CN108796251B - 一种金属基纳米复合材料的制备方法 - Google Patents
一种金属基纳米复合材料的制备方法 Download PDFInfo
- Publication number
- CN108796251B CN108796251B CN201810521494.6A CN201810521494A CN108796251B CN 108796251 B CN108796251 B CN 108796251B CN 201810521494 A CN201810521494 A CN 201810521494A CN 108796251 B CN108796251 B CN 108796251B
- Authority
- CN
- China
- Prior art keywords
- metal
- nano
- pure
- reinforcement
- ingot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (10)