CN108722361A - A kind of absorbent-type water pollution inorganic agent and preparation method thereof - Google Patents
A kind of absorbent-type water pollution inorganic agent and preparation method thereof Download PDFInfo
- Publication number
- CN108722361A CN108722361A CN201810519377.6A CN201810519377A CN108722361A CN 108722361 A CN108722361 A CN 108722361A CN 201810519377 A CN201810519377 A CN 201810519377A CN 108722361 A CN108722361 A CN 108722361A
- Authority
- CN
- China
- Prior art keywords
- added
- absorbent
- diatomite
- type water
- inorganic agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of absorbent-type water pollution inorganic agents, it is made of the raw material of following weight parts：Diatomite 100-130, nano-carbon powder 40-50, lauryl dimethyl amine oxide 1-2, calcium monohydrogen phosphate 3-4, hydroxyethyl cellulose 2-5, the primary sorbent that diatomite is added in the present invention, nano-carbon powder is water treatment agent, its safety in utilization is good, it is pollution-free to water body, and recycling is high, comprehensive performance is superior.
Description
Technical field
The invention belongs to water treatment fields, and in particular to a kind of absorbent-type water pollution inorganic agent and preparation method thereof.
Background technology
Water process refers to the physics centainly taken using standard to make water quality reach, chemical measure.Drinking water it is minimum
Standard is formulated by environmental protection administration.Industrial water has the requirement of oneself.The physics such as temperature, color, transparency, smell, the taste of water
Characteristic is to judge the basic standard of water quality quality.The chemical characteristic of water, such as its acid-base value, the solids concentration and oxygen dissolved
Content etc., and judge the major criterion of water quality.As in some grassland Natural Waters complete molten solids concentration be up to 1000 milligrams/
It rises, and complete molten solids concentration must not exceed 500 mg/litres in Canadian regulation drinking water, many industrial waters also require dense
Must not spend and is higher than 200 mg/litres.This water can not be used at will even if its physical property meets the requirements.In addition, from certainly
The radioactive element content of right boundary, nuclear accident and nuclear power station etc., and the key property that must be monitored.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of absorbent-type water pollution inorganic agent and
Preparation method.
To achieve the above object, the present invention uses following technical scheme：
A kind of absorbent-type water pollution inorganic agent, it is made of the raw material of following weight parts：
Diatomite 100-130, nano-carbon powder 40-50, lauryl dimethyl amine oxide 1-2, calcium monohydrogen phosphate 3-4, hydroxy ethyl fiber
Plain 2-5.
A kind of preparation method of absorbent-type water pollution inorganic agent, includes the following steps：
（1）Hydroxyethyl cellulose is taken, is added in the absolute ethyl alcohol of 10-18 times of its weight, stirs evenly, obtain fiber solution；
（2）Diatomite is taken, is added in the sodium hydroxide solution of 0.5-1mol/l, is impregnated 3-4 hours, discharging washing is added to
In above-mentioned fiber solution, it is 65-70 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains diatomite dispersion liquid；
（3）Lauryl dimethyl amine oxide, calcium monohydrogen phosphate are taken, is added in the deionized water of 30-40 times of mixture weight, is stirred
Uniformly, aqueous dispersions are obtained；
（4）Above-mentioned diatomite dispersion liquid, aqueous dispersions mixing are taken, stirs evenly, nano-carbon powder is added, is sent in baking oven,
Dry complete at 80-90 DEG C, fine powder is worn into discharging, crosses 100-200 mesh sieve to get the absorbent-type water pollution inorganic agent.
Advantages of the present invention
The primary sorbent that diatomite is added in the present invention, nano-carbon powder is water treatment agent, safety in utilization is good, to water body without dirt
Dye, and recycling is high, comprehensive performance is superior.
Specific implementation mode
Embodiment 1
A kind of absorbent-type water pollution inorganic agent, it is made of the raw material of following weight parts：
Diatomite 100, nano-carbon powder 40, lauryl dimethyl amine oxide 1, calcium monohydrogen phosphate 3, hydroxyethyl cellulose 2.
A kind of preparation method of absorbent-type water pollution inorganic agent, includes the following steps：
（1）Hydroxyethyl cellulose is taken, is added in the absolute ethyl alcohol of 10 times of its weight, is stirred evenly, obtain fiber solution；
（2）Diatomite is taken, is added in the sodium hydroxide solution of 0.5-ol/l, is impregnated 3 hours, discharging washing is added to above-mentioned
In fiber solution, it is 65 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains diatomite dispersion liquid；
（3）Lauryl dimethyl amine oxide, calcium monohydrogen phosphate are taken, is added in the deionized water of 30 times of mixture weight, stirring is equal
It is even, obtain aqueous dispersions；
（4）Above-mentioned diatomite dispersion liquid, aqueous dispersions mixing are taken, stirs evenly, nano-carbon powder is added, is sent in baking oven,
Dry complete at 80 DEG C, discharging is worn into fine powder, is sieved with 100 mesh sieve to get the absorbent-type water pollution inorganic agent.
Claims (2)
1. a kind of absorbent-type water pollution inorganic agent, which is characterized in that it is made of the raw material of following weight parts：
Diatomite 100-130, nano-carbon powder 40-50, lauryl dimethyl amine oxide 1-2, calcium monohydrogen phosphate 3-4, hydroxy ethyl fiber
Plain 2-5.
2. a kind of preparation method of absorbent-type water pollution inorganic agent as described in claim 1, which is characterized in that including following step
Suddenly：
（1）Hydroxyethyl cellulose is taken, is added in the absolute ethyl alcohol of 10-18 times of its weight, stirs evenly, obtain fiber solution；
（2）Diatomite is taken, is added in the sodium hydroxide solution of 0.5-1mol/l, is impregnated 3-4 hours, discharging washing is added to
In above-mentioned fiber solution, it is 65-70 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains diatomite dispersion liquid；
（3）Lauryl dimethyl amine oxide, calcium monohydrogen phosphate are taken, is added in the deionized water of 30-40 times of mixture weight, is stirred
Uniformly, aqueous dispersions are obtained；
（4）Above-mentioned diatomite dispersion liquid, aqueous dispersions mixing are taken, stirs evenly, nano-carbon powder is added, is sent in baking oven,
Dry complete at 80-90 DEG C, fine powder is worn into discharging, crosses 100-200 mesh sieve to get the absorbent-type water pollution inorganic agent.