CN105086675A - Anti-static radiation protection emulsion paint special for equipment rooms and preparing method of anti-static radiation protection emulsion paint - Google Patents
Anti-static radiation protection emulsion paint special for equipment rooms and preparing method of anti-static radiation protection emulsion paint Download PDFInfo
- Publication number
- CN105086675A CN105086675A CN201510474821.3A CN201510474821A CN105086675A CN 105086675 A CN105086675 A CN 105086675A CN 201510474821 A CN201510474821 A CN 201510474821A CN 105086675 A CN105086675 A CN 105086675A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation protection
- emulsion paint
- static radiation
- protection emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses anti-static radiation protection emulsion paint special for equipment rooms. The anti-static radiation protection emulsion paint is characterized by being prepared from, by weight, 28-30 parts of vinyl acetate-acrylic emulsion, 3-5 parts of cottonseed oil, 1-2 parts of coconut oil, 2-3 parts of laurinol polyoxyethylene ether sodium, 2-4 parts of hydroxyethyl cellulose, 5-7 parts of anhydrous aluminum silicate, 2-3 parts of nano-silver, 7-9 parts of blanc fixe, 2-4 parts of tin oxide, 25-27 parts of light calcium carbonate, 90-95 parts of water and 7-9 parts of mixed plant paste. According to the anti-static radiation protection emulsion paint, the conductive ingredients of the tin oxide, the nano-silver and the like are added to form a conductive film on a wall, anti-static radiation protection is achieved, the radiation protection effect can be greatly improved, and the harm to human bodies by radiation is greatly reduced; by adding the mixed plant paste, bacterium resistance, virus resistance and corrosion resistance are achieved, the smell is fresh, and the air quality is improved. The anti-static radiation protection emulsion paint is simple in production technology, safe, environmentally friendly, easy to brush, good in paint film anti-cracking performance and capable of being used for equipment rooms on various occasions.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, particularly a kind of Antistatic radiation-proof emulsion paint being specifically designed to canyon and preparation method thereof.
Background technology
Although the pollution of electromagnetic radiation we cannot see and can not touch, be self-evident to the body harm of people, the system that mainly affects the nerves, cardiovascular systems, immunity system, eyes and reproductive system.The harm of electromagnetic radiation can make people occur: the symptoms such as dizzy, headache, tired, absent minded, hypomnesis, insomnia, palpitaition, uncomfortable in chest, dry mouth and tougue, body's immunity decline, cataract, woman in menstrual period imbalance, sexual function reduction, and people's most of the time is all located to accept the harm of various electrical equipment radiation in this environment.
Some main equipment generally needs people to operate, and the harm of such electromagnetic radiation is inevitable, and the present invention manages radioprotective composition to combine with antimicrobial component, makes a kind of antibacterial, Radiation-proof emulsion paint of adding plant slurry.
Vegetable ingredients of the present invention comprises horseradish, Hemp Eupatorium, peppermint etc.Horseradish, has special aroma and pungent, can sterilization, anticorrosion, analgesia; Hemp Eupatorium, it is a kind of natural dyestuff, through high temperature infusion, can stained yellow, native tie-dye is used to, and the effect of mosquito repellent anti-inflammatory can be played, and dye bright-colored bright, the not fugitive color that come, Hemp Eupatorium has a kind of special smell in addition, has special driving away mosquito effect with the cloth that it dyes; The fragrance of Hemp Eupatorium can become the spice source manufacturing essence, can be used as natural insecticide, sterilant.
Summary of the invention
The object of this invention is to provide a kind of Antistatic radiation-proof emulsion paint being specifically designed to canyon and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
Be specifically designed to an Antistatic radiation-proof emulsion paint for canyon, be made up of the raw material of following weight part: acrylate and vinyl acetate emulsion 28-30, Oleum Gossypii semen 3-5, Oleum Cocois 1-2, ethoxylated dodecyl alcohol sodium sulfate 2-3, Natvosol 2-4, anhydrous aluminium silicate 5-7, nanometer silver 2-3, ground barium sulfate 7-9, stannic oxide 2-4, light calcium carbonate 25-27, water 90-95, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: horseradish 3.5-4.5, Hemp Eupatorium 1-2, peppermint 2-3, borneol 0.8-1, Radix Gentianae 3-4, leaf of bamboo 2.5-3.5, white bamboo charcoal 2-3, carboxymethyl cellulose 3-5, guar gum 1-1.5, water 45-50; Preparation method is after horseradish, Hemp Eupatorium, peppermint, borneol, Radix Gentianae, the leaf of bamboo being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then carboxymethyl cellulose, guar gum are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
A kind of Antistatic radiation-proof emulsion paint being specifically designed to canyon of the present invention, be made up of following concrete steps:
(1) acrylate and vinyl acetate emulsion, Oleum Gossypii semen, Oleum Cocois are mixed, under 500-600 rev/min of condition stirring reaction 0.5-1 hour stand-by;
(2) ground barium sulfate, stannic oxide, light calcium carbonate are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 50-60 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.
The invention has the beneficial effects as follows: the present invention forms conducting film by adding the conductive compositions such as stannic oxide, nanometer silver at metope, realizes anti-electrostatic radiation, greatly can improve radiation-proof effect, reduce the harm of Radiation On Human body; Coordinate the interpolation of mixed plant slurry, antibacterial, antiviral, corrosion-resistant, smell is pure and fresh, improves Air quality; Production technique of the present invention is simple, and safety and environmental protection, easily brushing, paint film splitting resistance are good, for the canyon in various place.
Specific embodiments
Below by specific examples, the present invention is described in detail.
Be specifically designed to an Antistatic radiation-proof emulsion paint for canyon, be made up of the raw material of following weight part (kilogram): acrylate and vinyl acetate emulsion 28, Oleum Gossypii semen 3, Oleum Cocois 1, ethoxylated dodecyl alcohol sodium sulfate 2, Natvosol 2, anhydrous aluminium silicate 5, nanometer silver 2, ground barium sulfate 7, stannic oxide 2, light calcium carbonate 25, water 90, mixed plant slurry 7;
Described mixed plant slurry is prepared from by the raw material of following weight part (kilogram): horseradish 3.5, Hemp Eupatorium 1, peppermint 2, borneol 0.8, Radix Gentianae 3, the leaf of bamboo 2.5, white bamboo charcoal 2, carboxymethyl cellulose 3, guar gum 1, water 45; Preparation method is after horseradish, Hemp Eupatorium, peppermint, borneol, Radix Gentianae, the leaf of bamboo being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then carboxymethyl cellulose, guar gum are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
A kind of Antistatic radiation-proof emulsion paint being specifically designed to canyon of the present invention, be made up of following concrete steps:
(1) acrylate and vinyl acetate emulsion, Oleum Gossypii semen, Oleum Cocois are mixed, under 500-600 rev/min of condition stirring reaction 0.5-1 hour stand-by;
(2) ground barium sulfate, stannic oxide, light calcium carbonate are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 50-60 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.
This emulsion paint can adopt the form of construction work of roller coating to construct.The emulsion paint appearance of film obtained according to the method is normal, and be less than 2 hours time of drying, water-fast 96 hours without exception, and alkaline-resisting 48 hours without exception, and abrasion resistance is greater than 2000 times.
Claims (2)
1. one kind is specifically designed to the Antistatic radiation-proof emulsion paint of canyon, it is characterized in that, be made up of the raw material of following weight part: acrylate and vinyl acetate emulsion 28-30, Oleum Gossypii semen 3-5, Oleum Cocois 1-2, ethoxylated dodecyl alcohol sodium sulfate 2-3, Natvosol 2-4, anhydrous aluminium silicate 5-7, nanometer silver 2-3, ground barium sulfate 7-9, stannic oxide 2-4, light calcium carbonate 25-27, water 90-95, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: horseradish 3.5-4.5, Hemp Eupatorium 1-2, peppermint 2-3, borneol 0.8-1, Radix Gentianae 3-4, leaf of bamboo 2.5-3.5, white bamboo charcoal 2-3, carboxymethyl cellulose 3-5, guar gum 1-1.5, water 45-50; Preparation method is after horseradish, Hemp Eupatorium, peppermint, borneol, Radix Gentianae, the leaf of bamboo being cleaned up, and then dry 3-5 hour at 60 DEG C-70 DEG C puts into pulverizer and be ground into 300-500 object mixed powder; Then carboxymethyl cellulose, guar gum are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
2. a kind of Antistatic radiation-proof emulsion paint being specifically designed to canyon according to claim 1, is characterized in that, be made up of following concrete steps:
(1) acrylate and vinyl acetate emulsion, Oleum Gossypii semen, Oleum Cocois are mixed, under 500-600 rev/min of condition stirring reaction 0.5-1 hour stand-by;
(2) ground barium sulfate, stannic oxide, light calcium carbonate are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 50-60 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.