CN108865494A - 一种高效玻璃清洗剂及其制备方法 - Google Patents
一种高效玻璃清洗剂及其制备方法 Download PDFInfo
- Publication number
- CN108865494A CN108865494A CN201810853115.3A CN201810853115A CN108865494A CN 108865494 A CN108865494 A CN 108865494A CN 201810853115 A CN201810853115 A CN 201810853115A CN 108865494 A CN108865494 A CN 108865494A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- sodium
- cleaning agent
- highly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种高效玻璃清洗剂及其制备方法，由以下成分制备而成：改性沸石粉、十二烷基苯磺酸钠、羟甲基纤维素钠、改性膨润土、脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠、聚乙二醇溶液、去污剂、丙二醇、螯合剂、防腐剂和去离子水。本发明制备的玻璃清洗剂的清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，值得推广生产。
Description
技术领域
本发明属于玻璃清洗技术领域，具体涉及一种高效玻璃清洗剂及其制备方法。
背景技术
玻璃清洗剂，玻璃清洗剂是用于清洗玻璃表面的油污，其主要成分是表面活性剂，略带碱性或具中性。玻璃清洗剂其分子中同时具有亲水的极性基团与亲油的非极性基团，当它的加入量很少时，即能大大降低溶剂（一般是水）的表面张力以及液界面张力，并且具有润滑、增溶、乳化、分散和洗涤等作用。玻璃清洗剂在家庭生活及工业生产的清洗中，有广泛的用途。
玻璃制品在生活中的应用越来越多，玻璃的表面也会附着很多污垢，污垢的主要成分为泥沙、灰尘、树胶、虫胶、汽柴油燃烧产生的油垢、昆虫遗体等。泥沙、灰尘可由水洗净，但油垢、动植物胶质很难被水洗净，必须用含有有机溶剂的液体将难以祛除的污垢溶解后，再用大量清水冲洗才能完全祛除；现有的用于清洗玻璃的清洁剂中，具有很强的异味，在清洗玻璃表面上的污垢时，需要用大量的清水冲洗，造成水资源的浪费，且冲洗之后玻璃上还能看到很明面的水痕，需要用抹布擦干，增加了工作量；在清理干净之后很短的一段时间内，玻璃又会迅速吸附各类污垢，增加了清洗的频率。
目前的玻璃清洁剂，其有效成分是化工合成的各类表面活性剂和各类化工助剂配置而成的。在生产和使用过程中产生的废水均会对环境产生一定的污染。
公开号为CN106520391A，公开了一种玻璃多效清洁剂，该清洁剂所述各材料由以下组分按重量百分比配制而成：乙醇8-15％、脂肪醇聚氧乙烯醚8-12％、磷酸四钾4-8％、蔗糖脂肪酸钠4-8％、柠檬酸钠4-8％、异丙醇钛0.1-0.5％、聚氧乙烯篦麻籽油2- 4％、余量为去离子水。该发明的目的是提供一种具有杀菌功能，去污力强的玻璃多效清洁剂。但是该发明的防冻能力不佳，而且去污能力能进一步提高。
公开号为CN107057881A，公开了一种钢化玻璃用清洁剂及其制备方法，包括以下重量份的原料：酒精30-50份、异丙醇15-20份、乙二醇12-15份、环氧大豆油1-3份、香精4-6份、防冻剂5-8份、缓蚀剂0.1-0.5份、表面活性剂0.2-1.5份、水70-80份；表面活性剂包括十二烷基二甲基氧化胺、乙二醇单丁醚、烷基醇酰胺和土耳其红油，三者之间的重量比为2.5:1:1:1.5。制备方法包括以下步骤：（1）、按上述重量份称取各种原料；（2）、将上述原料依次加入到搅拌机内搅拌8-10min，然后静置1-2h，得到混合液；（3）、测量混合液的pH，调节pH为7-8。该现有技术提供的清洁剂虽然具有了一定的防冻能力，但是其清洁效果有限，并且适用范围窄。
综上所述，因此需要一种更好的玻璃清洗剂，来改善现有技术的不足。
发明内容
本发明的目的是提供一种高效玻璃清洗剂及其制备方法，本发明制备的玻璃清洗剂的清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，值得推广生产。
本发明提供了如下的技术方案：
一种高效玻璃清洗剂，包括以下重量份的原料：改性沸石粉7-12份、十二烷基苯磺酸钠6-9份、羟甲基纤维素钠5-8份、改性膨润土8-11份、脂肪醇聚氧乙烯醚8-13份、海藻酸钠6-9份、柠檬酸钠5-9份、聚乙二醇溶液10-14份、去污剂8-14份、丙二醇5-9份、螯合剂4-8份、防腐剂3-6份和去离子水10-15份。
优选的，所述清洗剂包括以下重量份的原料：改性沸石粉9-12份、十二烷基苯磺酸钠6-8份、羟甲基纤维素钠5-7份、改性膨润土9-11份、脂肪醇聚氧乙烯醚11-13份、海藻酸钠7-9份、柠檬酸钠5-8份、聚乙二醇溶液10-13份、去污剂12-14份、丙二醇5-8份、螯合剂5-8份、防腐剂3-5份和去离子水13-15份。
优选的，所述清洗剂包括以下重量份的原料：改性沸石粉11份、十二烷基苯磺酸钠7份、羟甲基纤维素钠6份、改性膨润土10份、脂肪醇聚氧乙烯醚12份、海藻酸钠8份、柠檬酸钠7份、聚乙二醇溶液12份、去污剂13份、丙二醇7份、螯合剂7份、防腐剂4份和去离子水14份。
一种高效玻璃清洗剂的制备方法，包括以下制备步骤：
a、将改性沸石粉、丙二醇和去离子水混合，导入反应釜中，在70-74℃下加热并搅拌28-32min，反应结束后，得到混合物一；
b、向混合物一中依次加入十二烷基苯磺酸钠、羟甲基纤维素钠和改性膨润土，在58-61℃下，以350-380r/min的转速搅拌反应1.2-1.4h，再加入去污剂，缓慢搅拌混合5-10min，得到混合物二；
c、将脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠和聚乙二醇溶液混合，在均质机中进行匀质处理8-12min，得到混合物三；
d、将混合物二、混合物三、螯合剂和防腐剂混合搅拌均匀，进行离心分散处理10-15min，过滤除杂，即可得到成品。
优选的，所述步骤a的改性沸石粉的制备方法为：将沸石粉用水冲洗干净，置于82℃下干燥18min，再加入质量浓度为20%的氯化钠溶液与质量浓度为12%的氢氧化钠溶液的混合溶液，继续搅拌反应0.6h，过滤后，将沸石粉用蒸馏水冲洗至中性，再粉碎成纳米颗粒，置于70℃下干燥22min，即可得到改性沸石粉。
优选的，所述氯化钠溶液与氢氧化钠溶液按质量比1:3混合。
优选的，所述步骤b的改性膨润土的制备方法为：将膨润土粉末在750℃下焙烧3.8h，再用质量浓度为28%的双氧水浸泡1.5h，之后用去离子水冲洗，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散15min，经干燥、研细，即得改性膨润土。
优选的，所述步骤b的去污剂的制备方法为：将甲基丙烯酸甲酯、甘油和羧酸盐混合均匀，在65℃下加热反应1.6h，再加入苯酚和水，充分搅拌均匀，之后滴加氨水，调节pH值为9，即可得到去污剂。
优选的，所述步骤c的匀质处理的方法为：在4MPa的压力下，以200r/min的速度搅拌。
优选的，所述步骤d的防腐剂为1,2-苯并异噻唑啉-3-酮和聚六亚甲基胍按质量比2:5混合而成。
本发明的有益效果是：
本发明制备的玻璃清洗剂的清洁效果效果显著，制备方法简单，适用范围广，且不存在任何异味，对人体无任何危害，不需要用大量清水冲洗，节省了大量人力和物力，值得推广生产。
本发明中的改性沸石粉和改性膨润土，二者的协同作用下，有利于进一步降低制备的成品的流动性，增加溶液粘度，降低溶液挥发速度，从而提高去污能力。
本发明中的去污剂具有优异的增溶、增稠、乳化、起泡、稳泡、柔软、保湿、抗静电，对人体皮肤无刺激性，生理毒性小，易生物降解，其中的甘油成分，具有优良的渗透性、扩散性和润湿性，可使得制备的去污剂具有良好的相容性。
本发明中的匀质处理的方法有利于促进原料之间的混合，提高混合效率。
本发明中的海藻酸钠、柠檬酸钠，能够降低液体表面张力并改变溶液体系界面状态，具有润湿、分散、气泡、渗透、去污、增溶的作用。
本发明中的丙二醇、脂肪醇聚氧乙烯醚能有效地降低成品的凝固点，防止清洗剂不易结冻。
具体实施方式
实施例1
一种高效玻璃清洗剂，包括以下重量份的原料：改性沸石粉12份、十二烷基苯磺酸钠9份、羟甲基纤维素钠5份、改性膨润土8份、脂肪醇聚氧乙烯醚8份、海藻酸钠9份、柠檬酸钠5份、聚乙二醇溶液14份、去污剂14份、丙二醇5份、螯合剂8份、防腐剂3份和去离子水10份。
一种高效玻璃清洗剂的制备方法，包括以下制备步骤：
a、将改性沸石粉、丙二醇和去离子水混合，导入反应釜中，在70℃下加热并搅拌32min，反应结束后，得到混合物一；
b、向混合物一中依次加入十二烷基苯磺酸钠、羟甲基纤维素钠和改性膨润土，在61℃下，以380r/min的转速搅拌反应1.4h，再加入去污剂，缓慢搅拌混合5min，得到混合物二；
c、将脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠和聚乙二醇溶液混合，在均质机中进行匀质处理12min，得到混合物三；
d、将混合物二、混合物三、螯合剂和防腐剂混合搅拌均匀，进行离心分散处理15min，过滤除杂，即可得到成品。
步骤a的改性沸石粉的制备方法为：将沸石粉用水冲洗干净，置于82℃下干燥18min，再加入质量浓度为20%的氯化钠溶液与质量浓度为12%的氢氧化钠溶液的混合溶液，继续搅拌反应0.6h，过滤后，将沸石粉用蒸馏水冲洗至中性，再粉碎成纳米颗粒，置于70℃下干燥22min，即可得到改性沸石粉。
氯化钠溶液与氢氧化钠溶液按质量比1:3混合。
步骤b的改性膨润土的制备方法为：将膨润土粉末在750℃下焙烧3.8h，再用质量浓度为28%的双氧水浸泡1.5h，之后用去离子水冲洗，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散15min，经干燥、研细，即得改性膨润土。
步骤b的去污剂的制备方法为：将甲基丙烯酸甲酯、甘油和羧酸盐混合均匀，在65℃下加热反应1.6h，再加入苯酚和水，充分搅拌均匀，之后滴加氨水，调节pH值为9，即可得到去污剂。
步骤c的匀质处理的方法为：在4MPa的压力下，以200r/min的速度搅拌。
步骤d的防腐剂为1,2-苯并异噻唑啉-3-酮和聚六亚甲基胍按质量比2:5混合而成。
实施例2
一种高效玻璃清洗剂，包括以下重量份的原料：改性沸石粉12份、十二烷基苯磺酸钠8份、羟甲基纤维素钠5份、改性膨润土9份、脂肪醇聚氧乙烯醚11份、海藻酸钠7份、柠檬酸钠8份、聚乙二醇溶液13份、去污剂14份、丙二醇8份、螯合剂8份、防腐剂3份和去离子水13份。
一种高效玻璃清洗剂的制备方法，包括以下制备步骤：
a、将改性沸石粉、丙二醇和去离子水混合，导入反应釜中，在74℃下加热并搅拌32min，反应结束后，得到混合物一；
b、向混合物一中依次加入十二烷基苯磺酸钠、羟甲基纤维素钠和改性膨润土，在58℃下，以350r/min的转速搅拌反应1.4h，再加入去污剂，缓慢搅拌混合5min，得到混合物二；
c、将脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠和聚乙二醇溶液混合，在均质机中进行匀质处理8min，得到混合物三；
d、将混合物二、混合物三、螯合剂和防腐剂混合搅拌均匀，进行离心分散处理10min，过滤除杂，即可得到成品。
步骤a的改性沸石粉的制备方法为：将沸石粉用水冲洗干净，置于82℃下干燥18min，再加入质量浓度为20%的氯化钠溶液与质量浓度为12%的氢氧化钠溶液的混合溶液，继续搅拌反应0.6h，过滤后，将沸石粉用蒸馏水冲洗至中性，再粉碎成纳米颗粒，置于70℃下干燥22min，即可得到改性沸石粉。
氯化钠溶液与氢氧化钠溶液按质量比1:3混合。
步骤b的改性膨润土的制备方法为：将膨润土粉末在750℃下焙烧3.8h，再用质量浓度为28%的双氧水浸泡1.5h，之后用去离子水冲洗，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散15min，经干燥、研细，即得改性膨润土。
步骤b的去污剂的制备方法为：将甲基丙烯酸甲酯、甘油和羧酸盐混合均匀，在65℃下加热反应1.6h，再加入苯酚和水，充分搅拌均匀，之后滴加氨水，调节pH值为9，即可得到去污剂。
步骤c的匀质处理的方法为：在4MPa的压力下，以200r/min的速度搅拌。
步骤d的防腐剂为1,2-苯并异噻唑啉-3-酮和聚六亚甲基胍按质量比2:5混合而成。
实施例3
一种高效玻璃清洗剂，包括以下重量份的原料：改性沸石粉11份、十二烷基苯磺酸钠7份、羟甲基纤维素钠6份、改性膨润土10份、脂肪醇聚氧乙烯醚12份、海藻酸钠8份、柠檬酸钠7份、聚乙二醇溶液12份、去污剂13份、丙二醇7份、螯合剂7份、防腐剂4份和去离子水14份。
一种高效玻璃清洗剂的制备方法，包括以下制备步骤：
a、将改性沸石粉、丙二醇和去离子水混合，导入反应釜中，在74℃下加热并搅拌28min，反应结束后，得到混合物一；
b、向混合物一中依次加入十二烷基苯磺酸钠、羟甲基纤维素钠和改性膨润土，在58℃下，以380r/min的转速搅拌反应1.2h，再加入去污剂，缓慢搅拌混合10min，得到混合物二；
c、将脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠和聚乙二醇溶液混合，在均质机中进行匀质处理8min，得到混合物三；
d、将混合物二、混合物三、螯合剂和防腐剂混合搅拌均匀，进行离心分散处理15min，过滤除杂，即可得到成品。
步骤a的改性沸石粉的制备方法为：将沸石粉用水冲洗干净，置于82℃下干燥18min，再加入质量浓度为20%的氯化钠溶液与质量浓度为12%的氢氧化钠溶液的混合溶液，继续搅拌反应0.6h，过滤后，将沸石粉用蒸馏水冲洗至中性，再粉碎成纳米颗粒，置于70℃下干燥22min，即可得到改性沸石粉。
氯化钠溶液与氢氧化钠溶液按质量比1:3混合。
步骤b的改性膨润土的制备方法为：将膨润土粉末在750℃下焙烧3.8h，再用质量浓度为28%的双氧水浸泡1.5h，之后用去离子水冲洗，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散15min，经干燥、研细，即得改性膨润土。
步骤b的去污剂的制备方法为：将甲基丙烯酸甲酯、甘油和羧酸盐混合均匀，在65℃下加热反应1.6h，再加入苯酚和水，充分搅拌均匀，之后滴加氨水，调节pH值为9，即可得到去污剂。
步骤c的匀质处理的方法为：在4MPa的压力下，以200r/min的速度搅拌。
步骤d的防腐剂为1,2-苯并异噻唑啉-3-酮和聚六亚甲基胍按质量比2:5混合而成。
对比例1
采用现有技术中的普通玻璃清洗剂来检测对比。
检测以上实施例和对比例制备的成品，得到以下检测数据：
表一：
| 项目 | 实施例1 | 实施例2 | 实施例3 | 对比例1 |
| 钢化玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持8天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持10天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持11天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持6天 |
| 夹胶玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持12天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持12天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持14天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持7天 |
| 中空玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持11天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持12天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持12天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持6天 |
| 防火玻璃 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持10天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持9天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持10天 | 清洗后光亮如新、无异味、冲水量少，清洁时间可维持6天 |
由表一所得的实验数据，可以得出，本发明的制备方法制备的成品的各项性能显著优异于现有技术中的普通产品，并且在本发明的实施例3中优选的制备方案，其得到的成品性能最为优异。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种高效玻璃清洗剂，其特征在于，包括以下重量份的原料：改性沸石粉7-12份、十二烷基苯磺酸钠6-9份、羟甲基纤维素钠5-8份、改性膨润土8-11份、脂肪醇聚氧乙烯醚8-13份、海藻酸钠6-9份、柠檬酸钠5-9份、聚乙二醇溶液10-14份、去污剂8-14份、丙二醇5-9份、螯合剂4-8份、防腐剂3-6份和去离子水10-15份。
2.根据权利要求1所述的一种高效玻璃清洗剂，其特征在于，所述清洗剂包括以下重量份的原料：改性沸石粉9-12份、十二烷基苯磺酸钠6-8份、羟甲基纤维素钠5-7份、改性膨润土9-11份、脂肪醇聚氧乙烯醚11-13份、海藻酸钠7-9份、柠檬酸钠5-8份、聚乙二醇溶液10-13份、去污剂12-14份、丙二醇5-8份、螯合剂5-8份、防腐剂3-5份和去离子水13-15份。
3.根据权利要求1所述的一种高效玻璃清洗剂，其特征在于，所述清洗剂包括以下重量份的原料：改性沸石粉11份、十二烷基苯磺酸钠7份、羟甲基纤维素钠6份、改性膨润土10份、脂肪醇聚氧乙烯醚12份、海藻酸钠8份、柠檬酸钠7份、聚乙二醇溶液12份、去污剂13份、丙二醇7份、螯合剂7份、防腐剂4份和去离子水14份。
4.权利要求1-3任一项所述的一种高效玻璃清洗剂的制备方法，其特征在于，包括以下制备步骤：
a、将改性沸石粉、丙二醇和去离子水混合，导入反应釜中，在70-74℃下加热并搅拌28-32min，反应结束后，得到混合物一；
b、向混合物一中依次加入十二烷基苯磺酸钠、羟甲基纤维素钠和改性膨润土，在58-61℃下，以350-380r/min的转速搅拌反应1.2-1.4h，再加入去污剂，缓慢搅拌混合5-10min，得到混合物二；
c、将脂肪醇聚氧乙烯醚、海藻酸钠、柠檬酸钠和聚乙二醇溶液混合，在均质机中进行匀质处理8-12min，得到混合物三；
d、将混合物二、混合物三、螯合剂和防腐剂混合搅拌均匀，进行离心分散处理10-15min，过滤除杂，即可得到成品。
5.根据权利要求4所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述步骤a的改性沸石粉的制备方法为：将沸石粉用水冲洗干净，置于82℃下干燥18min，再加入质量浓度为20%的氯化钠溶液与质量浓度为12%的氢氧化钠溶液的混合溶液，继续搅拌反应0.6h，过滤后，将沸石粉用蒸馏水冲洗至中性，再粉碎成纳米颗粒，置于70℃下干燥22min，即可得到改性沸石粉。
6.根据权利要求5所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述氯化钠溶液与氢氧化钠溶液按质量比1:3混合。
7.根据权利要求4所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述步骤b的改性膨润土的制备方法为：将膨润土粉末在750℃下焙烧3.8h，再用质量浓度为28%的双氧水浸泡1.5h，之后用去离子水冲洗，经烘干后，加入到硅烷偶联剂溶液中，进行超声分散15min，经干燥、研细，即得改性膨润土。
8.根据权利要求4所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述步骤b的去污剂的制备方法为：将甲基丙烯酸甲酯、甘油和羧酸盐混合均匀，在65℃下加热反应1.6h，再加入苯酚和水，充分搅拌均匀，之后滴加氨水，调节pH值为9，即可得到去污剂。
9.根据权利要求4所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述步骤c的匀质处理的方法为：在4MPa的压力下，以200r/min的速度搅拌。
10.根据权利要求4所述的一种高效玻璃清洗剂的制备方法，其特征在于，所述步骤d的防腐剂为1,2-苯并异噻唑啉-3-酮和聚六亚甲基胍按质量比2:5混合而成。