CN103588465A - High-temperature-resistant purple sand container - Google Patents
High-temperature-resistant purple sand container Download PDFInfo
- Publication number
- CN103588465A CN103588465A CN201310546505.3A CN201310546505A CN103588465A CN 103588465 A CN103588465 A CN 103588465A CN 201310546505 A CN201310546505 A CN 201310546505A CN 103588465 A CN103588465 A CN 103588465A
- Authority
- CN
- China
- Prior art keywords
- purple sand
- sand container
- red
- electric stove
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-temperature-resistant purple sand container. The bottom of the purple sand container comprises three or more projection parts; the main body of the purple sand container comprises the following components in percentage by weight: 20-55% of purple sand soil, 40-60% of spodumene and 5-20% of kaolin. The purple sand container of the invention can be used for boiling water and tea on open fire and an electric stove, and buffer contact areas are formed between the purple sand container and the surface of the opening fire or the electric stove through the projection parts at the bottom, so that the purple sand container made of a natural material is prevented from rupture when used on the electric stove or the open fire; as a certain distance is reserved between the purple sand container and the electric stove, heated air flows upwards and evenly acts on the purple sand container, and thus the service lives of the purple sand container and the electric stove are long.
Description
Technical field
The present invention relates to a kind of purple-clay product, particularly a kind of resistant to elevated temperatures applicable open firing, electrically heated red stoneware ware.
Background technology
Boccaro is a kind of material that health is worth that has.Therefore from ancient times to the present, people like making tea or soaked with boccaro, as daily, drink.But, due to the characteristic of boccaro pug, make red stoneware ware (comprising dark-red enameled pottery, purple ceramic cup and purple casserole etc.) be not suitable for being placed directly on naked light as the vessel that heat.Once long-time heating, will damage in explosion.Therefore the people make tea with boccaro over the past thousands of years, and can not boil water with boccaro naked light, Baoshang.
Summary of the invention
Goal of the invention: technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of resistant to elevated temperatures red stoneware ware.
In order to solve the problems of the technologies described above, the invention discloses a kind of resistant to elevated temperatures red stoneware ware, described red stoneware ware bottom comprises three above lug bosses; The body of described red stoneware ware comprises that following components in weight percent forms:
Red Stone Ware 20 ~ 55%
Triphane 40 ~ 60%
Kaolin 5 ~ 20%.
Above-mentioned three kinds of component water mixings are even, adopt traditional technology to manufacture moulding, in 1180 ~ 1280 degree celsius temperature, burn till, to fire 6 ~ 12 hours, the grain numerical control of three kinds of materials is built in 40 ~ 100 orders.
In the present invention, the height of described lug boss is more than 5mm.
In the present invention, the height of described lug boss is more than 2cm.
Existing a kind of electrically heated Boccaro cooker, its heat-up time is very very long, often needs more than 1 hour, does not also meet that people dailyly boil water, the demand of Baoshang.Applicant tests rear discovery, and such Boccaro cooker is directly had a meeting less on naked light, equally can burst.
Through applicant, through long-time unremitting research, find, why traditional red stoneware ware can damage under naked light, its reason be electrothermal dark-red pottery while heating in the short period of time bottom temp up to 600 degree more than, the upper temp difference of bottom and dark-red enameled pottery is large, the coefficient of expansion that adds boccaro is large, easily makes dark-red enameled pottery break.Therefore, can say the discovery of the reason of this technical problem, be exactly to be difficult for very much.
Further, applicant adds triphane in red stoneware ware, finds can to improve heat resisting temperature after triphane adds and control is broken, but fires after tens of times, still there will be slight crack.Applicant is further, has added the technical pattern of bottom protrusion, finds both combinations, when greatly having promoted performance, high increase durability degree.
Applicant through the experiment of more than 3000 times, testing data is as table 1:
Table 1
| The shared weight percentage of triphane | There is 5mm bottom with projection | Bottom flat is without projection |
| Triphane 15% | Approximately Heating temperature 600 ~ 800, heats left and right 80 times, and vessel break | Approximately Heating temperature 600 ~ 800, heats left and right 20 times, and vessel break |
| Triphane 25% | Approximately Heating temperature 600 ~ 800, heats left and right 180 times, and vessel break | Approximately Heating temperature 600 ~ 800, heats left and right 50 times, and vessel break |
| Triphane 40% | Approximately Heating temperature 600 ~ 800, heats left and right 1500 times, and vessel break | Approximately Heating temperature 600 ~ 800, heats left and right 100 times, and vessel break |
| Triphane 50% | Approximately Heating temperature 600 ~ 800, heats left and right 2000 times, and vessel do not break | 600 ~ 800,200 left and right of about Heating temperature, vessel break |
Note, in table 1, except triphane content increases, all the other remain unchanged.
As can be seen here, triphane more than 40% has 5mm with projection in conjunction with bottom, can make the resistance to elevated temperatures of red stoneware ware be greatly improved, and product stability gets a promotion simultaneously.
Beneficial effect: red stoneware ware of the present invention can be on naked light and electric furnace boiled poach tea, also can cook by Baoshang, bottom protrusion portion makes red stoneware ware and naked light or electric furnace surface form buffering zone of action.Thereby make the red stoneware ware of natural material on electric furnace or naked light, use and not break, and because there is certain distance between red stoneware ware and electric furnace, the air of heating is upwards flowed and stepless action is on red stoneware ware more, the work-ing life of red stoneware ware and electric furnace is also more lasting.Red stoneware ware firing temperature of the present invention reaches 1180 ℃ ~ 1280 ℃, can guarantee that boccaro is high temperature resistant, simultaneously not broken at-10 ℃ ~+680 ℃ interval suddenly cold and hots, be achieved on electric furnace and naked light and use, use the burned water of this red stoneware ware or tea, Baoshang simultaneously, the pH value of water is weakly alkaline, useful to human body.And traditional dark-red enameled pottery is made tea, because adding rear temperature, constantly reduces by boiling water, and through applicant's experiment contrast, pH value is neutral, cannot realize the effect that boccaro is heated up water.
Embodiment
embodiment 1
The present embodiment discloses a kind of purple sand kettle, and its bottom is provided with protruding feet, surpasses kettle bottom surface 1cm.
The purple sand kettle of the present embodiment comprises that following components in weight percent forms:
Red Stone Ware 20%
Triphane 60%
Kaolin 20%.
Preparation technology is: above-mentioned three kinds of component water mixings are even, and adopt traditional technology to manufacture moulding, in 1180 ~ 1280 degree celsius temperature, burn till, to fire 6 ~ 12 hours, the grain numerical control of three kinds of materials is built in 40 ~ 100 orders.
embodiment 2
The present embodiment discloses a kind of Boccaro cooker, and its bottom is provided with protruding feet, surpasses kettle bottom surface 2cm.
The Boccaro cooker of the present embodiment comprises that following components in weight percent forms:
Red Stone Ware 55%
Triphane 40%
Kaolin 5%.
Preparation technology is identical with embodiment 1.
embodiment 3
The present embodiment discloses a kind of purple ceramic cup, and its bottom is provided with protruding feet, surpasses kettle bottom surface 0.5cm.
The purple ceramic cup of the present embodiment comprises that following components in weight percent forms:
Red Stone Ware 30%
Triphane 55%
Kaolin 15%.
Preparation technology is identical with embodiment 1.
The invention provides a kind of thinking and method of resistant to elevated temperatures red stoneware ware; method and the approach of this technical scheme of specific implementation are a lot; the above is only the preferred embodiment of the present invention; should be understood that; for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.In the present embodiment not clear and definite each integral part all available prior art realized.
Claims (3)
1. a resistant to elevated temperatures red stoneware ware, is characterized in that, described red stoneware ware bottom comprises three above lug bosses; The body of described red stoneware ware comprises that following components in weight percent forms:
Red Stone Ware 20 ~ 55%
Triphane 40 ~ 60%
Kaolin 5 ~ 20%.
2. a kind of resistant to elevated temperatures red stoneware ware according to claim 1, is characterized in that, the height of described lug boss is more than 5mm.
3. a kind of resistant to elevated temperatures red stoneware ware according to claim 1, is characterized in that, the height of described lug boss is more than 1cm.