CN104264357A - 55% Lyocell fiber, 25% cotton and 20% spun silk single-sided jacquard fabrics and production method thereof - Google Patents

55% Lyocell fiber, 25% cotton and 20% spun silk single-sided jacquard fabrics and production method thereof Download PDF

Info

Publication number
CN104264357A
CN104264357A CN201410547185.8A CN201410547185A CN104264357A CN 104264357 A CN104264357 A CN 104264357A CN 201410547185 A CN201410547185 A CN 201410547185A CN 104264357 A CN104264357 A CN 104264357A
Authority
CN
China
Prior art keywords
cotton
fabric
spun silk
shrinkage
silk
Prior art date
Application number
CN201410547185.8A
Other languages
Chinese (zh)
Inventor
朱炫钊
朱森波
Original Assignee
嘉兴金凯悦针织面料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 嘉兴金凯悦针织面料有限公司 filed Critical 嘉兴金凯悦针织面料有限公司
Priority to CN201410547185.8A priority Critical patent/CN104264357A/en
Publication of CN104264357A publication Critical patent/CN104264357A/en

Abstract

The invention relates to a production method of 55% Lyocell fiber, 25% cotton and 20% spun silk single-sided jacquard fabrics. The production method comprises the following steps of raw material preparation, weaving, scotching, clear water shaping and drying, mercerizing process, second time shaping, rubber blanket preshrinking, decating and steaming preshrinking. According to the produced 55% Lyocell fiber, 25% cotton and 20% spun silk single-sided jacquard fabrics, the characteristics of Lyocell fibers, the cotton and the spun silk are simultaneously achieved, the dry and wet strength is high, the resistance to swelling is high, the spinnability is good, the heat retention is good, the touch is soft, and the durability is good.

Description

Cotton 20% spun silk one side FIGURED CLOTH and the preparation method of 55% Lyocell fibers 25%
Technical field
The present invention relates to a kind of preparation method of fabric, particularly relate to a kind of preparation method of one side FIGURED CLOTH.
Background technology
Lyocell fibers has high dry, wet brute force, has higher swellability, good spinnability.
Cotton feature is that moisture absorption is strong---cotton fiber is porous material, interior molecules arrangement very irregular, and containing a large amount of hydrophilic-structures in molecule.Warmth retention property----cotton fiber is the non-conductor of heat, and the inner chamber of cotton fiber is filled with immobilising air, comfortable and easy to wear---can not produce electrostatic, good air permeability, anti-sensitivity, easily cleans.
It is high that spun silk has number, and gloss profit is beautiful, and feel is soft, is suitable for manufacturing light and soft fine fabrics.
Summary of the invention
The object of this invention is to provide the preparation method of the cotton 20% spun silk one side FIGURED CLOTH of a kind of 55% Lyocell fibers 25%, adopt one side FIGURED CLOTH prepared by the method, possesses the characteristic of Lyocell fibers, cotton and spun silk simultaneously, there is high dry, wet brute force, there is higher swellability, good spinnability, good warmth retention property, the soft durability of feel.
In order to realize above-mentioned object, present invention employs following technical scheme:
The preparation method of the cotton 20% spun silk one side FIGURED CLOTH of 55% Lyocell fibers 25%, the method comprises the following steps:
1) raw material prepares: the 120N/2 days cotton 25/ thin,tough silk 20 slub yarn dyed yarns of silk 55/;
2) weave: on 30 cun of 28G two-sided jacquards, by 96 tunnel row's pins, design flower pattern at computer software inediting, by computerized version figure and color matching, dyed yarn is accessed accordingly into yarn way, dyed yarn is evenly inweaved;
3) open-width; Adopt horizontal scutcher, expander linear velocity <50m/min;
4) clear water shaping and drying;
5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process 3+chelated dispersants improves water quality, NaOH concentration 210-250g/L, 0.2% silkete penetrating agent, by 25m/min normal temperature mercerising, adds 90g/L glacial acetic acid carry out acid-base neutralization, PH Zhi≤7 after alkali lye rolls and washes when open washing, and plays tint retention;
6) secondary sizing: secondary sizing adds the fluffy softener of 40 ~ 80g/L, ice-cold finishing agent 58 ~ 65g/L, smooth silicone oil 140 ~ 160g/L, temperature 140 ~ 160 DEG C, overfeeding 25m/min;
7) rubber blanket preshrunk: rubber blanket temperature should control at 55 ~ 75 DEG C, and the speed of a motor vehicle is at 25 ~ 45m/min;
8) decatizing and preshrinking process: continuous pressure decator is entered to fabric after mercerising and sizing and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects by steam-shrinkage machine and woollen blanket preshrinking machine to horizontal, longitudinal washing shrinkage of fabric after decatizing, patterns of fabric, effective gate width do processing adjustment;
9) steam-shrinkage: mechanical speed, 20-30m/min, saturated vapor 3-3.5Bar, compressed air 5Bar, to horizontal, longitudinal washing shrinkage of fabric, patterns of fabric, effective gate width do processing adjustment.
Another object of the present invention is to provide the one side FIGURED CLOTH adopting above-mentioned method to prepare.
The present invention is owing to have employed above-mentioned technical scheme, and the one side FIGURED CLOTH of preparation, possesses the characteristic of Lyocell fibers, cotton and spun silk simultaneously, there is high dry, wet brute force, there is higher swellability, good spinnability, good warmth retention property, the soft durability of feel.
Detailed description of the invention
The preparation method of the cotton 20% spun silk one side FIGURED CLOTH of 55% Lyocell fibers 25%, is characterized in that the method comprises the following steps:
1) raw material prepares: the 120N/2 days cotton 25/ thin,tough silk 20 slub yarn dyed yarns of silk 55/;
2) weave: on 30 cun of 28G two-sided jacquards, by 96 tunnel row's pins, design flower pattern at computer software inediting, by computerized version figure and color matching, dyed yarn is accessed accordingly into yarn way, dyed yarn is evenly inweaved;
3) open-width; Adopt horizontal scutcher, expander linear velocity <50m/min;
4) clear water shaping and drying;
5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process 3+chelated dispersants improves water quality, NaOH concentration 230g/L, 0.2% silkete penetrating agent, by 25m/min normal temperature mercerising, adds 90g/L glacial acetic acid carry out acid-base neutralization, PH Zhi≤7 after alkali lye rolls and washes when open washing, and plays tint retention;
6) secondary sizing: secondary sizing adds the fluffy softener of 60g/L, ice-cold finishing agent 60g/L, smooth silicone oil 150g/L, temperature 150 DEG C, overfeeding 25m/min;
7) rubber blanket preshrunk: rubber blanket temperature should control at 65 DEG C, and the speed of a motor vehicle is at 30m/min;
8) decatizing and preshrinking process: continuous pressure decator is entered to fabric after mercerising and sizing and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects by steam-shrinkage machine and woollen blanket preshrinking machine to horizontal, longitudinal washing shrinkage of fabric after decatizing, patterns of fabric, effective gate width do processing adjustment;
9) steam-shrinkage: mechanical speed, 25m/min, saturated vapor 3.3Bar, compressed air 5Bar, to horizontal, longitudinal washing shrinkage of fabric, patterns of fabric, effective gate width do processing adjustment.
One side FIGURED CLOTH project after testing prepared by above-mentioned method is as shown in the table.Examination criteria GB/T 22849-2009, GB18401-20 03 " B " class.

Claims (2)

  1. The preparation method of the cotton 20% spun silk one side FIGURED CLOTH of 1.55% Lyocell fibers 25%, is characterized in that the method comprises the following steps:
    1) raw material prepares: the 120N/2 days cotton 25/ thin,tough silk 20 slub yarn dyed yarns of silk 55/;
    2) weave: on 30 cun of 28G two-sided jacquards, by 96 tunnel row's pins, design flower pattern at computer software inediting, by computerized version figure and color matching, dyed yarn is accessed accordingly into yarn way, dyed yarn is evenly inweaved;
    3) open-width; Adopt horizontal scutcher, expander linear velocity <50m/min;
    4) clear water shaping and drying;
    5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process 3+chelated dispersants improves water quality, NaOH concentration 210-250g/L, 0.2% silkete penetrating agent, by 25m/min normal temperature mercerising, adds 90g/L glacial acetic acid carry out acid-base neutralization, PH Zhi≤7 after alkali lye rolls and washes when open washing, and plays tint retention;
    6) secondary sizing: secondary sizing adds the fluffy softener of 40 ~ 80g/L, ice-cold finishing agent 58 ~ 65g/L, smooth silicone oil 140 ~ 160g/L, temperature 140 ~ 160 DEG C, overfeeding 25m/min;
    7) rubber blanket preshrunk: rubber blanket temperature should control at 55 ~ 75 DEG C, and the speed of a motor vehicle is at 25 ~ 45m/min;
    8) decatizing and preshrinking process: continuous pressure decator is entered to fabric after mercerising and sizing and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects by steam-shrinkage machine and woollen blanket preshrinking machine to horizontal, longitudinal washing shrinkage of fabric after decatizing, patterns of fabric, effective gate width do processing adjustment;
    9) steam-shrinkage: mechanical speed, 20-30m/min, saturated vapor 3-3.5Bar, compressed air 5Bar, to horizontal, longitudinal washing shrinkage of fabric, patterns of fabric, effective gate width do processing adjustment.
  2. 2. the one side FIGURED CLOTH prepared of method according to claim 1.
CN201410547185.8A 2014-10-16 2014-10-16 55% Lyocell fiber, 25% cotton and 20% spun silk single-sided jacquard fabrics and production method thereof CN104264357A (en)