CN108610011A - A kind of novel environment friendly ceramics pepper mill and preparation method thereof - Google Patents

A kind of novel environment friendly ceramics pepper mill and preparation method thereof Download PDF

Info

Publication number
CN108610011A
CN108610011A CN201810343327.7A CN201810343327A CN108610011A CN 108610011 A CN108610011 A CN 108610011A CN 201810343327 A CN201810343327 A CN 201810343327A CN 108610011 A CN108610011 A CN 108610011A
Authority
CN
China
Prior art keywords
powder
paraffin
environment friendly
novel environment
finished product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810343327.7A
Other languages
Chinese (zh)
Inventor
余奕秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yixing Yu Wei Ceramic Products Co Ltd
Original Assignee
Yixing Yu Wei Ceramic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yixing Yu Wei Ceramic Products Co Ltd filed Critical Yixing Yu Wei Ceramic Products Co Ltd
Priority to CN201810343327.7A priority Critical patent/CN108610011A/en
Publication of CN108610011A publication Critical patent/CN108610011A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of novel environment friendly ceramics pepper mill and preparation method thereof, it includes ingredient and weight percent be：Calcinated talc powder 45~55%, raw talcum powder 10~20%, china powder 15~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~5%, calcium carbonate 2~5%, oleic acid 3~7% and paraffin 5~15%.Each raw material is weighed by weight proportion, is placed in grinder pulverizes after mixing；Powder is added in blender and is stirring evenly and then adding into paraffin, is condensed at room temperature blocking；Block is put into heat pressing forming machines, once hot pressing, then is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, finally obtains finished product；Finally porcelain standard is selected to be sorted, be classified, preservation to finished product by enterprise.Simple production process of the present invention, flow is few, low energy consumption, pollution-free, at low cost；Product environmentally-friendly sanitary, wear-resistant, high temperature resistant, corrosion-resistant, good insulating, can also customize, handsome in appearance.

Description

A kind of novel environment friendly ceramics pepper mill and preparation method thereof
Technical field
The present invention relates to ceramic technology field, specially a kind of novel environment friendly ceramic system pepper mill and preparation method thereof.
Background technology
With social progress, improvement of living standard, people increasingly focus on green, health, safe and healthy life Mode.Because of superior heat insulating ability, the feature of environmental protection, safety and corrosion resistance that ceramics have in itself, in addition its thick and heavy texture With simple and unsophisticated generous appearance, all kinds of ceramics gradually capture market.Pepper mill is kitchen regular supplies, can be used for storing all kinds of Seasoning.Common pepper mill mostly uses plastics or wooden, slim and graceful small and exquisite.But this kind of pepper mill is not durable, perishable, physical Can it is poor, intolerant to fall, it is not wear-resisting, fragile.And this kind of product is complex in composition, often carries harmful substance, is used for a long time and there is peace Full hidden danger.Traditional technology in producing porcelain, complex process, flow are more, expensive, requirement height, if making pepper using traditional handicraft Mill, and seem and waste one's talent on a petty job.
Invention content
The technical problem to be solved by the present invention is to overcome the existing defects, provide it is a kind of it is at low cost, simple for process, once at Novel environment friendly ceramics pepper mill of type and preparation method thereof.
In order to solve the above technical problem, the present invention provides the following technical solutions：
A kind of novel environment friendly ceramics pepper mill, including ingredient and weight percent be：Calcinated talc powder 45~55%, life Talcum powder 10~20%, china powder 15~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~5%, calcium carbonate 2 ~5%, oleic acid 3~7% and paraffin 5~15%.
Further, a kind of preparation method of novel environment friendly ceramics pepper mill, includes the following steps：
(1) each raw material, including calcinated talc powder 45~55%, raw talcum powder 10~20%, china are weighed by weight proportion Powder 15~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~5%, calcium carbonate 2~5%, 5~15% and of paraffin Oleic acid 3~7%；
(2) calcinated talc powder, raw talcum powder, china powder, calcium phosphate, silicon pyroxene, Suzhou soil, calcium carbonate and oleic acid are mixed It pulverizes in merging grinder after uniformly, powder diameter is less than 80 mesh；
(3) powder obtained in step (2) is added in blender, stirs 16 hours, paraffin is added after releasing, in room temperature Lower condensation is blocking；
(4) block obtained in step (3) is put into heat pressing forming machines, 60~80 DEG C of set temperature, disposable hot pressing Molding obtains ceramic embryo；
(5) the ceramic embryo obtained in step (4) is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, firing 20~24 is small When, obtain finished product；
(1) it selects porcelain standard to be sorted, be classified, preservation to finished product by enterprise, ensures finished product without water mark, elephant skin, bubble, change Shape, cracking, recess, defect, slip casting is insufficient or impurity.
The beneficial effects of the invention are as follows:(1) use ceramic-grade talc powder as major ingredient, cheap, even density, surface Smoothly, whiteness height, good luster, good forming effect；(2) traditional ceramics powder is replaced with china powder, while reducing cost, china material Matter is slimmer and more graceful, and resistance to thermal shocks is more preferable；(3) silicon pyroxene and Suzhou soil are added in the feed as filler, and silicon pyroxene can subtract Few green body shrinking percentage, the moisture expantion for reducing green body, to prevent the ceramic body later stage dry and cracked, and Suzhou soil whiteness is high, impurity is few, Finished appearance can be made more preferable；(4) it is also added with calcium phosphate, calcium carbonate and oleic acid in the feed, calcium phosphate is a kind of stabilizer, Finished product can also be helped to facilitate coloring；Calcium carbonate can increase glossiness and the brightness of finished product, additionally it is possible to improve the physics of material Performance；Oleic acid is a kind of industrial solvent, can auxiliary material dissolving mix and improve the caking property of batch mixing；(5) work is entirely produced Skill is simple, flow is few, low energy consumption, pollution-free, at low cost, and product environmentally-friendly sanitary, wear-resistant, high temperature resistant, corrosion-resistant, insulation Property is good, can also customize, handsome in appearance.
Specific implementation mode
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used In the description and interpretation present invention, it is not intended to limit the present invention.
A kind of novel environment friendly ceramics pepper mill of the present invention, including ingredient and weight percent be：Calcinated talc powder 45~ 55%, raw talcum powder 10~20%, china powder 15~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~5%, Calcium carbonate 2~5%, oleic acid 3~7% and paraffin 5~15%.Its material is few, cheap, for making pepper mill, keeps low It while cost, increases and is used under practicability and durability, especially kitchen environment, without load by open fire or electromagnetic oven The heart is burned.
It, can be with according to different needs, customization pattern or color, increase the entertaining of product in actual mechanical process Property.
It is three realities for being directed to a kind of novel environment friendly ceramics pepper mill of the present invention and preparation method thereof and carrying out below Example is applied, concrete condition is as follows.
Embodiment 1：
(1) each raw material, including calcinated talc powder 50%, raw talcum powder 15%, china powder 15%, phosphorus are weighed by weight proportion Sour calcium 1%, silicon pyroxene 2%, Suzhou soil 2%, calcium carbonate 2%, paraffin 10% and oleic acid 3%；
(2) calcinated talc powder, raw talcum powder, china powder, calcium phosphate, silicon pyroxene, Suzhou soil, calcium carbonate and oleic acid are mixed It pulverizes in merging grinder after uniformly, powder diameter is less than 80 mesh；
(3) powder obtained in step (2) is added in blender, stirs 16 hours, paraffin is added after releasing, in room temperature Lower condensation is blocking；
(6) block obtained in step (3) is put into heat pressing forming machines, 60 DEG C of set temperature, once hot pressing, Obtain ceramic embryo；
(7) the ceramic embryo obtained in step (4) is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, be burnt into 24 hours, obtain Obtain finished product；
(2) select porcelain standard to be sorted, be classified to finished product and preservation by enterprise, ensure finished product without water mark, elephant skin, bubble, Deformation, cracking, recess, defect, slip casting is insufficient or impurity.
Embodiment 2：
(1) each raw material, including calcinated talc powder 45%, raw talcum powder 20%, china powder 15%, phosphorus are weighed by weight proportion Sour calcium 2%, silicon pyroxene 2%, Suzhou soil 3%, calcium carbonate 2%, paraffin 8% and oleic acid 3%；
(2) calcinated talc powder, raw talcum powder, china powder, calcium phosphate, silicon pyroxene, Suzhou soil, calcium carbonate and oleic acid are mixed It pulverizes in merging grinder after uniformly, powder diameter is less than 80 mesh；
(3) powder obtained in step (2) is added in blender, stirs 16 hours, paraffin is added after releasing, in room temperature Lower condensation is blocking；
(4) block obtained in step (3) is put into heat pressing forming machines, 70 DEG C of set temperature, once hot pressing, Obtain ceramic embryo；
(5) the ceramic embryo obtained in step (4) is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, be burnt into 22 hours, obtain Obtain finished product；
(6) it selects porcelain standard to be sorted, be classified, preservation to finished product by enterprise, ensures finished product without water mark, elephant skin, bubble, change Shape, cracking, recess, defect, slip casting is insufficient or impurity.
Embodiment 3：
(1) each raw material, including calcinated talc powder 45%, raw talcum powder 15%, china powder 20%, phosphorus are weighed by weight proportion Sour calcium 1%, silicon pyroxene 2%, Suzhou soil 2%, calcium carbonate 2%, paraffin 9% and oleic acid 4%；
(2) calcinated talc powder, raw talcum powder, china powder, calcium phosphate, silicon pyroxene, Suzhou soil, calcium carbonate and oleic acid are mixed It pulverizes in merging grinder after uniformly, powder diameter is less than 80 mesh；
(3) powder obtained in step (2) is added in blender, stirs 16 hours, paraffin is added after releasing, in room temperature Lower condensation is blocking；
(4) block obtained in step (3) is put into heat pressing forming machines, 80 DEG C of set temperature, once hot pressing, Obtain ceramic embryo；
(5) the ceramic embryo obtained in step (4) is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, be burnt into 20 hours, obtain Obtain finished product；
(6) it selects porcelain standard to be sorted, be classified, preservation to finished product by enterprise, ensures finished product without water mark, elephant skin, bubble, change Shape, cracking, recess, defect, slip casting is insufficient or impurity
Simple production process of the present invention, flow is few, low energy consumption, pollution-free, at low cost, and product environmentally-friendly sanitary, wear-resisting Damage, high temperature resistant, corrosion-resistant, good insulating, can also customize, handsome in appearance.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation Technical solution recorded in example is modified or equivalent replacement of some of the technical features.All essences in the present invention With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.

Claims (3)

1. a kind of novel environment friendly ceramics pepper mill, which is characterized in that the ingredient and weight percent for including be：Calcinated talc powder 45 ~55%, raw talcum powder 10~20%, china powder 15~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~ 5%, calcium carbonate 2~5%, paraffin 5~15% and oleic acid 3~7%.
2. a kind of preparation method of novel environment friendly ceramics pepper mill according to claim 1, which is characterized in that including following Step：
(1) each raw material, including calcinated talc powder 45~55%, raw talcum powder 10~20%, china powder 15 are weighed by weight proportion ~20%, calcium phosphate 1~3%, silicon pyroxene 2~4%, Suzhou soil 2~5%, calcium carbonate 2~5%, paraffin 5~15% and oleic acid 3 ~7%；
(2) calcinated talc powder, raw talcum powder, china powder, calcium phosphate, silicon pyroxene, Suzhou soil, calcium carbonate and oleic acid are uniformly mixed It is placed in grinder and pulverizes afterwards；
(3) powder obtained in step (2) is added in blender, stirs 16 hours, paraffin is added after releasing, it is cold at room temperature Congeal into block；
(4) block obtained in step (3) is put into heat pressing forming machines, 60~80 DEG C of set temperature, once hot pressing, Obtain ceramic embryo；
(5) the ceramic embryo obtained in step (4) is placed in 1200 DEG C of high temperature electrical kilns and is burnt into, be burnt into 20~24 hours, obtain Obtain finished product.
(6) porcelain standard is selected to be sorted, be classified, preservation to finished product by enterprise.
3. a kind of preparation method of novel environment friendly ceramics pepper mill according to right 2, it is characterised in that：In step (2), institute It states the powder diameter after grinding and is less than 80 mesh.
CN201810343327.7A 2018-04-17 2018-04-17 A kind of novel environment friendly ceramics pepper mill and preparation method thereof Pending CN108610011A (en)