate fibre strength too low, soft, fiber easy damaged and winding needle tooth during combing, therefore
Using big gauge, small noil, light quantitative, the abundant technological principle for shifting, suitably combing in technique.To reduce the damage of fiber
Wound, feed plate raise 5mm, cylinder speed 330r/min, licker-in speed 785r/min, doffer speed 19r/min, cover plate speed
87.3mm/min, cylinder and the English silk of licker-in gauge 7, feed plate and the English silk of licker-in gauge 14, cylinder and the English silk of doffer's gauge 4, are removed
Dirt knife up degree is put down with machine frame, 90 ° of the knife back and machine frame horizontal plane angle, 20-25 DEG C of temperature, humidity 55-65%；
To make cylinder and the pin between cog carding effect of cover plate two good, the operating angle and pin tooth of Bearded-needle knitted cloth selection of small are high
Degree, pin cloth model used：Bearded-needle knitted cloth AC2530*1550, flat-clothing JST-36, doffer's pin cloth AD4030*2080, licker-in tooth
Bar AT5010*06332VP.Conference is crossed due to weight of card sliver and blocks up horn mouth, quantitatively should not be too big.
3) mixing in doubling step
Because alginate fibre is more fluffy, carded sliver irregularity is bigger, alginate fibre on drafting with combed long staple cotton, thin
Suede sliver carry out and first passed through before closing together it is pre- simultaneously, the quantitative 19g/5 rice of pre- and dry weight, then by three draftings and close；Head is simultaneously adopted
With 6,3 alginate fibres, 2 combed long staple cotton bars and 1 combing fine fleece sliver simultaneously close；Head and the quantitative 17.5g/5 rice of dry weight,；
Two and 6 quantitative 17g/5 rice of root dry weight, three and 6 quantitative 16.8g/5 rice of root dry weight, Uster sliver control within 3.5%, temperature
Spend 20-25 DEG C, humidity 55-65%.
By together it is pre- simultaneously, three draftings and after closing, strip is easily overdone excessively rotten, is also easy to produce accidental faults and cotton knot,
Sliver exporting speed is reduced, ensures that horn mouth, circle of inclined tube thang-kng are slided, to ensure the smooth of shaping.
4) Roving Frames
Rove produces on A456C fly frames, because alginate fibre is longer, easily occurs leading inextensible phenomenon, in rove
Using big gauge, light quantitative, pressurization, low velocity, the technological principle of the big twist again in technique.Ensureing rove not harmful drafting
On the basis of, suitably increase roving twist factor, rove gauge suitably increases, and is advantageous to improve bar evenness, is moved back to reduce rove
Around when misdraft.Roving twist 5 twists with the fingers/10cm, and roller gauge uses 22mm × 42mm, 1.21 times of back area draft, jaw every
Away from 6mm, the quantification of 4.20g/10 rice of rove dry weight, 8 times of weight drafting multiple, 8.24 times of mechanical commutation draft, front roller rotating speed 180r/
Min, moisture regain 9%, weight in wet base 4.58g/10m, special number 9.8tex, twist factor 107, front roller diameter 28mm, pressing device winding number 2 enclose, ingot
Cap winding number 3/4 encloses, within Uster sliver 4.5%, 20-25 DEG C of temperature, humidity 55-65%.
And unskilled workman's sequence prevents that sliver, rove bar are scared, more small-bore horn mouth is used on drawing frame, compression sliver makes it
Closely, three and horn mouth 3.0mm, operation cleaning is separately strengthened, it is ensured that horn mouth and the cleaning of can coiler channel part, it is hairless
Perverse, wounded, product flower etc..Tension bracket is flexible on Roving Frames, tension in the roving will uniformly, it is strict control rove front row, heel row,
Large, medium and small yarn Roving Elongation and variance rate, rove elongation control is within 1.2%, variance rate control is within 0.5%.
5) spinning process
In order to reduce details, the generation of filoplume is reduced, spinning process suitably increases back zone drafting multiple, the relatively low palm of ingot speed
Hold, and preferred ring-traveller.Spun yarn uses moderate coefficient of twist, 46.7 times of spinning process total draft multiple, weight drafting multiple
47.5 times, 49 times of mechanical commutation draft multiple, roller gauge is 17mm × 40mm, and back zone drafting multiple is 1.2 times, nip gauge
2.5mm, front roller diameter 25mm, spindle rotating speed 14000r/min, motor rotary speed the 1460r/min twist 121 twists with the fingers/10cm, twist with the fingers system
Number 380, rings model PG2/13851, wire loop model OSS120,20-25 DEG C of temperature, humidity 55-65%；
6) winding procedure
In order to reduce formation yarn nep and filoplume, produced on the automatic winder in Japanese village field alginate fibre and long-staple cotton,
Medium staple cotton blended high-grade stocking yarn.Effectively removed without knot technology, guarantee yarn defect using Wu Site electronic yarn clearers and empty twist with the fingers.
Because the yarn of production is more smooth, when being knotted on automatic winder, tieing easily slips, therefore increases on automatic winder
Conventional supercharging device, ensure stable gas pressure, so as to ensure tieing quality.Produced on automatic winder, using electronic clearing
Device and empty sth. made by twisting are without knot technology, electronic yarn clearer parameter：NSL1：350%0.4cm, NSL2：130%1.3cm, NSL3：100%4cm, NSL4：
25%100cm, T1：- 46%3.6cm, T2：- 38%9.5cm, T3：- 17%140cm, 20-25 DEG C of 55-65% of humiture are raw
Thin the high-grade knitted of (50/30/20) 9.8tex of output HZ/J length/J uses yarn.
Claims (7)
1. a kind of method of alginate fibre and combing medium staple cotton, combed long staple cotton blending production knitting yarn, it is characterised in that：
Alginate fibre：It is dry fracture strength 1.6CN/dtex, wet breaking strength 1.1CN/dtex, dry elongation at break 10.3%, wet
Elongation at break 16.8%, line density 1.7dtex, length 38mm, regain 9.7%；
Combed long staple cotton fiber：2.0 grades of grade of distributing cotton, principal length 37.1mm, beam fibre fracture strength 43.0CN/tex, fineness
1.35dtex, below 16mm short fiber content are 22%, regain 9.44%, percentage of impurity 3.6%；
Combing fine fleece cotton fiber：2.5 grades of grade of distributing cotton, principal length 29.2mm, fracture strength 28.8CN/tex, fineness
1.69dtex, below 16mm short fiber content are 15.8%, regain 9.67%, percentage of impurity 2%；
Alginate fibre through blowing, cotton carding, it is pre- and after on drawing frame with medium staple cotton, long-staple cotton yarn and closing, then through rove, thin
Yarn, winding procedure produce cylinder yarn, and blending rate is marine alga/combed long staple cotton fiber/combing fine fleece cotton fiber 50/30/20；It is raw
Production comprises the following steps that：
1) alginate fibre cotton cleaning process
Griping cotton machine hired roughneck's decrease speed each 3mm, rotating speed 960r/min, rotary machinery speed 2.8r/min, blade stretch out rib
3mm, Beater Speed 800r/min, fan speed 950r/min, the gauge 12mm of hired roughneck and pedal roller, 20-25 DEG C of temperature,
Humidity 55-65%；Lap roller speed 12r/min, alginate fibre cotton rolling quantity is 380g/m in production, and lap length is 36m.
Install rove device additional on blowing, 6 are added when coiled with the other rove of branch；
2) alginate fibre carding step
Feed plate raises 5mm, cylinder speed 330r/min, licker-in speed 785r/min, doffer speed 19r/min, cover plate speed
87.3mm/min, cylinder and the English silk of licker-in gauge 7, feed plate and the English silk of licker-in gauge 14, cylinder and the English silk of doffer's gauge 4, are removed
Dirt knife up degree flushes with machine frame, 90 ° of the mote knife knife back and machine frame horizontal plane angle, 20-25 DEG C of temperature, humidity 55-65%；
3) mixing in doubling step
Alginate fibre first passes through one in advance simultaneously, the quantitative 19g/5 rice of pre- and dry weight, then by three draftings and closes；Head and using 6
Root, 3 alginate fibres, 2 combed long staple cotton bars and 1 combing fine fleece sliver simultaneously close；Head and the quantitative 17.5g/5 rice of dry weight；Two and 6
The quantitative 17g/5 rice of root dry weight, three and 6 quantitative 16.8g/5 rice of root dry weight, Uster sliver control within 3.5%, humiture
20-25 DEG C of 55-65%；
4) Roving Frames
Roving twist 5 twists with the fingers/10cm, and roller gauge uses 22mm × 42mm, and 1.21 times of back area draft, nip gauge 6mm, rove is done
Big ration is 4.20g/10 rice, 8 times of weight drafting multiple, 8.24 times of mechanical commutation draft, front roller rotating speed 180r/min, moisture regain 9%,
Weight in wet base 4.58g/10m, special number 9.8tex, twist factor 107, front roller diameter 28mm, pressing device winding number 2 enclose, and spindle top winding number 3/4 encloses,
Within Uster sliver 4.5%, 20-25 DEG C of 55-65% of humiture；
5) spinning process
46.7 times of total draft multiple, 47.5 times of weight drafting multiple, 49 times of mechanical commutation draft multiple, roller gauge be 17mm ×
40mm, back zone drafting multiple are 1.2 times, nip gauge 2.5mm, front roller diameter 25mm, spindle rotating speed 14000r/min, motor
The rotating speed 1460r/min twists 121 twist with the fingers/10cm, twist factor 380, rings model PG2/13851, wire loop model OSS120,
20-25 DEG C of temperature, humidity 55-65%；
6) winding procedure
Produced on automatic winder, using electronic yarn clearer and empty sth. made by twisting without knot technology, electronic yarn clearer parameter：NSL1：350%0.4cm,
NSL2：130%1.3cm, NSL3：100%4cm, NSL4：25%100cm, T1：- 46%3.6cm, T2：- 38%9.5cm, T3：-
17%140cm, 20-25 DEG C of temperature, humidity 55-65%, produce the high-grade knitted of thin (50/30/20) 9.8tex of HZ/J length/J
Use yarn.
2. a kind of alginate fibre according to claim 1 and combing medium staple cotton, combed long staple cotton blending production knitting yarn
Method, it is characterised in that：Alginate fibre cotton carding production line using A002C types automatic plucker, A036B porcupine openers,
A092A types tandem feeder, A076C types lapper and A186D carding machines.
3. a kind of alginate fibre according to claim 2 and combing medium staple cotton, combed long staple cotton blending production knitting yarn
Method, it is characterised in that：Installed additional in alginate fibre cotton cleaning process, on porcupine opener SXFZ-103 types it is multi-functional it is anti-roll instrument,
Install the intelligent Homogeneous assay method systems of FLT600 on lapper additional.
4. a kind of alginate fibre according to claim 1 and combing medium staple cotton, combed long staple cotton blending production knitting yarn
Method, it is characterised in that：The production line of cotton is using A002C types automatic plucker, A035C mixed cotton slitters, A036B porcupine openers
Machine, A092A types tandem feeder, A076C types lapper and A186D carding machines.
5. a kind of alginate fibre according to claim 1 or 4 is used with combing medium staple cotton, combed long staple cotton blending production knitting
The method of yarn, it is characterised in that：Combing process is using double combings, double combing flows：FA317A drawing frames
Once it is pre- simultaneously, FA356 bars and roll up joint, FA266 combing machines, FA317A drawing frames second in advance simultaneously, FA356 bars and roll up joint,
FA266 combing.
6. a kind of alginate fibre according to claim 2 and combing medium staple cotton, combed long staple cotton blending production knitting yarn
Method, it is characterised in that：Install rove device additional on A076 type lappers, 6 are added when coiled with the other rove of branch, and add
The pressure of big calender roller.
7. a kind of alginate fibre according to claim 1 and combing medium staple cotton, combed long staple cotton blending production knitting yarn
Method, it is characterised in that：The operating angle of Bearded-needle knitted cloth selection of small and pin tooth height, pin used in alginate fibre carding step
Cloth model：Bearded-needle knitted cloth AC2530*1550, flat-clothing JST-36, doffer's pin cloth AD4030*2080, taker-in roller wire AT5010*
06332VP。