CN108840566A - Red glaze of low temperature and preparation method thereof - Google Patents
Red glaze of low temperature and preparation method thereof Download PDFInfo
- Publication number
- CN108840566A CN108840566A CN201810938050.2A CN201810938050A CN108840566A CN 108840566 A CN108840566 A CN 108840566A CN 201810938050 A CN201810938050 A CN 201810938050A CN 108840566 A CN108840566 A CN 108840566A
- Authority
- CN
- China
- Prior art keywords
- glaze
- low temperature
- oxide
- component
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses red glaze of a kind of low temperature and preparation method thereof, the component and each component mass percent that glaze used in the red glaze of low temperature contains are as follows:Silica 65%, aluminum oxide 20%, di-iron trioxide 0.05%, potassium oxide 2.8%, sodium oxide molybdena 2.3%, magnesia 0.14%, calcium oxide 0.3%, selenium 6%, titanium oxide 0.01%, remaining is inevitable impurity, amounts to 100%.The present invention can substantially reduce the coefficient of expansion of glaze, thus the phenomenon that making the coefficient of expansion of glaze and base match, prevent stripping glaze.
Description
Technical field
The present invention relates to red glaze of a kind of low temperature and preparation method thereof.
Background technique
Currently, ceramic colour glaze is mainly some nonferrous metal oxides, salt or double salt, there are many color glaze because of high-temperature calcination meeting
Decompose eclipsed, and can only quality at low temperature, therefore be referred to as low temperature color glaze, at present the decorated technique of ceramic utensil
Afterwards, glaze paint is bright and color is scarlet, only the red yellow glaze of low temperature.However the red glaze firing temperature of low temperature is at 750-950 DEG C, herein
At a temperature of allow ceramic body must first grand feu, then carry out the decoration of the red glaze of low temperature, but will appear new problem again at the same time
I.e. ceramics shell glaze during firing, cause defect.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of red glaze of low temperature is provided, it can be with
The coefficient of expansion of glaze is substantially reduced, thus the phenomenon that making the coefficient of expansion of glaze and base match, prevent stripping glaze.
In order to solve the above technical problems, the technical scheme is that:A kind of red glaze of low temperature, glaze used in it contain
Some components and each component mass percent are as follows:Silica 65%, aluminum oxide 20%, di-iron trioxide 0.05%,
Potassium oxide 2.8%, sodium oxide molybdena 2.3%, magnesia 0.14%, calcium oxide 0.3%, selenium 6%, titanium oxide 0.01%, remaining is not
Evitable impurity amounts to 100%.
The present invention also provides a kind of preparation method of the red glaze of low temperature, the step of method contains, is as follows:
S1:It stocks up according to each component and each component mass parts of glaze:
S2:By material:Ball:Mass ratio=1 of water:1.75:1.5, wet ball grinding 19~21 hours;
S3:After glaze after ball milling is sieved and removes iron, then it is tuned into the glaze slip of 45~60 Baume degrees of concentration;
S4:After the green body for taking appearance bright and clean immerses the glaze slip, then it is fired under 750 DEG C -950 DEG C of oxidizing atmosphere
Product.
After above-mentioned technical proposal, the basic anhydride of low molecular weight are added in the present invention, by with the ratio between molecular number
Replace high molecular weight to aoxidize flux, actually also correspondingly improve the content of silica in this way, the content of silica improves
The coefficient of expansion of glaze can be substantially reduced, thus the phenomenon that making the coefficient of expansion of glaze and base match, prevent stripping glaze.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
A kind of red glaze of low temperature, the component and each component mass percent that glaze used in it contains are as follows:Silica
65%, aluminum oxide 20%, di-iron trioxide 0.05%, potassium oxide 2.8%, sodium oxide molybdena 2.3%, magnesia 0.14%, oxygen
Change calcium 0.3%, selenium 6%, titanium oxide 0.01%, remaining is inevitable impurity, amounts to 100%.
The step of preparation method of the red glaze of the low temperature, method contains, is as follows:
S1:It stocks up according to each component and each component mass parts of glaze:
S2:By material:Ball:Mass ratio=1 of water:1.75:1.5, wet ball grinding 19~21 hours;
S3:After glaze after ball milling is sieved and removes iron, then it is tuned into the glaze slip of 45~60 Baume degrees of concentration;
S4:After the green body for taking appearance bright and clean immerses the glaze slip, then it is fired under 750 DEG C -950 DEG C of oxidizing atmosphere
Product.
The red glaze of the low temperature that the present embodiment is prepared passes through it has been observed that the phenomenon that shelling glaze does not occur in its glaze paint, reaches
Desired effect.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of red glaze of low temperature, it is characterised in that:The component and each component mass percent that glaze used in it contains are as follows:
Silica 65%, aluminum oxide 20%, di-iron trioxide 0.05%, potassium oxide 2.8%, sodium oxide molybdena 2.3%, magnesia
0.14%, calcium oxide 0.3%, selenium 6%, titanium oxide 0.01%, remaining is inevitable impurity, amounts to 100%.
2. a kind of preparation method of the red glaze of low temperature as described in claim 1, it is characterised in that the step of method contains is as follows:
S1:It stocks up according to each component and each component mass parts of glaze:
S2:By material:Ball:Mass ratio=1 of water:1.75:1.5, wet ball grinding 19~21 hours;
S3:After glaze after ball milling is sieved and removes iron, then it is tuned into the glaze slip of 45~60 Baume degrees of concentration;
S4:After the green body for taking appearance bright and clean immerses the glaze slip, finished product then is fired under 750 DEG C -950 DEG C of oxidizing atmosphere.