CN107385947A - A kind of nano-bamboo carbon PU synthesis of artificial leather and its manufacture method - Google Patents
A kind of nano-bamboo carbon PU synthesis of artificial leather and its manufacture method Download PDFInfo
- Publication number
- CN107385947A CN107385947A CN201710479282.1A CN201710479282A CN107385947A CN 107385947 A CN107385947 A CN 107385947A CN 201710479282 A CN201710479282 A CN 201710479282A CN 107385947 A CN107385947 A CN 107385947A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- bamboo
- synthesis
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of nano-bamboo carbon PU synthesis of artificial leathers and preparation method thereof, this method includes preparation, hot pressing fitting and the stoving process of the preparation of nano bamboo powdered carbon, the preparation of coatings slurry and adhesive linkage slurry, cortical layer and epithelium surface layer.Bamboo charcoal nano (nano modified bamboo charcoal) is applied in artificial leather production by the present invention, coordinate new preparation method, strict control technological production norm, make obtained bamboo charcoal nano artificial leather that there is powerful adsorptivity, and detoxicating, deodorization, purification and killing pathogenic microorganism effect;Using the new making raw material of nano-bamboo carbon PU synthesis of artificial leathers, add stearin and amino improves silicone oil, and the auxiliary agent of some row so that leather obtains very big improvement in quality, and color and luster is vivider, feels rich in oil, also increases the flexibility of leather;Whole Making programme is simple, conveniently realizes mass production, while also contribute to the protection of environment.
Description
Technical field
The present invention relates to dermatine technical field, more particularly to a kind of nano-bamboo carbon PU synthesis of artificial leather and its manufacture
Method.
Background technology
Because the genuine leather fabric common people of costliness can not consume, in response to the market demand, the artificial leather of counterfeit corium is gradually popular
Get up, be widely used in clothing, system bag.In China, it is accustomed to be that the artificial leather that raw material produces is referred to as PVC people with polyvinyl chloride resin
Fabricate-leather (abbreviation artificial leather), artificial leather is using polyvinyl chloride as coating material, using conventional fabrics as base fabric;With PU resins and non-woven fabrics
Artificial leather for raw material production is referred to as PU synthetic leather (abbreviation synthetic leather), and synthetic leather is using polyurethane resin as coating material, with non-
Woven cloths are base fabric.Also there is composite artificial leather (synthesis of artificial leather) in the market, i.e., by PVC and PU interworkings, or PVC, PU points
It is not modified with other materials interworking, so as to obtain the artificial leather with a performance requirement.The development experience of artificial leather
Three generation products, it is PVC (polyvinyl chloride) artificial leather, PU (polyurethane) artificial leather, superfine fibre artificial leather respectively.
Bamboo charcoal nano is by nanometer light catalyst material TiO with advanced technology2Load to the large, medium and small hole of bamboo charcoal
On gap wall and bamboo charcoal surface, make bamboo charcoal and photocatalyst material TiO2Perfect adaptation, thus the strong adsorptivity with bamboo charcoal matter, together
When also there is the performance of nano photocatalyst catalytic material, the organic substance of absorption, can be passed through ammonia, formaldehyde, phenol in such as air
TiO2In the presence of light, the OH that discharges-Ionization, it is decomposed into water and CO2, additionally with by virus, bacterium cell
Film and cytoplasmic protein denaturation and kill, thus with powerful adsorptivity, detoxicating, deodorization, purification and kill cause of disease it is micro-
Biological agent, it can be widely applied among industrial and agricultural production and environmental improvement, house life.
A kind of making side of bamboo charcoal nano PU synthesis of artificial leathers is disclosed in Publication No. CN104499300A file
Method, the production technology combined using Nano grade bamboo charcoal powder and artificial leather, obtains certain performance boost.But it is simply accomplished
Simply it is combined, many defects is present in the preparation of the raw material of artificial leather and bamboo charcoal, can not obtain more preferable Leather Properties,
Need improvement badly.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of nano-bamboo carbon PU synthesis of artificial leather and its manufacturer
Method, the invention solve Conventional nano bamboo charcoal and defect present on artificial leather combination technology, and provide a little improved places.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of preparation method of nano-bamboo carbon PU synthesis of artificial leathers, comprises the following steps:
A, bamboo charcoal powder is prepared by conventional pyrolysis technique, and is put into micronizer and is crushed to 120-150 mesh, by bamboo charcoal
Powder, which is put into boiling water, is made suspension, then by 4%-5% nano-TiO2With 3%-5% nano-TiO2Stabilizer mixes simultaneously
Mixed emulsion is made, after mixed emulsion and bamboo charcoal powder suspension are mixed, high temperature evaporation is abundant, and Ultramicro-powder is put into after drying
100-120 mesh is crushed in broken machine, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, is coated in after mixing and is at the uniform velocity driven
Release liners on, and obtain cortical layer with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into casting machine and flowed
Prolong film forming, casting temperature is controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, prepare base cloth layer, the epithelium surface layer that step c is obtained is covered on base cloth layer, cortical layer is then covered in skin
On film surface layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
Further improvement is that the coatings slurry is in parts by weight by aqueous polyurethane 50-60 parts, calcium carbonate 8-10
Part, stearin 5-8 parts, amino improve silicone oil 3-5 parts, bactericide 3-5 parts, plasticiser 4-6 parts, foaming agent 2-4 parts, colouring agent 1-
4 parts are mixed.
Further improvement is that the adhesive linkage slurry is in parts by weight by neoprene 5-8 parts, hydrogenation nitrile rubber 3-
5 parts, terpene resin 1-3 parts, formaldehyde 1-2 parts, dibasic stearic acid 3-5 parts is mixed.
Further improvement is that the nano-TiO2Stabilizer in polyvinylpyrrolidone or polystyrene one
Kind.
Further improvement is that the suspension described in step a is bamboo charcoal powder and boiling water 1:2-1:3 ratio mixing system
Into.
A kind of nano-bamboo carbon PU synthesis of artificial leathers, are made using above-mentioned preparation method.
The beneficial effects of the invention are as follows:
1) bamboo charcoal nano (nano modified bamboo charcoal) is applied in artificial leather production, coordinates new preparation method, strict control
Technological production norm processed, make obtained bamboo charcoal nano artificial leather that there is powerful adsorptivity, and detoxicating, deodorization, purify and kill
The pathogenic microorganism that goes out acts on;
2) using the new making raw material of nano-bamboo carbon PU synthesis of artificial leathers, add stearin and amino improve silicone oil,
And the auxiliary agent of some row so that leather obtains very big improvement in quality, and color and luster is vivider, rich in oil sense, also increases
Add the flexibility of leather;
3) whole Making programme is simple, conveniently realizes mass production, while also contribute to the protection of environment.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A, the trunk for choosing the bamboo of more than 3 years is cut into bamboo chip, with the conventional pyrolysis that carburizing temperature is 600 DEG C -800 DEG C
Technique processes to obtain the bamboo charcoal powder of 120-130 mesh, by bamboo charcoal powder and boiling water with 1:2 ratio is mixed to prepare suspension, then will
4% nano-TiO2With 3% nano-TiO2Stabilizer mix, be sufficiently stirred 30min and mixed emulsion be made, by mixed emulsion with
After bamboo charcoal powder suspension mixes, high temperature evaporation is abundant at 100 DEG C, is put into after drying in micronizer and is crushed to 100-
120 mesh, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, is coated in after mixing and is at the uniform velocity driven
Release liners on, and obtain 0.1-0.2mm cortical layer with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into
Casting film-forming in casting machine, casting temperature are controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, interweaved with non-woven fabrics and conventional fabrics (such as thin silk fabric) and base cloth layer is made, the epithelium surface layer that step c is obtained covers
On base cloth layer, then cortical layer is covered on epithelium surface layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
Embodiment 2
A, the trunk for choosing the bamboo of more than 3 years is cut into bamboo chip, with the conventional pyrolysis that carburizing temperature is 600 DEG C -800 DEG C
Technique processes to obtain the bamboo charcoal powder of 120-130 mesh, by bamboo charcoal powder and boiling water with 1:2 ratio is mixed to prepare suspension, then will
4% nano-TiO2With 5% nano-TiO2Stabilizer mix, be sufficiently stirred 30min and mixed emulsion be made, by mixed emulsion with
After bamboo charcoal powder suspension mixes, high temperature evaporation is abundant at 100 DEG C, is put into after drying in micronizer and is crushed to 100-
120 mesh, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, is coated in after mixing and is at the uniform velocity driven
Release liners on, and obtain 0.1-0.2mm cortical layer with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into
Casting film-forming in casting machine, casting temperature are controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, interweaved with non-woven fabrics and conventional fabrics (such as thin silk fabric) and base cloth layer is made, the epithelium surface layer that step c is obtained covers
On base cloth layer, then cortical layer is covered on epithelium surface layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
Embodiment 3
A, the trunk for choosing the bamboo of more than 3 years is cut into bamboo chip, with the conventional pyrolysis that carburizing temperature is 600 DEG C -800 DEG C
Technique processes to obtain the bamboo charcoal powder of 120-130 mesh, by bamboo charcoal powder and boiling water with 1:2 ratio is mixed to prepare suspension, then will
5% nano-TiO2With 3% nano-TiO2Stabilizer mix, be sufficiently stirred 30min and mixed emulsion be made, by mixed emulsion with
After bamboo charcoal powder suspension mixes, high temperature evaporation is abundant at 100 DEG C, is put into after drying in micronizer and is crushed to 100-
120 mesh, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, is coated in after mixing and is at the uniform velocity driven
Release liners on, and obtain 0.1-0.2mm cortical layer with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into
Casting film-forming in casting machine, casting temperature are controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, interweaved with non-woven fabrics and conventional fabrics (such as thin silk fabric) and base cloth layer is made, the epithelium surface layer that step c is obtained covers
On base cloth layer, then cortical layer is covered on epithelium surface layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
Embodiment 4
A, the trunk for choosing the bamboo of more than 3 years is cut into bamboo chip, with the conventional pyrolysis that carburizing temperature is 600 DEG C -800 DEG C
Technique processes to obtain the bamboo charcoal powder of 120-130 mesh, by bamboo charcoal powder and boiling water with 1:2 ratio is mixed to prepare suspension, then will
5% nano-TiO2With 5% nano-TiO2Stabilizer mix, be sufficiently stirred 30min and mixed emulsion be made, by mixed emulsion with
After bamboo charcoal powder suspension mixes, high temperature evaporation is abundant at 100 DEG C, is put into after drying in micronizer and is crushed to 100-
120 mesh, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, is coated in after mixing and is at the uniform velocity driven
Release liners on, and obtain 0.1-0.2mm cortical layer with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into
Casting film-forming in casting machine, casting temperature are controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, interweaved with non-woven fabrics and conventional fabrics (such as thin silk fabric) and base cloth layer is made, the epithelium surface layer that step c is obtained covers
On base cloth layer, then cortical layer is covered on epithelium surface layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
Coatings slurry changes by 55 parts of aqueous polyurethane, 8 parts of calcium carbonate, 6 parts of stearin, amino in the various embodiments described above
Enter 4 parts of silicone oil, 4 parts of bactericide, 5 parts of plasticiser, 3 parts of foaming agent, 2 parts of colouring agent to be mixed.
Wherein, bactericide is dimethylformamide (DMF), and plasticiser is dimethanol dioctyl ester (DOP), and foaming agent is sent out for AC
Infusion, colouring agent are needed voluntarily to choose different type by processing.
In the various embodiments described above adhesive linkage slurry by 6 parts of neoprene, hydrogenation 4 parts of nitrile rubber, 2 parts of terpene resin,
1 part of formaldehyde, 5 parts of dibasic stearic acid are mixed.
Nano-TiO in the various embodiments described above2Stabilizer is polyvinylpyrrolidone (PVP).
The basic principles, principal features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, the original for simply illustrating the present invention described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent circle
It is fixed.
Claims (6)
1. a kind of preparation method of nano-bamboo carbon PU synthesis of artificial leathers, it is characterised in that comprise the following steps:
A, bamboo charcoal powder is prepared by conventional pyrolysis technique, and is put into micronizer and is crushed to 120-150 mesh, bamboo charcoal powder is put
Enter and suspension is made in boiling water, then by 4%-5% nano-TiO2With 3%-5% nano-TiO2Stabilizer is mixed and is made
Mixed emulsion, after mixed emulsion and bamboo charcoal powder suspension are mixed, high temperature evaporation is abundant, and micronizer is put into after drying
In be crushed to 100-120 mesh, it is standby that nano bamboo powdered carbon is made;
B, configure coatings slurry in disposed chamber and adhesive linkage slurry is standby;
C, by nano bamboo powdered carbon and coatings slurry with 1:3 part by weight mixing, after mixing coated in be at the uniform velocity driven from
On type paper, and cortical layer is obtained with 105 DEG C of drying, it is standby to be cooled to normal temperature;Adhesive linkage slurry is put into casting machine and is cast into
Film, casting temperature are controlled at 140 DEG C -150 DEG C, and it is standby to form epithelium surface layer;
D, prepare base cloth layer, the epithelium surface layer that step c is obtained is covered on base cloth layer, cortical layer is then covered in epithelium face
On layer, hot pressing fitting 20s, obtains semi-finished product at 120 DEG C;
E, semi-finished product are placed at 130 DEG C and dried, nano-bamboo carbon PU synthesis of artificial leathers are made.
A kind of 2. preparation method of nano-bamboo carbon PU synthesis of artificial leathers according to claim 1, it is characterised in that:It is described
Coatings slurry improves silicone oil by aqueous polyurethane 50-60 parts, calcium carbonate 8-10 parts, stearin 5-8 parts, amino in parts by weight
3-5 parts, bactericide 3-5 parts, plasticiser 4-6 parts, foaming agent 2-4 parts, colouring agent 1-4 parts are mixed.
A kind of 3. preparation method of nano-bamboo carbon PU synthesis of artificial leathers according to claim 1, it is characterised in that:It is described
Adhesive linkage slurry is in parts by weight by neoprene 5-8 parts, hydrogenation nitrile rubber 3-5 parts, terpene resin 1-3 parts, formaldehyde 1-2
Part, dibasic stearic acid 3-5 parts are mixed.
A kind of 4. preparation method of nano-bamboo carbon PU synthesis of artificial leathers according to claim 1, it is characterised in that:It is described
Nano-TiO2The one kind of stabilizer in polyvinylpyrrolidone or polystyrene.
A kind of 5. preparation method of nano-bamboo carbon PU synthesis of artificial leathers according to claim 1, it is characterised in that:Step
Suspension described in a is bamboo charcoal powder and boiling water 1:2-1:3 ratio is mixed.
A kind of 6. nano-bamboo carbon PU synthesis of artificial leathers, it is characterised in that:Using the making side described in claim any one of 1-5
Method is made.