CN108559676A - 一种通用玻璃清洁剂及其制备方法 - Google Patents
一种通用玻璃清洁剂及其制备方法 Download PDFInfo
- Publication number
- CN108559676A CN108559676A CN201810453285.2A CN201810453285A CN108559676A CN 108559676 A CN108559676 A CN 108559676A CN 201810453285 A CN201810453285 A CN 201810453285A CN 108559676 A CN108559676 A CN 108559676A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- preparation
- zeolite powder
- glass cleaner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种通用玻璃清洁剂及其制备方法，由以下成分制备而成：改性硅藻土、改性沸石粉、月桂酸二乙醇酰胺、云母粉、硫酸钠、海藻酸钠、去污溶液、烷基苯磺酸钠、羟甲基纤维素钠、聚乙二醇、硅酸钙、苯甲酸钠和去离子水。本发明制备的清洁剂清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，适合推广生产。
Description
技术领域
本发明属于清洁剂制作技术领域，具体涉及一种通用玻璃清洁剂及其制备方法。
背景技术
玻璃制品在生活中的应用越来越多，玻璃的表面也会附着很多污垢，污垢的主要成分为泥沙、灰尘、树胶、虫胶、汽柴油燃烧产生的油垢、昆虫遗体等。泥沙、灰尘可由水洗净，但油垢、动植物胶质很难被水洗净，必须用含有有机溶剂的液体将难以祛除的污垢溶解后，再用大量清水冲洗才能完全祛除；现有的用于清洗玻璃的清洁剂中，具有很强的异味，在清洗玻璃表面上的污垢时，需要用大量的清水冲洗，造成水资源的浪费，且冲洗之后玻璃上还能看到很明面的水痕，需要用抹布擦干，增加了工作量；在清理干净之后很短的一段时间内，玻璃又会迅速吸附各类污垢，增加了清洗的频率。
目前的玻璃清洁剂，其有效成分是化工合成的各类表面活性剂和各类化工助剂配置而成的。在生产和使用过程中产生的废水均会对环境产生一定的污染。
综上所述，因此需要一种更好的玻璃清洗剂，来改善现有技术的不足。
发明内容
本发明的目的是提供一种通用玻璃清洁剂及其制备方法，本发明制备的清洁剂清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，值得推广生产。
本发明提供了如下的技术方案：
一种通用玻璃清洁剂，包括以下重量份的原料：改性硅藻土14-18份、改性沸石粉11-16份、月桂酸二乙醇酰胺8-12份、云母粉7-12份、硫酸钠6-13份、海藻酸钠6-12份、去污溶液12-17份、烷基苯磺酸钠7-14份、羟甲基纤维素钠8-13份、聚乙二醇7-11份、硅酸钙9-14份、苯甲酸钠5-9份和去离子水10-15份。
优选的，所述清洁剂包括以下重量份的原料：改性硅藻土14-16份、改性沸石粉13-16份、月桂酸二乙醇酰胺8-10份、云母粉9-12份、硫酸钠6-11份、海藻酸钠8-12份、去污溶液12-16份、烷基苯磺酸钠7-12份、羟甲基纤维素钠10-13份、聚乙二醇9-11份、硅酸钙9-12份、苯甲酸钠5-8份和去离子水10-14份。
优选的，所述清洁剂包括以下重量份的原料：改性硅藻土16份、改性沸石粉13份、月桂酸二乙醇酰胺10份、云母粉9份、硫酸钠11份、海藻酸钠8份、去污溶液16份、烷基苯磺酸钠7份、羟甲基纤维素钠13份、聚乙二醇11份、硅酸钙9份、苯甲酸钠5份和去离子水14份。
一种通用玻璃清洁剂的制备方法，包括以下制备步骤：
a、将改性硅藻土、烷基苯磺酸钠、羟甲基纤维素钠和去离子水混合，导入反应釜中加热至60-70℃，在140-200r/min的转速下搅拌反应10-15min，再加入硫酸钠、海藻酸钠和苯甲酸钠，持续搅拌20-25min，得到混合物一；
b、将改性沸石粉、云母粉和硅酸钙混合粉碎至过100-200目筛，再加入到聚乙二醇中，在60-70℃下加热反应30-50min，自然冷却至常温，得到混合物二；
c、向混合物二中加入月桂酸二乙醇酰胺、去污溶液，在50-55℃下超声分散30-40min，得到混合物三；
d、将混合物一、混合物三导入搅拌机中，升温至75-80℃搅拌30-40min，再持续搅拌直至自然冷却至室温，即可得到成品。
优选的，所述步骤a的改性硅藻土的制备方法为：将硅藻土在600-700℃下焙烧2-3h，再磨成粉末，用质量分数为20-25％的双氧水浸泡2-4h，用去离子水洗涤，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散20-30min，经干燥、研细，即得改性硅藻土。
优选的，所述步骤b的改性沸石粉的制备方法为：将沸石粉用水冲洗，去除可溶性杂质，置于80-90℃下干燥1-2h，再与改性剂混合，搅拌反应20-24h，过滤，将沸石粉用水冲洗至中性，进行超声分散，再置于90-100℃下干燥2-4h，即可得到改性沸石粉。
优选的，所述改性剂为氯化钠与氢氧化钠溶液按质量比2:3混合而成。
优选的，所述步骤c的去污溶液的制备方法为：将牛油果、甘油和皂荚油混合均匀，加入苯酚和水，充分搅拌均匀，再滴加氨水，调节pH值为9-10，即可得到去污溶液。
本发明的有益效果是：
本发明制备的清洁剂清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，值得推广生产。
本发明中加入的烷基苯磺酸钠、月桂酸二乙醇酰胺、海藻酸钠和苯甲酸钠成分，能够降低液体表面张力并改变溶液体系界面状态，具有润湿、分散、气泡、渗透、去污、增溶等作用，能够让溶液具有更好的去污性能，加入的改性硅藻土、改性沸石粉、云母粉和硅酸钙，可进一步降低溶液的流动性，增加溶液粘度，降低溶液挥发速度，从而提高去污能力。
具体实施方式
实施例1
一种通用玻璃清洁剂，包括以下重量份的原料：改性硅藻土14份、改性沸石粉16份、月桂酸二乙醇酰胺8份、云母粉12份、硫酸钠13份、海藻酸钠6份、去污溶液17份、烷基苯磺酸钠14份、羟甲基纤维素钠8份、聚乙二醇11份、硅酸钙9份、苯甲酸钠5份和去离子水15份。
一种通用玻璃清洁剂的制备方法，包括以下制备步骤：
a、将改性硅藻土、烷基苯磺酸钠、羟甲基纤维素钠和去离子水混合，导入反应釜中加热至70℃，在200r/min的转速下搅拌反应10min，再加入硫酸钠、海藻酸钠和苯甲酸钠，持续搅拌20min，得到混合物一；
b、将改性沸石粉、云母粉和硅酸钙混合粉碎至过100目筛，再加入到聚乙二醇中，在60℃下加热反应50min，自然冷却至常温，得到混合物二；
c、向混合物二中加入月桂酸二乙醇酰胺、去污溶液，在55℃下超声分散30min，得到混合物三；
d、将混合物一、混合物三导入搅拌机中，升温至75℃搅拌40min，再持续搅拌直至自然冷却至室温，即可得到成品。
步骤a的改性硅藻土的制备方法为：将硅藻土在700℃下焙烧2h，再磨成粉末，用质量分数为25％的双氧水浸泡2h，用去离子水洗涤，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散30min，经干燥、研细，即得改性硅藻土。
步骤b的改性沸石粉的制备方法为：将沸石粉用水冲洗，去除可溶性杂质，置于80℃下干燥2h，再与改性剂混合，搅拌反应24h，过滤，将沸石粉用水冲洗至中性，进行超声分散，再置于90℃下干燥2h，即可得到改性沸石粉。
改性剂为氯化钠与氢氧化钠溶液按质量比2:3混合而成。
步骤c的去污溶液的制备方法为：将牛油果、甘油和皂荚油混合均匀，加入苯酚和水，充分搅拌均匀，再滴加氨水，调节pH值为10，即可得到去污溶液。
实施例2
一种通用玻璃清洁剂，包括以下重量份的原料：改性硅藻土14份、改性沸石粉13份、月桂酸二乙醇酰胺8份、云母粉9份、硫酸钠6份、海藻酸钠8份、去污溶液12份、烷基苯磺酸钠7份、羟甲基纤维素钠10份、聚乙二醇9份、硅酸钙9份、苯甲酸钠5份和去离子水10份。
一种通用玻璃清洁剂的制备方法，包括以下制备步骤：
a、将改性硅藻土、烷基苯磺酸钠、羟甲基纤维素钠和去离子水混合，导入反应釜中加热至60℃，在140r/min的转速下搅拌反应10min，再加入硫酸钠、海藻酸钠和苯甲酸钠，持续搅拌25min，得到混合物一；
b、将改性沸石粉、云母粉和硅酸钙混合粉碎至过100目筛，再加入到聚乙二醇中，在60℃下加热反应30min，自然冷却至常温，得到混合物二；
c、向混合物二中加入月桂酸二乙醇酰胺、去污溶液，在50℃下超声分散30min，得到混合物三；
d、将混合物一、混合物三导入搅拌机中，升温至75℃搅拌30min，再持续搅拌直至自然冷却至室温，即可得到成品。
步骤a的改性硅藻土的制备方法为：将硅藻土在600℃下焙烧2h，再磨成粉末，用质量分数为20％的双氧水浸泡2h，用去离子水洗涤，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散20min，经干燥、研细，即得改性硅藻土。
步骤b的改性沸石粉的制备方法为：将沸石粉用水冲洗，去除可溶性杂质，置于80℃下干燥1h，再与改性剂混合，搅拌反应20h，过滤，将沸石粉用水冲洗至中性，进行超声分散，再置于90℃下干燥2h，即可得到改性沸石粉。
改性剂为氯化钠与氢氧化钠溶液按质量比2:3混合而成。
步骤c的去污溶液的制备方法为：将牛油果、甘油和皂荚油混合均匀，加入苯酚和水，充分搅拌均匀，再滴加氨水，调节pH值为9，即可得到去污溶液。
实施例3
一种通用玻璃清洁剂，包括以下重量份的原料：改性硅藻土16份、改性沸石粉13份、月桂酸二乙醇酰胺10份、云母粉9份、硫酸钠11份、海藻酸钠8份、去污溶液16份、烷基苯磺酸钠7份、羟甲基纤维素钠13份、聚乙二醇11份、硅酸钙9份、苯甲酸钠5份和去离子水14份。
一种通用玻璃清洁剂的制备方法，包括以下制备步骤：
a、将改性硅藻土、烷基苯磺酸钠、羟甲基纤维素钠和去离子水混合，导入反应釜中加热至70℃，在200r/min的转速下搅拌反应15min，再加入硫酸钠、海藻酸钠和苯甲酸钠，持续搅拌25min，得到混合物一；
b、将改性沸石粉、云母粉和硅酸钙混合粉碎至过200目筛，再加入到聚乙二醇中，在70℃下加热反应50min，自然冷却至常温，得到混合物二；
c、向混合物二中加入月桂酸二乙醇酰胺、去污溶液，在55℃下超声分散40min，得到混合物三；
d、将混合物一、混合物三导入搅拌机中，升温至80℃搅拌40min，再持续搅拌直至自然冷却至室温，即可得到成品。
步骤a的改性硅藻土的制备方法为：将硅藻土在700℃下焙烧3h，再磨成粉末，用质量分数为25％的双氧水浸泡4h，用去离子水洗涤，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散30min，经干燥、研细，即得改性硅藻土。
步骤b的改性沸石粉的制备方法为：将沸石粉用水冲洗，去除可溶性杂质，置于80℃下干燥2h，再与改性剂混合，搅拌反应24h，过滤，将沸石粉用水冲洗至中性，进行超声分散，再置于100℃下干燥4h，即可得到改性沸石粉。
改性剂为氯化钠与氢氧化钠溶液按质量比2:3混合而成。
步骤c的去污溶液的制备方法为：将牛油果、甘油和皂荚油混合均匀，加入苯酚和水，充分搅拌均匀，再滴加氨水，调节pH值为10，即可得到去污溶液。
检测以上实施例制备的成品，得到以下检测数据：
表一：
| 项目 | 实施例1 | 实施例2 | 实施例3 |
| 钢化玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持18天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持22天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持17天 |
| 夹胶玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持20天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持21天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持20天 |
| 中空玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持23天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持22天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持22天 |
| 防火玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持21天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持18天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持19天 |
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种通用玻璃清洁剂，其特征在于，包括以下重量份的原料：改性硅藻土14-18份、改性沸石粉11-16份、月桂酸二乙醇酰胺8-12份、云母粉7-12份、硫酸钠6-13份、海藻酸钠6-12份、去污溶液12-17份、烷基苯磺酸钠7-14份、羟甲基纤维素钠8-13份、聚乙二醇7-11份、硅酸钙9-14份、苯甲酸钠5-9份和去离子水10-15份。
2.根据权利要求1所述的一种通用玻璃清洁剂，其特征在于，所述清洁剂包括以下重量份的原料：改性硅藻土14-16份、改性沸石粉13-16份、月桂酸二乙醇酰胺8-10份、云母粉9-12份、硫酸钠6-11份、海藻酸钠8-12份、去污溶液12-16份、烷基苯磺酸钠7-12份、羟甲基纤维素钠10-13份、聚乙二醇9-11份、硅酸钙9-12份、苯甲酸钠5-8份和去离子水10-14份。
3.根据权利要求1所述的一种通用玻璃清洁剂，其特征在于，所述清洁剂包括以下重量份的原料：改性硅藻土16份、改性沸石粉13份、月桂酸二乙醇酰胺10份、云母粉9份、硫酸钠11份、海藻酸钠8份、去污溶液16份、烷基苯磺酸钠7份、羟甲基纤维素钠13份、聚乙二醇11份、硅酸钙9份、苯甲酸钠5份和去离子水14份。
4.权利要求1-3任一项所述的一种通用玻璃清洁剂的制备方法，其特征在于，包括以下制备步骤：
a、将改性硅藻土、烷基苯磺酸钠、羟甲基纤维素钠和去离子水混合，导入反应釜中加热至60-70℃，在140-200r/min的转速下搅拌反应10-15min，再加入硫酸钠、海藻酸钠和苯甲酸钠，持续搅拌20-25min，得到混合物一；
b、将改性沸石粉、云母粉和硅酸钙混合粉碎至过100-200目筛，再加入到聚乙二醇中，在60-70℃下加热反应30-50min，自然冷却至常温，得到混合物二；
c、向混合物二中加入月桂酸二乙醇酰胺、去污溶液，在50-55℃下超声分散30-40min，得到混合物三；
d、将混合物一、混合物三导入搅拌机中，升温至75-80℃搅拌30-40min，再持续搅拌直至自然冷却至室温，即可得到成品。
5.根据权利要求4所述的一种通用玻璃清洁剂的制备方法，其特征在于，所述步骤a的改性硅藻土的制备方法为：将硅藻土在600-700℃下焙烧2-3h，再磨成粉末，用质量分数为20-25％的双氧水浸泡2-4h，用去离子水洗涤，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散20-30min，经干燥、研细，即得改性硅藻土。
6.根据权利要求4所述的一种通用玻璃清洁剂的制备方法，其特征在于，所述步骤b的改性沸石粉的制备方法为：将沸石粉用水冲洗，去除可溶性杂质，置于80-90℃下干燥1-2h，再与改性剂混合，搅拌反应20-24h，过滤，将沸石粉用水冲洗至中性，进行超声分散，再置于90-100℃下干燥2-4h，即可得到改性沸石粉。
7.根据权利要求5所述的一种通用玻璃清洁剂的制备方法，其特征在于，所述改性剂为氯化钠与氢氧化钠溶液按质量比2:3混合而成。
8.根据权利要求4所述的一种通用玻璃清洁剂的制备方法，其特征在于，所述步骤c的去污溶液的制备方法为：将牛油果、甘油和皂荚油混合均匀，加入苯酚和水，充分搅拌均匀，再滴加氨水，调节pH值为9-10，即可得到去污溶液。