CN108716054A - A kind of novel natural feather directly fills fabric and its production technology - Google Patents
A kind of novel natural feather directly fills fabric and its production technology Download PDFInfo
- Publication number
- CN108716054A CN108716054A CN201810424338.8A CN201810424338A CN108716054A CN 108716054 A CN108716054 A CN 108716054A CN 201810424338 A CN201810424338 A CN 201810424338A CN 108716054 A CN108716054 A CN 108716054A
- Authority
- CN
- China
- Prior art keywords
- fabric
- compound
- cloth
- permeable membrane
- natural feather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to textile production fields, and in particular to a kind of novel natural feather directly fills fabric and its production technology.A kind of novel natural feather directly fills permeable membrane in permeable membrane in fabric, including face cloth, first, the double-deck channel cloth of knitting, second.Permeable membrane is complex as face layer in the face reverse of the cloth and first, the one side of knitting channel cloth is complex as bottom with permeable membrane in second, the another side of permeable membrane and bottom knitting channel cloth is compound in the first of face layer, obtains that the present invention does not bore suede and the good novel natural feather of penetrability directly fills fabric.The present invention is using stepped combined technique three times, and each bridging reaction ample time, combination process selects hot melt adhesive, and strictly controls hot melt adhesive dosage, combined temp, and tension etc. so that each layer is compound securely, not strike-through.It is knitted the weaving manner of channel cloth simultaneously, can also play the effect of compound not strike-through, and gained fabric hand feel is soft.
Description
Technical field
The invention belongs to textile production fields, and in particular to a kind of novel natural feather directly fills fabric and its production technology.
Background technology
As the improvement of people's living standards, people had both required clothes to meet outside traditional function of cold, more focus on clothes
Decorative beauty, it is desirable that clothes fashion is novel, dress is beautiful, generous proper, comfortable and easy to wear, and considers clothing function comprehensively.With day
Right natural feather is the textile fabrics of filler, has the characteristics such as light, soft, fluffy, comfortable, is winter excellent warming material,
Increasingly welcome by consumer.And in these down products, down jackets are even more the favor for having won countless consumers.Plumage
Chenille article due to the effects that in use, being often subject to various extruding, rubbing, collision, therefore is susceptible to and bores suede race
The problems such as suede, to affect the normal use of down products, and filoplume is also easy to stick on other articles.Natural feather is solved at present
Product bores there are mainly three types of the methods of suede problem：When overlay film or coating in base fabric, by film or coating come anti-leak-stopping
Suede, second is that high-density fabric is improved the anti-suede performance of fabric itself by post-processing, third, adding one in eiderdown shell fabric inner layer
Layer DOWNPROOF FABRIC.However fabric obtained by these three methods, still need to sew in follow-up use, then generate pin hole, filoplume then easily from
Pin hole drills out.It adds DOWNPROOF FABRIC or using treated high-density fabric, on the one hand increases fabric weight, change feel,
On the other hand, fabric gas permeability can also be affected.Therefore, these methods all in the presence of solve be not thorough or reduce fabric its
The problem of its required performance.
Invention content
In order to solve the above problem, a kind of quasi- novel natural feather of offer of the present invention directly fills fabric and its production technology.
A kind of novel natural feather directly fills permeable membrane in permeable membrane in fabric, including face cloth, first, the double-deck channel cloth of knitting, second.Institute
It states permeable membrane in face reverse of the cloth and first and is complex as face layer, the one side of knitting channel cloth is complex as bottom with permeable membrane in second, institute
It is compound to state the another side of permeable membrane and bottom knitting channel cloth in the first of face layer, obtains novel natural feather of the invention and directly fills fabric.
Knitting channel cloth, levels are woven into arbitrary flower pattern, i.e., are one layer of double-faced jacquard there is flower pattern part levels to interweave
Tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber.
Knitting channel cloth is 50D/72F polyester DTYs, 24 needle knittings on knitted double-faced jacquard machine.
The face cloth can be flexible fabric, for example, elastic spring Asia spinning, spandex fabric, through bullet, latitude elasticity fabric etc..
Permeable membrane in described first, moisture permeability is in 3000-5000g/m2* for 24 hours, thickness is at 12 μm or less.
Permeable membrane in described second, moisture permeability is in 3000-5000g/m2* for 24 hours, thickness is at 15 μm or less.
Knitting channel cloth, in non-flower pattern part, levels are respectively woven to plain weave, in flower pattern part, up and down
Layer is woven to arbitrary double-faced jacquard tissue.
Further, it is spaced in 4cm or more between the cloth Jacquard of the knitting channel.
A kind of novel natural feather directly fills the production technology of fabric, includes the following steps：
S1：Stock, knitting channel cloth use 50D/72F polyester DTYs, and face cloth, which uses, arbitrarily bullet or the fabric without bullet；
S2：Weaving, 24 needle knittings are knitted channel cloth on knitted double-faced jacquard machine, are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber；
S3：Face cloth arranges：Whole addition fluorine element waterproofing agent, makees water-proof finish after the face cloth；
S4：It is compound
It is once-combined：The one side and middle permeable membrane that are knitted channel cloth is compound, and 12-20h of bridging reaction obtains three-in-one bottom；
It is secondary compound：Compound, 12-20h of bridging reaction by face cloth and middle permeable membrane obtains two-in-one face layer；
It is compound three times：By compound good two-in-one face layer with compound good three-in-one bottom compound, 12-20h of bridging reaction,
It obtains novel natural feather and directly fills fabric；
The combination process is compound using hot melt adhesive, and the gluing mode of the hot melt adhesive is dotted gluing, combined temp 95-105
DEG C, hot melt adhesive 8-12gsm of dosage, compound tense, it is 95%-98% that each layer tension, which loosens, composite pressure 0.8Mpa, compound speed
8cm/s。
The beneficial effects of the present invention are：
（1）This directly fills fabric and uses knitting channel cloth and middle permeable membrane compound, passes through the figured texture weave for being knitted channel cloth, forms down-filling
Interval, no quilting is pin-free, has reached and has not bored suede and do not run suede and the good effect of penetrability.Meanwhile being knitted channel cloth and richness
After flexible middle permeable membrane is compound, itself has elasticity, therefore can be combined with each other with flexible face cloth, and face cloth
More comfortable, compound not strike-through is worn, and be resistant to -30 DEG C not by water-proofing treatment to make gained down products that there is elasticity
It is hardened.
（2）Using stepped combined technique three times, each bridging reaction ample time, combination process selects hot melt adhesive, and tight
Lattice control hot melt adhesive dosage, gluing mode, combined temp, tension, low pressure at a slow speed etc. so that each layer is compound securely, not strike-through, flower
Type keeps aesthetic integrity, while dotted gluing and knitting channel cloth can increase the frictional force of down-filling chamber, make after being filled with natural feather, no
Easily run suede.It is knitted the weaving manner of channel cloth simultaneously, can also play the effect of compound not strike-through, and gained fabric hand feel is soft
It is soft.
Specific implementation mode
Below in conjunction with specific implementation mode and specific embodiment, the invention will be further described, it should be noted that with
Lower embodiment is only used as explanation of the invention rather than limiting the scope of the invention, and protection scope of the present invention is to weigh
Subject to the range that sharp claim is showed, in the case where not departing from the scope of the invention defined by claims, to following
The embodiment and embodiment can carry out many alterations and modifications.
A kind of novel natural feather directly fills permeable membrane in permeable membrane in fabric, including face cloth, first, the double-deck channel cloth of knitting, second.The
One, in second the moisture permeability of permeable membrane in 3000-5000g/m2For 24 hours, in first the thickness of permeable membrane at 12 μm hereinafter, in second
The thickness of permeable membrane is at 15 μm or less.The face cloth can be flexible fabric, for example, from elastic spring Asia spinning, spandex fabric, through bullet,
Latitude elasticity fabric etc. can also be arbitrarily without elasticity fabric.Knitting channel cloth, in non-flower pattern part, levels respectively weave
For plain weave, in flower pattern part, levels are woven to arbitrary double-faced jacquard tissue, are spaced between knitting channel cloth Jacquard
In 4cm or more, down-filling is easily facilitated.
Permeable membrane is complex as face layer in the face reverse of the cloth and first, and one side and the permeable membrane in second for being knitted channel cloth are compound
For bottom, the face layer first in the another side of permeable membrane and bottom knitting channel cloth it is compound, obtain the novel natural feather of the present invention
Directly fill fabric.Knitting channel cloth, levels are woven into arbitrary flower pattern, i.e., are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber.
The Jacquard of the knitting channel cloth can be arbitrarily arranged, and can be a kind of repeated arrangement of flower pattern, can also
It is the combination of a variety of flower pattern.
Embodiment 1
A kind of novel natural feather directly fills the production technology of fabric, includes the following steps：
S1：Stock, knitting channel cloth use 50D/72F polyester DTYs, and face cloth, which uses, arbitrarily bullet or the fabric without bullet；
S2：Weaving, 24 needle knittings are knitted channel cloth on knitted double-faced jacquard machine, are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber；
S3：Face cloth arranges：Whole addition fluorine element waterproofing agent, makees water-proof finish after the face cloth；
S4：It is compound
（1）It is once-combined：The one side and middle permeable membrane that are knitted channel cloth is compound, and bridging reaction 12h obtains three-in-one bottom；
（2）It is secondary compound：Compound, the bridging reaction 12h by face cloth and middle permeable membrane obtains two-in-one face layer；
（3）It is compound three times：Compound good two-in-one face layer is compound with compound good three-in-one bottom, bridging reaction 12h is obtained
Fabric is directly filled to novel natural feather；The combination process is compound using hot melt adhesive, and the gluing mode of the hot melt adhesive is dotted gluing,
95 DEG C of combined temp, hot melt adhesive dosage 8gsm, compound tense, it is 95% that tension, which loosens, composite pressure 0.8Mpa, compound speed 8cm/
s。
Embodiment 2
A kind of novel natural feather directly fills the production technology of fabric, includes the following steps：
S1：Stock, knitting channel cloth use 50D/72F polyester DTYs, and face cloth, which uses, arbitrarily bullet or the fabric without bullet；
S2：Weaving, 24 needle knittings are knitted channel cloth on knitted double-faced jacquard machine, are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber；
S3：Face cloth arranges：Whole addition fluorine element waterproofing agent, makees water-proof finish after the face cloth；
S4：It is compound
（1）It is once-combined：The one side and middle permeable membrane that are knitted channel cloth is compound, and bridging reaction 20h obtains three-in-one bottom；
（2）It is secondary compound：Compound, the bridging reaction 20h by face cloth and middle permeable membrane obtains two-in-one face layer；
（3）It is compound three times：Compound good two-in-one face layer is compound with compound good three-in-one bottom, bridging reaction 20h is obtained
Fabric is directly filled to novel natural feather；The combination process is compound using hot melt adhesive, and the gluing mode of the hot melt adhesive is dotted gluing,
105 DEG C of combined temp, hot melt adhesive dosage 12gsm, compound tense, it is 98% that tension, which loosens, composite pressure 0.8Mpa, compound speed
8cm/s。
Embodiment 3
A kind of novel natural feather directly fills the production technology of fabric, includes the following steps：
S1：Stock, knitting channel cloth use 50D/72F polyester DTYs, and face cloth, which uses, arbitrarily bullet or the fabric without bullet；
S2：Weaving, 24 needle knittings are knitted channel cloth on knitted double-faced jacquard machine, are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber；
S3：Face cloth arranges：Whole addition fluorine element waterproofing agent, makees water-proof finish after the face cloth；
S4：It is compound
（1）It is once-combined：The one side and middle permeable membrane that are knitted channel cloth is compound, and bridging reaction 16h obtains three-in-one bottom；
（2）It is secondary compound：Compound, the bridging reaction 16h by face cloth and middle permeable membrane obtains two-in-one face layer；
（3）It is compound three times：Compound good two-in-one face layer is compound with compound good three-in-one bottom, bridging reaction 16h is obtained
Fabric is directly filled to novel natural feather；The combination process is compound using hot melt adhesive, and the gluing mode of the hot melt adhesive is dotted gluing,
100 DEG C of combined temp, hot melt adhesive dosage 10gsm, compound tense, it is 96% that tension, which loosens, composite pressure 0.8Mpa, compound speed
8cm/s。
Test example 1
Fabric is directly filled to the novel natural feather of 1 ~ 3 gained of embodiment below, makees physicochemical property testing experiment.
1. anti-chiseling down is tested
2. water vapour permeability is tested
According to the above test result it is found that the natural feather made of production technology provided by the present invention directly fills fabric, have outstanding
Anti-chiseling down performance, especially embodiment 2, testing result are not bore suede.Each embodiment water vapour permeability is also more excellent so that is made
Down products while having good anti-chiseling down performance, using will not be sultry.
Claims (10)
1. a kind of novel natural feather directly fills fabric, it is characterised in that：Including permeable membrane, the double-deck channel cloth of knitting, second in face cloth, first
Middle permeable membrane, permeable membrane is complex as face layer in the face reverse of the cloth and first, and one side and the permeable membrane in second for being knitted channel cloth are compound
For bottom, the face layer first in the another side of permeable membrane and bottom knitting channel cloth it is compound, obtain novel natural feather and directly fill fabric；
Knitting channel cloth, levels are woven into arbitrary flower pattern, i.e., are one layer of double-faced jacquard there is flower pattern part levels to interweave
Tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber.
2. novel natural feather according to claim 1 directly fills fabric, it is characterised in that：Knitting channel cloth is 50D/72F
Polyester DTY, 24 needle knittings on knitted double-faced jacquard machine.
3. novel natural feather according to claim 1 directly fills fabric, it is characterised in that：The face cloth is flexible fabric.
4. novel natural feather according to claim 1 directly fills fabric, it is characterised in that：Permeable membrane in described first, moisture permeability
In 3000-5000g/m2For 24 hours, thickness at 12 μm hereinafter, permeable membrane in described second, moisture permeability is in 3000-5000g/m2·
For 24 hours, thickness is at 15 μm or less.
5. novel natural feather according to claim 1 directly fills fabric, it is characterised in that：Knitting channel cloth Jacquard it
Between be spaced in 4cm or more.
6. directly filling the production technology of fabric according to any novel natural feathers of claim 1-5, include the following steps：
S1：Stock, knitting channel cloth use 50D/72F polyester DTYs, and face cloth, which uses, arbitrarily bullet or the fabric without bullet；
S2：Weaving, 24 needle knittings are knitted channel cloth on knitted double-faced jacquard machine, are one layer there is flower pattern part levels to interweave
Double-faced jacquard tissue, in non-flower pattern part, levels respectively weave, and form down-filling chamber；
S3：Face cloth arranges：Whole addition fluorine element waterproofing agent, makees water-proof finish after the face cloth；
S4：It is compound, it is carried out using hot melt adhesive compound；
It is once-combined：The one side and middle permeable membrane that are knitted channel cloth is compound, and 12-20h of bridging reaction obtains three-in-one bottom；
It is secondary compound：Compound, 12-20h of bridging reaction by face cloth and middle permeable membrane obtains two-in-one face layer；
It is compound three times：By compound good two-in-one face layer with compound good three-in-one bottom compound, 12-20h of bridging reaction,
It obtains novel natural feather and directly fills fabric.
7. novel natural feather according to claim 6 directly fills the production technology of fabric, it is characterised in that：The combination process heat
The gluing mode of melten gel is dotted gluing.
8. novel natural feather according to claim 6 directly fills the production technology of fabric, it is characterised in that：The combination process
Combined temp is 95-105 DEG C, composite pressure 0.8Mpa, compound speed 8cm/s.
9. novel natural feather according to claim 6 directly fills the production technology of fabric, it is characterised in that：The use of the hot melt adhesive
Amount is 8-12gsm.
10. novel natural feather according to claim 6 directly fills the production technology of fabric, it is characterised in that：Compound tense, each layer
It is 95% -98% that power, which is loosened,.