CN105086532A - Novel healthy emulsion paint with lignum cinnamomi camphorae powder replacing filler partially and preparation method thereof - Google Patents

Abstract

The invention discloses novel healthy emulsion paint with lignum cinnamomi camphorae powder replacing filler partially. The novel healthy emulsion paint is characterized by comprising, by weight, 2-3 parts of poly-alpha-vinyltoluene resin, 4-6 parts of acrylonitrile, 24-26 parts of fluorocarbon emulsion, 2-3 parts of magnesium oxide, 0.7-0.9 part of a cross-linking agent, 2-4 parts of water glass, 3-5 parts of precipitated barium sulfate, 5-7 parts of nanometer white earth, 4-6 parts of lignum cinnamomi camphorae powder, 14-17 parts of light calcium carbonate, 2-3 parts of dodecanol ester, 90-95 parts of water and 7-9 parts of mixing plant slurry. According to the novel healthy emulsion paint, the lignum cinnamomi camphorae powder is added into the emulsion paint, raw materials are abundant, the weight is low, the adhesive force to walls and the like is good, and the effects of insect bite control and the like are achieved; due to the addition of the mixing plant slurry, the original plant fragrance can resist bacteria and viruses, and the air quality index is improved. The high plant composition is adopted, so that the heavy metal content is lowered, and the novel healthy emulsion paint is environmentally friendly, healthy and suitable for a place needing the healthy indoor environment.

Description

New type health emulsion paint of a kind of Camphorwood powder Some substitute filler and preparation method thereof

Technical field

The present invention relates to a kind of coating and preparation method thereof, particularly a kind of new type health emulsion paint and preparation method thereof of Camphorwood powder Some substitute filler.

Background technology

Camphorwood is aiphyllium, and vegetative period is slow, is traditional rare famous and precious timber.Camphorwood can give out special strong fragrance, does not wane year in year out, and this fragrance makes Camphorwood furniture have unique utility function: insect protected is mothproof.The high-grade clothings such as wool, cashmere, silk, linen-cotton, eider down, the collectibles such as stamp, calligraphy and painting, books are put into wherein, and not only worm is not moth-eaten, and fragrant odour, refreshing.Energy insect protected, anticorrosion, deodorizing.

The present invention, by fillers such as Camphorwood powder Some substitute titanium dioxide, reduce cost, and the emulsion paint made also can be used for wood furniture, well can be attached together with wood furniture, of many uses.

Summary of the invention

The object of this invention is to provide new type health emulsion paint of a kind of Camphorwood powder Some substitute filler and preparation method thereof.

In order to realize object of the present invention, the present invention is by following scheme implementation:

A new type health emulsion paint for Camphorwood powder Some substitute filler, is made up of the raw material of following weight part: poly alpha methylstyrene resin 2-3, vinyl cyanide 4-6, fluorine carbon emulsion 24-26, magnesium oxide 2-3, linking agent TAIC0.7-0.9, water glass 2-4, process white 3-5, nanometer carclazyte 5-7, Camphorwood powder 4-6, light calcium carbonate 14-17, Lauryl Alcohol ester 2-3, water 90-95, mixed plant slurry 7-9;

Described mixed plant slurry is prepared from by the raw material of following weight part: wrinkled giant hyssop 2-3, tarragon 1-2, pomegranate rind 3-4, Root-bark of Densefruit Pittany 2.5-3.5, fragrant dill 1-2, N.F,USP MANNITOL 1-2, redispersable latex powder 1-2, polyvinyl alcohol 2-3, kaolin 2.5-3.5, Viscotrol C 1-2, water 40-45; Preparation method is after wrinkled giant hyssop, tarragon, pomegranate rind, Root-bark of Densefruit Pittany, fragrant dill being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, then puts into pulverizer and be ground into 300-500 object mixed powder; Then redispersable latex powder, polyvinyl alcohol are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.

The new type health emulsion paint of a kind of Camphorwood powder Some substitute filler of the present invention, be made up of following concrete steps:

(1) poly alpha methylstyrene resin is heated to melting, is incubated 0.5-1 hour while stirring, is then cooled to room temperature, slowly adds vinyl cyanide, fluorine carbon emulsion, linking agent TAIC, stirring reaction 30-40 minute, stand-by;

(2) just Camphorwood dried bean noodles dry after and process white, light calcium carbonate put into sand mill, grinding 1.5-2 hour, obtain 600-800 powder material, then add all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;

(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.

The invention has the beneficial effects as follows: Camphorwood powder adds in emulsion paint by the present invention's interpolation, abundant raw material, light weight, good with the sticking power such as metope, and there is the effects such as Anti-moth-eating, coordinate the interpolation of mixed plant slurry, the former perfume (or spice) of plant can anti-bacteria and anti-virus, improves air quality index; The plant constituent that the present invention adopts composition high, and heavy metal content in emulsion paint can be reduced, environment protection health, the place being applicable to the healthy indoor environment of demand uses.

Specific embodiments

Below by specific examples, the present invention is described in detail.

A new type health emulsion paint for Camphorwood powder Some substitute filler, is made up of the raw material of following weight part (kilogram): poly alpha methylstyrene resin 2, vinyl cyanide 4, fluorine carbon emulsion 24, magnesium oxide 2, linking agent TAIC0.7, water glass 2, process white 3, nanometer carclazyte 5, Camphorwood powder 4, light calcium carbonate 14, Lauryl Alcohol ester 2, water 90, mixed plant slurry 7;

Described mixed plant slurry is prepared from by the raw material of following weight part (kilogram): wrinkled giant hyssop 2, tarragon 1, pomegranate rind 3, Root-bark of Densefruit Pittany 2.5, fragrant dill 1, N.F,USP MANNITOL 1, redispersable latex powder 1, polyvinyl alcohol 2, kaolin 2.5, Viscotrol C 1, water 40; Preparation method is after wrinkled giant hyssop, tarragon, pomegranate rind, Root-bark of Densefruit Pittany, fragrant dill being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, then puts into pulverizer and be ground into 300-500 object mixed powder; Then redispersable latex powder, polyvinyl alcohol are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.

The new type health emulsion paint of a kind of Camphorwood powder Some substitute filler of the present invention, be made up of following concrete steps:

(1) poly alpha methylstyrene resin is heated to melting, is incubated 0.5-1 hour while stirring, is then cooled to room temperature, slowly adds vinyl cyanide, fluorine carbon emulsion, linking agent TAIC, stirring reaction 30-40 minute, stand-by;

(2) just Camphorwood dried bean noodles dry after and process white, light calcium carbonate put into sand mill, grinding 1.5-2 hour, obtain 600-800 powder material, then add all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;

(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.

This emulsion paint can adopt the form of construction work of roller coating to construct.The emulsion paint appearance of film obtained according to the method is normal, and be less than 2 hours time of drying, water-fast 96 hours without exception, and alkaline-resisting 48 hours without exception, and abrasion resistance is greater than 2000 times.

Claims (2)

1. the new type health emulsion paint with Camphorwood powder Some substitute filler, it is characterized in that, be made up of the raw material of following weight part: poly alpha methylstyrene resin 2-3, vinyl cyanide 4-6, fluorine carbon emulsion 24-26, magnesium oxide 2-3, linking agent TAIC0.7-0.9, water glass 2-4, process white 3-5, nanometer carclazyte 5-7, Camphorwood powder 4-6, light calcium carbonate 14-17, Lauryl Alcohol ester 2-3, water 90-95, mixed plant slurry 7-9;

Described mixed plant slurry is prepared from by the raw material of following weight part: wrinkled giant hyssop 2-3, tarragon 1-2, pomegranate rind 3-4, Root-bark of Densefruit Pittany 2.5-3.5, fragrant dill 1-2, N.F,USP MANNITOL 1-2, redispersable latex powder 1-2, polyvinyl alcohol 2-3, kaolin 2.5-3.5, Viscotrol C 1-2, water 40-45; Preparation method is after wrinkled giant hyssop, tarragon, pomegranate rind, Root-bark of Densefruit Pittany, fragrant dill being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, then puts into pulverizer and be ground into 300-500 object mixed powder; Then redispersable latex powder, polyvinyl alcohol are put into water and stirred, be heated to 65 DEG C-70 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.

2. the new type health emulsion paint of a kind of Camphorwood powder Some substitute filler according to claim 1, is characterized in that, be made up of following concrete steps:

(1) poly alpha methylstyrene resin is heated to melting, is incubated 0.5-1 hour while stirring, is then cooled to room temperature, slowly adds vinyl cyanide, fluorine carbon emulsion, linking agent TAIC, stirring reaction 30-40 minute, stand-by;

(2) just Camphorwood dried bean noodles dry after and process white, light calcium carbonate put into sand mill, grinding 1.5-2 hour, obtain 600-800 powder material, then add all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;

(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.