CN108689720A - A kind of manufacturing method of mixed sponge water-permeable brick - Google Patents
A kind of manufacturing method of mixed sponge water-permeable brick Download PDFInfo
- Publication number
- CN108689720A CN108689720A CN201810531483.6A CN201810531483A CN108689720A CN 108689720 A CN108689720 A CN 108689720A CN 201810531483 A CN201810531483 A CN 201810531483A CN 108689720 A CN108689720 A CN 108689720A
- Authority
- CN
- China
- Prior art keywords
- mixed powder
- permeable brick
- mixed
- water
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacturing methods of mixed sponge water-permeable brick, include the following steps:1)The flyash of drying, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash particle, polymer fiber celluar concrete and cement polymer reinforcing agent are uniformly mixed and obtain mixed powder;2)Then mixed powder is put into the mixed powder that brick-shaped is squeezed into square compressor;3)The mixed powder of brick-shaped is positioned over the heating of vacuum sintering furnace high temperature;Then room temperature is cooled to the furnace again, you can obtain the water-permeable brick of forming.The water-permeable brick of the method for the present invention production improves the rugged performance and water permeability of water-permeable brick on the whole, can penetrate the precipitation of drizzle or moderate rain rapidly, have permeable well and water moisture self restraint ability.
Description
Technical field
The present invention relates to a kind of manufacturing methods of mixed sponge water-permeable brick, belong to sponge water-permeable brick technical field.
Background technology
Since ground brick cannot effectively drain rainwater in city so that city is easy to ponding so that life is gone on a journey not
Just.
Invention content
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of mixed sponge water-permeable brick is provided
Manufacturing method includes the following steps:
1) by the flyash of drying, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash particle, poly-
It closes fibres celluar concrete and cement polymer reinforcing agent uniformly mixes and obtains mixed powder;
2) mixed powder and then is put into the mixed powder that brick-shaped is squeezed into square compressor;
3) mixed powder of brick-shaped is positioned over the heating of vacuum sintering furnace high temperature;Then room temperature is cooled to the furnace again.
Preferentially, in step 1), flyash grinding distribution to 30~50 mesh.
Preferentially, in step 1), flyash, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash
Particle, polymer fiber celluar concrete and cement polymer reinforcing agent are put into 100 DEG C in baking oven of drying 1.5h.
Preferentially, in step 1), by flyash, modified epoxy, natural colorful granite, waste and old refractory material, mistake
Fiery cash particle, polymer fiber celluar concrete and cement polymer reinforcing agent are by weight 130:30:37:4:7:3:1 carries out
Uniformly mixing obtains mixed powder, and mixed powder is poured into blender.
Preferentially, in step 2), then 3.2 kilograms of mixed powder is put into square compressor and is squeezed into brick-shaped
Mixed powder.
Preferentially, in step 3), the mixed powder of brick-shaped is positioned over 1750 DEG C of heating in vacuum sintering furnace;Then again
Cool to room temperature with the furnace, you can obtain the water-permeable brick of forming.
The advantageous effect that the present invention is reached:
The water-permeable brick produced using the method for the present invention, improves the rugged performance and water permeability of water-permeable brick on the whole, can
To penetrate the precipitation of drizzle or moderate rain rapidly, there is permeable well and water moisture self restraint ability;The present invention passes through high-temperature calcination, production
It is to melt the combination that postcooling is formed by physics between particle that product, which combine, and intensity is very high;The method of the present invention produces permeable
Brick surface particles are thicker, and non-skid property is good.
Specific implementation mode
The following examples are only intended to illustrate the technical solution of the present invention more clearly, and cannot limit the present invention with this
Protection domain.
A kind of manufacturing method of mixed sponge water-permeable brick, includes the following steps:
1) by the flyash of drying, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash particle, poly-
It closes fibres celluar concrete and cement polymer reinforcing agent uniformly mixes and obtains mixed powder;
2) mixed powder and then is put into the mixed powder that brick-shaped is squeezed into square compressor;
3) mixed powder of brick-shaped is positioned over the heating of vacuum sintering furnace high temperature;Then room temperature is cooled to the furnace again.
Further, in step 1), flyash grinding distribution to 30~50 mesh.
Further, in step 1), flyash, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire
Cash particle, polymer fiber celluar concrete and cement polymer reinforcing agent are put into 100 DEG C in baking oven of drying 1.5h.
Further, in step 1), by flyash, modified epoxy, natural colorful granite, waste and old refractory material,
Cash particle, polymer fiber celluar concrete and cement polymer reinforcing agent over-fire by weight 130:30:37:4:7:3:1 into
Uniformly mixing obtains mixed powder to row, and mixed powder is poured into blender.
Further, in step 2), then 3.2 kilograms of mixed powder is put into square compressor and is squeezed into brick-shaped
Mixed powder.
Further, in step 3), the mixed powder of brick-shaped is positioned over 1750 DEG C of heating in vacuum sintering furnace;Then
Cool to room temperature with the furnace again, you can obtain the water-permeable brick of forming.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvement and deformations can also be made, these improvement and deformations
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of manufacturing method of mixed sponge water-permeable brick, which is characterized in that include the following steps:
1)By the flyash of drying, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash particle, polymer
Fiber multihole concrete and cement polymer reinforcing agent, which uniformly mix, obtains mixed powder;
2)Then mixed powder is put into the mixed powder that brick-shaped is squeezed into square compressor;
3)The mixed powder of brick-shaped is positioned over the heating of vacuum sintering furnace high temperature;Then room temperature is cooled to the furnace again.
2. a kind of manufacturing method of mixed sponge water-permeable brick according to claim 1, which is characterized in that step 1)In, powder
Coal ash grinding distribution is to 30 ~ 50 mesh.
3. a kind of manufacturing method of mixed sponge water-permeable brick according to claim 1, which is characterized in that step 1)In, powder
Coal ash, modified epoxy, natural colorful granite, polypropylene fibre, excessive fire cash particle, polymer fiber celluar concrete and
Cement polymer reinforcing agent is put into 100 DEG C in baking oven of drying 1.5h.
4. a kind of manufacturing method of mixed sponge water-permeable brick according to claim 1, which is characterized in that step 1)In, it will
Flyash, modified epoxy, natural colorful granite, waste and old refractory material, excessive fire cash particle, the porous coagulation of polymer fiber
Soil and cement polymer reinforcing agent are by weight 130:30:37:4:7:3:1, which carries out uniformly mixing, obtains mixed powder, will mix
Powder pours into blender.
5. a kind of manufacturing method of mixed sponge water-permeable brick according to claim 1, which is characterized in that step 2)In, so
3.2 kilograms of mixed powder is put into the mixed powder that brick-shaped is squeezed into square compressor afterwards.
6. a kind of manufacturing method of mixed sponge water-permeable brick according to claim 1, which is characterized in that step 3)In,
The mixed powder of brick-shaped is positioned over 1750 DEG C of heating in vacuum sintering furnace;Then room temperature is cooled to the furnace again, you can obtain
The water-permeable brick of forming.