CN108823614A - 镀锌液 - Google Patents
镀锌液 Download PDFInfo
- Publication number
- CN108823614A CN108823614A CN201810689397.8A CN201810689397A CN108823614A CN 108823614 A CN108823614 A CN 108823614A CN 201810689397 A CN201810689397 A CN 201810689397A CN 108823614 A CN108823614 A CN 108823614A
- Authority
- CN
- China
- Prior art keywords
- brightener
- chloride
- organic solvent
- galvanizing flux
- softening agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镀锌液，其所述镀锌液中的每升溶液中含氯化锌60‑70g、氯化铵280‑360g、氯化钾30‑35g、氢氧化钠30‑38g、三乙醇胺55‑65g、硼酸28‑30g、有机溶剂15‑20ml、柔软剂1‑2g、主光亮剂5‑8ml、辅光亮剂20‑25ml，其于为水；所述主光亮剂为苄叉丙酮50‑100mg/L、苯甲酸钠200‑250mg/L、烟酸5‑10mg/L和壬基酚聚氧乙烯醚10‑20mg/L；所述辅助光亮剂为咪唑丙氧基缩合40‑90mg/L；所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧或氯化铈；所述有机溶剂为乙醇、丁醚、乙二醇甲醚任一或其组合，镀锌后的镀件镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；降低了镀厚的镀锌层时，镀锌层产生脆性，镀层厚度厚。
Description
技术领域
本发明属于电镀液，具体地说是涉及一种镀锌液。
背景技术
为了进一步提高某些特定加工件的钝化能力、良好的化学稳定性以及发光能力，进一步满足加工件的美观效果和防护目的，会在加工件的外表面镀上镀层，传统镀液采用铜、镍及铬类的金属镀液，这些重金属不仅会产生很大的污染，同时生产过程中产生的废水也很难处理，镀膜完成后的镀层耐磨能力较差。
发明内容
本发明的目的是提供一种镀锌液，其既能达到镜面光亮的效果，又能防止镀层变色，克服传统镀液采用铜、镍及铬类的金属镀液产生很大的污染的问题。
为解决上述技术问题，本发明的目的是这样实现的：
一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌60-70g、氯化铵280-360g、氯化钾30-35g、氢氧化钠30-38g、三乙醇胺55-65g、硼酸28-30g、有机溶剂15-20ml、柔软剂1-2g、主光亮剂5-8ml、辅光亮剂20-25ml，其于为水；
所述主光亮剂为苄叉丙酮50-100mg/L、苯甲酸钠200-250mg/L、烟酸5-10mg/L和壬基酚聚氧乙烯醚10-20mg/L；
所述辅助光亮剂为咪唑丙氧基缩合40-90mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧或氯化铈；
所述有机溶剂为乙醇、丁醚、乙二醇甲醚任一或其组合。
在上述方案的基础上并作为上述方案的优选方案：所述每升镀锌液中的pH为6.5。
在上述方案的基础上并作为上述方案的优选方案：所述主光亮剂为苄叉丙酮60-90mg/L、苯甲酸钠210-240mg/L、烟酸6-8mg/L和壬基酚聚氧乙烯醚12-18mg/L，所述辅助光亮剂为咪唑丙氧基缩合45-80mg/L。
在上述方案的基础上并作为上述方案的优选方案：一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌60g、氯化铵280g、氯化钾30g、氢氧化钠30g、三乙醇胺55g、硼酸28g、有机溶剂15ml、柔软剂1g、主光亮剂5ml、辅光亮剂20ml，其于为水；
所述主光亮剂为苄叉丙酮50mg/L、苯甲酸钠200mg/L、烟酸5mg/L和壬基酚聚氧乙烯醚10mg/L；
所述辅助光亮剂为咪唑丙氧基缩合40mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧；
所述有机溶剂为乙醇。
在上述方案的基础上并作为上述方案的优选方案：一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌70g、氯化铵360g、氯化钾35g、氢氧化钠38g、三乙醇胺65g、硼酸30g、有机溶剂20ml、柔软剂2g、主光亮剂8ml、辅光亮剂25ml，其于为水；
所述主光亮剂为苄叉丙酮100mg/L、苯甲酸钠250mg/L、烟酸10mg/L和壬基酚聚氧乙烯醚20mg/L；
所述辅助光亮剂为咪唑丙氧基缩合90mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化铈；
所述有机溶剂为乙醇、丁醚其组合。
本发明相比现有技术突出且有益的技术效果是：镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；
含有稀土添加剂，从而改善了镀液的分散能力，使镀液的电流密度工作范围得到提高，同时稀土添加的加入也使电流密度的分布更加均匀，降低了氢气析出，从而避免了镀厚的镀锌层时，镀锌层产生脆性；
机溶剂的加入降低了镀锌液的表面张力，帮助氢气从工件表面快速离开，降低了氢气的析出及加快了氢气的脱离，从而使镀锌层的脆性及工件的“氢脆”问题得到有效遏制，从而可以得到厚的镀锌层。
具体实施方式
为使本申请的目的、技术方案和优点更加清楚，下面将结合实施例,对技术方案进行清楚、完整地描述，
实施例一
一种镀锌液，镀锌液中的每升溶液中含氯化锌60g、氯化铵280g、氯化钾30g、氢氧化钠30g、三乙醇胺55g、硼酸28g、有机溶剂15ml、柔软剂1g、主光亮剂5ml、辅光亮剂20ml，其于为水；
主光亮剂为苄叉丙酮50mg/L、苯甲酸钠200mg/L、烟酸5mg/L和壬基酚聚氧乙烯醚10mg/L；
辅助光亮剂为咪唑丙氧基缩合40mg/L；
柔软剂为稀土添加剂，该稀土添加剂为氯化镧；
有机溶剂为乙醇。
每升镀锌液中的pH为6.5。
镀锌后的镀件镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；降低了镀厚的镀锌层时，镀锌层产生脆性，镀层厚度厚。
实施例二
一种镀锌液，镀锌液中的每升溶液中含氯化锌60-70g、氯化铵300g、氯化钾32g、氢氧化钠34g、三乙醇胺60g、硼酸29g、有机溶剂18ml、柔软剂1.5g、主光亮剂7ml、辅光亮剂22.5ml，其于为水；
所述主光亮剂为苄叉丙酮75mg/L、苯甲酸钠225mg/L、烟酸7.5mg/L和壬基酚聚氧乙烯醚15mg/L；
所述辅助光亮剂为咪唑丙氧基缩合65mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧；
所述有机溶剂为乙二醇甲醚。
每升镀锌液中的pH为6.5。
镀锌后的镀件镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；降低了镀厚的镀锌层时，镀锌层产生脆性，镀层厚度厚。
实施例三
一种镀锌液，镀锌液中的每升溶液中含氯化锌70g、氯化铵360g、氯化钾35g、氢氧化钠38g、三乙醇胺65g、硼酸30g、有机溶剂20ml、柔软剂2g、主光亮剂8ml、辅光亮剂25ml，其于为水；
所述主光亮剂为苄叉丙酮100mg/L、苯甲酸钠250mg/L、烟酸10mg/L和壬基酚聚氧乙烯醚20mg/L；
所述辅助光亮剂为咪唑丙氧基缩合90mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化铈；
所述有机溶剂为乙醇、丁醚其组合。
镀锌后的镀件镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；降低了镀厚的镀锌层时，镀锌层产生脆性，镀层厚度厚。
实施例四
一种镀锌液，镀锌液中的每升溶液中含氯化锌60g、氯化铵280g、氯化钾30g、氢氧化钠30g、三乙醇胺55g、硼酸28g、有机溶剂15ml、柔软剂1g、主光亮剂5ml、辅光亮剂20ml，其于为水；
主光亮剂为苄叉丙酮50mg/L、苯甲酸钠200mg/L、烟酸5mg/L和壬基酚聚氧乙烯醚10mg/L；
辅助光亮剂为咪唑丙氧基缩合40mg/L；
柔软剂为稀土添加剂，该稀土添加剂为氯化镧；
有机溶剂为乙醇、丁醚、乙二醇甲醚三者混合。
每升镀锌液中的pH为6.5。
镀锌后的镀件镜面光亮的效果好、其抗腐蚀性能较好、镀液的深镀能力强、镀膜具有优良的耐磨能力；降低了镀厚的镀锌层时，镀锌层产生脆性，镀层厚度厚。
上述实施例仅为本发明的较佳实施例，并非依此限制本发明的保护范围，故：凡依本发明的结构、形状、原理所做的等效变化，均应涵盖于本发明的保护范围之内。
Claims (5)
1.一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌60-70g、氯化铵280-360g、氯化钾30-35g、氢氧化钠30-38g、三乙醇胺55-65g、硼酸28-30g、有机溶剂15-20ml、柔软剂1-2g、主光亮剂5-8ml、辅光亮剂20-25ml，其于为水；
所述主光亮剂为苄叉丙酮50-100mg/L、苯甲酸钠200-250mg/L、烟酸5-10mg/L和壬基酚聚氧乙烯醚10-20mg/L；
所述辅助光亮剂为咪唑丙氧基缩合40-90mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧或氯化铈；
所述有机溶剂为乙醇、丁醚、乙二醇甲醚任一或其组合。
2.根据权利要求1所述的一种镀锌液，其特征在于：所述每升镀锌液中的pH在6.5范围内。
3.根据权利要求1所述的一种镀锌液，其特征在于：所述主光亮剂为苄叉丙酮60-90mg/L、苯甲酸钠210-240mg/L、烟酸6-8mg/L和壬基酚聚氧乙烯醚12-18mg/L，所述辅助光亮剂为咪唑丙氧基缩合45-80mg/L。
4.根据权利要求1所述的一种镀锌液，其特征在于：一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌60g、氯化铵280g、氯化钾30g、氢氧化钠30g、三乙醇胺55g、硼酸28g、有机溶剂15ml、柔软剂1g、主光亮剂5ml、辅光亮剂20ml，其于为水；
所述主光亮剂为苄叉丙酮50mg/L、苯甲酸钠200mg/L、烟酸5mg/L和壬基酚聚氧乙烯醚10mg/L；
所述辅助光亮剂为咪唑丙氧基缩合40mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化镧；
所述有机溶剂为乙醇。
5.根据权利要求1所述的一种镀锌液，其特征在于：一种镀锌液，其特征在于：所述镀锌液中的每升溶液中含氯化锌70g、氯化铵360g、氯化钾35g、氢氧化钠38g、三乙醇胺65g、硼酸30g、有机溶剂20ml、柔软剂2g、主光亮剂8ml、辅光亮剂25ml，其于为水；
所述主光亮剂为苄叉丙酮100mg/L、苯甲酸钠250mg/L、烟酸10mg/L和壬基酚聚氧乙烯醚20mg/L；
所述辅助光亮剂为咪唑丙氧基缩合90mg/L；
所述柔软剂为稀土添加剂，该稀土添加剂为氯化铈；
所述有机溶剂为乙醇、丁醚其组合。