CN1087995C - 低固含量免清洗助焊剂 - Google Patents

低固含量免清洗助焊剂 Download PDF

Info

Publication number
CN1087995C
CN1087995C CN97106056A CN97106056A CN1087995C CN 1087995 C CN1087995 C CN 1087995C CN 97106056 A CN97106056 A CN 97106056A CN 97106056 A CN97106056 A CN 97106056A CN 1087995 C CN1087995 C CN 1087995C
Authority
CN
China
Prior art keywords
scaling powder
present
low solid
ethanol
benzotriazole
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN97106056A
Other languages
English (en)
Other versions
CN1209374A (zh
Inventor
李圣波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN97106056A priority Critical patent/CN1087995C/zh
Publication of CN1209374A publication Critical patent/CN1209374A/zh
Application granted granted Critical
Publication of CN1087995C publication Critical patent/CN1087995C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种低固含量助焊剂，它主要由以下原料及重量份组成：己二酸10-20癸二酸5-10碳氟离子表面活性剂1-10苯骈三氮唑1-2单硬酸甘油脂0.1-1乙二醇单丁醚20-80乙酸丁脂10-50乳化剂OP-10 5-10快速渗透剂OT 2-10乙醇250-350：它以一般的常规生产工艺制备，其各项技术性能指标优于电子工业部，免清洗助焊机监测标准技术要求，并且价格低。

Description

低固含量免清洗助焊剂
技术领域：本发明涉及一种锡焊接助焊剂，特别是一种低固含量的免清洗助焊剂。
背景技术：近几十年来，在电子产品生产锡焊工艺过程中，一般多使用由松香、树脂、含卤化物的活性剂、添加剂和有机溶剂组成的松香树脂系助焊剂。这种助焊剂虽然可焊性好、成本低，但是，焊后残留物高。其残留物含有氯粒子，会逐步引起电气绝缘性能下降和短路迁移等问题。要解决这一问题，必须对电子印制板上的松香树脂系焊剂残留物进行清洗，不仅会增加生产成本，而且清洗松香树脂系焊剂残留物的清洗剂主要是氟氯烷化合物。这种化合物是大气臭氧层的损耗物质，属于禁用和被淘汰之列。因此，随着电子表面组装技术的迅速发展和需求，新型低固含量的免清洗助焊剂便应运而生。现有技术中的免清洗助焊剂一般质量较差，可焊性低，干燥度差，固含量高，焊后仍有残留，并且价格比较昂贵，有一定的毒性和气味，现有焊接设备也不通用。
发明内容：本发明的任务是提供一种高质量的低固含量助焊剂，这种助焊剂可焊性好，易干燥，固含量低，焊后无残留，无腐蚀，电气绝缘性能好，无毒性和气味，现有焊接设备通用，仅稍增部分设备即可，从而克服现有技术所存在的上述缺陷。其技术方案是：一、本发明助焊剂的配方，原料总量以1000重量份计，各种原料及重量份为：
己二酸                                      13-15
癸二酸                                      6-8
碳氟离子表面活性剂                          5-6
快速渗透剂OT                                4-6
乳化剂OP-10                                 5-10
苯骈三氮唑                            1-2
单硬脂酸甘油脂                        0.1-1
乙二醇单丁醚                          20-80
乙酸丁脂                              10-50
乙醇                                  250-350
异丙醇                                余量
优选的各原料及重量份为：
己二酸                                13-15
癸二酸                                6-8
碳氟离子表面活性剂                    5-6
快速渗透剂OT                          4-6
乳化剂OP-10                           6-8
苯骈三氮唑                            1-2
单硬脂酸甘油脂                        0.3-0.6
乙二醇单丁醚                          35-55
乙酸丁脂                              30-40
乙醇                                  300-350
异丙醇                               余量
二、本发明低固含量免清洗助焊剂的生产，可以采用一般的常规生产方法，其工艺步骤如下：
(1)将己二酸、癸二酸、苯骈三氮唑、单硬脂酸甘油脂加入乙醇中，再加入异丙醇、助溶剂乙二醇单丁醚、乙酸丁脂、乳化剂OP-10、快速渗透剂OT，以及碳氯离子表面活性剂；
(2)在60-80℃温度条件下搅拌，使原料充分溶解混合；
(3)过滤；
(4)沉淀：
(5)取上清液包装，即获得本发明免清洗助焊成品。
本发明低固含量免清洗助焊剂现已应用于大屏幕彩色投影电视机、彩色电视机和黑白电视机等电子印制板锡焊工艺，在PCB上润湿性好，扩展率≥85％，涂布均匀，可焊性好；固含量低，一般＜3.5％，可达到1.8％左右，
焊后表面干净，不留任何有损PCB和电子元器件的残留物质，无需清洗即可满足美国军标MIL-P-28809A对离子洁净度要求：离子污染度＜1.0ugNacl/cm2，通常在0.5ugNacl/cm2左右；干燥度好，无腐蚀，表面绝缘电阻高，焊接前后及温湿度交变试验的表面绝缘电阻≥3.0×1011Ω，各项技术性能指标优于电子工业部免清洗助焊剂暂行标准的技术要求，达到国际先进水平。另外，无毒性，无气味，其价格低，基本上相当于进口同类产品价格的三分之一，使用时，现有焊接设备可以通用，不需要更换，仅添置少许即可。
具体实施方式：实施例1：
原料配方(Kg)
碳氟离子表面活性剂                                1
快速渗透剂OT                                      2
乳化剂OP-10                                       10
己二酸                                            10
癸二酸                                            8
苯骈三氮唑                                        1
单硬脂酸甘油脂                                    0.1
乙二醇单丁醚                                      55
乙酸丁脂                                          20
乙醇                                              250
异丙醇                                            642.9
生产方法工艺步骤
(1)把乙醇倒入搪瓷反应釜，将己二酸、癸二酸、苯骈三氮唑和单硬脂酸甘油脂加入乙醇中，再加入异丙醇和助溶剂乙二醇单丁醚、乙酸丁脂、乳化剂OP-10、快速渗透剂OT以及碳氟离子表面活性剂；
(2)在60℃温度条件下，搅拌大体30分钟，使原料充分溶解；
(3)原料充分溶解后，用400目过滤网过滤；
(4)将过滤液置入塑料溶器中，沉淀24小时；
(5)取沉淀好的上清液，经包装，即制得本发明免清洗助焊剂。
上述制得的免清洗助焊剂无色，澄清透明，无刺激性气味，比重0.806g/m1，固含量1.8％，离子污染度0.5ugNacl/cm2，扩展率85％，焊后绝缘电阻4×1011Ω，腐蚀性、干燥度合格。
实施例2：
原料配方(Kg)
碳氟离子表面活性剂                            4
快速渗透剂OT                                  2
乳化剂OP-10                                   7
己二酸                                        15
癸二酸                                        5
苯骈三氮唑                                    1.5
单硬脂酸甘油脂                                0.5
乙二醇单丁醚                                  30
乙酸丁脂                                      10
乙醇                                          300
异丙醇                                        625
生产方法工艺步骤同实施例1，其中步骤(2)中温度为70℃，步骤(4)中沉淀时间为30小时。
该例制得的免清洗助焊剂，无色，澄清透明，无刺激性气味，比重0.8082g/ml，固含量2.0％，离子污染度＜0.7ugNacl/cm2，扩展率86％，焊后绝缘电阻3.5×1011Ω，腐蚀性、干燥度合格。
实施例3：
原料配方(Kg)
碳氟离子表面活性剂                             10
快速渗透剂OT                                   2
乳化剂OP-10                                    5
己二酸                                         20
癸二酸                                         5
苯骈三氮唑                                     2
单硬脂酸甘油脂                                1
乙二醇单丁醚                                  20
乙酸丁脂                                      40
乙醇                                          350
异丙醇                                        545
生产方法工艺步骤同实施例1，其中步骤(2)中温度为80℃，步骤(4)中沉淀时间为36小时。
该实施例制得的免清洗助焊剂，无色，澄清透明，无刺激性气味，比重0.8162g/ml，固含量2.5％，离子污染度＜1.0ugNacl/cm2，扩展率89％，焊后绝缘电阻3.0×1011Ω，腐蚀性、干燥度合格。

Claims (2)

1、一种低固含量免清洗助焊剂，其特征在于它的配方，原料总量以1000重量份计，各原料及重量份为：
己二酸                                        10-20
癸二酸                                        5-10
碳氟离子表面活性剂                            1-10
快速渗透剂OT                                  2-10
乳化剂OP-10                                   5-10
苯骈三氮唑                                    1-2
单硬脂酸甘油脂                                0.1-1
乙二醇单丁醚                                  20-80
乙酸丁脂                                      10-50
乙醇                                          250-350
异丙醇                                        余量
2、根据权利要求1所述的助焊剂，其特征在于各原料及重量份为：
己二酸                                        13-15
癸二酸                                        6-8
碳氟离子表面活性剂                             5-6
快速渗透剂OT                                  4-6
乳化剂OP-10                                   6-8
苯骈三氮唑                                    1-2
单硬脂酸甘油脂                                0.3-0.6
乙二醇单丁醚                                  35-55
乙酸丁脂                                      30-40
乙醇                                          300-350
异丙醇                                        余量
CN97106056A 1997-08-22 1997-08-22 低固含量免清洗助焊剂 Expired - Fee Related CN1087995C (zh)