CN108587524A - 一种新型建筑壳模板用高效粘合剂 - Google Patents

一种新型建筑壳模板用高效粘合剂 Download PDF

Info

Publication number
CN108587524A
CN108587524A CN201810492117.4A CN201810492117A CN108587524A CN 108587524 A CN108587524 A CN 108587524A CN 201810492117 A CN201810492117 A CN 201810492117A CN 108587524 A CN108587524 A CN 108587524A
Authority
CN
China
Prior art keywords
parts
polyvinyl alcohol
dibutyl phthalate
sodium bicarbonate
mold plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810492117.4A
Other languages
English (en)
Inventor
陆永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810492117.4A priority Critical patent/CN108587524A/zh
Publication of CN108587524A publication Critical patent/CN108587524A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.3‑0.8份、来苏糖4‑9份、二甲酸二乙酯0.3‑0.8份、改性海藻酸纤维4‑8份、聚乙烯醇0.3‑0.8份、六亚甲基四胺0.2‑0.5份、碳酸氢钠0.2‑0.6份、石蜡2‑6份、碳酸钙0.8‑1.5份、聚乙烯醇0.6‑1.2份、聚醋酸乙烯酯乳液4‑10份、化学助剂5‑10份、邻苯二甲酸二丁酯10‑19份、过硫酸铵0.3‑0.8份、碳酸氢钠0.7‑1.2份、乙酸丁酯0.4‑0.8份、聚乙烯醇0.6‑1.5份、邻苯二甲酸二丁酯0.3‑0.8份、十二烷基苯硫酸钠0.4‑0.7份、聚醚0.4‑0.9份、邻苯二甲酸二丁酯0.3‑0.9份、聚丙烯铣铵0.2‑0.7份、环己烷0.2‑0.5份、尿素7‑10份和硫酸铝0.3‑0.8份。本发明的粘合剂，贮存稳定性较好，施胶量相对较低，粘合强度和耐水性较高，且制造工艺、设备简单，可采用一般的脲醛树脂生产设备生产等有益效果。

Description

一种新型建筑壳模板用高效粘合剂
技术领域
本发明涉及建筑壳模板相关技术领域，尤其涉及一种新型建筑壳模板用高效粘合剂。
背景技术
脲醛树脂属氨基树脂，是一种大量应用于木材人造板的粘合剂。但脲醛树脂胶粘剂会释放甲醛，污染环境、危害人体健康。为解决其污染问题，一般采用如下解决方法，a.采用低醛 / 脲摩尔比的脲醛树脂，在合成脲醛树脂时，适当降低原料的甲醛与尿素的摩尔比，可在一定程度上降低树脂和人造板的游离醛含量 ；b. 加入甲醛捕捉剂，这些捕捉剂在一定条件下能与甲醛产生化学反应生成另一种稳定的新物质并稳定地吸收甲醛 ；c. 改进人造板的制板工艺。选择合理的制板工艺，严格控制热压温度、热压时间、施胶量和人造板的含水率等技术参数 ；d. 对人造板进行后期处理，主要是进行熏氨工艺，即将人造板成品置于氨气氛围中，让板内的游离醛与氨气进行化学反应，生成无危害性的六次甲基四胺(CH2)6N4。上述 a、b 方法存在许多难以克服的缺点，如物理力学性能下降，粘合剂成本提高、贮存期缩短，热压时间增长 ；c 方法降醛效果有限 ；d 方法降醛效果刚处理完时尚可，但经过一段时间后，游离甲醛释放量会反弹上升。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种新型建筑壳模板用高效粘合剂。
为了实现上述目的，本发明采用了如下技术方案：
一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.3-0.8份、来苏糖4-9份、二甲酸二乙酯0.3-0.8份、改性海藻酸纤维4-8份、聚乙烯醇0.3-0.8份、六亚甲基四胺0.2-0.5份、碳酸氢钠0.2-0.6份、石蜡2-6份、碳酸钙0.8-1.5份、聚乙烯醇0.6-1.2份、聚醋酸乙烯酯乳液4-10份、化学助剂5-10份、邻苯二甲酸二丁酯10-19份、过硫酸铵0.3-0.8份、碳酸氢钠0.7-1.2份、乙酸丁酯0.4-0.8份、聚乙烯醇0.6-1.5份、邻苯二甲酸二丁酯0.3-0.8份、十二烷基苯硫酸钠0.4-0.7份、聚醚0.4-0.9份、邻苯二甲酸二丁酯0.3-0.9份、聚丙烯铣铵0.2-0.7份、环己烷0.2-0.5份、尿素7-10份和硫酸铝0.3-0.8份。
上述的一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.3-0.7份、来苏糖4-8份、二甲酸二乙酯0.3-0.7份、改性海藻酸纤维4-7份、聚乙烯醇0.3-0.7份、六亚甲基四胺0.2-0.4份、碳酸氢钠0.2-0.5份、石蜡2-5份、碳酸钙0.8-1.4份、聚乙烯醇0.6-1.1份、聚醋酸乙烯酯乳液4-9份、化学助剂5-9份、邻苯二甲酸二丁酯10-18份、过硫酸铵0.3-0.7份、碳酸氢钠0.7-1.1份、乙酸丁酯0.4-0.7份、聚乙烯醇0.6-1.4份、邻苯二甲酸二丁酯0.3-0.7份、十二烷基苯硫酸钠0.4-0.6份、聚醚0.4-0.8份、邻苯二甲酸二丁酯0.3-0.8份、聚丙烯铣铵0.2-0.6份、环己烷0.2-0.4份、尿素7-9份和硫酸铝0.3-0.7份。
上述的一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.4-0.7份、来苏糖5-8份、二甲酸二乙酯0.4-0.7份、改性海藻酸纤维5-7份、聚乙烯醇0.4-0.7份、六亚甲基四胺0.3-0.4份、碳酸氢钠0.3-0.5份、石蜡3-5份、碳酸钙0.9-1.4份、聚乙烯醇0.7-1.1份、聚醋酸乙烯酯乳液5-9份、化学助剂6-9份、邻苯二甲酸二丁酯11-18份、过硫酸铵0.4-0.7份、碳酸氢钠0.8-1.1份、乙酸丁酯0.5-0.7份、聚乙烯醇0.7-1.4份、邻苯二甲酸二丁酯0.4-0.7份、十二烷基苯硫酸钠0.5-0.6份、聚醚0.5-0.8份、邻苯二甲酸二丁酯0.4-0.8份、聚丙烯铣铵0.3-0.6份、环己烷0.3-0.4份、尿素8-9份和硫酸铝0.4-0.7份。
上述的一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.55份、来苏糖6.5份、二甲酸二乙酯0.55份、改性海藻酸纤维6份、聚乙烯醇0.55份、六亚甲基四胺0.35份、碳酸氢钠0.4份、石蜡4份、碳酸钙1.15份、聚乙烯醇0.9份、聚醋酸乙烯酯乳液7份、化学助剂7.5、邻苯二甲酸二丁酯14.5份、过硫酸铵0.55份、碳酸氢钠0.95份、乙酸丁酯0.6份、聚乙烯醇1.05份、邻苯二甲酸二丁酯0.55份、十二烷基苯硫酸钠0.55份、聚醚0.65份、邻苯二甲酸二丁酯0.6份、聚丙烯铣铵0.45份、环己烷0.35份、尿素8.5份和硫酸铝0.55份。
与现有技术相比，本发明的有益效果为：
本发明的一种新型建筑壳模板用高效粘合剂，贮存稳定性较好，施胶量相对较低，粘合强度和耐水性较高，且制造工艺、设备简单，可采用一般的脲醛树脂生产设备生产等有益效果。
具体实施方式
实施例1
一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.3份、来苏糖4份、二甲酸二乙酯0.3份、改性海藻酸纤维4份、聚乙烯醇0.3份、六亚甲基四胺0.2份、碳酸氢钠0.2份、石蜡2份、碳酸钙0.8份、聚乙烯醇0.6份、聚醋酸乙烯酯乳液4份、化学助剂5份、邻苯二甲酸二丁酯10份、过硫酸铵0.3份、碳酸氢钠0.7份、乙酸丁酯0.4份、聚乙烯醇0.6份、邻苯二甲酸二丁酯0.3份、十二烷基苯硫酸钠0.4份、聚醚0.4份、邻苯二甲酸二丁酯0.3份、聚丙烯铣铵0.2份、环己烷0.2份、尿素7份和硫酸铝0.3份。
实施例2
上述的一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.8份、来苏糖9份、二甲酸二乙酯0.8份、改性海藻酸纤维8份、聚乙烯醇0.8份、六亚甲基四胺0.5份、碳酸氢钠0.6份、石蜡6份、碳酸钙1.5份、聚乙烯醇1.2份、聚醋酸乙烯酯乳液10份、化学助剂10份、邻苯二甲酸二丁酯19份、过硫酸铵0.8份、碳酸氢钠1.2份、乙酸丁酯0.8份、聚乙烯醇1.5份、邻苯二甲酸二丁酯0.8份、十二烷基苯硫酸钠0.7份、聚醚0.9份、邻苯二甲酸二丁酯0.9份、聚丙烯铣铵0.7份、环己烷0.5份、尿素10份和硫酸铝0.8份。
实施例3
上述的一种新型建筑壳模板用高效粘合剂，按照重量份有以下原料组成：聚乙烯醇0.55份、来苏糖6.5份、二甲酸二乙酯0.55份、改性海藻酸纤维6份、聚乙烯醇0.55份、六亚甲基四胺0.35份、碳酸氢钠0.4份、石蜡4份、碳酸钙1.15份、聚乙烯醇0.9份、聚醋酸乙烯酯乳液7份、化学助剂7.5、邻苯二甲酸二丁酯14.5份、过硫酸铵0.55份、碳酸氢钠0.95份、乙酸丁酯0.6份、聚乙烯醇1.05份、邻苯二甲酸二丁酯0.55份、十二烷基苯硫酸钠0.55份、聚醚0.65份、邻苯二甲酸二丁酯0.6份、聚丙烯铣铵0.45份、环己烷0.35份、尿素8.5份和硫酸铝0.55份。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种新型建筑壳模板用高效粘合剂，其特征在于，按照重量份有以下原料组成：聚乙烯醇0.3-0.8份、来苏糖4-9份、二甲酸二乙酯0.3-0.8份、改性海藻酸纤维4-8份、聚乙烯醇0.3-0.8份、六亚甲基四胺0.2-0.5份、碳酸氢钠0.2-0.6份、石蜡2-6份、碳酸钙0.8-1.5份、聚乙烯醇0.6-1.2份、聚醋酸乙烯酯乳液4-10份、化学助剂5-10份、邻苯二甲酸二丁酯10-19份、过硫酸铵0.3-0.8份、碳酸氢钠0.7-1.2份、乙酸丁酯0.4-0.8份、聚乙烯醇0.6-1.5份、邻苯二甲酸二丁酯0.3-0.8份、十二烷基苯硫酸钠0.4-0.7份、聚醚0.4-0.9份、邻苯二甲酸二丁酯0.3-0.9份、聚丙烯铣铵0.2-0.7份、环己烷0.2-0.5份、尿素7-10份和硫酸铝0.3-0.8份。
2.根据权利要求1所述的一种新型建筑壳模板用高效粘合剂，其特征在于，按照重量份有以下原料组成：聚乙烯醇0.3-0.7份、来苏糖4-8份、二甲酸二乙酯0.3-0.7份、改性海藻酸纤维4-7份、聚乙烯醇0.3-0.7份、六亚甲基四胺0.2-0.4份、碳酸氢钠0.2-0.5份、石蜡2-5份、碳酸钙0.8-1.4份、聚乙烯醇0.6-1.1份、聚醋酸乙烯酯乳液4-9份、化学助剂5-9份、邻苯二甲酸二丁酯10-18份、过硫酸铵0.3-0.7份、碳酸氢钠0.7-1.1份、乙酸丁酯0.4-0.7份、聚乙烯醇0.6-1.4份、邻苯二甲酸二丁酯0.3-0.7份、十二烷基苯硫酸钠0.4-0.6份、聚醚0.4-0.8份、邻苯二甲酸二丁酯0.3-0.8份、聚丙烯铣铵0.2-0.6份、环己烷0.2-0.4份、尿素7-9份和硫酸铝0.3-0.7份。
3.根据权利要求1所述的一种新型建筑壳模板用高效粘合剂，其特征在于，按照重量份有以下原料组成：聚乙烯醇0.4-0.7份、来苏糖5-8份、二甲酸二乙酯0.4-0.7份、改性海藻酸纤维5-7份、聚乙烯醇0.4-0.7份、六亚甲基四胺0.3-0.4份、碳酸氢钠0.3-0.5份、石蜡3-5份、碳酸钙0.9-1.4份、聚乙烯醇0.7-1.1份、聚醋酸乙烯酯乳液5-9份、化学助剂6-9份、邻苯二甲酸二丁酯11-18份、过硫酸铵0.4-0.7份、碳酸氢钠0.8-1.1份、乙酸丁酯0.5-0.7份、聚乙烯醇0.7-1.4份、邻苯二甲酸二丁酯0.4-0.7份、十二烷基苯硫酸钠0.5-0.6份、聚醚0.5-0.8份、邻苯二甲酸二丁酯0.4-0.8份、聚丙烯铣铵0.3-0.6份、环己烷0.3-0.4份、尿素8-9份和硫酸铝0.4-0.7份。
4.根据权利要求1所述的一种新型建筑壳模板用高效粘合剂，其特征在于，按照重量份有以下原料组成：聚乙烯醇0.55份、来苏糖6.5份、二甲酸二乙酯0.55份、改性海藻酸纤维6份、聚乙烯醇0.55份、六亚甲基四胺0.35份、碳酸氢钠0.4份、石蜡4份、碳酸钙1.15份、聚乙烯醇0.9份、聚醋酸乙烯酯乳液7份、化学助剂7.5、邻苯二甲酸二丁酯14.5份、过硫酸铵0.55份、碳酸氢钠0.95份、乙酸丁酯0.6份、聚乙烯醇1.05份、邻苯二甲酸二丁酯0.55份、十二烷基苯硫酸钠0.55份、聚醚0.65份、邻苯二甲酸二丁酯0.6份、聚丙烯铣铵0.45份、环己烷0.35份、尿素8.5份和硫酸铝0.55份。
CN201810492117.4A 2018-05-22 2018-05-22 一种新型建筑壳模板用高效粘合剂 Withdrawn CN108587524A (zh)