CN108815567A - A kind of preparation method of antiseptic dressing aquagel - Google Patents
A kind of preparation method of antiseptic dressing aquagel Download PDFInfo
- Publication number
- CN108815567A CN108815567A CN201810566933.5A CN201810566933A CN108815567A CN 108815567 A CN108815567 A CN 108815567A CN 201810566933 A CN201810566933 A CN 201810566933A CN 108815567 A CN108815567 A CN 108815567A
- Authority
- CN
- China
- Prior art keywords
- aquagel
- solution
- preparation
- chitosan
- antiseptic dressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of antiseptic dressing aquagel, specifically include following steps:Chitosan is dissolved in obtained solution A in acetum first, Tween 80 is dissolved in obtained solution B in petroleum ether, solution A is added drop-wise in solution B and is stirred, and glutaraldehyde solution is added dropwise, chitosan porous microsphere is made;Then surface being carried out to chitosan porous microsphere using dopamine hydrochloride to be modified, being then modified using acrylic ester monomer, aquagel is made.This method is easy to operate, and aquagel stability obtained is good, and anti-microbial property is excellent.
Description
Technical field:
The present invention relates to field of medical materials, are specifically related to a kind of preparation side of antiseptic dressing aquagel
Method.
Background technique:
A kind of net high-polymer swelling body containing large quantity of moisture that aerogel dressing is made of water-insoluble polymer,
With good water imbibition, when contacting aquation repeatedly can occur for hydrogel and the surface of a wound, have and provide moisture to the surface of a wound and inhale
The dual function for receiving sepage is a kind of current clinically used Medical dressing.
Traditional aerogel dressing has absorbable wound fluid, keeps the surface of a wound wet, reduces scar and is formed, promotes wound
It the advantages that mouth healing, has been to be concerned by more and more people.Especially suitable for the protecting wound surfaces such as wound, scald, burn and treatment.This
A little aerogel dressing products are generally thicker, and antibacterial effect is less desirable, and stability is poor.
Summary of the invention:
The object of the present invention is to provide a kind of preparation method of antiseptic dressing aquagel, this method operation letters
Single, aquagel stability obtained is good, and anti-microbial property is excellent.
To achieve the above object, the present invention uses following technical scheme:
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in acetum, obtained solution A, Tween 80 is dissolved in obtained solution B in petroleum ether;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
Glutaraldehyde solution is added dropwise into lotion and stirs 3-6h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1-2h, after reaction plus
Enter acrylic ester monomer, initiator is to slowly warm up to 60-70 DEG C of reaction 30-50min, is cooled to room temperature after reaction, room
Temperature is placed 3-4 days, and aquagel is made.
As a preferred embodiment of the above technical solution, in step (1), the mass concentration of the acetum is 15-20%.
As a preferred embodiment of the above technical solution, in step (1), the mass ratio of chitosan and acetum is 1:(20-30).
As a preferred embodiment of the above technical solution, Tween 80 in step (1), petroleum ether volume ratio be 1:(20-40).
As a preferred embodiment of the above technical solution, in step (1), chitosan, Tween 80 mass ratio be 1:(0.013-
0.015)。
As a preferred embodiment of the above technical solution, in step (2), the mass concentration of the glutaraldehyde solution is 5%, and molten
The volume ratio of liquid A is 3:(10-20).
As a preferred embodiment of the above technical solution, in step (3), the chitosan porous microsphere, dopamine hydrochloride, three hydroxyls
Aminomethane, acrylic ester monomer mass ratio be 5:(0.2-0.6):0.01:(1-2).
As a preferred embodiment of the above technical solution, in step (3), the acrylic ester monomer is acrylic acid, metering system
One of acid, ethyl acrylate or a variety of mixing.
As a preferred embodiment of the above technical solution, the dosage of the initiator is the 1%-3% of acrylic ester monomer quality.
The invention has the advantages that:
The method comprises the steps of firstly, preparing chitosan microballs, good dispersion, have certain anti-microbial property, and have the effect of hemostasis
Fruit, in order to improve its mechanical property, poly-dopamine is modified its surface by the present invention first, so that poly-dopamine is grafted on
The surface of chitosan microball effectively improves its mechanical property under the premise of not influencing chitosan anti-bacteria performance, in order into one
Step improves the water absorbing properties of hydrogel material, and the present invention is further modified it using acrylic ester monomer, water-setting obtained
Glue stability is good, and anti-microbial property is excellent.
Specific embodiment:
In order to better understand the present invention, below by embodiment, the present invention is further described, and embodiment is served only for solving
The present invention is released, any restriction will not be constituted to the present invention.
Embodiment 1
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 15%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:20:0.013;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 3h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1h, be added after reaction
Acrylic ester monomer, initiator are to slowly warm up to 60-70 DEG C of reaction 30min, are cooled to room temperature after reaction, room temperature is put
It sets 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane, third
The mass ratio of olefin(e) acid esters monomer is 5:0.2:0.01:1.
Embodiment 2
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 20%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:30:0.015;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 6h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 2h, be added after reaction
Acrylic ester monomer, initiator are to slowly warm up to 60-70 DEG C of reaction 50min, are cooled to room temperature after reaction, room temperature is put
It sets 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane, third
The mass ratio of olefin(e) acid esters monomer is 5:0.6:0.01:2.
Embodiment 3
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 16%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:22:0.0135;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 3.5h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1.2h, after reaction plus
Enter acrylic ester monomer, initiator is to slowly warm up to 60-70 DEG C of reaction 35min, is cooled to room temperature after reaction, room temperature
It places 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane,
The mass ratio of acrylic ester monomer is 5:0.3:0.01:1.2.
Embodiment 4
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 17%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:24:0.014;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 4h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1.4h, after reaction plus
Enter acrylic ester monomer, initiator is to slowly warm up to 60-70 DEG C of reaction 40min, is cooled to room temperature after reaction, room temperature
It places 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane,
The mass ratio of acrylic ester monomer is 5:0.4:0.01:1.4.
Embodiment 5
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 18%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:26:0.014;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 4.5h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1.6h, after reaction plus
Enter acrylic ester monomer, initiator is to slowly warm up to 60-70 DEG C of reaction 40min, is cooled to room temperature after reaction, room temperature
It places 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane,
The mass ratio of acrylic ester monomer is 5:0.5:0.01:1.6.
Embodiment 6
A kind of preparation method of antiseptic dressing aquagel, includes the following steps:
(1) chitosan is dissolved in the acetum that mass concentration is 18%, Tween 80 is dissolved in petroleum by obtained solution A
Obtained solution B in ether;Wherein, the mass ratio of chitosan and acetum, Tween 80 is 1:28:0.0145;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made,
The glutaraldehyde solution that mass concentration is 5% is added dropwise into lotion and stirs 5.5h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, is then added more
Bar amine hydrochlorate, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1.8h, after reaction plus
Enter acrylic ester monomer, initiator is to slowly warm up to 60-70 DEG C of reaction 45min, is cooled to room temperature after reaction, room temperature
It places 3-4 days, aquagel is made;Wherein, chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane,
The mass ratio of acrylic ester monomer is 5:0.5:0.01:1.8.
Anti-bacterial hydrogel stability produced by the present invention is good, is up to the bacteriostasis rate of Escherichia coli and staphylococcus aureus
98.9% or more.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of preparation method of antiseptic dressing aquagel, which is characterized in that include the following steps:
(1) chitosan is dissolved in acetum, obtained solution A, Tween 80 is dissolved in obtained solution B in petroleum ether;
(2) solution A is added drop-wise in solution B, continues to stir 30min after agitation and dropping when being added dropwise, lotion is made, to cream
Glutaraldehyde solution is added dropwise in liquid and stirs 3-6h, filters, it is dry, chitosan porous microsphere is made;
(3) chitosan porous microsphere obtained above is dispersed in deionized water and is dispersed with stirring uniformly, dopamine is then added
Hydrochloride, trishydroxymethylaminomethane are added dropwise ammonium hydroxide and adjust pH value of solution to 8-9, be stirred to react 1-2h, third is added after reaction
Olefin(e) acid esters monomer, initiator are to slowly warm up to 60-70 DEG C of reaction 30-50min, are cooled to room temperature after reaction, room temperature is put
It sets 3-4 days, aquagel is made.
2. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(1) in, the mass concentration of the acetum is 15-20%.
3. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(1) in, the mass ratio of chitosan and acetum is 1:(20-30).
4. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(1) Tween 80 in, petroleum ether volume ratio be 1:(20-40).
5. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(1) in, chitosan, Tween 80 mass ratio be 1:(0.013-0.015).
6. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(2) in, the mass concentration of the glutaraldehyde solution is 5%, and the volume ratio with solution A is 3:(10-20).
7. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(3) in, the chitosan porous microsphere, dopamine hydrochloride, trishydroxymethylaminomethane, acrylic ester monomer mass ratio
It is 5:(0.2-0.6):0.01:(1-2).
8. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:Step
(3) in, the acrylic ester monomer is one of acrylic acid, methacrylic acid, ethyl acrylate or a variety of mixing.
9. a kind of preparation method of antiseptic dressing aquagel as described in claim 1, it is characterised in that:It is described to draw
The dosage for sending out agent is the 1%-3% of acrylic ester monomer quality.