CN101508549A - Water-proof jade powder paint - Google Patents
Water-proof jade powder paint Download PDFInfo
- Publication number
- CN101508549A CN101508549A CNA200910010626XA CN200910010626A CN101508549A CN 101508549 A CN101508549 A CN 101508549A CN A200910010626X A CNA200910010626X A CN A200910010626XA CN 200910010626 A CN200910010626 A CN 200910010626A CN 101508549 A CN101508549 A CN 101508549A
- Authority
- CN
- China
- Prior art keywords
- water
- polyvinyl alcohol
- jade powder
- reactor
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A water-proof jade powder coating is characterized in that the coating is prepared by the following ingredients with the proportion by weight: 5-15 of polyvinyl alcohol, 50-100 of water, 1-2 of 4% (weight) sodium tetraborate solution, 5-10 of sodium bentonite, 25-40 of jade powder (400 mesh), 5-15 of white cement, 0.1-0.5 of SKANEM-8 mould inhibitor and 0.1-0.25 of NATROSOL250 thickener; polyvinyl alcohol is added into a reaction vessel and then water is added and heated to cause the polyvinyl alcohol to be completely dissolved; the sodium tetraborate solution is dropped into the reaction vessel and conduct cross linking reaction with the polyvinyl alcohol, and the polyvinyl alcohol is gelated; cooling water is used for cooling reaction to obtain colorless glue and then the sodium bentonite, jade powder, white cement, mould inhibitor and NATROSOL250 thickener are added; after being stirred evenly, the mixture is put into a grinder for grinding, thus preparing the water-proof jade powder coating.
Description
Technical field
The present invention relates to the architectural decoration coating material field, relate to a kind of water-proof jade powder paint concretely.
Background technology
The interior wall coating that existing market is sold, all contain harmful volatile organic compounds, as free formaldehyde, soluble heavy metal lead, copper, chromium, mercury etc., what have also has a radioactive substance, as gamma ray etc.,, also can slowly volatilize for a long time even be strict controlled in the national standard, people's refreshing smart and respiratory system constituted endanger, its peculiar smell of dispelling, antibiotic, anti-mildew, sticking power, intensity, physicochemical property such as shock-resistant, fire-retardant, ageing-resistant are relatively poor.Be used for now porcelain-imitated coating that indoor wall, top ceiling decorate in addition on the market, just change coating, dry powder paint etc., owing to do not have waterproof, moisture proof, leakage performance, in case body of wall, top ceiling etc. have drainage, coating is just drenched easily, cause fall in flakes, efflorescence, mouldy, can not adapt to the needs of modern architecture decorations industry.
Summary of the invention
The present invention contains volatile organic compounds and the relatively poor deficiency of physicochemical property in order to overcome existing interior wall coating, and it is main interior wall coating that a kind of jade powder is provided; The object of the present invention is to provide a kind of waterproof, mildew-resistant, strong adhesion, not efflorescence, can not only reach the inner wall decoration purpose with conventional construction technology construction, and utilize the intrinsic chemical property of jade, reach a kind of water-proof jade powder paint of indoor environment-friendly decorative effect.
Another object of the present invention is to provide the preparation method of this water [proof coating materials.
Water [proof provided by the invention village coating, make by the following weight proportion raw material:
Polyvinyl alcohol 5～15, water 50～100,0.4% (weight) sodium tetraborate solution 1～2, sodium bentonite 5～10, jade powder (400 order) 25～40, white cement 5～15, SKANEM-8 mould inhibitor 0.1～0.5, NATROSOL250 thickening material 0.1～0.25.
Above-mentioned raw materials is prepared method of the present invention, may further comprise the steps successively:
(1) polyvinyl alcohol is added in the reactor, add entry then, stir, heating water temperature to 90～100 ℃ make that polyvinyl alcohol dissolves fully in the reactor;
(2) sodium tetraborate solution is slowly splashed in the reactor and polyvinyl alcohol generation crosslinking reaction in the thread mode under constantly stirring;
(3) drip off sodium tetraborate solution after, kept 75～80 ℃ of thermotonuses 40～60 minutes, make polyvinyl alcohol gelization;
(4) reacted after, use the water quench reactor, make its temperature reduce to 20～30 ℃, filter, colorless glue;
(5) above-mentioned colorless glue is added in the stirrer, add sodium bentonite, jade powder and white cement again, start is stirred, and after 50～70 minutes, adds the SKANEM-8 mould inhibitor, continues to stir after 5～15 minutes, adds the NATROSOL250 thickening material, and then stirs;
(6) stir after, put into shredder and grind, promptly make waterproof paint of the present invention.
The present invention with existing various imitative porcelain, just change coating and compare, have that waterproof, protection against the tide, mildew-resistant, water logging are non-leakage, bonding strong adhesion, not efflorescence, do not come off, characteristics such as nonpoisonous and tasteless, long service life, easy construction, be applicable to luxurious hotel, office building, interior decoration at home, also can be used as the waterproof paint of vault, underground storehouse body of wall.
Embodiment
The present invention is further illustrated below in conjunction with embodiment.
Embodiment 1:
The 50kg polyvinyl alcohol is added in the reactor, add 50kg water then, stir, heating water temperature to 50 ℃ makes that polyvinyl alcohol dissolves fully in the reactor; Be that 0.4% sodium tetraborate solution slowly splashes in the reactor and polyvinyl alcohol generation crosslinking reaction in the thread mode under constantly stirring with the 1kg concentration expressed in percentage by weight: after dripping off sodium tetraborate solution, kept 75 ℃ of thermotonuses 40 minutes, and made polyvinyl alcohol gelization; After having reacted, use the water quench reactor, make its temperature battle array to 22 ℃, filter, colorless glue; Above-mentioned colorless glue is added in the stirrer, add 5kg sodium bentonite, 25kg jade powder and 5kg white cement again, start is stirred, and after 50 minutes, adds 0.1kg SKANEM-8 mould inhibitor, continue to stir after 8 minutes, add the 0.1kgNATROSOL250 thickening material, and then stir, after stirring, put into shredder and grind, promptly make waterproof paint of the present invention.
Embodiment 2
The 80kg polyvinyl alcohol is added in the reactor, add 10kg water then, stir, heating water temperature to 95 ℃ makes that polyvinyl alcohol dissolves fully in the reactor; Be that 0.4% sodium tetraborate solution slowly splashes in the reactor and polyvinyl alcohol generation crosslinking reaction in the thread mode under constantly stirring with the 1.5kg concentration expressed in percentage by weight; After dripping off sodium tetraborate solution, kept 78 ℃ of thermotonuses 50 minutes, make polyvinyl alcohol gelization; After having reacted, use the water quench reactor, make its temperature reduce to 25 ℃, filter, get colorless glue; Above-mentioned colorless glue is added in the stirrer, add 8kg sodium bentonite, 30kg jade powder and 10kg white cement again, start is stirred, and after 60 minutes, adds the 0.3kgSKANEM-8 mould inhibitor, continue to stir after 10 minutes, add the 0.2kgNATROSOL250 thickening material, and then stir, after stirring, put into shredder and grind, promptly make waterproof paint of the present invention.
Embodiment 3
The 100kg polyvinyl alcohol is added in the reactor, add 15kg water then, stir, heating water temperature to 100 ℃ makes that polyvinyl alcohol dissolves fully in the reactor; Be that 0.4% sodium tetraborate solution slowly splashes in the reactor and acid polyethylene generation crosslinking reaction in the thread mode under constantly stirring with the 2kg concentration expressed in percentage by weight; After dripping off sodium tetraborate solution, visit and held 80 ℃ of thermotonuses 60 minutes, make polyvinyl alcohol gelization; After having reacted, use the water quench reactor, make its temperature reduce to 30 ℃, filter, get colorless glue: above-mentioned colorless glue is added in the stirrer, add 10kg sodium bentonite, 40kg jade powder and 15kg white cement again, start is stirred, and after 70 minutes, adds the 0.5kgSKANEM-8 mould inhibitor, continue to stir after 15 minutes, add the 0.25kgNATROSOL250 thickening material, and then stir, after stirring, put into shredder and grind, promptly make waterproof paint of the present invention.
Claims (2)
1, a kind of water-proof jade powder paint is characterized in that being made by the following weight proportion raw material:
Polyvinyl alcohol 5～15, water 50～100,0.4% (weight) sodium tetraborate solution 1～2, sodium bentonite 5～10, jade powder (400 order) 25～40, white cement 5～15, SKANEM-8 mould inhibitor 0.1～0.5, NATROSOL250 thickening material 0.1～0.25.
2, the preparation method of a kind of water-proof jade powder paint according to claim 1 may further comprise the steps successively:
(1) polyvinyl alcohol is added in the reactor, add entry then, stir, heating water temperature to 90～100 ℃ make that polyvinyl alcohol dissolves fully in the reactor;
(2) sodium tetraborate solution is slowly splashed in the reactor and polyvinyl alcohol generation crosslinking reaction in the thread mode under constantly stirring;
(3) drip off sodium tetraborate solution after, kept 75-80C thermotonus 4M0 minute, make polyvinyl alcohol gelization;
(4) reacted after, use the water quench reactor, make its temperature reduce to 20-30t, filter, colorless glue;
(5) above-mentioned colorless glue is added in the stirrer, add sodium bentonite, jade powder and white cement again, start is stirred, and after 50-70 minutes, adds SXIWEM-8 anti-virus agent, continues to stir 5～after going through minute, add the NATROSOL250 thickening agents, and then stir;
(6) stir after, put into shredder and grind, promptly make water-proof jade powder paint.