CN106747297A - Red stoneware tea kettle and preparation method thereof - Google Patents
Red stoneware tea kettle and preparation method thereof Download PDFInfo
- Publication number
- CN106747297A CN106747297A CN201710088888.2A CN201710088888A CN106747297A CN 106747297 A CN106747297 A CN 106747297A CN 201710088888 A CN201710088888 A CN 201710088888A CN 106747297 A CN106747297 A CN 106747297A
- Authority
- CN
- China
- Prior art keywords
- kettle
- parts
- preparation
- raw material
- boccaro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ceramic field, specially red stoneware tea kettle and preparation method thereof, it is made up according to parts by weight of following raw material：45 ~ 65 parts of purple clay, 34 ~ 45 parts of spodumene.Red stoneware tea kettle that the present invention is provided and preparation method thereof, make use of the characteristic of boccaro, and water quality can be improved when heating up water, and this kettle teapot can be such that the kettle is heated on naked light due to having added spodumene composition inside raw material, meet demand of heating up water.
Description
Technical field
The invention belongs to ceramic field, specially red stoneware tea kettle and preparation method thereof.
Background technology
Dark-red enameled pottery is as one kind of tea set, for soaking tealeaves traditionally；Because dark-red enameled pottery has the ventilative knot of double stomatas
Structure, therefore millet paste is overnight undergoes no deterioration, and uses for a long time, double stomata ventilating structures make dark-red enameled pottery easily form tea hill in immersion
(tea stain), causes dark-red enameled pottery to retain the tea perfume of tealeaves, and dark-red enameled pottery is handsome in appearance, is the first-selected tea set that numerous tea lovers sample tea.
But existing dark-red enameled pottery cannot be directly used to boil water, i.e., can not be heated on naked light, can burst.
The content of the invention
For above-mentioned technical problem, the present invention provides a kind of purple sand kettle that directly can be heated up water on naked light.
Specifically technical scheme is：
Boccaro kettle, is made up of following raw material according to parts by weight：
45 ~ 65 parts of purple clay, 34 ~ 45 parts of spodumene.
The preparation method of the boccaro kettle includes procedure below：
Raw material processing is not more than 25 μm into fineness, by proportioning mixing, stirring, grinding, old, pugging, shaping, drying；
Then fired under the conditions of 1100 ~ 1200 DEG C, preferred temperature is 1175 DEG C, is burnt till 6-10 hours, and purple is obtained after cooling
Sand kettle.
Red stoneware tea kettle that the present invention is provided and preparation method thereof, make use of the characteristic of boccaro, and water can be improved when heating up water
Matter and this kettle teapot can be such that the kettle heat on naked light because raw material the inside has added spodumene composition, meet burning
Water demand.
Specific embodiment
It is described in conjunction with the embodiments specific embodiment of the invention.
Embodiment 1
Boccaro kettle, is made up of following raw material according to parts by weight：
45 parts of purple clay, 38 parts of spodumene.
The preparation method of the boccaro kettle includes procedure below：
Raw material processing is not more than 25 μm into fineness, by proportioning mixing, stirring, grinding, old, pugging, shaping, drying；
Then fired under the conditions of 1175 DEG C, burnt till 7 hours, boccaro kettle is obtained after cooling.
Embodiment 1
Boccaro kettle, is made up of following raw material according to parts by weight：
55 parts of purple clay, 34 parts of spodumene.
The preparation method of the boccaro kettle includes procedure below：
Raw material processing is not more than 25 μm into fineness, by proportioning mixing, stirring, grinding, old, pugging, shaping, drying；
Then fired under the conditions of 1120 DEG C, burnt till 10 hours, boccaro kettle is obtained after cooling.
Embodiment 1
Boccaro kettle, is made up of following raw material according to parts by weight：
65 parts of purple clay, 45 parts of spodumene.
The preparation method of the boccaro kettle includes procedure below：
Raw material processing is not more than 25 μm into fineness, by proportioning mixing, stirring, grinding, old, pugging, shaping, drying；
Then fired under the conditions of 1200 DEG C, burnt till 6 hours, boccaro kettle is obtained after cooling.
Claims (3)
1. boccaro kettle, it is characterised in that be made up according to parts by weight of following raw material：
45 ~ 65 parts of purple clay, 34 ~ 45 parts of spodumene.
2. boccaro kettle according to claim 1, it is characterised in that preparation method includes procedure below：
Raw material processing is not more than 25 μm into fineness, by proportioning mixing, stirring, grinding, old, pugging, shaping, drying；
Then fired under the conditions of 1100 ~ 1200 DEG C, burnt till 6-10 hours, boccaro kettle is obtained after cooling.
3. boccaro kettle according to claim 2, it is characterised in that described firing temperature is 1175 DEG C.