CN108796895A - It is a kind of based on the tencel production technology for padding silkete penetrating agent - Google Patents
It is a kind of based on the tencel production technology for padding silkete penetrating agent Download PDFInfo
- Publication number
- CN108796895A CN108796895A CN201810640423.8A CN201810640423A CN108796895A CN 108796895 A CN108796895 A CN 108796895A CN 201810640423 A CN201810640423 A CN 201810640423A CN 108796895 A CN108796895 A CN 108796895A
- Authority
- CN
- China
- Prior art keywords
- clothes
- penetrating agent
- obtains
- tencel
- silkete penetrating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of based on the tencel production technology for padding silkete penetrating agent, includes the following steps：The first step bleaches tencel cotton cloth, obtains A clothes；Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；4th step carries out dyeing processing to C clothes, obtains D clothes；5th step carries out final finishing to D clothes, obtains finished product cloth.The invention enables tencel cotton cloths under the premise of ensure that even dyeing, the characteristics of also making it have good feel and style.
Description
Technical field
It is especially a kind of to be produced based on the tencel for padding silkete penetrating agent the present invention relates to a kind of tencel treatment process
Technique.
Background technology
Traditional tencel cotton cloth generally obtains the day of product after bleaching, half mercerising or double mercerized finish, dyeing and final finishing
Silk flosssilk wadding fabric.But existing tencel cotton face fabric, after half mercerization finish, the mercerization effect of the cotton in tencel cotton cloth is not
It is good, obtain color depth so as to cause tencel when dyeing, it is shallow that cotton obtains color, cloth cover occurs and dyes non-uniform phenomenon.Moreover, to color depth
Cloth when being dyed, the entirety colouring of cloth is shallower.When tencel cotton face fabric uses double mercerized finish process, cloth obtains color
Uniformly, but tencel feel is hardened, and is easily abraded, and its style loses pendency effect.Therefore, existing tencel cotton cloth is deposited
The problem of can not have both even dyeing and excellent handle and style.
Invention content
The object of the present invention is to provide a kind of based on the tencel production technology for padding silkete penetrating agent.The present invention makes
The characteristics of tencel cotton cloth is obtained under the premise of ensure that even dyeing, also makes it have good feel and style.
Technical scheme of the present invention：It is a kind of based on the tencel production technology for padding silkete penetrating agent, include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
Above-mentioned a kind of based in the tencel production technology for padding silkete penetrating agent, A clothes are padded in second step
Silkete penetrating agent processing detailed process be：First A clothes are put into the hopper for filling silkete penetrating agent solution and are impregnated, obtained
To b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B clothes.
Above-mentioned a kind of based in the tencel production technology for padding silkete penetrating agent, the temperature of stenter is 125-135
DEG C, the speed of stenter is 55-65m/min.
It is above-mentioned a kind of based in the tencel production technology for padding silkete penetrating agent, contain in the silkete penetrating agent solution
There is the silkete penetrating agent of a concentration of 5-8g/l.
Compared with prior art, the present invention has carried out padding silkete penetrating agent before to half mercerization finish of tencel cotton cloth
Processing, the permeability of mercerized cotton cloth is improved with this, is conducive to cellulose of the lye in subsequent processing to tencel cotton cloth
Intracapsular portion is permeated, and the swelling effect of fiber is promoted, to improve cotton mercerization effect so that tencel and cotton obtain in dyeing
Color is consistent, even dyeing, also improves color fastness, at the same also enable to dye color depth promotes 10-15%, saved dyestuff
Use.It is simple for process by tencel cotton cloth pad the processing of silkete penetrating agent, in no raising mercerising concentration
Under the premise of, it can either ensure even dyeing, and enable to fabric that there is good feel, moreover it is possible to original style be kept to imitate
Fruit.In conclusion invention makes tencel cotton cloth under the premise of ensure that even dyeing, also make it have good
Feel and style the characteristics of.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.It is a kind of based on the tencel production technology for padding silkete penetrating agent, include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
The detailed process that A clothes pad silkete penetrating agent processing in second step is：First A clothes are put into and fill mercerising
It is impregnated in the hopper of osmotic agent solution, obtains b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B
Cloth.
The temperature of stenter is 125-135 DEG C, and the speed of stenter is 55-65m/min.
Contain the silkete penetrating agent of a concentration of 5-8g/l in the silkete penetrating agent solution.
Embodiment 2.It is a kind of based on the tencel production technology for padding silkete penetrating agent, include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
The detailed process that A clothes pad silkete penetrating agent processing in second step is：First A clothes are put into and fill mercerising
It is impregnated in the hopper of osmotic agent solution, obtains b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B
Cloth.
The temperature of stenter is 125 DEG C, and the speed of stenter is 55m/min.
Contain the silkete penetrating agent of a concentration of 5g/l in the silkete penetrating agent solution.
Embodiment 3.It is a kind of based on the tencel production technology for padding silkete penetrating agent, include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
The detailed process that A clothes pad silkete penetrating agent processing in second step is：First A clothes are put into and fill mercerising
It is impregnated in the hopper of osmotic agent solution, obtains b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B
Cloth.
The temperature of stenter is 130 DEG C, and the speed of stenter is 60m/min.
Contain the silkete penetrating agent of a concentration of 6g/l in the silkete penetrating agent solution.
Embodiment 4.It is a kind of based on the tencel production technology for padding silkete penetrating agent, include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
The detailed process that A clothes pad silkete penetrating agent processing in second step is：First A clothes are put into and fill mercerising
It is impregnated in the hopper of osmotic agent solution, obtains b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B
Cloth.
The temperature of stenter is 135 DEG C, and the speed of stenter is 65m/min.
Contain the silkete penetrating agent of a concentration of 8g/l in the silkete penetrating agent solution.
Silkete penetrating agent be green allusion quotation refine company production silkete penetrating agent JNL.
Claims (4)
1. a kind of based on the tencel production technology for padding silkete penetrating agent, which is characterized in that include the following steps：
The first step bleaches tencel cotton cloth, obtains A clothes；
Second step carries out A clothes to pad silkete penetrating agent processing, obtains B clothes；
Third walks, and carries out half mercerization finish to B clothes, obtains C clothes；
4th step carries out dyeing processing to C clothes, obtains D clothes；
5th step carries out final finishing to D clothes, obtains finished product cloth.
2. according to claim 1 a kind of based on the tencel production technology for padding silkete penetrating agent, it is characterised in that：The
The detailed process that A clothes pad silkete penetrating agent processing in two steps is：First A clothes are put into and fill silkete penetrating agent solution
Hopper in impregnated, obtain b1 clothes；Then, b1 clothes are carried out by stenter rolling processing, obtains B clothes.
3. according to claim 2 a kind of based on the tencel production technology for padding silkete penetrating agent, it is characterised in that：It draws
The temperature of width machine is 125-135 DEG C, and the speed of stenter is 55-65m/min.
4. according to claim 1 a kind of based on the tencel production technology for padding silkete penetrating agent, it is characterised in that：Institute
State the silkete penetrating agent for containing a concentration of 5-8g/l in silkete penetrating agent solution.