CN107141010A - A kind of sponge water-permeable brick and its production technology - Google Patents
A kind of sponge water-permeable brick and its production technology Download PDFInfo
- Publication number
- CN107141010A CN107141010A CN201710324995.0A CN201710324995A CN107141010A CN 107141010 A CN107141010 A CN 107141010A CN 201710324995 A CN201710324995 A CN 201710324995A CN 107141010 A CN107141010 A CN 107141010A
- Authority
- CN
- China
- Prior art keywords
- parts
- permeable brick
- water
- sponge water
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of sponge water-permeable brick and its production technology, described sponge water-permeable brick includes following raw materials：Quartz, potassium feldspar, albite, lithium feldspar, cement, shraff, build slag waste material, cinder, foaming agent, plasticiser, waterglass；Its production technology, comprises the following steps：By shraff, build slag waste material and cinder is respectively crushed into powder；Then each raw material is well mixed to obtain compound, adds water and be well mixed into compound, enter mold forming and obtain adobe body；Dry brick body；Calcine to obtain described sponge water-permeable brick.Beneficial effects of the present invention are：The foaming agent and plasticiser contained in sponge water-permeable brick of the present invention can make sponge water-permeable brick produce a large amount of uniform tiny micropores, and the generation of micropore increases the water conservation of sponge water-permeable brick, permeable effect.Because the micropore inside sponge water-permeable brick of the present invention is relatively fine, while making described sponge water-permeable brick that there is good water conservation, pervious function, it may have certain dust removing effects.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of sponge water-permeable brick and its production technology.
Background technology
During long-term Development of Urbanization, large-scale waterproof ground pavement instead of original forest, greenery patches and
Field, forms city desert, causes Permeable stratum area to greatly increase so that urban rainwater can not successfully back to nature, make
Reduced into underground water magnitude of recruitment, crest discharge is greatly increased.Heavy rain is met in many cities one, and its rainwater on road surface can not quickly ooze
Leakage, can only be by pumping equipment draining, when pumping equipment is not smooth, it is easy to cause urban waterlogging.Meanwhile, hardened ground reduction
The respiratory function of urban environment, causes scorching in city, airborne dust and noise aggravation, is degrading urban microclimate, reduces city
The comfort level in city.
Therefore a permeable ground is the key for maintaining city ecology system balance.Compared to other rainwater recycle skills
Art, the road of water-permeable brick laying is a selection well.Water-permeable brick possesses the advantageous properties such as high water-permeability, environmental protection.Mesh
Preceding water-permeable brick on the market is mostly made of cement or ceramics, but both water-permeable bricks are the drawbacks of have certain, exist
It is aqueous it is good, the drawbacks of water-retaining property is bad or good water-retaining property and water penetration does not reach requirement, and the mistake of both water-permeable bricks is filtered out
Miscellaneous effect is nor very well.
The content of the invention
In order to solve the above mentioned problem of prior art presence, there is good permeable and water conservation work(the invention provides a kind of
Can, and sponge water-permeable brick and its production technology with impurity removal function.
The technical solution adopted in the present invention is：
A kind of sponge water-permeable brick：Raw material including following weight parts, quartzy 6-42 parts, 9-42 parts of potassium feldspar, albite 8-
42 parts, 7-42 parts of lithium feldspar, 8-30 parts of cement, 6-30 parts of shraff, build 6-30 parts of slag waste material, 6-30 parts of cinder, foaming agent
0.2-8 parts, 0.2-8 parts of plasticiser, 0.2-8 parts of waterglass, 1-20 parts of dolomite.
Further, described sponge water-permeable brick, includes the raw material of following weight parts, 20 parts of quartz, 25 parts of potassium feldspar, sodium
22 parts of feldspar, 18 parts of lithium feldspar, 20 parts of cement, 15 parts of shraff, build 15 parts of slag waste material, 15 parts of cinder, 4 parts of foaming agent, modeling
4 parts of agent, 4 parts of waterglass, 10 parts of dolomite.
Further, described one kind or its mixture for building slag waste material for brick waste material or cement waste material.
Further, the foaming agent is cement blowing agent.Cement blowing agent also known as foam concrete foamer, it can
The tension force of liquid surface is reduced, a large amount of uniform and stable foam is produced.The addition of foaming agent can produce sponge water-permeable brick
A large amount of uniform tiny micropores, the generation of micropore increases the Water-saving effect of sponge water-permeable brick, reduces that city is scorching, airborne dust is existing
As.
Further, the plasticiser is DINP, DOTP, TOTM or DINCH.Plasticiser has the effect of emulsion foam,
There is the function of cooperateing with foaming agent, the abundance of micropore in sponge water-permeable brick can be increased.
Quartz is one of Main Rock-forming Minerals, is physical property and chemical property sufficiently stable mineral resources.
Potassium feldspar is generally also referred to as orthoclase, density 2.54-2.57g/cm3, proportion 2.56~2.59, hardness 6, potassium feldspar
Addition can improve the drying property of sponge water-permeable brick, shorten its drying time, can improve the mechanical strength of sponge water-permeable brick.
Albite is generally glassy crystal, can be colourless, it is possibility to have white, yellow, red, green or black, is manufacture
The raw material of glass and ceramics.Albite can equally reduce the dry time, improve the mechanical strength of sponge water-permeable brick.
Lithium feldspar because containing biological cycle more than 7%, in feldspar category should entitled potassium albite, but in order to distinguish potassium
With in the feldspar of sodium be free of lithium, so it is named as lithium feldspar by mining area manufacturer.Outward appearance is white or canescence, and hardness is 6-
6.5, it is the more excellent feldspar of wearability, in the manufacturing process of sponge water-permeable brick, mineralizer can be played a part of, shorten it
The time of calcining.
Cement is powdery hydraulicity inorganic coagulation material, can in atmosphere harden or preferably be hardened in water, and energy
The materials such as sand, stone is cemented together securely.
Shraff, with social economy and the fast development of ceramic industry, ceramic industry waste material is increasing, and it is not only
Huge pressure is caused to urban environment, and also limit the sustainable development of development and the ceramic industry of urban economy, is made pottery
The utilization of porcelain waste material can not only reduce the pollution to environment, and can turn waste into wealth and increase economic efficiency.
Slag waste material is built, construction, unit in charge of construction or individual is referred mainly to herein all kinds of buildings, structures, official website etc. is entered
Brick waste material or cement produced by row construction, laying or dismounting, reparative processes.
Cinder is one kind of industrial solid wastes, thermal power plant, industry and civil boiler and other equipment fire coal discharge
Waste residue, also known as clinker.Main component is silica, aluminum oxide, iron oxide, calcium oxide, magnesia etc..Cinder throws aside heap
Product, not only land occupation, releases sulfurous gas pollution air, and harm environment, or even meeting spontaneous combustion are on fire.Original is used as using cinder
Material, also achieving turns waste into wealth, increases economic efficiency, and reduces effect of environmental pollution.
Waterglass refers generally to sodium metasilicate, is a kind of water-soluble silicate, can improve the compactness, strong of sponge water-permeable brick
Degree, impervious, frost resistance and water resistance.
Dolomite is carbonate mineral, there is ankerite and mangandolomite respectively, is composition dolomite and dolomitic limestone
Main mineral constituent.
The production technology of the sponge water-permeable brick, comprises the following steps：
(1) by shraff, build slag waste material and cinder and crushed respectively, obtain waste ceramic feed powder, build slag waste powder and coal
Ground-slag；
(2) by quartz, potassium feldspar, albite, lithium feldspar, cement, waste ceramic feed powder, build slag waste powder, cinder powder, foaming
Agent, plasticiser, waterglass and dolomite are mixed evenly, and obtain compound, and water is added into compound, are stirred for mixing equal
It is even, then enter mold forming, obtain adobe body；
(3) adobe body obtained by step (2) is dried；
(4) dried adobe body is calcined, described sponge water-permeable brick is obtained.
Further, the waste ceramic feed powder, the slag waste powder and the fineness of the cinder powder of building are 20-300 mesh.
Further, in step (2), the weight added water is the 10%-30% of compound weight.
Further, in step (3), the drying is under conditions of 80-100 DEG C, to dry to the water content of adobe body
Below 3%.
Further, in step (4), it in temperature is to calcine 3-9h under conditions of 950-1280 DEG C that the calcining, which is,.
Beneficial effects of the present invention are：Sponge water-permeable brick of the present invention using shraff, build slag waste material and cinder
Based on material, resource is saved to a certain extent, the pollution to environment is reduced, reduces production cost.Institute of the present invention
Potassium feldspar, albite and the lithium feldspar contained in the sponge water-permeable brick stated can shorten make sponge water-permeable brick when dry when
Between, that is, save the production time, and the mechanical strength of produced water-permeable brick can be increased, extend its service life.In addition, of the invention
The foaming agent and plasticiser contained in the sponge water-permeable brick can make sponge water-permeable brick produce a large amount of uniform tiny micropores, micro-
The generation in hole increases the water conservation of sponge water-permeable brick, permeable effect, reduces that city is scorching, effectively reduces PM2.5 and raises
The phenomenon of dirt.Because the micropore inside sponge water-permeable brick of the present invention is relatively fine, there is described sponge water-permeable brick
While good water conservation, pervious function, it may have certain dust removing effects.
Embodiment
To make the object, technical solutions and advantages of the present invention clearer, technical scheme will be carried out below
Detailed description.Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Base
Embodiment in the present invention, those of ordinary skill in the art are resulting on the premise of creative work is not made to be owned
Other embodiment, belongs to the scope that the present invention is protected.
Embodiment one
A kind of sponge water-permeable brick, includes the raw material of following weight parts, and quartzy 6kg, potassium feldspar 9kg, albite 8kg, lithium are long
Stone 7kg, cement 8kg, shraff 6kg, build slag waste material 6kg, cinder 6kg, foaming agent 0.2kg, DINP 0.2kg, waterglass
0.2kg, dolomite 1kg.
The production technology of the sponge water-permeable brick, comprises the following steps：
(1) by shraff, build slag waste material and cinder and crushed respectively, obtain waste ceramic feed powder that fineness is 20 mesh, build
Slag waste powder and cinder powder；
(2) by quartz, potassium feldspar, albite, lithium feldspar, cement, waste ceramic feed powder, build slag waste powder, cinder powder, foaming
Agent, DINP, waterglass and dolomite are mixed evenly, and obtain compound, and the water of compound weight 10% is added into compound,
It is stirred for being well mixed, then enters mold forming, obtains adobe body；
(3) by adobe body obtained by step (2) under conditions of temperature is 80 DEG C, the water content to adobe body is dried 3%
Below；
(4) dried adobe body is calcined into 3h under conditions of temperature is 950 DEG C, obtains described sponge water-permeable brick.
The performance indications of sponge water-permeable brick described in embodiment one and the performance indications of common water-permeable brick to the such as institute of table 1
Show：
Table 1
| Project | Standard index (JC/T945-2005) | Water-permeable brick of the present invention |
| Compression strength | Average value >=35.0MPa | 49MPa |
| Wearability | Mill hole length≤35mm | 28mm |
| Water-retaining property | ≥0.6g/cm2 | 3g/cm2 |
| Coefficient of permeability (15 DEG C of water temperature) | ≥1×10-2cm/s | 5.7×10-2cm/s |
It can be obtained by table 1：Water-permeable brick described in embodiment one for standard index, wearability, water-retaining property and thoroughly
Aqueous aspect is significantly improved, i.e., the water-permeable brick described in embodiment one has preferable water conservation, pervious function, and makes
With lasting a long time.
Embodiment two
A kind of sponge water-permeable brick, includes the raw material of following weight parts, quartzy 20kg, potassium feldspar 25kg, albite 22kg, lithium
Feldspar 18kg, cement 20kg, shraff 15kg, brick waste material 15kg, cinder 15kg, cement blowing agent 4kg, DOTP 4kg, water
Glass 4kg, dolomite 10kg.
The production technology of the sponge water-permeable brick, comprises the following steps：
(1) by shraff, build slag waste material and cinder and crushed respectively, obtain waste ceramic feed powder that fineness is 100 mesh, build
Slag waste powder and cinder powder；
(2) by quartz, potassium feldspar, albite, lithium feldspar, cement, waste ceramic feed powder, brick waste powder, cinder powder, foaming
Agent, DOTP, waterglass and dolomite are mixed evenly, and obtain compound, and the water of compound weight 20% is added into compound,
It is stirred for being well mixed, then enters mold forming, obtains adobe body；
(3) by adobe body obtained by step (2) under conditions of temperature is 90 DEG C, the water content to adobe body is dried 3%
Below；
(4) dried adobe body is calcined into 8h under conditions of temperature is 1000 DEG C, obtains described sponge water-permeable brick.
The performance indications of sponge water-permeable brick described in embodiment two and the performance indications of common water-permeable brick to the such as institute of table 2
Show：
Table 2
| Project | Standard index (JC/T945-2005) | Water-permeable brick of the present invention |
| Compression strength | Average value >=35.0MPa | 49.5MPa |
| Wearability | Mill hole length≤35mm | 26mm |
| Water-retaining property | ≥0.6g/cm2 | 3g/cm2 |
| Coefficient of permeability (15 DEG C of water temperature) | ≥1×10-2cm/s | 5.8×10-2cm/s |
It can be obtained by table 2：Water-permeable brick described in embodiment two for standard index, wearability, water-retaining property and thoroughly
Aqueous aspect is significantly improved, i.e., the water-permeable brick described in embodiment two has preferable water conservation, pervious function, and makes
With lasting a long time.
Embodiment three
A kind of sponge water-permeable brick, includes the raw material of following weight parts, quartzy 42kg, potassium feldspar 42kg, albite 42kg, lithium
Mixture 30kg, cinder 30kg, the water of the quality such as feldspar 42kg, cement 30kg, shraff 30kg, brick waste material and cement waste material
Cement foaming agent 8kg, TOTM 8kg, waterglass 8kg, dolomite 20kg.
The production technology of the sponge water-permeable brick, comprises the following steps：
(1) by shraff, build slag waste material and cinder and crushed respectively, obtain waste ceramic feed powder that fineness is 300 mesh, build
Slag waste powder and cinder powder；
(2) by quartz, potassium feldspar, albite, lithium feldspar, cement, waste ceramic feed powder, build slag waste powder, cinder powder, foaming
Agent, TOTM, waterglass and dolomite are mixed evenly, and obtain compound, and the water of compound weight 30% is added into compound,
It is stirred for being well mixed, then enters mold forming, obtains adobe body；
(3) by adobe body obtained by step (2) under conditions of temperature is 100 DEG C, the water content to adobe body is dried 3%
Below；
(4) dried adobe body is calcined into 9h under conditions of temperature is 1280 DEG C, obtains described sponge water-permeable brick.
The performance indications of sponge water-permeable brick described in embodiment three and the performance indications of common water-permeable brick to the such as institute of table 3
Show：
Table 3
| Project | Standard index (JC/T945-2005) | Water-permeable brick of the present invention |
| Compression strength | Average value >=35.0MPa | 50MPa |
| Wearability | Mill hole length≤35mm | 25mm |
| Water-retaining property | ≥0.6g/cm2 | 3g/cm2 |
| Coefficient of permeability (15 DEG C of water temperature) | ≥1×10-2cm/s | 6.0×10-2cm/s |
It can be obtained by table 3：Water-permeable brick described in embodiment three for standard index, wearability, water-retaining property and thoroughly
Aqueous aspect is significantly improved, i.e., the water-permeable brick described in embodiment three has preferable water conservation, pervious function, and makes
With lasting a long time.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, should all be contained
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be based on the protection scope of the described claims.
Claims (10)
1. a kind of sponge water-permeable brick, it is characterised in that：Raw material including following weight parts, quartzy 6-42 parts, 9-42 parts of potassium feldspar,
8-42 parts of albite, 7-42 parts of lithium feldspar, 8-30 parts of cement, 6-30 parts of shraff, build 6-30 parts of slag waste material, cinder 6-30
Part, 0.2-8 parts of foaming agent, 0.2-8 parts of plasticiser, 0.2-8 parts of waterglass, 1-20 parts of dolomite.
2. sponge water-permeable brick according to claim 1, it is characterised in that：Raw material including following weight parts, quartzy 20 parts, potassium
25 parts of feldspar, 22 parts of albite, 18 parts of lithium feldspar, 20 parts of cement, 15 parts of shraff, build 15 parts of slag waste material, 15 parts of cinder, hair
4 parts of infusion, 4 parts of plasticiser, 4 parts of waterglass, 10 parts of dolomite.
3. sponge water-permeable brick according to claim 1, it is characterised in that：The slag waste material of building is brick waste material or cement waste material
A kind of or its mixture.
4. sponge water-permeable brick according to claim 1, it is characterised in that：The foaming agent is cement blowing agent.
5. sponge water-permeable brick according to claim 1, it is characterised in that：The plasticiser be DINP, DOTP, TOTM or
DINCH。
6. the production technology of one of the claim 1-5 sponge water-permeable bricks, it is characterised in that：Comprise the following steps：
(1) by shraff, build slag waste material and cinder and crushed respectively, obtain waste ceramic feed powder, build slag waste powder and cinder powder；
(2) by quartz, potassium feldspar, albite, lithium feldspar, cement, waste ceramic feed powder, build slag waste powder, cinder powder, foaming agent,
Plasticiser, waterglass and dolomite are mixed evenly, and obtain compound, and water is added into compound, are stirred for being well mixed, so
After enter mold forming, obtain adobe body；
(3) adobe body obtained by step (2) is dried；
(4) dried adobe body is calcined, described sponge water-permeable brick is obtained.
7. the production technology of sponge water-permeable brick according to claim 6, it is characterised in that：In step (1), the shraff
Powder, the slag waste powder and the fineness of the cinder powder of building are 20-300 mesh.
8. the production technology of sponge water-permeable brick according to claim 6, it is characterised in that：In step (2), the weight added water
For the 10%-30% of compound weight.
9. the production technology of sponge water-permeable brick according to claim 6, it is characterised in that：In step (3), the drying be
Under conditions of 80-100 DEG C, the water content to adobe body is dried below 3%.
10. the production technology of sponge water-permeable brick according to claim 6, it is characterised in that：In step (4), the calcining is
3-9h is calcined under conditions of temperature is 950-1280 DEG C.