CN108588972A - A kind of production method of permanent soft towel - Google Patents

A kind of production method of permanent soft towel Download PDF

Info

Publication number
CN108588972A
CN108588972A CN201810452986.4A CN201810452986A CN108588972A CN 108588972 A CN108588972 A CN 108588972A CN 201810452986 A CN201810452986 A CN 201810452986A CN 108588972 A CN108588972 A CN 108588972A
Authority
CN
China
Prior art keywords
yarn
production method
count yarn
fine
towel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810452986.4A
Other languages
Chinese (zh)
Inventor
王红星
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LOFTEX CHINA Ltd
Original Assignee
LOFTEX CHINA Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LOFTEX CHINA Ltd filed Critical LOFTEX CHINA Ltd
Publication of CN108588972A publication Critical patent/CN108588972A/en
Pending legal-status Critical Current

Abstract

The present invention relates to field of textiles, and in particular to a kind of production method of permanent soft towel.This method includes spinning, water process, bleaching process processing, the several processes of final finishing, the towel produced can be made after repeatedly washing, still to keep even being promoted the softness of towel, and have lasting quick-drying, hydrophile function.

Description

A kind of production method of permanent soft towel
Technical field：
The present invention relates to field of textiles, and in particular to a kind of production method of permanent soft towel.
Background technology：
With the continuous social and economic development, requirement of the consumer for daily necessities such as towels is also higher and higher, makees For the towel products of daily necessities, bulkiness, pliability and water absorbing properties are indispensable.
But present towel products are typically by being handled with chemical assistant during post-processing, towel being made to obtain Required bulkiness and pliability, but such towel pliability is not lasting, after repeatedly washing, can all become it is dry, It hardens, loses its use value.
Invention content
In order to overcome above-mentioned disadvantage of the existing technology, the purpose of the present invention is to provide a kind of permanent soft towels Production method can make the towel produced after repeatedly washing, still keep even promoting towel using this method Softness, and with lasting quick-drying, hydrophile function.
A kind of production method of permanent soft towel, technical solution include mainly spinning, water process, bleaching process processing, The several processes of final finishing, are as follows：
1) it spins：By weight percentage, low count yarn 10-90%, fine-count yarn 10-90%；By low count yarn and fine-count yarn into Row spinning Split Down and twisting, gained yarn twist factor are 30~340；
Wherein, the thickness of low count yarn and fine-count yarn, material are different, and low count yarn is natural fiber or natural fibre blended, Or natural fiber and chemical fibre is blended；Fine-count yarn used is the chemical-fibres filaments with heat-shrinkable, or has heat-shrinkable Can staple fibre, or the chemical fibre with thermal contraction performance and other fibers is blended；Wherein, the hot water shrinkage of low count yarn Hot water shrinkage for 0-10%, fine-count yarn is 0-60%；
2) it weaves：Yarn obtained by step 1) is used to be carried out on jet terry cloth loom or rapier towel loom as plush yarn Weaving；Ground warp and weft yarns are the mixed yarn of Quality Pure Cotton Yarn Production or cotton fiber and other fibers (such as terylene short fiber)；
3) refining, preshrunk water process：Concrete technology temperature is 50-85 DEG C, and the time is 30-60 minutes.When hot water treatment 3-10g/l bleeding agents are added in water-bath, the bleeding agent is using prior art, such as penetrant t/JFC etc..This method utilizes chemical fibre The characteristics of long filament heat-shrinkable is better than low count yarn makes towel looped pile obtain certain elasticity, achievees the effect that towel permanent soft；
4) high-temperature bleaching：According to processing needs, bleaching process processing processing can be carried out to fabric；Specific process parameter can be with It is：The Ionic Membrane of mass concentration 32% is added in water：3-10g/l, the hydrogen peroxide of concentration 27.5%：3-15g/l, dioxygen Water stabilizer：0.5g/l, refining agent JN-98：1-3g/l, 98 DEG C of processing 60min.
After can also step 4) being replaced with to step 3) process, terylene degreaser JL-308-A is added：3g/l, it is highly concentrated Refining agent：JN-98：2g/l, 98 DEG C of processing 30min.
The towel made by said program is handled by high temperature boiling water, so that chemical-fibres filaments is shunk under hot conditions, And the finish in chemical-fibres filaments or yarn is removed, to ensure that product has preferable permeability and water imbibition.
This process carries out bleaching and kiering, first, the water repellent substance on removal cotton fiber or other natural fibers, promotes production The hydrophilicity of product creates basic condition second is that improving the whiteness of above-mentioned fiber for dyeing.
5) final finishing：Utilize hydrophilic softener soft finish；Concrete technology can be to be used using DT530 softening agents Amount is 3%-12%, 35 DEG C of processing 30min.It is to ensure that the hydrophilicity of product is unaffected using hydrophilic softener.
Prior art realization can be used in other steps of the present invention, and details are not described herein.
The present invention solves the drawbacks of existing towel is dry after repeatedly washing, hardens, and extends towel and uses comfortably Sense.
Compared with the existing technology, there are following features using the product of the method for the present invention production：
1, product is fluffy, and appearance is full thick and solid.
2, product has good water absorbing properties.
3, the washing resistance performance of product is excellent, repeatedly still possesses soft feel after washing.
Specific implementation mode
The specific implementation mode of form by the following examples does further specifically the above of the present invention It is bright, but the range that this should not be interpreted as to the above-mentioned theme of the present invention is only limitted to example below.It is all to be based on the above of the present invention The technology realized all belongs to the scope of the present invention, and it is complete to be all made of conventional prior unless otherwise specified, in following embodiments At.Involved reagent dosage, is weighed with the volume of water in the present invention.
Embodiment 1
A kind of production method of permanent soft towel, detailed process are：
Then and strong 60s or more the chemical-fibres filaments of upper pyrocondensation performance 1) low count yarn of 14s is spun with pure cotton,.Wherein, low count yarn Hot water shrinkage be 2-10%, the hot water shrinkage of fine-count yarn is 20-60%；
The low count yarn and fine-count yarn is in doubling, by twisting and the yarn at a twist factor between 30~340, Low count yarn accounts for the 10% of folded yarn overall weight, and fine-count yarn accounts for the 90% of folded yarn overall weight；
2) weave, use above-mentioned steps 1) method make yarn as plush yarn, Quality Pure Cotton Yarn Production do warp and weft yarns in jet Terry cloth loom is weaved；
3) refining preshrinking water process, specially by 85-95 DEG C of hot water treatment 30 minutes of fabric；
4) high-temperature bleaching, the Ionic Membrane of mass concentration 32%：3-10g/l, the hydrogen peroxide of concentration 27.5%：3-15g/ L, hydrogen peroxide stabilizer：0.5g/l, refining agent JN-98：1-3g/l, 98 DEG C of processing 60min.
5) final finishing：Using hydrophilic softener soft finish, concrete technology is softening agent DT530 usage amounts 12%, 35 DEG C processing 30min.
In addition to above-mentioned parameter, other techniques used by the present embodiment and parameter with common towel in the prior art Method for weaving is identical, and details are not described herein.
Embodiment 2
A kind of production method of permanent soft towel, detailed process are：
1) it spins：Then and strong 60s or more the chemical-fibres filaments of upper pyrocondensation performance the low count yarn of 13s is spun with pure cotton,.Wherein, The hot water shrinkage of low count yarn is 0-10%, and the hot water shrinkage of fine-count yarn is 0-40%；
The low count yarn and fine-count yarn is in doubling, by twisting and the yarn at a twist factor between 30~200, Low count yarn accounts for the 90% of folded yarn overall weight, and fine-count yarn accounts for the 10% of folded yarn overall weight；
2) weave, use above-mentioned steps 1) yarn that makes of method is as plush yarn, the mixed yarn of Quality Pure Cotton Yarn Production and terylene short fiber Ground warp and weft yarns are done to be weaved on jet terry cloth loom or rapier towel loom；
3) refining preshrinking water process, specially by 85-95 DEG C of hot water treatment 30 minutes of fabric；
4) high-temperature bleaching, the Ionic Membrane of mass concentration 32%：3-10g/l；The hydrogen peroxide of concentration 27.5%：3-15g/ L, hydrogen peroxide stabilizer：0.5g/l, refining agent JN-98：1-3g/l, 98 DEG C of processing 60min.
5) final finishing, using hydrophilic softener soft finish, concrete technology is softening agent DT530 usage amounts 3%, 35 DEG C Handle 30min.
Embodiment 3
A kind of production method of permanent soft towel, detailed process are：
1) it spins：Then and strong 60s or more the chemical-fibres filaments of upper pyrocondensation performance the low count yarn of 13s is spun with pure cotton,.Wherein, The hot water shrinkage of low count yarn is 0-10%, and the hot water shrinkage of fine-count yarn is 30-60%；
The low count yarn and fine-count yarn passes through twisting and the yarn at a twist factor between 100~340 in doubling Line, low count yarn account for the 50% of folded yarn overall weight, and fine-count yarn accounts for the 50% of folded yarn overall weight；
2) weave, use above-mentioned steps 1) method make yarn as plush yarn, Quality Pure Cotton Yarn Production do warp and weft yarns in arrow shaft It is weaved on terry cloth loom；
3) refining preshrinking water process, specially by 85-95 DEG C of hot water treatment 30 minutes of fabric；
4) high-temperature bleaching specially uses the Ionic Membrane of mass concentration 32%：3-10g/l；The dioxygen of concentration 27.5% Water：3-15g/l, hydrogen peroxide stabilizer：0.5g/l, refining agent JN-98：1-3g/l, 98 DEG C of processing 60min.
5) final finishing, using hydrophilic softener soft finish, concrete technology is softening agent DT530 usage amounts 6%, 35 DEG C Handle 30min.
In addition to above-mentioned parameter, other techniques used by the present embodiment and parameter with common towel in the prior art Method for weaving is identical, and details are not described herein.
It is flat will not to generate looped pile rich in resilience because of the extruding of product for towel feel made by above example Feel, is squeezed even across prolonged transport, still high resilience and bulkiness；And feel after the just drying of common soft towel High resilience, it is fluffy, but resilience disappears after extruding, and especially in transportational process, product mutually squeezes for a long time, When counter is sold, the elasticity and bulkiness of product disappear substantially, it is seen that method provided by the present invention can obviously improve existing general The drawbacks of logical towel, realizes preferably soft enduring quality.

Claims (5)

1. a kind of production method of permanent soft towel, including spinning, weaving, water process, high-temperature bleaching, final finishing step, It is characterized in that：The spinning, weaving, water treatment procedure are as follows：
1) it spins：By weight percentage, low count yarn 10-90%, fine-count yarn 10-90%；Low count yarn and fine-count yarn are spun Yarn Split Down and twisting, gained yarn twist factor are 30~340；
2) it weaves：Yarn obtained by step 1) is used to be weaved on jet terry cloth loom or rapier towel loom as plush yarn；
3) refining preshrinking water process：Concrete technology temperature is 50-85 DEG C, and the time is 30-60 minutes, when hot water treatment in a water bath 3-10g/l bleeding agents are added；
Wherein, the low count yarn described in step 1) is the mixed of natural fiber or natural fibre blended or natural fiber and chemical fibre It spins；The fine-count yarn is the chemical-fibres filaments with heat-shrinkable or the staple fibre with thermal contraction performance or is received with heat The chemical fibre of contracting performance is blended with other fibers；The hot water shrinkage of the low count yarn is 0-10%, and the hot water of fine-count yarn is received Shrinkage is 0-60%.
2. a kind of production method of permanent soft towel according to claim 1, it is characterised in that：Ground described in step 2) Warp and weft yarns are the mixed yarn of Quality Pure Cotton Yarn Production or cotton fiber and other fibers.
3. a kind of production method of permanent soft towel according to claim 1, it is characterised in that：Step described in further including After rapid 3) process, terylene degreaser JL-308-A is added：3g/l, highly concentrated refining agent：JN-98：2g/l, 98 DEG C of processing 30min。
4. a kind of production method of permanent soft towel according to claim 1, it is characterised in that：Step described in further including After rapid 3) process, step 4) high-temperature bleaching is carried out, specially：The Ionic Membrane of mass concentration 32% is added in water： 3-10g/l, the hydrogen peroxide of concentration 27.5%：3-15g/l, hydrogen peroxide stabilizer：0.5g/l, refining agent JN-98：1-3g/l, 98 DEG C processing 60min.
5. a kind of production method of permanent soft towel according to claim 1, it is characterised in that：The final finishing, Specially utilize hydrophilic softener soft finish；Concrete technology can be using DT530 softening agents, usage amount 3%- 12%, 35 DEG C of processing 30min.
CN201810452986.4A 2017-12-07 2018-05-11 A kind of production method of permanent soft towel Pending CN108588972A (en)