CN108795272A - A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture and preparation method thereof - Google Patents
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture and preparation method thereof Download PDFInfo
- Publication number
- CN108795272A CN108795272A CN201811153101.7A CN201811153101A CN108795272A CN 108795272 A CN108795272 A CN 108795272A CN 201811153101 A CN201811153101 A CN 201811153101A CN 108795272 A CN108795272 A CN 108795272A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- agent
- bath
- kitchen
- led
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture and preparation method thereof, and the coating calculates by weight, including：20~40 parts of aqueous aliphatic urethane acrylate, 30~50 parts of aqueous aliphatic polyurethane dispersion, 0.15~0.75 part of aqueous dispersion, 0.1~0.5 part of aqueous wetting agent agent, 0.15~0.75 part of aqueous aerosil, 15~30 parts of titanium dioxide, 0.1~0.5 part of aqueous defoamer, 0.15~0.75 part of aqueous levelling agent, 1~3 part of water-based thickener, 2~8 parts of water-soluble photoinitiator, 0.05~0.3 part of fungicide, 0.05~0.3 part of in-can preservation agent, 5.5~10.3 parts of deionized water；The paint solidification energy is low, and curing rate is fast, equally applicable to thermo-responsive base material；It is environmentally protective, it has good workability；The preparation method is easy to implement, and curing apparatus is simple, does not generate ozone in the process.
Description
Technical field
The present invention relates to UV LED water paints and its preparing technical field, more particularly to a kind of UV LED aquosity ultraviolet lights
Cure kitchen and bath's coatings for furniture and preparation method thereof.
Background technology
Traditional UV water paints refer to waterborne ultraviolet curing resin UV coating, i.e., using ultraviolet light as solidification energy
Source, the water-base resin UV coating that Quick cross-linking forms a film at normal temperatures.
But waterborne ultraviolet curing resin UV coating high energy consumptions, a large amount of ozone is will produce in the curing process, to ring
Border pollution is big, endangers the health of people.
UV LED（UV LED）It is a cold light source, is not exported in infrared range of spectrum, need not be made
With complicated cooling equipment thermo-responsive base material, electrical-optical high conversion efficiency, to environment friend can be used for such as chill roll and black-out cloth
It is good, do not generate harm to human body.
As it can be seen that the prior art could be improved and improve.
Invention content
Place in view of above-mentioned deficiencies of the prior art, it is solid that the purpose of the present invention is to provide a kind of UV LED aquosity ultraviolet lights
Change kitchen and bath's coatings for furniture and preparation method thereof, it is intended to solve ultraviolet-curing paint solidification energy height in the prior art, solidification
The ozone to human body and environmental danger is generated in the process, and curing apparatus is complicated, is not suitable for photosensitivity materials'use
Problem.
In order to achieve the above object, this invention takes following technical schemes：
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
20~40 parts of aqueous aliphatic urethane acrylate,
30~50 parts of aqueous aliphatic polyurethane dispersion,
0.15~0.75 part of aqueous dispersion,
0.1~0.5 part of aqueous wetting agent agent,
0.15~0.75 part of aqueous aerosil,
15~30 parts of titanium dioxide,
0.1~0.5 part of aqueous defoamer,
0.15~0.75 part of aqueous levelling agent,
1~3 part of water-based thickener,
2~8 parts of water-soluble photoinitiator,
0.05~0.3 part of fungicide,
0.05~0.3 part of in-can preservation agent,
5.5~10.3 parts of deionized water.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the aqueous dispersion and aqueous gas phase titanium dioxide
The weight ratio of silicon is 1: 1.
It is the aqueous defoamer, aqueous levelling agent, aqueous in UV LED UV-curable waterbornes kitchen and bath's coatings for furniture
The weight ratio of dispersant is 2: 3: 3.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the aqueous dispersion is to contain the affine base of pigment
The block copolymer of group.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the aqueous wetting agent agent is the alkane of acidic polymer
Alcohol amine salt.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the aqueous defoamer is TEGO Airex
904W, the aqueous levelling agent are TEGO Glide 410.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the water-based thickener is aqueous non-ionic associative
Type rheology modifier.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the water-soluble photoinitiator is（2,4,6- front threes
Base benzoyl）The compound product of diphenyl phosphine oxide and isooctyl p-dimethylaminobenzoate.
In UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, the fungicide is 2- n-octyl -4- isothiazole
Quinoline -3- ketone, the in-can preservation agent are 2-methyl-4-isothiazolin-3-one.
A kind of preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, includes the following steps：
S001. according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, and 10~15min is disperseed under the rotating speed of 750~850rpm；
S002. aqueous aerosil, R706 titanium dioxides, lower point of the rotating speed of 1200~1500rpm are put into reactor again
Dissipate 10~15min；
S003. inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1200~
Disperse 10~15min under the rotating speed of 1500rpm；
S004. inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water,
Fungicide, in-can preservation agent disperse 10~15min under 750~850rpm rotating speeds, are uniformly mixed, obtain finished product coating.
Advantageous effect：
The present invention provides a kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture and preparation method thereof, the paint solidifications
Energy is low, and curing rate is fast, under the irradiation of the UV LED light sources of 395nm, curing rate 25m/min, and it can save 50%~
75% electric power, it is equally applicable to thermo-responsive base material；It is environmentally protective, it not will produce the harmful substances such as VOC, have good workability, Gu
Hardness of film after change reaches Chinese pencil hardness 1H, and for adhesive force up to 0 grade, gloss of film degree is high, has excellent levelability, plentiful
Degree, hardness, yellowing resistance, covering power is strong, is suitable for the external coating of various kitchen and bath's furniture；The preparation method is easy real
It applies, curing apparatus is simple, need not use cooling or shading device, not generate ozone in the process.
Description of the drawings
Fig. 1 is ultra-violet absorption spectrum of the water-soluble photoinitiator provided by the invention under different quality percentage concentration
Figure.
Specific implementation mode
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture of present invention offer and preparation method thereof, to make the present invention
Purpose, technical solution and effect it is clearer, clear, the present invention is described in more detail by the following examples.It should manage
Solution, described herein specific examples are only used to explain the present invention, is not intended to limit the present invention.
The present invention provides a kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
20~40 parts of aqueous aliphatic urethane acrylate,
30~50 parts of aqueous aliphatic polyurethane dispersion,
0.15~0.75 part of aqueous dispersion,
0.1~0.5 part of aqueous wetting agent agent,
0.15~0.75 part of aqueous aerosil,
15~30 parts of titanium dioxide,
0.1~0.5 part of aqueous defoamer,
0.15~0.75 part of aqueous levelling agent,
1~3 part of water-based thickener,
2~8 parts of water-soluble photoinitiator,
0.05~0.3 part of fungicide,
0.05~0.3 part of in-can preservation agent,
5.5~10.3 parts of deionized water.
In above-mentioned coating, aqueous aliphatic urethane acrylate and aqueous aliphatic polyurethane dispersion be it is main at
Membrane substance has outstanding physics and chemistry patience, has good adhesive force to ground, and in the coating, collocation uses particle size
Different aqueous aliphatic urethane acrylates and aqueous aliphatic polyurethane dispersion, improve the coating to kitchen and bath family
The adhesive force of tool keeps coating finer and smoother.
Preferably, the weight ratio of the aqueous dispersion and aqueous aerosil is 1: 1；The aqueous dispersion is
Block copolymer containing pigment affinity groups, in a kind of embodiment, the aqueous dispersion is BYK 190, in the painting
It mainly better disperses aqueous aerosil in material, stablizes the viscosity of coating, improve its storage stability；It is described aqueous
Aerosil uses the WR 8520 of Bi Ke chemistry, is mainly used for adjusting stream of the coating in production, storage and construction
Denaturation, the mobility and thickness of paint film when improving construction；When the mass ratio of the aqueous dispersion and aqueous aerosil
When being 1: 1, the dispersion effect of the aerosil is best, and the storage stability of the coating is best.
Preferably, the aqueous defoamer, aqueous levelling agent, the weight ratio of aqueous dispersion are 2: 3: 3；A kind of embodiment party
In formula, the aqueous defoamer is that TEGO Airex 904W, TEGO Airex 904W are free of solvent, has excellent anti-shrinkage cavity
Property, it can prevent the coating from forming bubble and pin hole in stirring and construction；The aqueous levelling agent is TEGO Glide
410, TEGO Glide, 410 efficiency is high, and the mobility and levelability on surface, subtract when can control and improve the coating application
There is shrinkage cavity in few film, is also prevented from pigment floating, adjusts the smoothness and resistance to scraping of film；The aqueous defoaming
When agent, aqueous levelling agent, aqueous dispersion use said ratio, the dispersion effect of the coating, anti-shrinkage cavity effect are best.
Preferably, the aqueous wetting agent agent is the alkanolamine of acidic polymer；It is described aqueous wet in a kind of embodiment
Profit agent is TEGO Wet 270, is efficient wetting agent, the paint ingredient is made uniformly to soak, and is had to ground good wet
The surface of the relatively rough metal product of lubricant nature, especially surface can greatly improve adhesive force of the coating system to ground,
And there is excellent nonshrink pore performance, improve the levelability of the coating.
In a kind of embodiment, the titanium dioxide uses R706 titanium dioxides, R706 titanium dioxides to compare, have with similar product
Better glossiness and weatherability, covering power is strong, easily soaks.
Preferably, the water-based thickener is aqueous non-ionic associative type rheology modifier；It is described in a kind of embodiment
Water-based thickener uses the RM-8W of ROHM AND HAAS, a kind of aqueous non-ionic associative type rheology modifier without oil solvent, in institute
It states and splendid flowing and levelability, uniform filming performance is provided in coating system.
Preferably, the water-soluble photoinitiator is（2,4,6- trimethylbenzoyls）Diphenyl phosphine oxide and to diformazan
The compound product of the different monooctyl ester of aminobenzoic acid, isooctyl p-dimethylaminobenzoate can neutralize（2,4,6- trimethylbenzoyls
Base）Diphenyl phosphine oxide is efficient photoinitiator, there is absorption peak at 393nm, close to the solidification wavelength of the coating, and
And the photolytic product for compounding photoinitiator is trimethylbenzoyl free radical and diphenylphosphine free acyl radical, is all to cause activity very
High free radical, and it is conducive to UV light permeability, excellent in stability improves the surface drying effect of coating.Referring to Fig. 1, Fig. 1 is
After the water-soluble photoinitiator is by resins dilute, the uv absorption spectra under different quality percentage concentration, as shown,
The water-soluble photoinitiator has strong absorption near 395nm.
Preferably, the fungicide is Kathon, hinders the new of coating microorganism and bacterium
Old metabolism blocks photosynthesis；The in-can preservation agent is 2-methyl-4-isothiazolin-3-one, is a kind of efficient sterilization
Agent can inhibit the growth and heredity of microorganism in the coating, destroy it to inhibiting the growth of microorganism to have good effect
Cell wall and cell membrane.
In above-mentioned coating, the aqueous aliphatic polyurethane dispersion and the various work(of aqueous aliphatic polyurathane emulsion collocation
Energy auxiliary agent synergistic effect, obtained coating application performance is good, has excellent levelability, richness, hardness, yellowing resistance, hides
Gai Liqiang, curing reaction is fast, and solidification energy is low, is suitable for the external coating of various kitchen and bath's furniture；The coating deionized water
As solvent, the risk that solvent generates VOC is avoided, it is environmentally protective.
A kind of preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, includes the following steps：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, and 10~15min is disperseed under the rotating speed of 750~850rpm；
Put into aqueous aerosil, R706 titanium dioxides into reactor again, dispersion 10 under the rotating speed of 1200~1500rpm~
15min；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1200~
Disperse 10~15min under the rotating speed of 1500rpm；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 10~15min under 750~850rpm rotating speeds, are uniformly mixed, obtain finished product coating.
Jitter time and rate of dispersion in the preparation process of above-mentioned coating are determined by the ingredient and proportioning of the coating
, in 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.
The coating finished product prepared by the above method is applied in various kitchen and bath's furniture surfaces, it is solid in the UV LED of 395nm
Change and irradiated under light source, the hardness of curing rate 25m/min, the paint film coating of formation are Chinese pencil hardness 1H, by GB
9286-88S standards are detected, and up to 0 grade, gloss of film degree is high for the adhesive force of coating, have excellent levelability, richness,
Hardness, yellowing resistance, strong covering power.
Embodiment 1
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
29 parts of aqueous aliphatic urethane acrylate,
38 parts of aqueous aliphatic polyurethane dispersion,
0.3 part of aqueous dispersion,
0.3 part of aqueous wetting agent agent,
0.3 part of aqueous aerosil,
20 parts of titanium dioxide,
0.2 part of aqueous defoamer,
0.3 part of aqueous levelling agent,
1.2 parts of water-based thickener,
3.5 parts of water-soluble photoinitiator,
0.1 part of fungicide,
0.1 part of in-can preservation agent,
6.7 parts of deionized water.
The preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, including：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, disperse 15min under the rotating speed of 800rpm；
Aqueous aerosil, R706 titanium dioxides are put into reactor again, disperses 12min under the rotating speed of 1200rpm；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1500rpm's turns
Speed is lower to disperse 10min；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 10min under 800rpm rotating speeds, are uniformly mixed, obtain finished product coating.
In 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.By institute
It states coating finished product and is applied in various kitchen and bath's furniture surfaces, irradiated under the UV LED curing light sources of 395nm, curing rate 25m/
The hardness of min, the paint film coating of formation are Chinese pencil hardness 1H, are detected by GB 9286-88S standards, the attachment of coating
For power up to 0 grade, gloss of film degree is high, has excellent levelability, richness, hardness, yellowing resistance, strong covering power.
Embodiment 2
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
20 parts of aqueous aliphatic urethane acrylate,
50 parts of aqueous aliphatic polyurethane dispersion,
0.15 part of aqueous dispersion,
0.1 part of aqueous wetting agent agent,
0.15 part of aqueous aerosil,
15 parts of titanium dioxide,
0.1 part of aqueous defoamer,
0.15 part of aqueous levelling agent,
1.5 parts of water-based thickener,
2.8 parts of water-soluble photoinitiator,
0.3 part of fungicide,
0.05 part of in-can preservation agent,
5.5 parts of deionized water.
The preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, including：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, disperse 15min under the rotating speed of 750rpm；
Aqueous aerosil, R706 titanium dioxides are put into reactor again, disperses 10min under the rotating speed of 1500rpm；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1300rpm's turns
Speed is lower to disperse 10min；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 15min under 750rpm rotating speeds, are uniformly mixed, obtain finished product coating.
In 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.By institute
It states coating finished product and is applied in various kitchen and bath's furniture surfaces, irradiated under the UV LED curing light sources of 395nm, curing rate 25m/
The hardness of min, the paint film coating of formation are Chinese pencil hardness 1H, are detected by GB 9286-88S standards, the attachment of coating
For power up to 0 grade, gloss of film degree is high, has excellent levelability, richness, hardness, yellowing resistance, strong covering power.
Embodiment 3
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
32 parts of aqueous aliphatic urethane acrylate,
30 parts of aqueous aliphatic polyurethane dispersion,
0.75 part of aqueous dispersion,
0.5 part of aqueous wetting agent agent,
0.75 part of aqueous aerosil,
24 parts of titanium dioxide,
0.5 part of aqueous defoamer,
0.75 part of aqueous levelling agent,
1 part of water-based thickener,
2 parts of water-soluble photoinitiator,
0.15 part of fungicide,
0.12 part of in-can preservation agent,
7.2 parts of deionized water.
The preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, including：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, disperse 12min under the rotating speed of 850rpm；
It is put into again into reactor under the rotating speed of aqueous aerosil, R706 titanium dioxides, 1400rpm and disperses 10min；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1500rpm's turns
Speed is lower to disperse 10min；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 12min under 750rpm rotating speeds, are uniformly mixed, obtain finished product coating.
In 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.By institute
It states coating finished product and is applied in various kitchen and bath's furniture surfaces, irradiated under the UV LED curing light sources of 395nm, curing rate 25m/
The hardness of min, the paint film coating of formation are Chinese pencil hardness 1H, are detected by GB 9286-88S standards, the attachment of coating
For power up to 0 grade, gloss of film degree is high, has excellent levelability, richness, hardness, yellowing resistance, strong covering power.
Embodiment 4
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
25 parts of aqueous aliphatic urethane acrylate,
42 parts of aqueous aliphatic polyurethane dispersion,
0.6 part of aqueous dispersion,
0.2 part of aqueous wetting agent agent,
0.6 part of aqueous aerosil,
30 parts of titanium dioxide,
0.4 part of aqueous defoamer,
0.6 part of aqueous levelling agent,
2 parts of water-based thickener,
4.2 parts of water-soluble photoinitiator,
0.08 part of fungicide,
0.3 part of in-can preservation agent,
8.6 parts of deionized water.
The preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, including：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, disperse 10min under the rotating speed of 800rpm；
Aqueous aerosil, R706 titanium dioxides are put into reactor again, disperses 12min under the rotating speed of 1500rpm；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1500rpm's turns
Speed is lower to disperse 15min；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 10min under 800rpm rotating speeds, are uniformly mixed, obtain finished product coating.
In 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.
The coating finished product is applied in various kitchen and bath's furniture surfaces, is irradiated under the UV LED curing light sources of 395nm, Gu
Change speed is 25m/min, and the hardness of the paint film coating of formation is Chinese pencil hardness 1H, is examined by GB 9286-88S standards
It surveys, for the adhesive force of coating up to 0 grade, gloss of film degree is high, has excellent levelability, richness, hardness, yellowing resistance, covers
Power is strong.
Embodiment 5
A kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, calculates by weight, including：
40 parts of aqueous aliphatic urethane acrylate,
35 parts of aqueous aliphatic polyurethane dispersion,
0.45 part of aqueous dispersion,
0.4 part of aqueous wetting agent agent,
0.45 part of aqueous aerosil,
18 parts of titanium dioxide,
0.3 part of aqueous defoamer,
0.45 part of aqueous levelling agent,
3 parts of water-based thickener,
8 parts of water-soluble photoinitiator,
0.05 part of fungicide,
0.08 part of in-can preservation agent,
10.3 parts of deionized water.
The preparation method of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, including：
First, according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, disperse 15min under the rotating speed of 780rpm；
It is put into again into reactor under the rotating speed of aqueous aerosil, R706 titanium dioxides, 1400rpm and disperses 12min；
Inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1300rpm's turns
Speed is lower to disperse 13min；
Inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water, sterilization
Agent, in-can preservation agent disperse 15min under 820rpm rotating speeds, are uniformly mixed, obtain finished product coating.
In 30 DEG C/75 ± 2KU, fineness≤20 μm have good workability the viscosity of the coating prepared by the above method.
The coating finished product is applied in various kitchen and bath's furniture surfaces, is irradiated under the UV LED curing light sources of 395nm, Gu
Change speed is 25m/min, and the hardness of the paint film coating of formation is Chinese pencil hardness 1H, is examined by GB 9286-88S standards
It surveys, for the adhesive force of coating up to 0 grade, gloss of film degree is high, has excellent levelability, richness, hardness, yellowing resistance, covers
Power is strong.
It, can according to the technique and scheme of the present invention and its hair it is understood that for those of ordinary skills
Bright design is subject to equivalent substitution or change, and all these changes or replacement should all belong to the guarantor of appended claims of the invention
Protect range.
Claims (10)
1. a kind of UV LED UV-curable waterbornes kitchen and bath's coatings for furniture, which is characterized in that it calculates by weight, including：
20~40 parts of aqueous aliphatic urethane acrylate,
30~50 parts of aqueous aliphatic polyurethane dispersion,
0.15~0.75 part of aqueous dispersion,
0.1~0.5 part of aqueous wetting agent agent,
0.15~0.75 part of aqueous aerosil,
15~30 parts of titanium dioxide,
0.1~0.5 part of aqueous defoamer,
0.15~0.75 part of aqueous levelling agent,
1~3 part of water-based thickener,
2~8 parts of water-soluble photoinitiator,
0.05~0.3 part of fungicide,
0.05~0.3 part of in-can preservation agent,
5.5~10.3 parts of deionized water.
2. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
The weight ratio of dispersant and aqueous aerosil is 1: 1.
3. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Antifoaming agent, aqueous levelling agent, the weight ratio of aqueous dispersion are 2: 3: 3.
4. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Dispersant is the block copolymer containing pigment affinity groups.
5. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Wetting agent is the alkanolamine of acidic polymer.
6. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Antifoaming agent is TEGO Airex 904W, and the aqueous levelling agent is TEGO Glide 410.
7. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Thickener is aqueous non-ionic associative type rheology modifier.
8. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that described aqueous
Photoinitiator is（2,4,6- trimethylbenzoyls）The compounding of diphenyl phosphine oxide and isooctyl p-dimethylaminobenzoate is produced
Product.
9. UV LED UV-curable waterbornes kitchen and bath's coatings for furniture according to claim 1, which is characterized in that the sterilization
Agent is Kathon, and the in-can preservation agent is 2-methyl-4-isothiazolin-3-one.
10. a kind of preparation side of such as claim 1~9 any one of them UV LED UV-curable waterborne kitchen and bath's coatings for furniture
Method, which is characterized in that include the following steps：
S001. according to the above proportioning by aqueous aliphatic urethane acrylate, aqueous aliphatic polyurethane dispersion, aqueous point
Powder, aqueous wetting agent agent are put into reactor respectively, and 10~15min is disperseed under the rotating speed of 750~850rpm；
S002. aqueous aerosil, R706 titanium dioxides, lower point of the rotating speed of 1200~1500rpm are put into reactor again
Dissipate 10~15min；
S003. inspection by sampling, when fineness≤20 μm, input aqueous defoamer, aqueous levelling agent, water-based thickener, 1200~
Disperse 10~15min under the rotating speed of 1500rpm；
S004. inspection by sampling, coating painting scrape on a glass without shrinkage cavity phenomenon after, input water-soluble photoinitiator, deionized water,
Fungicide, in-can preservation agent disperse 10~15min under 750~850rpm rotating speeds, are uniformly mixed, obtain finished product coating.